CN101972045A - technology for making whitening sun-block clothes - Google Patents
technology for making whitening sun-block clothes Download PDFInfo
- Publication number
- CN101972045A CN101972045A CN201010513142XA CN201010513142A CN101972045A CN 101972045 A CN101972045 A CN 101972045A CN 201010513142X A CN201010513142X A CN 201010513142XA CN 201010513142 A CN201010513142 A CN 201010513142A CN 101972045 A CN101972045 A CN 101972045A
- Authority
- CN
- China
- Prior art keywords
- fiber
- whitening
- uvioresistant
- nano
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a technology for making whitening sun-block clothes, comprising the following technical steps of: firstly, preparing whitening fiber and uvioresistant fiber used as raw materials; secondly, proportioning the whitening fiber, the uvioresistant fiber and orlon fiber 6 according to a certain percentage; next, respectively opening, picking and carding the mixed fiber of the whitening fiber and the orlon fiber 6 and the mixed fiber of the uvioresistant fiber and the orlon fiber 6 to prepare into strips; then, preparing the obtained two fiber strips into union yarn by the processing of strip combination, coarse yarn and a spun yarn cheese winder; and finally, preparing the obtained union yarn into a knitting fabric or a woven fabric to further make the whitening sun-block clothes. The invention discloses the technology for making whitening sun-block clothes. The whitening sun-block clothes has the characteristics of light texture, attractive appearance and durability of common clothes, has excellent uvioresistant effect and whitening skin effect at the same time, good ventilation property and low manufacturing cost and is especially suitable for being worn in scorching summer.
Description
Technical field
The present invention relates to a kind of preparation technology of whitening sun protection clothing, especially a kind of functional clothes with uvioresistant and skin whitening belongs to clothing class field.
Background technology
The various clothes clothes that the clothes general reference is worn on one's body, the original idea of clothes is a warming, the medium of flak jacket; Be the decorative article of human body and developed gradually, to have signified a people's standard of living and social status in the time of more at modern society's clothes; Simultaneously on clothes basic function basis of invariable, people more and more pay attention to the health-care effect of clothing to health, constantly the new material of research and development clothes utilizes suitable technology that the various effects of different materials are added in the dress material, has increased garment baffle.Clothes also has the opposing ultraviolet radiation except the warming effect, deodorization and sterilization discharges effects such as anion and infrared ray emission.The excessive meeting of its middle-ultraviolet lamp causes human body to get skin disease, or even the skin cancer, also may cause and reduce the organism immunologic function, and the people is fallen ill easily.How to prevent uv damage skin so people begin one's study, now generally adopt anti-ultraviolet method that spin processes, coating and finishing method are arranged on the market.Wherein spin processes and finishing method less stable, cost is higher, and coating stability is general, and feel is relatively poor, and the performance of gas permeability aspect is also unsatisfactory.Therefore, researching and developing a kind of novel material just has certain certainty and urgency, and this material should have stability preferably, and production cost can not be too high, and anti-ultraviolet ability is good than the former again.Certainly people can also play the effect of skin whitening, the thing that this numerous just women's fellow citizens is dreamed of to the functional requirement of clothing more than that when wearing clothes.
Summary of the invention
At the demand, the invention provides a kind of preparation technology of whitening sun protection clothing, by rational material mixture ratio, suitable processing method, make the clothes that makes have better anti-ultraviolet function, cost is not high again, and the effect of skin whitening can also be arranged when wearing this clothes simultaneously.
The present invention is a kind of preparation technology of whitening sun protection clothing, and this processing step is as follows: at first, preparation whitening fiber and uvioresistant fiber are as getting the raw materials ready; Secondly, whitening fiber, uvioresistant fiber and acrylic fibers 6 fibers are carried out proportioning according to certain percentage composition; Then, respectively the composite fibre of whitening fiber and uvioresistant fiber and acrylic fibers 6 fibers is carried out opening picking, carding step is made bar; Then, two kinds of ribbons with gained make scribbled through drafting, rove, spun yarn winder; At last, make the gained scribbled knitting or woven fabric and then make the whitening sun protection clothing.
