CN101914869A - Porous-starch-containing water-based paint for cigarette wrapping paper - Google Patents

Porous-starch-containing water-based paint for cigarette wrapping paper Download PDF

Info

Publication number
CN101914869A
CN101914869A CN 201010238757 CN201010238757A CN101914869A CN 101914869 A CN101914869 A CN 101914869A CN 201010238757 CN201010238757 CN 201010238757 CN 201010238757 A CN201010238757 A CN 201010238757A CN 101914869 A CN101914869 A CN 101914869A
Authority
CN
Grant status
Application
Patent type
Prior art keywords
water
parts
starch
porous
based paint
Prior art date
Application number
CN 201010238757
Other languages
Chinese (zh)
Inventor
代家红
何金星
尹康德
常忠
Original Assignee
玉溪思润印刷有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

The invention provides a porous-starch-containing water-based paint for cigarette wrapping paper, aiming to the improve the condition that at present, the function of wrapping paper is only limited to binding up tobacco shreds and has no direct effect on reducing harms and improving the taste of the cigarettes. The water-based paint comprises the following raw materials in parts by weight: 100 parts of water, 8-30 parts of porous starch, 5-15 parts of carboxymethylcellulose and 3-12 parts of guar gum. The water-based paint is prepared from the following steps of: heating water up to 60-100 DEG C; and sufficiently stirring the mixture of the porous starch, the carboxymethylcellulose and the guar gum with the water to prepare a crosslinking mixed liquor so as to obtain the water-based paint for the cigarette wrapping paper. The water-based paint for the cigarette wrapping paper can be better adhered on the wrapping paper so as to reduce harmful substances in cigarette smoke; because the water is used as the solvent, volatile organic solvent residues do not exist after coating; and the water-based paint has the advantages of energy saving, safety without pollution and safer suction.

Description

含多孔淀粉的卷烟成型纸用水性涂料 The starch-containing porous cigarette paper forming an aqueous coating

技术领域 FIELD

[0001] 本发明属于一种加工成品纸的涂料。 [0001] The present invention pertains to the coating of processing a finished paper. 背景技术 Background technique

[0002] 众所周知,卷烟烟雾中含有多种有害物质,吸烟后这些有害成份沉积在人体内会引发肺部、呼吸道以及胃部等脏器产生多种疾病,虽然大家都知道吸烟有害于健康,但香烟具有提神、醒脑的多种功能,适当吸烟能使人兴奋、激发灵感、提高工作效率,所以烟民们还是很难戒烟。 [0002] As we all know, cigarette smoke contains many harmful substances deposited after smoking these harmful ingredients in the human body can cause lung, stomach and respiratory tract and other organs produce a variety of diseases, although we all know that smoking is harmful to health, but cigarettes with a refreshing, refreshing variety of functions, appropriate smoking can make people excited, inspired, improve work efficiency, so smokers are still difficult to quit smoking.

[0003] 多孔淀粉又名微孔淀粉,是由天然植物原料,经现代生物工程技术加工制成的具有高效吸附性能的降焦减害剂。 [0003] Porous starch, also known as microporous starch, tar is less harmful agents from natural plant raw materials, processing of modern biotechnology has made high adsorption properties. 它具有生淀粉酶活力的酶在低于糊化温度下作用于生淀粉而形成的多孔性蜂窝状产物。 An enzyme having raw amylase action in the porous honeycomb raw starch product formed below the gelatinization temperature. 微孔淀粉表面布满直径为Iym左右的小孔,小孔由表面向中心深入,孔的容积占颗粒体积的50%左右。 Microporous starch surface covered with a diameter of about Iym aperture, orifice depth from the surface to the center, the volume of the hole about 50 percent by volume of the particles. 将天然生淀粉经过水解处理以后,在其颗料表面形成小孔,并一直延伸到颗粒内部,是一种类似马蜂窝状的中空颗粒,可以盛装各种物质于其中,具有吸附能力强的特点,特别对含有链状和芳香族有机化合物、含孤对电子的新核化合物具有很强的选择性吸附力。 After natural raw starch hydrolysis process after forming the hole on the granule surface, and extends into the interior of the particles, similar to a horse honeycomb hollow particles, containing various substances therein, having a strong adsorption capacity characteristic, and especially for a chain containing an aromatic organic compound containing a lone highly selective adsorption force to the new core compound electrons.

[0004] 随着人们对健康的关注越来越高,“吸烟与健康”问题已越来越受到重视,人们对卷烟提出了更高的要求,不但要求其具有很好的口感,而且要能降低卷烟对人体的危害,而作为卷烟滤棒重要组成部分的成型纸,目前的功能仅限于将丝束捆绑起来,如何有效的对成型纸进行改进,将其同具有能吸附焦油、烟碱,粒相物、改善吸味功能的多孔淀粉结合起来,使其在对丝束进行包覆的同时,也能有效降低卷烟烟气中的有害成分,并且不会降低多孔淀粉自身的吸附功能,充分发挥其作为卷烟辅料的降害作用,已成为烟草科技发展的方向。 [0004] As people become increasingly concerned about health, "smoking and health" issue has been more and more attention, people put forward higher requirements cigarettes, not only required to have good taste, but also to be able to reduce cigarette harm to human body, and as forming an important part of the paper cigarette filter, the current functionality is limited to the tow tied up, how to effectively improve the molded paper, it has the same energy absorption tar, nicotine, particulate matter, improving smoke flavor porous starch functions combine to make it the same time the coated tow, can effectively reduce the harmful components in cigarette smoke, porous starch without compromising their adsorption function, fully to play its role in reducing harmful as cigarette accessories, tobacco has become the direction of technological development.

