CN101879834B - Decoration method capable of forming raised picture on ceramic green body - Google Patents

Decoration method capable of forming raised picture on ceramic green body Download PDF

Info

Publication number
CN101879834B
CN101879834B CN 201010202197 CN201010202197A CN101879834B CN 101879834 B CN101879834 B CN 101879834B CN 201010202197 CN201010202197 CN 201010202197 CN 201010202197 A CN201010202197 A CN 201010202197A CN 101879834 B CN101879834 B CN 101879834B
Authority
CN
China
Prior art keywords
picture
firing
glaze
green
decoration
Prior art date
Application number
CN 201010202197
Other languages
Chinese (zh)
Other versions
CN101879834A (en
Inventor
张洪波
Original Assignee
张志强
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张志强 filed Critical 张志强
Priority to CN 201010202197 priority Critical patent/CN101879834B/en
Publication of CN101879834A publication Critical patent/CN101879834A/en
Application granted granted Critical
Publication of CN101879834B publication Critical patent/CN101879834B/en

Abstract

The invention discloses a decoration method capable of forming a raised picture on a ceramic green body, which belongs to the technical field of ceramic decoration and solves the problems of unnatural rise of the profile of the raised pattern picture on the green body, non-singular production, limited glaze and pattern raised height and undesirable embossment effect of the prior art. The method comprises: a step of preparing a coating, in which 40 to 60 weight parts of color chips and 35 to 65 weight parts of 95 weight percent ethanol are proportioned in a container, and when the color chips are dissolved completely and the solution become pasty, stirring the solution uniformly; and a step of making the raised picture on the green body, in which the green body is completely cleaned, a picture is drawn on the green body with the prepared coating, the coating is allowed to be dried completely after the picture is drawn, the picture is cleaned slightly by sponge dipped with water repeatedly till the picture shows a three-dimensional effect, and the raised picture is made by biscuiting and color decoration. With raised picture, the decoration effect and quality are more outstanding; and the raised part is natural and smooth without any unnatural feel that is offered by a caving mold. The method can draw natural and vivid pictures on three-dimensional and flat green bodies freely so as to create artistic conception and special artistic effect.

Description

A kind of trailing that forms raised picture on ceramic green body

Technical field

The present invention relates to the trailing of picture projection in a kind of ceramic decoration, belong to the ceramic decoration technical field.

Background technology

At present, the trailing of the ceramic picture projection of using in Production of Ceramics substantially is divided into and decorates on blue or green base and decorate two large classes on glaze, decorates on blue or green base and divides again engraving and mould to suppress two kinds.Although decorate the picture clear-cut on blue or green base, its shortcoming is smoothness, nature and flexible and the diversity that there is no the Freehandhand-drawing picture, and stiff sense is arranged, and especially mould compacting is only suitable for batch production, is not suitable for single drafting; The shortcoming of decorating on glaze is the picture relief that is not easy to do, and the high-temperature firing picture easily flows, and three-dimensional ceramic type is more easily met the high temperature trickling, can not form profile and color picture clearly.In view of this, how to overcome defects, make the protruding colored decoration technology of base be more widely used, opening up new field for ceramic decoration production is the problem that the ceramic industry technical staff needs to be resolved hurrily.

Summary of the invention

Technical problem to be solved by this invention is to provide a kind of trailing that forms raised picture on ceramic green body, to solve not nature of the protruding colored picture profile projection of prior art base, can not singlely produce, the protruding colored height of projection of glaze is restricted, the difficult problem that anaglyph is undesirable.

