CN102010605B - Fog sealing layer asphalt emulsion admixture and use method thereof - Google Patents

Fog sealing layer asphalt emulsion admixture and use method thereof Download PDF

Info

Publication number
CN102010605B
CN102010605B CN201010567413XA CN201010567413A CN102010605B CN 102010605 B CN102010605 B CN 102010605B CN 201010567413X A CN201010567413X A CN 201010567413XA CN 201010567413 A CN201010567413 A CN 201010567413A CN 102010605 B CN102010605 B CN 102010605B
Authority
CN
China
Prior art keywords
zhejiang
green
cyan
emulsion
emulsifier
Prior art date
Application number
CN201010567413XA
Other languages
Chinese (zh)
Other versions
CN102010605A (en
Inventor
商博明
徐培华
王安玲
蔡乾东
贾晓放
Original Assignee
陕西长大博源公路养护科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陕西长大博源公路养护科技有限公司 filed Critical 陕西长大博源公路养护科技有限公司
Priority to CN201010567413XA priority Critical patent/CN102010605B/en
Publication of CN102010605A publication Critical patent/CN102010605A/en
Application granted granted Critical
Publication of CN102010605B publication Critical patent/CN102010605B/en

Abstract

The invention provides a fog sealing layer asphalt emulsion admixture and a use method thereof. The admixture consists of the following raw materials in percentage by mass: 30 to 60 percent of asphalt reclaiming agent, 5 to 10 percent of asphalt reclaiming aid, 1 to 3 percent of penetrant, 1 to 5 percent of emulsifier, 2 to 8 percent of tackifier, and the balance water. When the admixture is added into a fog sealing material, the infiltrability of the fog sealing layer asphalt emulsion can be reinforced, thus the emulsion can be quickly filled in pores and microcracks on road surfaces, so that the water seepage resistance of the pavement is reinforced, and the asphalt pavement is prevented from water damage; the admixture can be quickly infiltrated to an aged asphalt layer to harmonize the components in the aged asphalt, so that the aged asphalt is regenerated; the admixture has strong bonding capability with the asphalt pavement, after traffic is open, the fog sealing layer material and the pavement are bonded firmly, and the admixture is not easy to adhere to vehicle wheels; and the molded admixture has accordant color with the newly built pavement, thus the road appearance is beautified.

Description

雾封层沥青乳液外加剂及其使用方法 Fog seal asphalt emulsion admixture and method of use

技术领域 FIELD

[0001] 本发明属于材料技术领域,具体涉及道路预防性养护所用雾封层浙青乳液外加剂及其使用方法。 [0001] The present invention belongs to the technical field of materials, particularly relates to preventive road maintenance used fog seal Zhejiang cyan emulsion admixture and methods of use.

背景技术 Background technique

[0002] 雾封层全称为雾状封层,是一种新型路面预防性养护技术。 [0002] called the fog of fog seal layer seal, a new pavement preventive maintenance techniques. 雾封层通过采用专用雾封层浙青洒布车,在路面面层上均勻喷洒的一层流体材料,其目的是为了有效封闭路表孔隙、防水抗渗、稳定松散集料、修复老化路面、改善路容路貌,从而实现延长路面使用寿命、节约养护资金。 Fog seal layer is formed by use of special fog seal Zhejiang Green spreaders, on the road surface uniformly sprayed layer of fluid material, which are designed to effectively seal the pore of pavement, water impermeability, a loose aggregate stability, road repair aging improve the capacity road appearance, in order to achieve prolong pavement life, save maintenance funds. 常见的雾封层材料主要有乳化浙青、改性乳化浙青及其道路养护剂等, 由于材料喷洒时,呈现雾状,因此统称为雾封层。 Common fog seal materials are emulsified Zhejiang blue, green and modified emulsion Zhejiang road maintenance and the like, since the material is sprayed, exhibit mist, fog seal thus collectively.

[0003] 雾封层材料性能的好坏直接影响到雾封层工程质量,通常应满足以下技术要求: (1)粘附性能,雾封层形成的浙青乳液与原浙青路面表面颗粒裹覆均勻、粘结牢固。 [0003] The material properties of fog seal direct impact on the quality of the project fog seal, generally should meet the following technical requirements: (1) the adhesive properties, fog seal Zhejiang cyan emulsion layer and green pavement surface of the particles of the original wrapped Zhejiang a uniform coating, bonded firmly. 夏季高温时不易软化、不泛油或被车轮粘掉跑光,冬季低温或雨天时无脱落现象,并不影响原路面抗滑、抗磨耗性能。 Summer easy to soften at high temperatures, do not stick out weeping or wheel running light, non-shedding phenomenon winter temperature or rain, it does not affect the original pavement skid, anti-wear performance. (2)防水渗透性能,雾封层形成的浙青乳液能够快速填充、渗透至路表孔隙及路面轻微裂缝的裂隙中,稳定松散颗粒,封闭路面孔隙,增强路面的抗水损坏性能。 (2) water permeability, Zhejiang cyan fog seal layer formed emulsion can be filled quickly, damage resistance to water penetration into the pore and fracture properties of the road surface cracks in the pavement minor, loose particles stability, road closed porosity, enhanced road. (3) 浙青再生性能,雾封层形成的浙青乳液快速渗透到老化浙青层中,调和老化浙青的组分,使原路面老化浙青得到再生。 (3) Green Zhejiang reproduction performance, fog seal Zhejiang cyan emulsion layer formed rapidly penetrate into the cyan layer Zhejiang aging, aging Zhejiang harmonic components cyan, so that the original road aging Zhejiang Green regenerated. (4)施工性能,雾封层浙青乳液体系稳定、无离析现象,确保喷洒均勻,色泽一致,同时由于雾封层施工速度较快,材料供应要求及时,雾封层浙青乳液的粘度或浙青固含量可根据路况不同情况随用随调,并具备成型快,开放交通早等性能。 (4) workability, fog seal Zhejiang cyan emulsion system stabilized, no segregation phenomenon, to ensure a uniform spray, the same color, and because of fog seal construction speed, material supply requirements in a timely manner, the viscosity of the emulsion cyan fog seal or Zhejiang Zhejiang green solids content depending on the traffic situation can be used with the transfer, and includes a rapid prototyping, early traffic opening properties.