发明内容 SUMMARY

[0005] 本发明旨在提供一种能很好的粘附在成型纸上,并能减少卷烟烟气中的有害物质,生产工艺简单、安全无污染的含多孔淀粉的成型纸用水性涂料。 [0005] The present invention aims to provide a good adherence to the forming sheet, and can reduce the harmful substances in cigarette smoke, the production process is simple, safe and non-polluting starch-containing porous plugwrap water-based coating.

[0006] 本发明通过以下技术手段来实现上述目的: [0006] The present invention achieves the above object is achieved by the following technical means:

[0007] —种含多孔淀粉的卷烟成型纸用水性涂料,所用原料按重量份数计算配比如下: 水100份,多孔淀粉8〜30份,羧甲基纤维素5〜15份,瓜尔胶3〜12份。 [0007] - species cigarette paper forming an aqueous coating containing porous starch starting material was prepared as follows in parts by weight calculated used: 100 parts of water, parts of porous starch 8~30, 5~15 parts of carboxymethyl cellulose, guar glue 3~12 parts.

[0008] 优选地,所用原料按重量份数计算配比如下冰100份,多孔淀粉10〜20份,羧甲基纤维素6〜10份,瓜尔胶4〜6份。 [0008] Preferably, the ratio of raw materials in parts by weight calculated as 100 parts of ice, porous starch 10-20 parts, 6~10 parts carboxymethyl cellulose, guar gum with 4 ~ 6 parts.

[0009] 按照以下方法制备:将水加热到60〜100°C,用水将多孔淀粉、羧甲基纤维素、瓜尔胶的混合物充分搅拌,制得交联混合液,即得卷烟成型纸用水性涂料。 [0009] was prepared according to the following method: The water was heated to 60~100 ° C, water and porous starch, carboxymethyl cellulose, guar gum mixture was sufficiently stirred to obtain a mixture of cross-linking, to obtain a cigarette wrap water-based paint.

[0010] 有益效果 [0010] beneficial effects

[0011] ①本发明所述的成型纸用水性涂料能很好的粘附在成型纸上,能有效保证多孔淀粉的功能,以减少卷烟烟气中的有害物质; [0011] ① wrap aqueous coating material according to the present invention can be formed in good adherence to the paper, porous starch can effectively guarantee function to reduce the harmful substances in cigarette smoke;

3[0012] ②本发明生产工艺简单,成本低,采用水作为溶剂,涂布后无挥发性有机溶剂残留问题,节约能源,安全无污染,抽吸更安全; 3 [0012] ② of the present invention, the production process is simple, low cost, using water as a solvent, volatile organic solvent after coating residues, energy conservation, safety and pollution-free, safe pumping;

[0013] ③羧甲基纤维素能够增强纸的强度,提高了涂布成型纸的成品率。 [0013] ③ carboxymethylcellulose paper strength can be enhanced, improving the yield of coated wrap. 具体实施方式 detailed description

[0014] 下面结合具体实施例对本发明作进一步说明。 [0014] The following embodiments in conjunction with specific embodiments of the present invention will be further described.

[0015] 实施例1 [0015] Example 1

[0016] 一种含多孔淀粉的卷烟成型纸用水性涂料,所用原料为:水100g,多孔淀粉10g, 羧甲基纤维素5g,瓜尔胶3g ;将上述原料按照以下步骤制备得卷烟成型纸用水性涂料:将水加热到60°C,用水将多孔淀粉、羧甲基纤维素、瓜尔胶搅拌使其充分溶解熟化,制得交联混合液,即得卷烟成型纸用水性涂料。 [0016] A starch-containing porous cigarette paper forming an aqueous coating material, used as raw material: water 100g, porous starch 10g, carboxymethyl cellulose 5g, guar gum 3G; the above raw materials was prepared as follows to give cigarette wrap Waterborne coating: the water was heated to 60 ° C, water and porous starch, carboxymethyl cellulose, guar gum aged with stirring to fully dissolve, to obtain a mixture of cross-linking, i.e., the cigarette wrap to obtain an aqueous coating material.

[0017] 实施例2 [0017] Example 2

[0018] 一种含多孔淀粉的卷烟成型纸用水性涂料,所用原料为:水100g,多孔淀粉20g, 羧甲基纤维素15g,瓜尔胶12g ;将上述原料按照以下步骤制备得卷烟成型纸用水性涂料: 将水加热到ioo°c,用水将多孔淀粉、羧甲基纤维素、瓜尔胶搅拌使其充分溶解熟化,制得交联混合液,即得卷烟成型纸用水性涂料。 [0018] A starch-containing porous cigarette paper forming an aqueous coating material, used as raw material: water 100g, porous starch 20g, carboxymethyl cellulose 15g, 12g guar gum; have the above prepared cigarette wrap material in accordance with the following steps Waterborne coating: the water was heated to ioo ° c, the water porous starch, carboxymethyl cellulose, guar gum aged with stirring to fully dissolve, to obtain a mixture of cross-linking, i.e., the cigarette wrap to obtain an aqueous coating material.