The technical scheme that solves the problems of the technologies described above is:

A kind of trailing that forms raised picture on ceramic green body, it carries out according to following steps:

1, preparation coating: take by weight coating agent which has to be dissolved in alcohol before use 40-60, concentration expressed in percentage by weight and be in 95% ethanol 35-65 to a container, steep to dissolve fully to coating agent which has to be dissolved in alcohol before use and be thick, stir;

2, make raised picture on blue or green base:

(1) prepare blue or green base and draw tool, comprise the drawing coating that writing brush and above-mentioned steps make;

(2) with blue or green base wiped clean, according to creation request, with the coating rendered frame on blue or green base that modulates;

(3) treat that coating parches after painting, dip in water wiping gently with sponge, repeatedly dip in water with sponge, wiping repeatedly is until picture is stereoeffect;

3, biscuiting:

The base substrate of completing the projection decoration is fired, and firing temperature is 1150 ℃--1250 ℃, firing time is 6-10 hour, and the coating agent which has to be dissolved in alcohol before use solvent on base substrate volatilizees when the high temperature biscuiting fully.Because whole base substrate is the consubstantiality material, the part of projection is namely blue or green base itself, so biscuiting can not make blank deformation;

4, colored drawing: can adopt underglaze colour to paint or over-glaze decoration:

(1) underglaze colour is painted: according to the creation demand, painting with high temperature decorating colour under glaze on plain tire, then forming through glaze spraying, glaze firing.Temperature of glaze firing is 1000 ℃-1100 ℃, and firing time is 6-10 hour;

(2) over-glaze decoration: plain tire according to creation request, is painted with the low temperature colorant on vitreous enamel, then is formed through color roasting after glaze spraying, glaze firing, and the color roasting temperature is 700 ℃-850 ℃, and firing time is 4-8 hour.

The above-mentioned trailing that forms raised picture on ceramic green body, in described biscuiting step, preferred firing temperature is 1150 ℃-1200 ℃, firing time is 7-9 hour; In described glaze firing step, preferred firing temperature is 1050 ℃-1100 ℃, and firing time is 7-9 hour; In described color roasting step, preferred firing temperature is 750 ℃-800 ℃, and firing time is 5-7 hour.

Coating agent which has to be dissolved in alcohol before use claims again shellac, is a kind of insect secretion on the trees of torrid areas, and Main Ingredients and Appearance is resin, wax, pigment and other hydrotrope etc.Water insoluble, be dissolved in the organic solvents such as ethanol, can quick-drying and produce gloss, decoration, durable film, the surface of various objects is shown the adherence of height, firm and high resilience.Therefore, waterproof, protection against the tide, the characteristics such as antirust are arranged, object is shielded, on sale in the industrial chemicals shop.Though containing the lower alcohol of hydroxyl, the available methyl alcohol of component ethanol, propyl alcohol etc. substitute, because other solvent that dissolves coating agent which has to be dissolved in alcohol before use except ethanol has certain harm to human body, therefore preferred alcohol is made dissolving coating agent which has to be dissolved in alcohol before use two solvents.

Use this trailing to make picture projection decorative effect texture outstanding, jut is natural and tripping, there is no the stiff sense of engraved die.No matter can paint freely on the blue or green base of solid or plane, method is simple, naturally lively, is rich in artistic conception, embodies a kind of special artistic effect, for new field is opened up in ceramic decoration production.

The specific embodiment:

The present embodiment forms for using following coating to carry out rendered frame the method that protruding flower is decorated " Fuchun Village figure " on kettle.Carry out according to the following steps:

1, preparation coating (claiming again solvent)

Below several components (in weight portion, the concentration expressed in percentage by weight of ethanol is 95%) that form protruding colored decorative paint embodiment on ceramic green body.

Embodiment 1: coating agent which has to be dissolved in alcohol before use 40, ethanol 50.

Embodiment 2: coating agent which has to be dissolved in alcohol before use 60, ethanol 35.

Embodiment 3: coating agent which has to be dissolved in alcohol before use 50, ethanol 60.

Embodiment 4: coating agent which has to be dissolved in alcohol before use 45, ethanol 42.

Embodiment 5: coating agent which has to be dissolved in alcohol before use 55, ethanol 45.

Embodiment 6: coating agent which has to be dissolved in alcohol before use 48, ethanol 55.

Embodiment 7: coating agent which has to be dissolved in alcohol before use 40, ethanol 65.

Embodiment 8: coating agent which has to be dissolved in alcohol before use 52, ethanol 40.

According to putting into a container after the composition of above-described embodiment coating and weight portion weighing, infusion 2-3 hour (the infusion time in winter can be longer) soaks rear coating agent which has to be dissolved in alcohol before use and dissolves be thick fully.Stir, flow down as good as the pearl of the line that broken with the nib dipping coating.Specifically can add again a small amount of ethanol according to creator's needs, the viscosity of coating is finely tuned.