[0004] 目前,雾封层材料选用普通乳化浙青相对较多,在工程实践过程中发现存在以下质量缺陷:(1)乳化浙青材料与原有旧路面粘结性差,开放交通后,雾封层浙青材料容易被行驶车辆碾掉、粘走;(2)乳化浙青材料渗透力差,无法渗透到旧路面内,填充路表孔隙、防水效果差;(3)现有雾封层乳化浙青材料不具有使旧路面老化浙青材料再生的功能;(4)现有雾封层乳化浙青材料破乳速度慢,封闭交通时间长;(5)现有雾封层乳化浙青材料破乳后,颜色比新建路面颜色浅,影响外观效果。 [0004] Currently, fog seal layer material use an ordinary emulsion Zhejiang relatively more green, in practice the process engineering quality defects found the following: (1) emulsified Zhejiang green materials and replacement of the old pavement poor adhesion, open traffic, fog Zhejiang green sealing material layer is easily milled off with the vehicle, walking stick; (2) emulsion blue Zhejiang material penetrates poor, unable to penetrate into the old road surface, the road surface is filled pores, poor water; (3) prior fog seal Zhejiang emulsion has a green material without the old road surface material aging Zhejiang green regeneration function; (4) prior Zhejiang emulsified cyan fog seal material breaking slow closure long travel time; (5) prior cyan fog seal emulsified Zhejiang after breaking the material, lighter color than the color of the new road, affect the appearance.

发明内容 SUMMARY

[0005] 本发明所要解决的技术问题在于克服上述雾封层浙青乳液与原有旧路面粘结性差、渗透力差,不能使旧路面老化浙青材料再生的缺陷,提供一种能有效提高雾封层浙青乳液的粘结力、耐久性、抗渗性及路面再生性能的雾封层浙青乳液外加剂及其使用方法。 [0005] The present invention is to overcome the above technical problem Zhejiang cyan fog seal replacement of the old road surface with an emulsion poor adhesion, poor penetration, can not make the old road surface material aging defects Zhejiang Green regenerated, to provide an effective increase fog seal adhesion Zhejiang cyan emulsion fog seal, durability, impermeability and reproduction performance of pavement Zhejiang cyan emulsion admixture and methods of use.

[0006] 解决上述技术问题所采用的技术方案由下述质量百分配比的原料制成: [0006] The raw material of the above-described technical problems by the following technical solutions adopted a mass percentage ratio is made:

[0007] 浙青再生剂 30%〜60% [0007] Zhejiang green regenerant 30% ~ 60%

[0008] 浙青再生助剂 5%〜10% [0008] Green Zhejiang 5% ~ 10% regeneration aid

[0009] 渗透剂 〜3% [0009] ~ 3% penetrant

[0010] 乳化剂 〜5% [0010] ~ 5% emulsifier

[0011] 增粘剂 2%〜8%[0012]水 加至100% [0011] 2% ~ 8% thickener [0012] Water to 100%

[0013] 上述的浙青再生剂为糠醛抽出油、芳烃油中的任意一种;浙青再生助剂为煤焦油、 煤油、柴油中的任意一种;渗透剂为渗透剂JFC、渗透剂JFC-1、渗透剂JFC-2中的任意一种; 乳化剂为烷基酚聚氧乙烯醚OP系列或壬基酚聚氧乙烯醚TX系列,其中烷基酚聚氧乙烯醚OP系列为烷基酚聚氧乙烯醚0P-9、烷基酚聚氧乙烯醚0P-10、烷基酚聚氧乙烯醚0P-13中的任意一种,壬基酚聚氧乙烯醚TX系列为壬基酚聚氧乙烯醚TX-7、壬基酚聚氧乙烯醚TX-10、 壬基酚聚氧乙烯醚TX-15中的任意一种;增粘剂为氯丁胶乳、丁腈胶乳、乙烯-乙酸乙烯胶乳、丁基胶乳中的任意一种。 [0013] The green regenerant Zhejiang furfural extract any oil, aromatic oil; Zhejiang green aid regeneration coal tar, kerosene, diesel any; JFC penetrant penetrant, penetrant JFC -1 any one of penetrant JFC-2; emulsifiers are alkylphenol ethoxylates OP series or nonylphenol ether TX series, wherein the alkylphenol polyoxyethylene alkyl OP series phenol polyoxyethylene ether 0P-9, polyoxyethylene alkylphenol ether 0P-10, any one of the 0P-13 alkylphenol ether, polyoxyethylene nonylphenyl ether TX series nonylphenol polyoxyethylene ethers TX-7, nonylphenol polyoxyethylene ether TX-10, any one of polyoxyethylene nonyl phenyl ether in the TX-15; tackifier is neoprene latex, nitrile latex, ethylene - vinyl acetate latex, butyl latex of any one. 渗透剂JFC、渗透剂JFC-1、渗透剂JFC-2、烷基酚聚氧乙烯醚0P-9、烷基酚聚氧乙烯醚0P-10、烷基酚聚氧乙烯醚0P-13、壬基酚聚氧乙烯醚TX-7、壬基酚聚氧乙烯醚TX-10、壬基酚聚氧乙烯醚TX-15由江苏海安石油化工厂销售。 Penetrant JFC, penetrant JFC-1, penetrant JFC-2, alkylphenol ether 0P-9, polyoxyethylene alkylphenol ether 0P-10, alkylphenol ether 0P-13, nonyl phenol polyoxyethylene ether TX-7, nonylphenol polyoxyethylene ether TX-10, nonyl phenol polyoxyethylene ether TX-15 sold by Jiangsu MSC petrochemical plants.

