CN102189143A - ECAE (equal channel angular extrusion) based preparation method of ultrafine crystal NiTi shape memory alloy tube - Google Patents
ECAE (equal channel angular extrusion) based preparation method of ultrafine crystal NiTi shape memory alloy tube Download PDFInfo
- Publication number
- CN102189143A CN102189143A CN2011100720507A CN201110072050A CN102189143A CN 102189143 A CN102189143 A CN 102189143A CN 2011100720507 A CN2011100720507 A CN 2011100720507A CN 201110072050 A CN201110072050 A CN 201110072050A CN 102189143 A CN102189143 A CN 102189143A
- Authority
- CN
- China
- Prior art keywords
- niti
- memorial alloy
- alloy tube
- shape memory
- memory alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an ECAE (equal channel angular extrusion) based preparation method of an ultrafine crystal NiTi shape memory alloy tube. A metal core is inserted into a NiTi shape memory alloy tube blank to be shaped, then the NiTi shape memory alloy tube blank is enclosed in a metal covering, and the metal covering, the NiTi shape memory alloy tube blank and the metal core are simultaneously extruded to generate shear plastic deformation in an ECAE production tool consisting of male die and a female die, so as to realize grain refinement of the NiTi shape memory alloy tube blank. Based on the fundamental of the ECAE method, a preparation method of an ultrafine crystal NiTi shape memory alloy tube is provided by the invention, so that high quality ultrafine crystal NiTi shape memory alloy tube can be produced, and production costs of the ultrafine crystal NiTi shape memory alloy tube can be reduced substantially.
Description
Technical field
What the present invention relates to is a kind of ultra-fine brilliant preparation of pipes method, specifically a kind of method for preparing ultra-fine brilliant niti-shaped memorial alloy tubing based on the Equal Channel Angular Pressing technology.
Background technology
Niti-shaped memorial alloy tubing is since nineteen nineties comes out, obtain people's attention day by day in field of medical applications, especially aspect intervention inner chamber stent applications, because of it can bear bigger mechanical stress, has stronger radial support power, experiences bigger flexural deformation and have bigger resilience and the shape recovery capability, thereby shown good application prospects.Though niti-shaped memorial alloy tubing can adopt multiple manufacturing process to make, but different processing conditions can produce different influences for the microstructure of niti-shaped memorial alloy tubing (as the size of crystal grain, deformation texture, deformation twin etc.), thereby the further SME and the load deflection mechanical behavior that influence niti-shaped memorial alloy tubing of meeting, especially suitable phase transition temperature and good super-elasticity are the important assurances that nickel-titanium shape memory tubing is applied at biomedical sector.
Equal Channel Angular Pressing (ECAE or ECAP) technology is a kind of advanced technology that obtains super fine crystal material, this technology is the passage that equates by two axes intersect and cross sectional dimensions, machined material is extruded, made metal material produce the purpose that big shear strain realizes crystal grain thinning by the corner effect.This technology has also obtained application at present in niti-shaped memorial alloy.Document Principles of equal-channel angular pressing as a processing tool for grain refinement (Ruslan Z.Valiev, Terence G.Langdon. " Progress in Materials Science " .2006,51:881-981) with Nanostructured TiNi-based shape memory alloys processed by severe plastic deformation (V.G.Pushin, V.V.Stolyarov, R.Z.Valiev et al. " Materials Science and Engineering A " .2005,410-411:386-389), reported that two kinds of compositions (are respectively Ni
50.2Ti
49.8, Ni
50.6Ti
49.4) the ECAE technology of niti-shaped memorial alloy block materials, the grain refinement that can be 80 μ m with average-size after solution treatment is that average-size is the ultra-fine grain of 250nm, make the yield strength of alloy improve 2 times, tensile strength has improved 30%, has also significantly improved the SME and the super-elasticity of niti-shaped memorial alloy.But present ECAE technology generally can only be used for preparing the block materials (circle or square-section) with ultra-fine grain, can not directly prepare the tubing with ultra-fine grain.Though at publication number is in the patent documentation of CN2690068Y, proposed a kind of device for preparing ultra-fine grain tubing, but owing to have plug on its device, fixing being difficult to of plug realized in the specific implementation, thereby, must on the extruder of special use, carry out the having relatively high expectations of equipment.And since during Equal Channel Angular Pressing the inboard included angle and the outside angle ψ of mould inconsistent, the pipe tissue of a time shaping gained is inevitable inhomogeneous, must carry out multi-pass extrusion molding ability uniform formation, but because of this outer surface that installs used blank is the face of cylinder, the position of each passage is difficult to accurately determine during conversion direction, so be difficult to guarantee to obtain uniform tissue.In addition, because intensity height, hardening capacity are strong at a lower temperature, plasticity is poor for niti-shaped memorial alloy, so Equal Channel Angular Pressing having relatively high expectations of block nickel-titanium shape memory alloy material to equipment, when the ultra-fine brilliant niti-shaped memorial alloy block materials of manufacturing is used for preparing ultra-fine brilliant niti-shaped memorial alloy tubing again, production cost is greatly increased.