2, make raised picture on blue or green base:

(1) prepare the blue or green base of a kind of teapot, writing brush, drawing coating agent which has to be dissolved in alcohol before use solvent material;

(2) with the blue or green base wiped clean of teapot, according to creation request, draw Fuchun Village figure with the coatings volatile organic compounds that modulates on the blue or green base of teapot;

(3) treat that coatings volatile organic compounds parches after painting, dip in water wiping gently with sponge, repeatedly dip in water with sponge, wiping repeatedly is until picture shows required stereoeffect.Do not have the part of coating protection to be wiped out on blue or green base, have the part of coating to be protected because of the coating waterproof, can not wipe out, have like this coating partly to form projection, namely picture part forms projection.Can control the blue or green base amount of wiping according to creation request, namely control height of projection, make it form the picture of nature projection;

3, biscuiting: projection is decorated the teapot base substrate of completing fire, firing temperature is 1150 ℃-1200 ℃, and firing time is 7-9 hour;

4, colored drawing:

When (1) adopting underglaze colour to paint technique: according to the creation demand, in as red in wrapping up with high temperature decorating colour under glaze on the teapot biscuit, general Huang, the colouring such as sapphire blue, then form through glaze spraying, glaze firing, temperature of glaze firing is 1050 ℃-1100 ℃, and firing time is 7-9 hour;

When (2) adopting over-glaze decoration technique: after the oil spout of teapot biscuit process, glaze firing, according to creation request, the colourings such as reddish brown with as red in the west, the thin Huang of low temperature colorant, generation on vitreous enamel, fuchsin, then form through decoration firing, the decoration firing temperature is that 750 ℃ of-800 ℃ of firing times are 5-7 hour.

The decorative effect of the embodiment of the present invention: mountain stone third dimension nearby is obvious, and is true lively, becomes the actual situation contrast with chevron at a distance, increases the spatial impression of creation picture.

Claims (2)

1. a trailing that forms raised picture on ceramic green body, is characterized in that, it carries out according to following steps:
(1), preparation coating: take by weight coating agent which has to be dissolved in alcohol before use 40-60, concentration expressed in percentage by weight and be in 95% ethanol 35-65 to a container, steep to dissolve fully to coating agent which has to be dissolved in alcohol before use and be thick, stir;
(2), make raised picture on blue or green base:
1. prepare blue or green base and draw tool, comprise the drawing coating that writing brush and above-mentioned steps make;
2. with blue or green base wiped clean, according to creation request, with the coating rendered frame on blue or green base that modulates;
3. treat after painting that coating parches, dip in water wiping gently with sponge, repeatedly dip in water with sponge, wiping repeatedly is until picture is stereoeffect;
(3), biscuiting: the base substrate that will complete the projection decoration is fired, and firing temperature is 1150 ℃-1250 ℃, and firing time is 6-10 hour;
(4), colored drawing: adopt underglaze colour to paint or over-glaze decoration:
1. underglaze colour is painted: according to the creation demand, painting with high temperature decorating colour under glaze on plain tire, then forming through glaze spraying, glaze firing, temperature of glaze firing is 1000 ℃-1100 ℃, and firing time is 6-10 hour;
2. over-glaze decoration: biscuit according to creation request, with the colouring of low temperature colorant, then forms through color roasting on vitreous enamel after glaze spraying, glaze firing, and the color roasting temperature is 700 ℃-850 ℃, and firing time is 4-8 hour.
2. according to forming the trailing of raised picture on ceramic green body claimed in claim 1, it is characterized in that, in described biscuiting step, firing temperature is 1150 ℃-1200 ℃, and firing time is 7-9 hour; In described glaze firing step, firing temperature is 1050 ℃-1100 ℃, and firing time is 7-9 hour; In described color roasting step, firing temperature is 750 ℃-800 ℃, and firing time is 5-7 hour.
CN 201010202197 2010-06-18 2010-06-18 Decoration method capable of forming raised picture on ceramic green body CN101879834B (en)