[0014] 本发明雾封层浙青乳液外加剂优选由下述质量百分配比的原料制成: [0014] The present invention is made of fog seal Zhejiang cyan emulsion admixture is preferably represented by the following mass percentage ratio of raw material:

[0015] 浙青再生剂 40%〜60% [0015] Zhejiang green regenerant 40% ~ 60%

[0016] 浙青再生助剂 5%〜8% [0016] Green Zhejiang 5% ~ 8% regeneration aid

[0017] 渗透剂 〜2% [0017] ~ 2% penetrant

[0018] 乳化剂 〜3% [0018] ~ 3% emulsifier

[0019] 增粘剂 3%〜7% [0019] ~ 7% 3% thickener

[0020]水 加至100% [0020] Water to 100%

[0021] 本发明雾封层浙青乳液外加剂最佳由下述质量百分配比的原料制成: [0021] The present invention Zhejiang fog seal cyan emulsion additives best prepared from the following proportions of weight percentage of raw materials:

[0022] 浙青再生剂 50% [0022] 50% Zhejiang green regenerant

[0023] 浙青再生助剂 6% [0023] Green Zhejiang reproduction assistant 6%

[0024] 渗透剂 2% [0024] 2% penetrant

[0025] 乳化剂 2% [0025] Emulsifier 2%

[0026] 增粘剂 5% [0026] 5% of a thickener

[0027]水 加至100% [0027] Water to 100%

[0028] 上述雾封层浙青乳液外加剂的制备方法为:按照上述原料的质量百分配比,将浙青再生剂、浙青再生助剂加热到熔融状态,将乳化剂、渗透剂加入到30〜70°C水中,搅拌溶解,将熔融状态的浙青再生剂和熔融状态的浙青再生助剂、溶解有乳化剂和渗透剂的水溶液、增粘剂加入到乳化机中,乳化1〜5分钟,形成分散、均勻的乳液,制备成雾封层浙青乳液外加剂。 [0028] The method for preparing the cyan fog seal Zhejiang emulsion admixture is: a mass percentage ratio of the raw material, the regenerant Zhejiang green, blue reproduction assistant Zhejiang heated to a molten state, an emulsifier, was added to the penetrant 30~70 ° C water and dissolved with stirring, the green regenerative agent Zhejiang Zhejiang green molten state and a molten state aid regeneration, an aqueous solution dissolving an emulsifier and osmotic agent, a thickener is added to the emulsification machine, emulsified 1 ~ 5 minutes to form a dispersion, a uniform emulsion, prepared as a fog seal Zhejiang cyan emulsion admixture.

[0029] 本发明的雾封层浙青乳液外加剂的使用方法如下: [0029] Green Emulsion Zhejiang admixture fog seal layer of the present invention is used as follows:

[0030] 1、制备高浓改性乳化浙青 [0030] 1. Preparation of highly concentrated modified emulsion cyan Zhejiang

[0031] 将基质浙青加热到110〜140°C,将浙青乳化剂加入到50〜70°C水中,搅拌均勻, 形成浙青乳化剂水溶液,将加热的基质浙青、浙青乳化剂水溶液和丁苯胶乳改性剂加入到乳化机中,乳化1〜3分钟,制备成高浓改性乳化浙青。 [0031] The substrate was heated to a cyan Zhejiang 110~140 ° C, the emulsifier is added to the green Zhejiang 50~70 ° C water and stirred uniformly, Zhejiang cyan aqueous emulsifier solution formed, heating the substrate Zhejiang blue, green emulsifier Zhejiang and aqueous SBR latex modifier to the emulsifying machine, emulsified 1~3 minutes to obtain a highly concentrated emulsifiable modified Zhejiang green.

[0032] 上述的高浓改性乳化浙青由下述质量百分配比的原料制成:基质浙青60%〜 70 %,丁苯胶乳改性剂3. 0 %〜6. 0 %,浙青乳化剂1. 5 %〜3. 0 %,余量为水。 [0032] The high concentration modified emulsion Zhejiang green mass percentage proportions by the following raw materials: a matrix Zhejiang 60% to 70% of cyan, SBR latex modifier 3.0% 0% ~ 6, Zhejiang. green emulsifier 1.5% ~ 3. 0%, the balance being water.

[0033] 上述的浙青乳化剂为PN-Ol阳离子中裂型乳化剂、PN-02阳离子中裂型乳化剂、 JL-COl中裂浙青乳化剂、JL-COlA中裂浙青乳化剂、JL-AOl浙青乳化剂、JY-R2Y型中裂阳离子浙青乳化剂、JY-R2S型中裂阳离子浙青乳化剂中的任意一种。 [0033] The emulsifiers Zhejiang Green PN-Ol cations crack emulsifier, PN-02 cation crack emulsifier, JL-COl crack in Zhejiang green emulsifier, JL-COlA crack in Zhejiang green emulsifier, green JL-AOl Zhejiang emulsifier, JY-R2Y split type cyan Zhejiang cationic emulsifier, any one of a cyan crack cationic emulsifiers Zhejiang JY-R2S type. [0034] PN-Ol阳离子中裂型乳化剂、PN-02阳离子中裂型乳化剂由博兴县派尼化工厂销售JL-COl中裂浙青乳化剂、JL-COlA中裂浙青乳化剂、JL-AOl浙青乳化剂由漯河市天龙化工有限公司销售JY-R2Y型中裂阳离子浙青乳化剂、JY-R2S型中裂阳离子浙青乳化剂由扬中市金阳化工有限公司销售。 [0034] PN-Ol cation crack emulsifier, PN-02 cationic emulsifier in split sales JL-COl crack in Zhejiang by the Green emulsifier Boxing County Piney chemical plant, the JL-COlA crack Zhejiang Green emulsifier , JL-AOl Zhejiang green emulsifier split by the Luohe City Tianlong Chemical Co., JY-R2Y type cationic emulsifier Zhejiang green, JY-R2S type split cationic emulsifier sold by Zhejiang green Chemical Co., Ltd. Zhenjiang City Jinyang.

[0035] 2、制备雾封层材料 [0035] 2, fog seal layer material was prepared

[0036] 将步骤1制备的高浓改性乳化浙青加水稀释成浙青的质量分数为30%〜50%的浙青乳液,向浙青乳液中加入其质量1.0%〜3.0%的雾封层浙青乳液外加剂,搅拌均勻, 加热到50〜70°C,制备成雾封层材料,备施工使用。 [0036] The highly concentrated modified emulsion prepared in Step 1 diluted with water into green Zhejiang mass fraction of 30% cyan Zhejiang ~ 50% of Zhejiang cyan emulsion which was added 1.0% ~3.0% by mass of the cyan fog seal to the emulsion Zhejiang Zhejiang cyan emulsion layer additives, uniformly stirred and heated to 50~70 ° C, fog seal layer material prepared, using the apparatus construction.