In a preferred embodiment of the present invention, described whitening fiber is to add the nano-pearl fiber in polyster fibre, makes by melt spinning process.
In a preferred embodiment of the present invention, described melt spinning process may further comprise the steps: 1) heat drying raw material (polyster fibre and nano-pearl fiber); 2) with the nano-pearl fibers melt in polyster fibre, make the spinning fluid; 3) under constant compression force and temperature, the spinning fluid of fusion is extruded from spinneret orifice, be frozen into silk by cooling medium; 4) with the fiber that makes by twisting, wash operations such as pressure, drying, thermal finalization, obtain the whitening fiber fiber.
In a preferred embodiment of the present invention, the spinning fluid of described fusion is at 220 ℃-240 ℃, and force value is to extrude from spinneret orifice under the condition of 1.1MPa.
In a preferred embodiment of the present invention, described cooling medium is the aqueous solution.
In a preferred embodiment of the present invention, described uvioresistant fiber is that processes such as the nano-carbon powder made by nano-bamboo carbon and fraction silk, fiber crops, hair operation such as merge, reel off raw silk from cocoons makes.
In a preferred embodiment of the present invention, described nano-bamboo carbon is to be raw material by old bamboo, lasts 30 days under 1000 ℃ of-1150 ℃ of high temperature, and pyrolysis, distillation, carbonization form.
In a preferred embodiment of the present invention, described per distribution ratio is as follows: whitening fiber 15%-20%, uvioresistant fiber 15%-18%, acrylic fibers 6 fiber 80%-85%.。
The present invention has disclosed a kind of preparation technology of whitening sun protection clothing, this whitening sun protection clothing has acted on slim and graceful, the attractive and durable characteristics of normal laundry quality, have the excellent uvioresistant and the special efficacy of skin whitening simultaneously, good permeability, manufacturing cost are not high, are particularly suitable for wearing when summer, heat was hot.
Description of drawings
The present invention is further detailed explanation below in conjunction with the drawings and specific embodiments:
Fig. 1 is preparation technology's flow chart of a kind of whitening sun protection clothing of the embodiment of the invention;
The specific embodiment
In order to make those skilled in the art person understand technical scheme of the present invention better, and above-mentioned purpose of the present invention, feature and advantage can be become apparent more, the present invention is further detailed explanation below in conjunction with embodiment.
Embodiment 1
At first, preparation whitening fiber and uvioresistant fiber;
The preparation process of whitening fiber is as follows: 1) heat drying polyster fibre and nano-pearl fiber; 2) with the nano-pearl fibers melt in polyster fibre, make the spinning fluid; 3) at 220 ℃, force value is under the condition of 1.1MPa the spinning fluid of fusion to be extruded from spinneret orifice, is frozen into silk by cooling medium water; 4) with the fiber that makes by twisting, wash operations such as pressure, drying, thermal finalization, obtain the whitening fiber fiber.
Uvioresistant fiber then adopts processes such as nano-carbon powder that nano-bamboo carbon makes and fraction silk, fiber crops, hair operation such as merge, reel off raw silk from cocoons to make, and wherein nano-bamboo carbon is to be raw material by old bamboo, lasts 30 days under 1100 ℃ of high temperature, and pyrolysis, distillation, carbonization form.
Secondly, whitening fiber, uvioresistant fiber and acrylic fibers 6 fibers are carried out proportioning according to following percentage composition: whitening fiber 15%, uvioresistant fiber 20%, acrylic fibers 6 fibers 65%.
Then, bar is made in whitening fiber opening picking, comb and parallel cotton fibers prior to spinning, uvioresistant fiber and acrylic fibers 6 fiber mixing, opening picking, comb and parallel cotton fibers prior to spinning are made blended sliver.Make scribbled by drafting, rove, spun yarn winder.
At last, scribbled is made knit fabric and then make the whitening sun protection clothing.