Summary of the invention
The purpose of this invention is to provide and a kind ofly can prepare uniform superfine crystalline grain niti-shaped memorial alloy tubing, and can significantly reduce the ultra-fine brilliant niti-shaped memorial alloy tube preparation method based on Equal Channel Angular Pressing of the production cost of ultra-fine brilliant niti-shaped memorial alloy tubing.
The object of the present invention is achieved like this:
Inside at the niti-shaped memorial alloy pipe that will be shaped is filled in metal-cored, then the niti-shaped memorial alloy pipe is enclosed in the metallic sheath, in the ECAE frock of forming by punch and die, to metallic sheath, niti-shaped memorial alloy pipe with metal-coredly push, produce the shearing plastic deformation simultaneously, realize the grain refinement of niti-shaped memorial alloy pipe.
The outer surface of described metallic sheath is regular polygon, metallic sheath, niti-shaped memorial alloy pipe and metal-cored finish a passage crimp after, change certain angle and carry out multi-pass crimp.
Described regular polygon is a kind of in square, regular hexagon, octagon or the dodecagon.
The invention has the advantages that:
1. this method only needs simple mould can realize directly pipe being made the tubing that interior tissue is a ultra-fine grain on common hydraulic press, and the even tissue unanimity of tubing inside.
2. the rotational angle of blank when setting the jacket cross sectional shape and set every time extruding, and can accurately locating by the plane of jacket outer surface, thus realize the homogeneous deformation of whole blank, guaranteed the uniformity of pipe interior tissue.
3. by violent detrusion, can realize that niti-shaped memorial alloy tubing interior microscopic organizes ultra-fineization of grain size, improve mechanical property and the SME and the super-elasticity of tubing greatly.
4. when adopting the inventive method to prepare niti-shaped memorial alloy tubing, the filling metal of pipe inside and outside jacket metal all adopt high-ductility and low intensive metal material, for the block niti-shaped memorial alloy Equal Channel Angular Pressing of difficulty distortion, can significantly reduce resistance of deformation, the niti-shaped memorial alloy pipe is in the three-dimensional compressive stress state simultaneously, help improving the plasticity of material, therefore can obtain bigger distortion, and pipe is difficult for breaking.
The present invention is based on the basic principle of Equal Channel Angular Pressing, a kind of method for preparing ultra-fine brilliant niti-shaped memorial alloy tubing has been proposed, the ultra-fine brilliant niti-shaped memorial alloy tubing of high-quality can be produced, and the production cost of ultra-fine brilliant niti-shaped memorial alloy tubing will be significantly reduced.
Description of drawings
Fig. 1 adopts Equal Channel Angular Pressing technology jacket to prepare the basic principle schematic of ultra-fine grain niti-shaped memorial alloy tubing method.
The adoptable cross sectional shape of Fig. 2 a-Fig. 2 d metallic sheath.
Fig. 3 wrapping structure schematic diagram.
Fig. 4 extrusion process used for forming schematic diagram.
The specific embodiment
For example the present invention is done more detailed description below in conjunction with accompanying drawing:
In conjunction with Fig. 1, the basic principle for preparing ultra-fine grain niti-shaped memorial alloy tubing method based on Equal Channel Angular Pressing technology jacket of the present invention is: the inside at the niti-shaped memorial alloy pipe 4 that will be shaped fills in metal-cored 5, it is enclosed in the metallic sheath 3 then, utilize ECAE frock (forming) that metallic sheath 3 and inner metal pipe 4 and filling metal 5 thereof are sheared plastic deformation simultaneously greatly, realize the grain refinement of niti-shaped memorial alloy pipe by punch 1 and die 6.Because the metal-cored and outside jacket metal of metal pipe inside all adopts high-ductility and low intensive metal material, for the block niti-shaped memorial alloy ECAE of difficulty distortion, can significantly reduce its resistance of deformation, the niti-shaped memorial alloy pipe is in the three-dimensional compressive stress state simultaneously, help improving the plasticity of material, therefore can obtain bigger distortion, and pipe is difficult for breaking.