[0037] 本发明外加剂添加到雾封层材料中,可增强雾封层浙青乳液的渗透能力,使乳液快速填充到路表孔隙及微裂纹中,增强路面的抗渗水性能,防止出现浙青路面水损害;能够快速渗透到老化浙青层,调和老化浙青的组分,使老化浙青得到再生;与浙青路面的粘结能力强,开放交通后,雾封层材料与路面胶结牢固,不易被行车车轮粘掉;成型后与新建路面颜色一致,美化了路容路貌。 [0037] The admixture of the present invention is added to the material of fog seal, fog seal layer can be enhanced permeability Zhejiang cyan emulsion, the emulsion quickly to fill the pores and microcracks way table, the enhanced water impermeability of the road surface, to prevent Zhejiang green water Pavement damage; Zhejiang fast cyan layer penetrate into the aging, aging Zhejiang green harmonic components, so that the aging green regenerated Zhejiang; Zhejiang green intensity and bonding capacity of the road surface, after the opening of traffic, fog seal layer material and the road surface cementing solid, easy to stick out by driving the wheels; consistent with the new road surface color after molding, beautify the appearance capacity road.

具体实施方式 Detailed ways

[0038] 下面结合具体实施例对本发明进一步详细说明,但本发明不限于这些实施例。 [0038] Specific embodiments of the present invention is described below with more detail, but the present invention is not limited to these embodiments.

[0039] 实施例1 [0039] Example 1

[0040] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0040] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0041]芳烃油 50kg [0041] The aromatic oil 50kg

[0042] 煤焦油 6kg [0042] Coal tar 6kg

[0043]渗透剂 JFC 2kg [0043] penetrant JFC 2kg

[0044] 烷基酚聚氧乙烯醚0P-10 2kg [0044] alkylphenol ether 0P-10 2kg

[0045]氯丁胶乳 5kg [0045] Latex 5kg

[0046] /K 35kg [0046] / K 35kg

[0047] 其制备方法如下: [0047] was prepared as follows:

[0048] 将芳烃油、煤焦油加热到熔融状态,渗透剂JFC、烷基酚聚氧乙烯醚0P-10加入到50°C水中,搅拌溶解,将熔融状态的芳烃油和煤焦油、溶解有渗透剂JFC和烷基酚聚氧乙烯醚0P-10的水溶液、氯丁胶乳加入到乳化机中,乳化3分钟,形成分散、均勻的乳液,制备成雾封层浙青乳液外加剂。 [0048] The aromatic oil, coal tar heated to a molten state, the JFC penetrant, alkylphenol ether 0P-10 was added to a 50 ° C water and dissolved with stirring, the aromatic oil and coal tar molten state, dissolved JFC aqueous penetrants and alkylphenol polyoxyethylene ethers 0P-10, the neoprene latex is added to the emulsification machine, emulsified for 3 minutes to form a dispersion, a uniform emulsion, prepared as a fog seal Zhejiang cyan emulsion admixture.

[0049] 本发明的雾封层浙青乳液外加剂的使用方法如下: [0049] The admixture of the emulsion Zhejiang cyan fog seal layer of the present invention is used as follows:

[0050] 1、制备高浓改性乳化浙青 [0050] 1. Preparation of highly concentrated modified emulsion cyan Zhejiang

[0051] 将基质浙青加热到125°C,PN-Ol阳离子中裂型乳化剂加入到60°C水中,搅拌均勻,形成浙青乳化剂水溶液,将加热的基质浙青、PN-Ol阳离子中裂型乳化剂水溶液和丁苯胶乳改性剂加入到乳化机中,乳化2分钟,制备成高浓改性乳化浙青。 [0051] The substrate was heated to a cyan Zhejiang 125 ° C, PN-Ol cationic emulsifiers are split into 60 ° C water was added, stirred uniformly, Zhejiang cyan aqueous emulsifier solution is formed, the substrate is heated Zhejiang Green, PN-Ol cation the styrene-butadiene latex and an aqueous solution of crack emulsifier modifier to emulsifying machine, emulsified for 2 minutes to prepare a highly concentrated modified emulsion Zhejiang green.

[0052] 上述的高浓乳化浙青由下述质量百分配比的原料制成:基质浙青65%,丁苯胶乳改性剂4. 5%, PN-Ol阳离子中裂型乳化剂2. 0%,余量为水。 Made [0052] The high concentration emulsion Zhejiang green mass percentage ratio by the following materials: a matrix of 65% cyan Zhejiang, SBR latex modifier 4. 5%, PN-Ol cationic emulsifiers split in two. 0%, the balance being water.

[0053] 上述的PN-Ol阳离子中裂型乳化剂也可用等质量的PN-02阳离子中裂型乳化剂、 JL-COl中裂浙青乳化剂、JL-COlA中裂浙青乳化剂、JL-AOl浙青乳化剂、JY-R2Y型中裂阳离子浙青乳化剂、JY-R2S型中裂阳离子浙青乳化剂中的任意一种替换。 [0053] The cation of PN-Ol split emulsifiers and the like may also be quality PN-02 cation crack emulsifier, JL-COl crack in Zhejiang green emulsifier, JL-COlA crack in Zhejiang Green emulsifiers, JL Zhejiang green -AOl emulsifier, JY-R2Y split type cationic emulsifiers Zhejiang cyan, cyan any crack cationic emulsifiers Zhejiang JY-R2S an alternative type. [0054] 2、制备雾封层材料 [0054] 2, fog seal layer material was prepared

[0055] 将步骤1制备的高浓改性乳化浙青加水稀释成浙青的质量分数为45%的浙青乳液,向浙青乳液中加入其质量2. 0 %的雾封层浙青乳液外加剂,搅拌均勻,加热到60°C,制备成雾封层材料,备施工使用。 [0055] The highly concentrated modified emulsion prepared in Step 1 diluted with water into green Zhejiang mass fraction of 45% cyan Zhejiang Zhejiang cyan emulsion which was added 2.0% by mass of cyan fog seal Zhejiang Zhejiang cyan emulsion to emulsion additive, uniformly stirring, heated to 60 ° C, fog seal layer material prepared, using the apparatus construction.

