CN101904665A - Manufacture method of decorated glass vessel - Google Patents

Manufacture method of decorated glass vessel Download PDF

Info

Publication number
CN101904665A
CN101904665A CN2009100400130A CN200910040013A CN101904665A CN 101904665 A CN101904665 A CN 101904665A CN 2009100400130 A CN2009100400130 A CN 2009100400130A CN 200910040013 A CN200910040013 A CN 200910040013A CN 101904665 A CN101904665 A CN 101904665A
Authority
CN
China
Prior art keywords
glass
vessel
decorated
glass vessel
flat glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009100400130A
Other languages
Chinese (zh)
Inventor
黄学强
Original Assignee
黄学强
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 黄学强 filed Critical 黄学强
Priority to CN2009100400130A priority Critical patent/CN101904665A/en
Publication of CN101904665A publication Critical patent/CN101904665A/en
Pending legal-status Critical Current

Abstract

The invention discloses a manufacture method of a decorated glass vessel. The preparation method comprises the following steps of: firstly, preparing a vessel shape die; cutting flat glass according to the vessel shape; pasting stained paper on the surface of the flat glass or painting the flat glass; mounting the flat glass on the die; and roasting the die in a kiln into a finished glass vessel product by one step under a high temperature capable of surely softening glass while melting patterns on the stained paper or the painted patterns on the surface of the glass vessel. In the roasting process, the decorated glass vessel is roasted at the glass-softening temperature, melted stained paper pigments are permeated in the shallow surface of the softened glass for mutual combination so that the product has smooth surface and vivid colors and resists abrasion and shedding, and the like. Meanwhile, the invention has the advantages of using the flat glass as a forming base and being convenient and simple to purchase in comparison with the prior art. The vessel shape forming and pattern forming of the invention product are finished in the same procedure to facilitate the independent development of the product vessel shape. In the pasting process, patterns are pasted on the upper surface of the flat glass, and the pasting process has the advantages of simple and easy operation, small errors and high efficiency.