[0019] 实施例3 [0019] Example 3

[0020] 一种含多孔淀粉的卷烟成型纸用水性涂料,所用原料为:水100g,多孔淀粉30g, 羧甲基纤维素6g,瓜尔胶4g ;将上述原料按照以下步骤制备得卷烟成型纸用水性涂料:将水加热到70°C,用水将多孔淀粉、羧甲基纤维素、瓜尔胶搅拌使其充分溶解熟化,制得交联混合液,即得卷烟成型纸用水性涂料。 [0020] A starch-containing porous cigarette paper forming an aqueous coating material, used as raw material: water 100g, porous starch 30g, carboxymethylcellulose 6g, guar gum 4G; above prepared material obtained according to the following steps cigarette wrap Waterborne coating: the water was heated to 70 ° C, water and porous starch, carboxymethyl cellulose, guar gum aged with stirring to fully dissolve, to obtain a mixture of cross-linking, i.e., the cigarette wrap to obtain an aqueous coating material.

[0021] 实施例4 [0021] Example 4

[0022] 一种含多孔淀粉的卷烟成型纸用水性涂料,所用原料为:水100g,多孔淀粉15g, 羧甲基纤维素10g,瓜尔胶6g ;将上述原料按照以下步骤制备得卷烟成型纸用水性涂料:将水加热到80°C,用水将多孔淀粉、羧甲基纤维素、瓜尔胶搅拌使其充分溶解熟化,制得交联混合液,即得卷烟成型纸用水性涂料。 [0022] A starch-containing porous cigarette paper forming an aqueous coating material, used as raw material: water 100g, porous starch 15g, carboxymethyl cellulose 10g, guar gum 6g; the above raw materials was prepared as follows cigarette wrap to give Waterborne coating: the water was heated to 80 ° C, water and porous starch, carboxymethyl cellulose, guar gum aged with stirring to fully dissolve, to obtain a mixture of cross-linking, i.e., the cigarette wrap to obtain an aqueous coating material.

[0023] 实施例5 [0023] Example 5

[0024] 一种含多孔淀粉的卷烟成型纸用水性涂料,所用原料为:7jC 100g,多孔淀粉12g, 羧甲基纤维素8g,瓜尔胶5g ;将上述原料按照以下步骤制备得卷烟成型纸用水性涂料:将水加热到90°C,用水将多孔淀粉、羧甲基纤维素、瓜尔胶搅拌使其充分溶解熟化,制得交联混合液,即得卷烟成型纸用水性涂料。 [0024] A starch-containing porous cigarette paper forming an aqueous coating material, used as raw materials: 7jC 100g, porous starch 12g, carboxymethylcellulose 8g, guar gum 5g; prepared in the above raw materials to give the following steps cigarette wrap Waterborne coating: the water was heated to 90 ° C, water and porous starch, carboxymethyl cellulose, guar gum aged with stirring to fully dissolve, to obtain a mixture of cross-linking, i.e., the cigarette wrap to obtain an aqueous coating material.

4 4

Claims (2)

  1. 一种含多孔淀粉的卷烟成型纸用水性涂料,其特征在于,所用原料按重量份数计算配比如下:水100份,多孔淀粉8~30份,羧甲基纤维素5~15份,瓜尔胶3~12份,制备方法如下:将水加热到60~100℃,用水将多孔淀粉、羧甲基纤维素、瓜尔胶的混合物充分搅拌,制得交联混合液,即得卷烟成型纸用水性涂料。 Starch containing porous cigarette paper forming an aqueous coating material, characterized in that, in parts by weight calculated as a raw material was prepared as follows: 100 parts of water, 8 to 30 parts by porous starch, carboxymethyl cellulose, 5 to 15 parts, melon guar 3 to 12 parts, was prepared as follows: water was heated to 60 ~ 100 ℃, water and porous starch, carboxymethyl cellulose, guar gum mixture was sufficiently stirred to prepare a crosslinked mixture was molded to obtain cigarettes aqueous paper coating.
  2. 2.根据权利要求1所述的含多孔淀粉的卷烟成型纸用水性涂料,其特征在于,所用原料按重量份数计算配比如下冰100份,多孔淀粉10〜20份,羧甲基纤维素6〜10份,瓜尔胶4〜6份。 The starch-containing porous cigarette paper forming an aqueous coating material according to claim 1, characterized in that the materials used in parts by weight calculated as proportion of 100 parts of ice, porous starch 10-20 parts of carboxymethyl cellulose 6~10 parts of guar gum 4 ~ 6 parts.
CN 201010238757 2010-07-28 2010-07-28 Porous-starch-containing water-based paint for cigarette wrapping paper CN101914869A (en)