Embodiment 2
At first, preparation whitening fiber and uvioresistant fiber;
The preparation process of whitening fiber is as follows: 1) heat drying polyster fibre and nano-pearl fiber; 2) with the nano-pearl fibers melt in polyster fibre, make the spinning fluid; 3) at 220 ℃, force value is under the condition of 1.1MPa the spinning fluid of fusion to be extruded from spinneret orifice, is frozen into silk by cooling medium water; 4) with the fiber that makes by twisting, wash operations such as pressure, drying, thermal finalization, obtain the whitening fiber fiber.
Uvioresistant fiber then adopts processes such as nano-carbon powder that nano-bamboo carbon makes and fraction silk, fiber crops, hair operation such as merge, reel off raw silk from cocoons to make, and wherein nano-bamboo carbon is to be raw material by old bamboo, lasts 30 days under 1100 ℃ of high temperature, and pyrolysis, distillation, carbonization form.
Secondly, whitening fiber, uvioresistant fiber and acrylic fibers 6 fibers are carried out proportioning according to following percentage composition: whitening fiber 16%, uvioresistant fiber 18%, acrylic fibers 6 fibers 66%.
Then, bar is made in whitening fiber opening picking, comb and parallel cotton fibers prior to spinning, uvioresistant fiber and acrylic fibers 6 fiber mixing, opening picking, comb and parallel cotton fibers prior to spinning are made blended sliver.Make scribbled by drafting, rove, spun yarn winder.
At last, scribbled is made knit fabric and then make the whitening sun protection clothing.
The present invention has disclosed a kind of preparation technology of whitening sun protection clothing, this whitening sun protection clothing has acted on slim and graceful, the attractive and durable characteristics of normal laundry quality, have the excellent uvioresistant and the special efficacy of skin whitening simultaneously, good permeability, manufacturing cost are not high, are particularly suitable for wearing when summer, heat was hot.
Protection scope of the present invention is not limited thereto, and anyly is familiar with those skilled in the art in the technical scope that the present invention discloses, and the variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claim was defined.
Claims (8)
1. the invention provides a kind of preparation technology of whitening sun protection clothing, this processing step is as follows: at first, preparation whitening fiber and uvioresistant fiber are as getting the raw materials ready; Secondly, whitening fiber, uvioresistant fiber and acrylic fibers 6 fibers are carried out proportioning according to certain percentage composition; Then, respectively the composite fibre of whitening fiber and uvioresistant fiber and acrylic fibers 6 fibers is carried out opening picking, carding step is made bar; Then, two kinds of ribbons with gained make scribbled through drafting, rove, spun yarn winder; At last, make the gained scribbled knitting or woven fabric and then make the whitening sun protection clothing.
2. preparation technology according to claim 1 is characterized in that, described whitening fiber is to add the nano-pearl fiber in polyster fibre, makes by melt spinning process.
3. preparation technology according to claim 2 is characterized in that, described melt spinning process may further comprise the steps: 1) heat drying raw material (polyster fibre and nano-pearl fiber); 2) with the nano-pearl fibers melt in polyster fibre, make the spinning fluid; 3) under constant compression force and temperature, the spinning fluid of fusion is extruded from spinneret orifice, be frozen into silk by cooling medium; 4) with the fiber that makes by twisting, wash operations such as pressure, drying, thermal finalization, obtain the whitening fiber fiber.
4. preparation technology according to claim 3 is characterized in that, the spinning fluid of described fusion is at 220 ℃-240 ℃, and force value is to extrude from spinneret orifice under the condition of 1.1MPa.
5. preparation technology according to claim 2 is characterized in that, described cooling medium is the aqueous solution.
6. preparation technology according to claim 1 is characterized in that, described uvioresistant fiber is that processes such as the nano-carbon powder made by nano-bamboo carbon and fraction silk, fiber crops, hair operation such as merge, reel off raw silk from cocoons makes.
7. preparation technology according to claim 6 is characterized in that, described nano-bamboo carbon is to be raw material by old bamboo, lasts 30 days under 1000 ℃ of-1150 ℃ of high temperature, and pyrolysis, distillation, carbonization form.
8. preparation technology according to claim 1 is characterized in that, described per distribution ratio is as follows: whitening fiber 15%-20%, uvioresistant fiber 15%-18%, acrylic fibers 6 fiber 80%-85%.