CN102011243A - Method for preparing double-mercerized yarn-dyed jacquard fabric - Google Patents

Method for preparing double-mercerized yarn-dyed jacquard fabric Download PDF

Info

Publication number
CN102011243A
CN102011243A CN 201010530601 CN201010530601A CN102011243A CN 102011243 A CN102011243 A CN 102011243A CN 201010530601 CN201010530601 CN 201010530601 CN 201010530601 A CN201010530601 A CN 201010530601A CN 102011243 A CN102011243 A CN 102011243A
Authority
CN
China
Prior art keywords
fabric
mariages
photochromic
loom
knits
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010530601
Other languages
Chinese (zh)
Other versions
CN102011243B (en
Inventor
盛光辉
郁晓冬
王设军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO RENFENG HOME TEXTILE CO Ltd
Original Assignee
NINGBO RENFENG HOME TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO RENFENG HOME TEXTILE CO Ltd filed Critical NINGBO RENFENG HOME TEXTILE CO Ltd
Priority to CN2010105306015A priority Critical patent/CN102011243B/en
Publication of CN102011243A publication Critical patent/CN102011243A/en
Application granted granted Critical
Publication of CN102011243B publication Critical patent/CN102011243B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a method for preparing a double-mercerized yarn-dyed jacquard fabric, which comprises: (1) performing mercerization treatment of 100s/2 or 120s/2 high grade all-cotton yarns in solution of NaOH, dyeing, drying and spooling to form tight cones; (2) warping; (3) weaving on a machine; (4) performing mercerization treatment of the fabric; and (5) inspection and packaging. In the invention, the warps and wefts are made of the same material, so the fabric offers the same touchfeel in texture; due to the mercerization of the yarns and the mercerization of the fabric, the finished fabric has the same effect as silk; and the prepared fabric is uniform in fabric cloth width, excellent in color and luster, clear in grain, full in particle and strong in three-dimensional sense and has the characteristics of beautiful appearance, high breathability, touchfeel comfort and the like.