[0056] 实施例2 [0056] Example 2

[0057] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0057] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0058] 糠醛抽出油 30kg [0058] 30kg furfural extract oil

[0059]煤油 5kg [0059] kerosene 5kg

[0060]渗透剂 JFC-I Ikg [0060] penetrant JFC-I Ikg

[0061] 壬基酚聚氧乙烯醚TX-10 Ikg [0061] nonylphenol ether TX-10 Ikg

[0062]氯丁胶乳 2kg [0062] Latex 2kg

[0063] /K 61kg [0063] / K 61kg

[0064] 其制备方法如下: [0064] was prepared as follows:

[0065] 将糠醛抽出油、煤油加热到熔融状态,渗透剂JFC-I、壬基酚聚氧乙烯醚TX-10加入到30°C水中,搅拌溶解,将熔融状态的糠醛抽出油和煤油、溶解有渗透剂JFC-I和壬基酚聚氧乙烯醚TX-10的水溶液、氯丁胶乳加入到乳化机中,乳化1分钟,形成分散、均勻的乳液,制备成雾封层浙青乳液外加剂。 [0065] The furfural extract oil, kerosene heated to a molten state, penetrant JFC-I, polyoxyethylene nonyl phenyl ether TX-10 was added to a 30 ° C water and dissolved with stirring, in a molten state furfural extract oil and kerosene, an aqueous solution containing penetrant JFC-I and nonylphenol polyoxyethylene ether TX-10, the neoprene latex is added to the emulsification machine, emulsified for 1 minute to form a dispersion, a uniform emulsion, prepared as an emulsion cyan fog seal layer applied Zhejiang agents.

[0066] 本发明的雾封层浙青乳液外加剂的使用方法如下: [0066] Green Emulsion Zhejiang admixture fog seal layer of the present invention is used as follows:

[0067] 1、制备高浓改性乳化浙青 [0067] 1. Preparation of highly concentrated modified emulsion cyan Zhejiang

[0068] 将基质浙青加热到110°C,PN-Ol阳离子中裂型乳化剂加入到50°C水中,搅拌均勻,形成PN-Ol阳离子中裂型乳化剂水溶液,将加热的基质浙青、PN-Ol阳离子中裂型乳化剂水溶液和丁苯胶乳改性剂加入到乳化机中,乳化1分钟,制备成高浓改性乳化浙青。 [0068] The substrate was heated to a cyan Zhejiang 110 ° C, PN-Ol cationic emulsifier was added to split the 50 ° C water and stirred uniformly to form a PN-Ol cationic emulsifiers in an aqueous solution of cracking the heated substrate Zhejiang Green , PN-Ol cations crack emulsifier and an aqueous solution of SBR latex modifier to emulsification machine, emulsified for 1 minute to prepare a highly concentrated modified emulsion Zhejiang green.

[0069] 上述的高浓乳化浙青由下述质量百分配比的原料制成: [0069] The high concentration cyan emulsion Zhejiang by the following mass percentage ratio of raw materials:

[0070] 基质浙青60 %,丁苯胶乳改性剂3.0%,PN-01阳离子中裂型乳化剂1. 5 %,余量为水。 [0070] Green matrix Zhejiang 60% SBR latex modifier 3.0%, PN-01 cation crack emulsifier 1.5%, the balance being water.

[0071] 2、制备雾封层材料 [0071] 2, fog seal layer material was prepared

[0072] 将步骤1制备的高浓改性乳化浙青加水稀释成浙青的质量分数为30%的浙青乳液,向浙青乳液中加入其质量1. 0%的雾封层浙青乳液外加剂,搅拌均勻,加热到50°C,制备成雾封层材料,备施工使用。 [0072] The highly concentrated modified emulsion prepared in Step 1 diluted with water into green Zhejiang mass fraction of 30% cyan Zhejiang Zhejiang cyan emulsion which was added 1.0% by mass of cyan fog seal Zhejiang Zhejiang cyan emulsion to emulsion additive, uniformly stirring, heated to 50 ° C, fog seal layer material prepared, using the apparatus construction.

[0073] 实施例3 [0073] Example 3

[0074] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0074] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0075]芳烃油 60kg [0075] The aromatic oil 60kg

[0076]柴油 IOkg [0076] Diesel IOkg

[0077]渗透剂 JFC-2 3kg [0077] penetrant JFC-2 3kg

[0078] 烷基酚聚氧乙烯醚0P-9 5kg [0078] alkylphenol ether 0P-9 5kg

[0079] 丁腈胶乳 8kg [0079] The nitrile latex 8kg

[0080] /K 14kg [0080] / K 14kg

[0081] 其制备方法如下: [0081] was prepared as follows:

[0082] 将芳烃油、柴油加热到熔融状态,渗透剂JFC-2、烷基酚聚氧乙烯醚0P-9加入到70°C水中,搅拌溶解,将熔融状态的芳烃油和柴油、溶解有渗透剂JFC-2和烷基酚聚氧乙烯醚0P-9的水溶液、丁腈胶乳加入到乳化机中,乳化5分钟,形成分散、均勻的乳液,制备成雾封层浙青乳液外加剂。 [0082] The aromatic oil, diesel oil heated to a molten state, penetrant JFC-2, alkylphenol ether 0P-9 was added to a 70 ° C water and dissolved with stirring, the aromatic oil and diesel fuel in a molten state, dissolved aqueous penetrant JFC-2 and alkylphenol polyoxyethylene ethers of 0P-9, was added to a nitrile latex emulsion machine, emulsified for 5 minutes to form a dispersion, a uniform emulsion, prepared as a fog seal Zhejiang cyan emulsion admixture.