Description

A kind of preparation method of decorated glass vessel
Technical field
The present invention relates to a kind of preparation method of manufacturing process field, particularly a kind of decorated glass vessel of glassware.
Background technology
At present the firework technology of utility glass ware is after pasting glass marble paper or colored drawing on the glassware that has formed by a firing, and makes through kiln roasting (burnings), make on the glass marble paper or the pigment clinkering of colored drawing on the surface of glassware.This firework technology, it mainly is glassware based on moulding, in order to prevent at high temperature to be out of shape, therefore can only be in kiln with lower temperature baking (melt temperature with marble paper or coloured drawing pigment is a benchmark), but when temperature is not high, will cause colored face bonding degree relatively poor, the surface is smooth inadequately, and easy to wear, come off, the quality to product is caused great influence.Particularly the consumer in use if the flower emaciated face falls, may sneak in the food of glassware, and consumer healthy also caused disadvantageous consequence.If but adopted higher baking temperature to improve colored face sintering quality, then the glassware easy deformation would cause percent defective and defect rate to raise.And, owing to be to adopt in type glassware to be the basis, therefore on product type style and price, be subjected to the restriction of glassware manufacturer.
Summary of the invention
The technical problem to be solved in the present invention is to overcome the shortcoming of prior art, provides a kind of and spends that face is smooth, not easy to wear, the preparation method of the decorated glass vessel of difficult drop-off.
Realize that technical scheme of the present invention is: a kind of preparation method of decorated glass vessel, it is characterized in that: make type mold earlier, cut plate glass by type, behind surface of plate glass decal paper or colored drawing, be contained in the kiln baking of going forward side by side on the mould, under with the softening high temperature of assurance glass, a baking becomes the glassware finished product, on the marble paper or the clinkering simultaneously of the pattern of colored drawing on the dinner glass surface.
The bottom surface of described type mold forming surface is provided with steam vent.Described steam vent is one or more, so that the air between glass and mould is discharged smoothly.
The shape of described type mold adapts with the decorated glass vessel that will make.
The softening high temperature of described glass is 800 ℃-900 ℃.
The present invention and prior art have following difference:
1, in the baking process, the present invention is with the glass transition temperature baking, and the fusing flower color infiltrates the softening shallow table of glass, and both fuse mutually, make product have smooth surface, and pattern is bright-coloured, and is not easy to wear, advantages such as difficult drop-off.
2, the moulding of product basis is different, and the present invention is the moulding basis with plate glass, and prior art then adopts various molded glasswares to be the basis, and is convenient, simple than prior art in material purchases;
3, the type moulding of product of the present invention and firework are molded in the same operation and finish; And need elder generation in the prior art, and then finish the firework moulding on the type surface with the type moulding; Compared with prior art the present invention can control the independence of product type exploitation;
4, the present invention is at the enterprising parallel planes applique of plate glass in the applique process, and prior art is for to carry out three-dimensional applique in type vessel surface, and compared with prior art the present invention is simple to operate in applique process, easy, error is little, efficient is high.
Description of drawings
Fig. 1 is the schematic diagram before the decorated glass vessel loading of kiln of the present invention;
Fig. 2 is the schematic diagram of decorated glass vessel of the present invention when burning till.
The specific embodiment
Be described further below in conjunction with the manufacturing process of the drawings and specific embodiments decorated glass vessel of the present invention.The type design and fabrication mould 1 of the decorated glass vessel that makes at first as required is schematic diagram as shown in Figure 1, and according to product type difference, the shape of mould is also different.After then plate glass 2 size as required being cut and cleans up, on plate glass 2, stick the paster 3 of printed colored face pattern, the mould 1 of packing into then and making in advance, as shown in Figure 1.Then mould 1 is advanced kiln with the plate glass 2 of band paster 3, guaranteeing that a baking becomes glassware 5 finished products, makes colored face pattern fuse into glassware 5 surfaces under the suitably softening high temperature of glass, when burning till as shown in Figure 2.Wherein the suitably softening high temperature of glass is 800 ℃-900 ℃, for example can select 850 ℃ for use, specifically according to thickness, the size of plate glass 2 and want the complexity of the glassware 5 of moulding to decide.In addition, discharge smoothly, be provided with one or more steam vents 4 in the bottom surface of mould 1 forming surface for the air that makes 1 in glass 2 and mould in the baking process.Formed product stage of the present invention and color roasting technology are merged into an operation, are finished by the color roasting kiln, and the formed product that is different from prior art is before color roasting technology, and first glassware workshop is finished, and then carry out color roasting technology.
Wherein, in above-mentioned manufacturing process, also can replace paster 3 by carrying out colored drawing on plate glass 2 surfaces.
Generally speaking, the present invention is affixed on plate glass 2 surfaces of having cut out shape by the colored face Pattern paste paper 3 with printed glass pigment, and 2 bakings become the utility glass ware 5 of different shape to plate glass with suitable temperature and atmosphere glass 2 to be gone into kiln again.The present invention comes baking and baking to make in the process that the high temperature baking is yielding, the smooth inadequately shortcoming bright-coloured, easy to wear of low temperature baking flower face having solved on the technology at the higher molded glassware of existing glass firework arts demand procurement price.Thereby can autonomous Design product type style, by improving product baking temperature, make product surface smooth and not easy to wear, simplified production technology simultaneously, reduce production costs.

Claims (5)

1. the preparation method of a decorated glass vessel, it is characterized in that: make type mold earlier, cut plate glass by type, behind surface of plate glass decal paper or colored drawing, be contained in the kiln baking of going forward side by side on the mould, under with the softening high temperature of assurance glass, a baking becomes the glassware finished product, on the marble paper or the clinkering simultaneously of the pattern of colored drawing on the dinner glass surface.
2. the preparation method of decorated glass vessel according to claim 1, it is characterized in that: the bottom surface of described type mold forming surface is provided with steam vent.
3. the preparation method of decorated glass vessel according to claim 2, it is characterized in that: described steam vent is one or more.
4. the preparation method of decorated glass vessel according to claim 1 is characterized in that: the shape of described type mold adapts with the decorated glass vessel that will make.
5. the preparation method of decorated glass vessel according to claim 1 is characterized in that: the softening high temperature of described glass is 800 ℃-900 ℃.
CN2009100400130A 2009-06-05 2009-06-05 Manufacture method of decorated glass vessel Pending CN101904665A (en)