Description

The photochromic preparation method who knits jacquard fabrics of a kind of mariages
Technical field
The invention belongs to the preparation field of jacquard fabrics, particularly relate to the photochromic preparation method who knits jacquard fabrics of a kind of mariages.
Background technology
From world wide, developed countries such as Europe, the United States, day, the household textiles consumption accounts for 50% of the whole world; And mostly be expensive goods again, and demand is rising year by year, himself production capacity only accounts for about 20% of its consumption figure, and its production throughput is descending year by year, this series products is again for producing intensive high-end product, there is the clear superiority on the resource in China in this, adds the so big market space and potentiality, and spinning industry for China man is a great opportunity.And highly dense big jacquard weave man's textile fabric is knitted in ultra-fine number, look because soft, and cloth cover is highly polished, and the outward appearance noble quality is magnificent, and decorative pattern is full lively, and product meets the demand in Europe, the United States, day and domestic top-grade consumption market.
Summary of the invention
Technical problem to be solved by this invention provides the photochromic preparation method who knits jacquard fabrics of a kind of mariages, and this preparation method is simple, is suitable for suitability for industrialized production; The lining cloth cover that makes is even, color and luster good, lines is clear, full grains, third dimension are strong, and outward appearance, good permeability, sense of touch with aesthetic feeling are comfortable.
The photochromic preparation method who knits jacquard fabrics of a kind of mariages of the present invention comprises:
(1) raw material is prepared: carry out mercerising again after adopting 100s/2 or the high count all cotton yarn line of 120s/2 to handle by conventional refining agent, chelating agent in the NaOH of 260-280g/L solution and handle, time was strict controlled in 8 minutes, dye according to the required color of yarn again, drying winder at last becomes the compact form bobbin, uses for warp thread, weft yarn;
(2) warping;
(3) looming weaving, the loom speed of a motor vehicle are 275~450 rev/mins;
(4) lining after above-mentioned the weaving is earlier through singing, after enzyme desizing makes cloth cover bright and clean, carrying out mercerising then and handle in the NaOH of 220-250g/L solution;
(5) check, packing, the cloth inspecting machine speed of a motor vehicle≤15 meter/minute.
The control of alkali number in the reeled yarn mercerising dyeing course in the described step (1) guarantees that promptly yarn has good gloss, and makes powerful loss minimum.
The high count all cotton yarn line of 100s/2 in the described step (1) or 120s/2 is for adopting 100s long-staple cotton spinning also Become bifilar 100s/2 or 120s/2 combed cotton strand.
Described step (2) is by batch warping, and the warping radical is 580~680.
The loom car is the wide cut shuttleless loom of electronic jacquard in the described step (3), and the door width of cloth of loom is 100~120 inches.
Woven technological design is in the described step (3), and warp-wise density is 678/10cm, and latitudinal density is 464/10cm.
Design technology route of the present invention:
Long-staple cotton → spinning → doubling → twisting → mercerising → dyeing → warping → sizing → weave → singe → pre-treatment (move back, boil) → mercerising → post processing → packing.
Technological difficulties of the present invention: (1) yarn (containing auxiliary agent) in the NaOH of 260-280g/L solution carries out mercerising to be handled, and the time was strict controlled in 8 minutes, guaranteed that yarn has good gloss, and made powerful loss minimum.(2) lining mercerising in the NaOH of 220-250g/L solution is handled, and reduces the TEAR STRENGTH of lining, makes lining gloss good, has the silk effect
Beneficial effect
(1) preparation method of the present invention is simple, and owing to warp, weft yarn adopt same materials, the material of the double-edged exposure of lining is identical, and physicochemical characteristics is identical, also gives identical sense of touch on quality; And the dual mercerising through yarn and lining makes lining reach the silk effect;
(2) the present invention compares with the jacquard fabrics of present use, and cloth cover is even, color and luster good, lines is clear, full grains, third dimension are strong, has the comfortable characteristics of outward appearance, good permeability, sense of touch of aesthetic feeling, is a kind of desirable high-grade tame textile fabric.
Description of drawings
Fig. 1 is an institutional framework DESIGN SKETCH of the present invention.
The specific embodiment
Below in conjunction with specific embodiment, further set forth the present invention.Should be understood that these embodiment only to be used to the present invention is described and be not used in and limit the scope of the invention.Should be understood that in addition those skilled in the art can make various changes or modifications the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims institute restricted portion equally.
Embodiment 1
As shown in Figure 1, the photochromic jacquard fabrics of knitting of a kind of mariages comprises warp thread and weft yarn, and described warp thread and weft yarn all adopt 100s/2 or the high count all cotton yarn line of 120s/2 behind the mercerising, and the vertical line among the figure is represented warp thread; Horizontal line is represented weft yarn.Warp thread and weft yarn are intertwined to form big figured texture weave.Described lining carries out mercerising to be handled, and makes lining reach the silk effect.Go up floating-point among the figure and represent that with " ■ " following floating-point is represented with " ".Different big figured texture weave on this lining shows by the combination of upper and lower floating-point.The specification of this lining: warp count is 678/10cm; Weft count is 464/10cm.
A kind of pure day silk dyed jacquard product production method comprises:
1) raw material is prepared, at first adopt high-intensity 100s long-staple cotton spinning and become bifilar 100s/2 or 120s/2 combed cotton strand, after the skeining, handle by carrying out mercerising again after refining agent, the chelating agent processing in the NaOH of 260-280g/L solution, the time was strict controlled in 8 minutes, guaranteed that yarn has good gloss, and make powerful loss minimum, dye according to the required color of yarn, drying winder at last becomes the compact form bobbin again, uses for warp thread, weft yarn;
2) warping, by batch warping, the warping radical is 580~680;
3) dress is made preparation, prepares harness cord, hanging, wear plank, connect the monofilament assembly, compiling and twist;
4) wear tying-in, wear menopause tablet, wear monofilament, eye-splice;
5) looming weaving, the loom speed of a motor vehicle are 275~450 rev/mins; Woven technological design is, warp-wise density is 678/10cm, and latitudinal density is 464/10cm; The loom car is the wide cut shuttleless loom of electronic jacquard, and the door width of cloth of loom is 100~120 inches;
6) lining after above-mentioned the weaving earlier through singing, enzyme desizing carries out mercerising in the NaOH solution by 220-250g/L again after making cloth cover bright and clean and handles;
7) check, packing, the cloth inspecting machine speed of a motor vehicle≤15 meter/minute.

Claims (4)

1. photochromic preparation method who knits jacquard fabrics of mariages comprises:
(1) raw material is prepared: carry out mercerising again after adopting 100s/2 or the high count all cotton yarn line of 120s/2 to handle by refining agent, chelating agent in the NaOH of 260-280g/L solution and handle, time is 8 minutes, dye according to the required color of yarn again, drying winder at last becomes the compact form bobbin, uses for warp thread, weft yarn;
(2) warping;
(3) looming weaving, the loom speed of a motor vehicle are 275~450 rev/mins;
(4) lining after above-mentioned the weaving earlier through singing, enzyme desizing, in the NaOH of 220-250g/L solution, carry out mercerising then and handle;
(5) check, packing, the cloth inspecting machine speed of a motor vehicle≤15 meter/minute.
2. the photochromic preparation method who knits jacquard fabrics of a kind of mariages according to claim 1 is characterized in that: described step (2) is by batch warping, and the warping radical is 580~680.
3. the photochromic preparation method who knits jacquard fabrics of a kind of mariages according to claim 1 is characterized in that: the loom car is the wide cut shuttleless loom of electronic jacquard in the described step (3), and the door width of cloth of loom is 100~120 inches.
4. the photochromic preparation method who knits jacquard fabrics of a kind of mariages according to claim 1 is characterized in that: woven technological design is in the described step (3), and warp-wise density is 678/10cm, and latitudinal density is 464/10cm.
CN2010105306015A 2010-11-03 2010-11-03 Method for preparing double-mercerized yarn-dyed jacquard fabric Expired - Fee Related CN102011243B (en)