[0083] 本发明的雾封层浙青乳液外加剂的使用方法如下: [0083] Green Emulsion Zhejiang admixture fog seal layer of the present invention is used as follows:

[0084] 1、制备高浓改性乳化浙青 [0084] 1. Preparation of highly concentrated modified emulsion cyan Zhejiang

[0085] 将基质浙青加热到140°C,PN-Ol阳离子中裂型乳化剂加入到70°C水中,搅拌均勻,形成PN-Ol阳离子中裂型乳化剂水溶液,将加热的基质浙青、PN-Ol阳离子中裂型乳化剂水溶液和丁苯胶乳改性剂加入到乳化机中,乳化3分钟,制备成高浓改性乳化浙青。 [0085] The substrate was heated to a cyan Zhejiang 140 ° C, PN-Ol cationic emulsifiers are split into 70 ° C water was added and stirred uniformly to form a PN-Ol cationic emulsifiers in an aqueous solution of cracking the heated substrate Zhejiang Green , PN-Ol cations crack emulsifier and an aqueous solution of SBR latex modifier to emulsification machine, emulsified for 3 minutes to prepare a highly concentrated modified emulsion Zhejiang green.

[0086] 上述的高浓乳化浙青由下述质量百分配比的原料制成:基质浙青70%,丁苯胶乳改性剂6. 0%, PN-Ol阳离子中裂型乳化剂3. 0%,余量为水。 Made [0086] The high concentration emulsion Zhejiang green mass percentage ratio by the following materials: a matrix Zhejiang Green 70% SBR latex modifier 6. 0%, PN-Ol cationic emulsifiers are 3 cleft. 0%, the balance being water.

[0087] 2、制备雾封层材料 [0087] 2, fog seal layer material was prepared

[0088] 将步骤1制备的高浓改性乳化浙青加水稀释成浙青的质量分数为50%的浙青乳液,向浙青乳液中加入其质量3. 0 %的雾封层浙青乳液外加剂,搅拌均勻,加热到70°C,制备成雾封层材料,备施工使用。 [0088] The highly concentrated modified emulsion prepared in Step 1 diluted with water into green Zhejiang mass fraction of 50% cyan Zhejiang Zhejiang cyan emulsion which was added 3.0% by mass of cyan fog seal Zhejiang Zhejiang cyan emulsion to emulsion additive, uniformly stirring, heated to 70 ° C, fog seal layer material prepared, using the apparatus construction.

[0089] 实施例4 [0089] Example 4

[0090] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0090] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0091]芳烃油 40kg [0091] The aromatic oil 40kg

[0092] 煤焦油 7kg [0092] Coal tar 7kg

[0093]渗透剂 JFC 1. 5kg [0093] JFC 1. 5kg penetrant

[0094] 壬基酚聚氧乙烯醚TX-15 3.5kg [0094] nonylphenol ether TX-15 3.5kg

[0095] 乙烯-乙酸乙烯胶乳 6kg [0095] an ethylene - vinyl acetate latex 6kg

[0096] /K 42kg [0096] / K 42kg

[0097] 其制备方法和使用方法与实施例1相同。 [0097] The preparation and methods of using the same as in Example 1.

[0098] 实施例5 [0098] Example 5

[0099] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0099] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0100] 糠醛抽出油 55kg [0100] 55kg furfural extract oil

[0101]煤油 8kg [0101] kerosene 8kg

[0102]渗透剂 JFC-I 2.5kg [0102] penetrant 2.5kg JFC-I

[0103] 烷基酚聚氧乙烯醚0P-13 4.5kg [0103] alkylphenol ether 0P-13 4.5kg

[0104] 丁基胶乳 3kg [0104] butyl latex 3kg

[0105] 水 27kg [0105] 27kg of water

[0106] 其制备方法和使用方法与实施例1相同。 [0106] their preparation and use the same as in Example 1.

[0107] 实施例6 [0107] Example 6

[0108] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0108] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0109]芳烃油 45kg [0109] 45kg aromatic oil

[0110]柴油 9kg [0110] Diesel 9kg

[0111]渗透剂 JFC-2 2kg [0111] penetrant JFC-2 2kg

[0112] 壬基酚聚氧乙烯醚TX-7 3kg [0112] nonylphenol ether TX-7 3kg

[0113]氯丁胶乳 7kg[0114] 水 34kg [0113] Latex 7kg [0114] Water 34kg

[0115] 其制备方法和使用方法与实施例1相同。 [0115] their preparation and use the same as in Example 1.

[0116] 实施例7 [0116] Example 7

[0117] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0117] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0118]芳烃油 30kg [0118] 30kg aromatic oil

[0119] 煤焦油 5kg [0119] 5kg of coal tar

[0120]渗透剂 JFC Ikg [0120] penetrant JFC Ikg

[0121] 烷基酚聚氧乙烯醚0P-10 Ikg [0121] alkylphenol ether 0P-10 Ikg

[0122]氯丁胶乳 2kg [0122] Latex 2kg

[0123] /K 61kg [0123] / K 61kg

[0124] 其制备方法和使用方法与实施例1相同。 [0124] their preparation and use the same as in Example 1.

[0125] 实施例8 [0125] Example 8

[0126] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0126] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0127]芳烃油 60kg [0127] 60kg aromatic oil

[0128]煤焦油 IOkg [0128] Coal tar IOkg

[0129]渗透剂 JFC 3kg [0129] penetrant JFC 3kg

[0130] 烷基酚聚氧乙烯醚0P-10 5kg [0130] alkylphenol ether 0P-10 5kg

[0131]氯丁胶乳 8kg [0131] Latex 8kg

[0132] 水 14kg [0132] 14kg of water

[0133] 其制备方法和使用方法与实施例1相同。 [0133] their preparation and use the same as in Example 1.

