CN102101105A - 一种新的木门涂装方法 - Google Patents

一种新的木门涂装方法 Download PDF

Info

Publication number
CN102101105A
CN102101105A CN2009102013274A CN200910201327A CN102101105A CN 102101105 A CN102101105 A CN 102101105A CN 2009102013274 A CN2009102013274 A CN 2009102013274A CN 200910201327 A CN200910201327 A CN 200910201327A CN 102101105 A CN102101105 A CN 102101105A
Authority
CN
China
Prior art keywords
priming paint
look
paint
adopt
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009102013274A
Other languages
English (en)
Inventor
王向科
邓静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Fuchen Chemical Co Ltd
Original Assignee
Shanghai Fuchen Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Fuchen Chemical Co Ltd filed Critical Shanghai Fuchen Chemical Co Ltd
Priority to CN2009102013274A priority Critical patent/CN102101105A/zh
Publication of CN102101105A publication Critical patent/CN102101105A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种新的木门涂装方法,包括如下步骤:(1)将基材用砂纸打磨处理,除尘;(2)施工UV真空喷涂底漆(根据涂装要求确定施工遍数),并经紫外光固化;(3)UV底漆砂光后,喷涂PU修色面漆;(4)轻砂后,喷涂PU面,干燥完全后即可获得成品。本发明优点:UV真空喷涂底漆涂装时无VOC排放、提高板面硬度、大幅度提高生产率和市场竞争力,同时节约生产场地。