By ultra-fine grain niti-shaped memorial alloy preparation of pipes schematic diagram shown in Figure 1 as can be known, because the inboard included angle and the outside angle ψ of mould are inconsistent during Equal Channel Angular Pressing, can cause suffered shearing force size inhomogeneous everywhere, thereby make that the blank tissue odds of an extrusion molding gained is even.Therefore, in order to obtain to have the tubing of uniform superfine crystalline grain, blank must be changed certain angle and carry out multi-pass crimp.In order accurately to locate the angle that blank is changed, the employing Equal Channel Angular Pressing technology jacket that the present invention proposes prepares the cross sectional shape (shown in Fig. 2 a-Fig. 2 d) that the used jacket of ultra-fine grain niti-shaped memorial alloy tubing method can adopt multiple regular polygon, the concrete jacket of selecting which kind of cross section, to determine according to the degree of refinement of material grains, as the less passage of need, can select square or regular hexagonal section for use, as need than multi-pass, can select octagon or dodecagon cross section for use, can make the more multi-section position of pipe obtain maximum shear strain like this, thereby realize the even refinement of crystal grain.
Specific implementation process of the present invention is divided into three phases, i.e. preparatory stage, deformation stage and go the material stage.
Preparatory stage: in conjunction with figure, at first the cross sectional shape that ready sheath material is processed into as shown in Figure 2 (is got wherein a kind of, decide on arts demand, here with the square sectional example), then in one of place, its axle center processing and the identical blind hole of niti-shaped memorial alloy pipe 4 external diameter nominal sizes that will prepare, the assurance pipe can be put in the hole, and hole depth will exceed the height of niti-shaped memorial alloy pipe 4, reserves one section space and is used to dose metal plug 2; Then the outer surface in the niti-shaped memorial alloy pipe 4 that processes and metal-cored 5 all applies the last layer metal material, preventing, and fill in the pipe 4 metal-cored 5 because of each layer intermetallic generation seam influences the later separation work of niti-shaped memorial alloy pipe with jacket metal and core metal; Again populated metal-cored 5 pipe 4 is put into metallic sheath 3; Block with the aperture of metal plug 5 at last metallic sheath 3 upper ends.
Deformation stage: in conjunction with Fig. 4, the composite blank for preparing is put into the hole of die, the mould and the blank integral body that will be fixed on the hydraulic press by heater are heated to uniform temperature and are incubated certain hour, start hydraulic press then and carry out the extrusion molding first time, after extrusion molding finishes for the first time, note blank which face up, and carry out mark; Then the hole of putting into die behind this blank half-twist is again carried out the extruding second time, also will carry out mark after the end that is shaped; Use again with quadrat method and finish the 3rd, the 4th time of back extruding, even four faces of blank all carry out crimp towards the last time.
The discharging stage: after extrusion process used for forming is finished, adopt proper method that metallic sheath 3 is cut open, and from pipe, take out with metal-cored 5.
So just finished the preparation process of whole ultra-fine brilliant niti-shaped memorial alloy pipe.
Claims (3)
1. ultra-fine brilliant niti-shaped memorial alloy tube preparation method based on Equal Channel Angular Pressing, it is characterized in that: the inside at the niti-shaped memorial alloy pipe that will be shaped is filled in metal-cored, then the niti-shaped memorial alloy pipe is enclosed in the metallic sheath, in the ECAE frock of forming by punch and die, to metallic sheath, niti-shaped memorial alloy pipe with metal-coredly push, produce the shearing plastic deformation simultaneously, realize the grain refinement of niti-shaped memorial alloy pipe.
2. the ultra-fine brilliant niti-shaped memorial alloy tube preparation method based on Equal Channel Angular Pressing according to claim 1, it is characterized in that: the outer surface of described metallic sheath is regular polygon, metallic sheath, niti-shaped memorial alloy pipe and metal-cored finish a passage crimp after, change certain angle and carry out multi-pass crimp.
3. the ultra-fine brilliant niti-shaped memorial alloy tube preparation method based on Equal Channel Angular Pressing according to claim 2 is characterized in that: described regular polygon is a kind of in square, regular hexagon, octagon or the dodecagon.