[0134] 实施例9 [0134] Example 9

[0135] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0135] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0136] 在以上的实施例1、7、8中,所用的原料芳烃油用糠醛抽出油替换,用量与芳烃油相等;煤焦油用煤油替换,也可用柴油替换,用量与煤焦油相等;渗透剂JFC用渗透剂JFC-I 替换,也可用渗透剂JFC-2替换,用量与渗透剂JFC相等;烷基酚聚氧乙烯醚0P-10用烷基酚聚氧乙烯醚0P-9替换,也可用烷基酚聚氧乙烯醚0P-13替换,用量与烷基酚聚氧乙烯醚0P-10相等;氯丁胶乳用丁腈胶乳替换,也可用乙烯-乙酸乙烯胶乳替换,还可用丁基胶乳替换,用量与氯丁胶乳相等。 [0136] In the above examples 1,7,8, aromatic oil feedstock used in the extraction of oil furfural replaced with an equal amount of aromatic oil; tar Alternatively kerosene, diesel fuel may also be replaced, an amount equal to the coal tar; permeation agent JFC JFC-I with alternative osmotic agent, penetrant JFC-2 can also be replaced, an amount equal to the penetrant JFC; alkylphenol ether 0P-10 0P-9 was replaced with polyoxyethylene alkylphenol ether, also alkylphenol ethoxylates available 0P-13 Alternatively, the amount of the alkylphenol polyoxyethylene ether 0P-10 equal; latex with nitrile rubber latex alternatively, it may also be an ethylene - vinyl acetate latex Alternatively, also with butyl latex Alternatively, an amount equal to the chloroprene latex. 水加至100kg。 Water was added to 100kg.

[0137] 其制备方法和使用方法与实施例1相同。 [0137] their preparation and use the same as in Example 1.

[0138] 实施例10 [0138] Example 10

[0139] 以制备本发明雾封层浙青乳液外加剂IOOkg为例所用原料的质量配比如下: [0139] In the present invention was prepared fog seal cyan emulsion admixture IOOkg Example Zhejiang the quality of raw materials used was prepared as follows:

[0140] 在以上的实施例9中,所用的原料烷基酚聚氧乙烯醚0P-10用壬基酚聚氧乙烯醚TX-7替换,也可用壬基酚聚氧乙烯醚TX-10替换,还可用壬基酚聚氧乙烯醚TX-15替换,用量与烷基酚聚氧乙烯醚0P-10相等。 [0140] In the above Example 9, the raw material used alkylphenol polyoxyethylene 0P-10 was replaced with polyoxyethylene nonyl phenyl ether TX-7, can also be used nonylphenol ether replaced TX-10 , TX-15 may also be replaced with an ether of polyoxyethylene nonylphenol, alkylphenol and the amount of polyoxyethylene is equal 0P-10. 其它原料以及原料的用量与实施例9相同。 The other raw materials and the amounts of materials described in Example 9. 水加至IOOkg0 Water is added to IOOkg0

[0141] 其制备方法和使用方法与实施例1相同。 [0141] their preparation and use the same as in Example 1.

[0142] 为了证明本发明的有益效果,发明人将按实施例1〜6配制好的雾封层材料涂刷到连霍高速(连云港-霍尔果斯)SK2492+608-SK2496+700试验路段超车道上,检测材料的渗透效果、路面颜色、车辆行驶后与路面的粘附情况、路面抗渗水性能及路面抗滑性能。 [0142] In order to demonstrate the beneficial effects of the present invention, the inventors formulated embodiment 1~6 fog seal layer material will embodiment brushing high Huo (Lianyungang - Huoerguosi) SK2492 608-SK2496 + 700 + test section passing lane, the detection material penetration effect, the color of the road, the vehicle is traveling and the road surface adhesion, the water impermeability and the road pavement skid resistance. 材料渗透效果采用钻芯取样试验,测定渗透深度(mm);路面颜色、车辆行驶后雾封层材料与路面的粘附情况采用目测;路面抗渗水性能采用渗水系数试验测定;路面抗滑性能采用路面摩擦系数摆值试验测定;路面渗水系数试验及路面摩擦系数摆值试验按交通部部颁标准JTG E60-2008《公路路基路面现场测试规程》,技术指标要求按JTG F40-2004《公路浙青路面施工技术规范》,路面检测结果见表1。 Materials employed penetration effect drilling core test to measure the penetration depth (mm); the color of the road, where the vehicle travels fog seal adhesive material to the road surface by visual; Pavement water impermeability permeability coefficient was measured using the test; performance using Antiskid road surface friction coefficient value pendulum test measures; seepage coefficient test and road surface friction coefficient value pendulum test according to the Ministry of Transportation ministerial standard JTG E60-2008 "roadbed Pavement field testing procedures", technical specifications required by the JTG F40-2004 "road Zhejiang green Pavement construction technical specification "road test results in Table 1.

[0143] 表1添加外加剂后雾封层路用性能测试结果 [0143] After the addition of additives in Table 1 road fog seal performance test results with

[0144] [0144]

Figure CN102010605BD00101

[0145] 由表1可见,添加了本发明外加剂的雾封层材料喷洒到路面上,乳液破乳后路面颜色均勻一致,呈黑色;乳液破乳后与路面粘附面积均大于98%;雾封层材料的渗透深度大于2mm ;路面抗渗水性能大幅度提高,渗水系数提高率超过50% ;路面抗滑性能较原路面损失率较小,均小于10%,相关性能指标均满足JTG F40-2004《公路浙青路面施工技术规范》 的要求,具有良好的抗渗水和抗滑性能。 [0145] As shown in Table 1, was added a fog seal layer material according to the present invention, the admixture is sprayed onto the road surface, after the emulsion breaking pavement uniform color, black; emulsion breaking and the road surface after the adhesion area greater than 98%; fog seal layer material is greater than the penetration depth of 2mm; Pavement greatly improved water impermeability, permeability coefficient increase more than 50%; Antiskid smaller than the original road performance loss rate, less than 10%, the relevant performance indicators meet JTG F40 2004 "green Zhejiang road pavement construction specifications" requirement, has a good water impermeability and skid resistance.