Description

一种新的木门涂装方法
技术领域
[0001] 本发明涉及一种新的木门涂装方法。 背景技术
[0002] 随着人们生活水平日益提高,木门的更新换代的越来越快,市场需求量与日俱增。 传统的木门底漆涂装以聚氨酯涂料(PU)为主,普遍存在VOC较大、涂层薄、硬度低、效率低、 生产场地大等问题,因此家俱业界迫切需要新的工艺替代现有的生产模式来满足大规模提 高效率的生产需求。
发明内容
[0003] 本发明的目的在于克服上述缺陷,提供一种新的木门涂装方法。
[0004] 本发明的方法,包括如下步骤:
[0005] (1)将基材用240#砂纸打磨处理,除尘;
[0006] (2)施工UV真空喷涂底漆,50°C红外加热流平后过紫外灯固化(半固化紫外灯能 量为120〜150mj/cm2,全固化紫外灯能量为200〜250mj/cm2);
[0007] (3)按着色要求PU修色,待干1〜2小时;
[0008] (4)将修色层用1000#砂纸轻抛,均勻喷涂PU面漆(25°C,施工粘度为:岩田2号 杯,12〜13¾,完全干燥后获得涂装产品。
[0009] 所述UV真空喷涂底漆可采用市售产品,如上海富臣化工UV真空喷涂底漆 VU2110B ;
[0010] 所述PU修色面漆可采用市售产品,如上海富臣化工PU修色面漆V500 ;
[0011] 所述PU面漆可采用市售产品,如上海富臣化工PU七分哑光清面漆V517E面漆;
[0012] 本发明步骤⑴的目的是除去基材上的垃圾、灰尘,以达到平整干净;
[0013] 步骤O)的专用UV真空喷涂底漆是为了快速获得底漆涂层;
[0014] 步骤(3)的目的按要求着色;
[0015] 步骤的目的获得手感良好的哑光面漆。
[0016] 本发明优点:底漆涂装时无VOC排放,板面硬度高、大幅度提高生产率和市场竞争 力,同时节约生产场地。
具体实施方式
[0017] 以下实施例中,所述UV真空喷涂底漆可采用市售产品,如上海富臣化工UV真空喷 涂底漆VU2110B ;
[0018] 所述PU修色面漆可采用市售产品,如上海富臣化工PU修色面漆V500 ;
[0019] 所述PU面漆可采用市售产品,如上海富臣化工PU七分哑光清面漆V517E面漆;
[0020] 实施例1
[0021] (1)将橡木或水曲柳板用600#砂纸打磨处理,除尽灰尘;[0022] (2)用真空喷涂机喷涂UV真空喷涂底漆,涂布量:100〜120g/m2,(可采用市售产 品,如上海富臣化工UV真空喷涂底漆VU2110B),50°C红外流平2〜3分钟后,将紫外灯能量 调至MOmj/cm2,过紫外灯全固化;
[0023] (3)将底漆用320#砂纸砂光平整后,按着色要求加入适量色精进行PU修色(可采 用市售产品,如上海富臣化工PU修色面漆V500);
[0024] (4)PU修色面漆待干1小时后,将修色层用1000#砂纸轻抛,均勻喷涂PU面漆 (25°C,施工粘度为:岩田2号杯12〜13S) —度半,(可采用市售产品,如上海富臣化工PU 七分哑光清面漆V517E面漆),待PU面漆完全干透后,即获得半开放哑光涂装效果的成品。
[0025] 采用GB/T18581 VOC测定法,检测UV真空喷涂底漆的VOC,结果如下:
[0026]
Figure CN102101105AD00041
[0027] 采用GB/T9286-88附着力划格测定法,检测成品附着力,结果如下:
[0028]
Figure CN102101105AD00042
[0029] 采用GB/T6739-1996涂膜硬度铅笔测定法,检测成品硬度,结果如下:
Figure CN102101105AD00043
[0031] 所述半干,指的是触感是用手指接触略为粘手,但不粘灰尘等垃圾。
[0032] 实施案例2
[0033] (1)将橡木或水曲柳板用600#砂纸打磨处理,除尽灰尘;
[0034] (2)用真空喷涂机喷涂UV真空喷涂底漆,涂布量:60〜80g/m2,(可采用市售产品, 如上海富臣化工UV真空喷涂底漆VU2110B),50°C红外流平2〜3分钟后,将紫外灯能量调 至120mj/cm2,过紫外灯半固化;用真空喷涂机喷涂UV真空喷涂底漆,涂布量:60〜80g/m2, (可采用市售产品,如上海富臣化工UV真空喷涂底漆VU2110B),50°C红外流平2〜3分钟 后,将紫外灯能量调至250mj/cm2,过紫外灯全固化;将底漆用320#砂纸砂光平整后,用真 空喷涂机喷涂UV真空喷涂底漆,涂布量:100〜120g/m2,(可采用市售产品,如上海富臣化 工UV真空喷涂底漆VU2110B),50°C红外流平2〜3分钟后,将紫外灯能量调至MOmj/cm2, 过紫外灯全固化。
[0035] (3)将底漆用320#砂纸砂光平整后,按着色要求加入适量色精进行PU修色(可采 用市售产品,如上海富臣化工PU修色面漆V500);
[0036] (4)PU修色面漆待干1小时后,将修色层用1000#砂纸轻抛,均勻喷涂PU面漆(25°C,施工粘度为:岩田2号杯12〜13S)两度,(可采用市售产品,如上海富臣化工PU七 分哑光清面漆V517E面漆),待PU面漆完全干透后,即获得全封闭哑光涂装效果的成品。
[0037] 采用GB/T18581 VOC测定法,检测UV真空喷涂底漆的V0C,结果如下:
[0038]
Figure CN102101105AD00051
[0039] 采用GB/T9286-88附着力划格测定法,检测成品附着力,结果如下:
[0040]
Figure CN102101105AD00052
[0041] 采用GB/T6739-1996涂膜硬度铅笔测定法,检测成品硬度,结果如下:
[0042]
Figure CN102101105AD00053
[0043] 实施例3
[0044] (1)将樱桃木或沙比利板用600#砂纸打磨处理,除尽灰尘;
[0045] (2)用真空喷涂机喷涂UV真空喷涂底漆,涂布量:80〜100g/m2,(可采用市售产 品,如上海富臣化工UV真空喷涂底漆VU2110B),50°C红外流平2〜3分钟后,将紫外灯能 量调至250mj/cm2,过紫外灯全固化;将底漆用320#砂纸砂光平整后,用真空喷涂机喷涂UV 真空喷涂底漆,涂布量:100〜120g/m2,(可采用市售产品,如上海富臣化工UV真空喷涂底 漆VU2110B),50°C红外流平2〜3分钟后,将紫外灯能量调至MOmj/cm2,过紫外灯全固化。
[0046] (3)将底漆用320#砂纸砂光平整后,按着色要求加入适量色精进行PU修色(可采 用市售产品,如上海富臣化工PU修色面漆V500);
[0047] (4)PU修色面漆待干1小时后,将修色层用1000#砂纸轻抛,均勻喷涂PU面漆 (25°C,施工粘度为:岩田2号杯12〜13S)两度,(可采用市售产品,如上海富臣化工PU七 分哑光清面漆V517E面漆),待PU面漆完全干透后,即获得全封闭哑光涂装效果的成品。
[0048] 采用GB/T18581 VOC测定法,检测UV真空喷涂底漆的V0C,结果如下:
[0049]
Figure CN102101105AD00054
[0050] 采用GB/T9286-88附着力划格测定法,检测成品附着力,结果如下:
[0051]
Figure CN102101105AD00055
Figure CN102101105AD00061
[0052] 采用GB/T6739-1996涂膜硬度铅笔测定法,检测成品硬度,结果如下:
[0053]
Figure CN102101105AD00062

Claims (4)

1. 一种新的木门涂装方法,其特征在于,包括如下步骤:(1)将基材用240#砂纸打磨处理,除尘;(2)施工UV真空喷涂底漆;(3)按着色要求PU修色;(4)将修色层用1000#砂纸轻抛,均勻喷涂PU面漆。
2.根据权利要求1所述的方法,其特征在于,步骤O)的UV真空喷涂底漆所用红外流 平机温度设为50°C,半固化紫外灯能量为120〜150mj/cm2,全固化紫外灯能量为200〜 250mj/cm2。
3.根据权利要求1所述的方法,其特征在于,步骤(3)的PU修色后,需待干1〜2小时。
4.根据权利要求1所述的方法,其特征在于,步骤⑷的PU面漆施工粘度为岩田2号 杯12〜13S,施工温度为25°C。
CN2009102013274A 2009-12-17 2009-12-17 一种新的木门涂装方法 Pending CN102101105A (zh)