Claims (4)

1. 一种雾封层浙青乳液外加剂,其特征在于由下述质量百分配比的原料制成: 浙青再生剂 30%〜60%浙青再生助剂 5%〜10%渗透剂 〜3%乳化剂 〜5%增粘剂 2%〜8%水 加至100%上述的浙青再生剂为糠醛抽出油、芳烃油中的任意一种;浙青再生助剂为煤焦油、煤油、柴油中的任意一种;渗透剂为渗透剂JFC、渗透剂JFC-1、渗透剂JFC-2中的任意一种; 乳化剂为烷基酚聚氧乙烯醚OP系列或壬基酚聚氧乙烯醚TX系列,其中烷基酚聚氧乙烯醚OP系列为烷基酚聚氧乙烯醚0P-9、烷基酚聚氧乙烯醚0P-10、烷基酚聚氧乙烯醚0P-13中的任意一种,壬基酚聚氧乙烯醚TX系列为壬基酚聚氧乙烯醚TX-7、壬基酚聚氧乙烯醚TX-10、 壬基酚聚氧乙烯醚TX-15中的任意一种;增粘剂为氯丁胶乳、丁腈胶乳、乙烯-乙酸乙烯胶乳、丁基胶乳中的任意一种。 A fog seal Zhejiang cyan emulsion additives, characterized in that the ratio of the mass percentage is made of the following materials: Zhejiang green regenerant ~ 60% 30% 5% Zhejiang blue reproduction assistant ~ 10% ~ penetrant 3% emulsifier 2% ~ 5% ~ 8% tackifier water to 100% the above green regenerant Zhejiang furfural extract oil, any one of aromatic oil; Zhejiang green aid regeneration coal tar, kerosene, either diesel; penetrants penetrant JFC, penetrant JFC-1, any one of the penetrant JFC-2; emulsifiers are alkylphenol ethoxylates OP series or nonylphenol TX series ethers, polyoxyethylene alkyl phenol wherein the OP series of alkylphenol ethoxylates 0P-9, polyoxyethylene alkylphenol ether 0P-10, any one of 0P-13 alkylphenol ether one of nonylphenol ether TX series nonylphenol polyoxyethylene ether TX-7, nonylphenol polyoxyethylene ether TX-10, polyoxyethylene nonyl phenyl ether, TX-15 of any one of ; tackifier is a neoprene latex, nitrile latex, ethylene - vinyl acetate latex, butyl latex of any one.
2.根据权利要求1所述的雾封层浙青乳液外加剂,其特征在于由下述质量百分配比的原料制成:浙青再生剂 40%〜60%浙青再生助剂 5%〜8%渗透剂 〜2%乳化剂 〜3%增粘剂 3%〜7%水 加至100%。 According to claim 1, the fog seal Zhejiang cyan emulsion additives, characterized in that the ratio of the mass percentage is made of the following materials: Zhejiang Green 40% ~ 60% regenerated catalyst regeneration aid Zhejiang Green 5% 8% emulsifier penetrant ~ 2 ~ 3% 3% ~ 7% tackifier% water to 100%.
3.根据权利要求1所述的雾封层浙青乳液外加剂,其特征在于由下述质量百分配比的原料制成:浙青再生剂 50%浙青再生助剂 6%渗透剂 2%乳化剂 2%增粘剂 5%水 加至100%。 The fog seal of claim 1 to claim Zhejiang cyan emulsion additives, characterized in that the ratio of the mass percentage is made of the following materials: 50% Zhejiang Zhejiang Green Green regenerated catalyst regeneration aid 2% 6% penetrant emulsifier 2% thickener 5% water to 100%.
4. 一种权利要求1所述的雾封层浙青乳液外加剂,其特征在于该外加剂的使用方法如下:(1)制备高浓改性乳化浙青将基质浙青加热到110〜140°C,浙青乳化剂加入到50〜70°C水中,搅拌均勻,形成浙青乳化剂水溶液,将加热的基质浙青、浙青乳化剂水溶液和丁苯胶乳改性剂加入到乳化机中,乳化1〜3分钟,制备成高浓改性乳化浙青;上述的高浓改性乳化浙青由下述质量百分配比的原料制成:基质浙青60%〜70%,丁苯胶乳改性剂3.0%〜6.0%,浙青乳化剂1.5%〜3.0%,余量为水;上述的浙青乳化剂为PN-Ol阳离子中裂型乳化剂、PN-02阳离子中裂型乳化剂、JL-COl中裂浙青乳化剂、JL-COlA中裂浙青乳化剂、JL-AOl浙青乳化剂、JY-R2Y型中裂阳离子浙青乳化剂中的任意一种; (2)制备雾封层材料将步骤(1)制备的高浓改性乳化浙青加水稀释成浙青的质量分数为30%〜50%的浙青乳液,向浙 Zhejiang cyan fog seal emulsion admixture according to claim 1 A, wherein the admixture is used as follows: (1) high concentration of the modified emulsion was prepared Zhejiang blue green substrate is heated to 110~140 Zhejiang ° C, an emulsifier is added to the green Zhejiang 50~70 ° C water and stirred uniformly, Zhejiang cyan aqueous emulsifier solution formed, heating the substrate Zhejiang blue, green Zhejiang and aqueous emulsifier solution was added to the emulsion SBR latex modifiers machine , ~ 3 minutes emulsification, to prepare a highly concentrated modified emulsion Zhejiang cyan; made of the above high concentration modified emulsion Zhejiang green mass percentage ratio by the following materials: a matrix of 60% ~ 70% cyan Zhejiang, SBR latex 3.0% ~6.0% modifier, Zhejiang 1.5% ~3.0% cyan emulsifier, the balance water; and the cyan Zhejiang emulsifiers PN-Ol cations crack emulsifier, PN-02 cationic emulsifiers are split , JL-COl crack in Zhejiang green emulsifier, JL-COlA crack in Zhejiang green emulsifier, any emulsifier green JL-AOl Zhejiang, JY-R2Y split type cyan Zhejiang cationic emulsifiers; (2) preparation of fog seal layer material of step (1) high concentration modified emulsion prepared Zhejiang green dilution with water content of 30% cyan Zhejiang ~ 50% of cyan emulsion Zhejiang, the Zhejiang 青乳液中加入其质量1. 0%〜3. 0%的雾封层浙青乳液外加剂,搅拌均勻,力口热到50〜70°C,制备成雾封层材料,备施工使用。 Green emulsion was added 1.0% of its mass ~ 3 0% of the cyan fog seal Zhejiang emulsion additives, stir, thermal power port to 50~70 ° C, to prepare a fog seal material prepared using the construction.
CN201010567413XA 2010-11-26 2010-11-26 Fog sealing layer asphalt emulsion admixture and use method thereof CN102010605B (en)