CN101838954B - Method for producing crystal decorative paper - Google Patents
Method for producing crystal decorative paper Download PDFInfo
- Publication number
- CN101838954B CN101838954B CN201010039176XA CN201010039176A CN101838954B CN 101838954 B CN101838954 B CN 101838954B CN 201010039176X A CN201010039176X A CN 201010039176XA CN 201010039176 A CN201010039176 A CN 201010039176A CN 101838954 B CN101838954 B CN 101838954B
- Authority
- CN
- China
- Prior art keywords
- paper
- radium
- shine powder
- printing machine
- powder coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a method for producing crystal decorative paper and relates to the method for printing and producing a new product of the decorative paper, which aims to solve the problems of low production efficiency and high processing cost of the conventional method for producing a laser powder decorative plate. The invention provides the method for producing the crystal decorative paper, which comprises the following steps of: dissolving an adhesive resin into an organic solvent; adding laser powder into the solvent with uniform stirring to prepare a laser powder coating material; printing an ink bottom layer on paper; and transferring the laser powder coating material onto the ink bottom layer of the paper with a coating roll and a pressing roll, and then drying and cooling the paper. The method for producing the crystal decorative paper can realize production automation, and has sanitary and healthy production process. In addition, the product produced by the method is the soft paper product, can be stuck onto surfaces of various decorative materials and is widely used.
Description
Technical field
The invention belongs to veneer paper printing technical field, relate to the print production method that a kind of surfaces coated is covered with the facing paper new product of radium-shine bisque.
Background technology
In the prior art; With the present invention approaching be a kind of method of doing of radium-shine powder decorative panel, this method at first will be split ash polishing on plank or fiberboard, the polishing back is with mopping or the method priming that sprays paint; Make at the bottom of the solid color on the flat board; On at the bottom of the solid color, manufacture adhesive-layer and spray radium-shine powder then, do cover with polyester lacquer or UV varnish again, again through making radium-shine decorative panel after the oven dry at adhesive-layer.Radium-shine powder is to become particulate to make with the radium-shine film of plastics through grinding and processing, also radium-shine powder is called seven color powder in the market.Radium-shine decorative panel product in use, that the radium-shine powder on the primer surface can reflect fragmentarily in the sun, have is dynamic, the seven-colour-light awns as the diamond, very attractive in appearance.Its defective is when on base plate, making skin of paint, because base plate is the flat board of hard, to be difficult to carry out automatic continuous production with machinery, and its production efficiency is low, production cost is big; Radium-shine powder embeds on the adhesive-layer of base plate through the mode of spraying, and its uniformity coefficient is restive, and product quality is relatively poor; Because radium-shine powder footpath is less, the dust of kicking up during sprinkling is bigger, and contaminated environment influences health of operators.
Summary of the invention
Low for the manufacturing approach production efficiency that solves existing radium-shine powder decorative panel, processing cost big, poor product quality and the antihygienic problem of working environment; The present invention provides a kind of production method of crystal decorative paper; The crystal decorative paper that this method of using is produced; Pasting on plank or the fiberboard is alternative existing radium-shine powder decorative panel, and its embodiment is following:
A kind of production method of crystal decorative paper is characterized in that: this method may further comprise the steps:
(a) get 100 weight portion adhering resins, it is dissolved in the organic solvent of 60-70 weight portion, and in above-mentioned mixed solution, add radium-shine powder 8-12 weight portion, it is stirred, it is subsequent use to make radium-shine powder coating;
(b) in the printing element of printing machine, printing-ink bottom on paper is then with the drying in oven of paper at printing machine;
(c) the radium-shine powder coating that makes in the step (a) is put into feeding box, while stirring it is pumped in the charging tray of coater unit of printing machine;
(d) in the coater unit of printing machine; The paper that is printed with ink bottom layer in the step (b) is passed between the applicator roll of coater unit and roller platen; Applicator roll is transferred to the radium-shine powder coating in the charging tray on the ink bottom layer of paper, then paper is cooled off after the drying in oven of printing machine.
When the crystal decorative paper that uses the inventive method to make, can on the adhesive-layer of crystal decorative paper, apply one deck polyester lacquer protective layer.
As preferred version of the present invention, in the said step (a), radium-shine powder directly is the 0.1-1 millimeter, and adhering resin is a butyl acrylate, and organic solvent is butyl ester or ethyl ester.
As further improvement project of the present invention; Can get 100 parts by weight of acrylic acid butyl esters in the said step (a), it is dissolved in the butyl ester of 65 weight portions, and in above-mentioned mixed solution, add radium-shine powder 10 weight portions; It is stirred, and it is subsequent use to make radium-shine powder coating.
As further improvement project of the present invention, in the said step (b), the average longitudinal tensile strain rate of paper is 3.6%, and tensile strength is 2.7kn/m.
The crystal decorative paper that adopts said method to produce pastes on plank or the fiberboard, manufactures last layer polyester lacquer protective layer on its surface, will have identical result of use with radium-shine powder decorative panel product, alternative existing radium-shine powder decorative panel.Because the crystal decorative paper bottom is a paper; Each chromatograph of on paper, making is printed through mode of printing and is accomplished, and the continuous performance of the automation of production is higher, and radium-shine powder also is to be worked on the paper through the mode of printing; The dust of can not kicking up in the production process, production process is health relatively; The product of producing through this method in addition is soft paper product, can paste various ornament materials surface, and purposes very extensively.
Description of drawings
Fig. 1 is the structural representation of printing machine coater unit.
The specific embodiment
Embodiment one: a kind of production method of crystal decorative paper, and this method may further comprise the steps:
(a) get 100 parts by weight of acrylic acid butyl esters; It is dissolved in the butyl ester of 65 weight portions; And the adding particle diameter is radium-shine powder 10 weight portions of 0.1-1 millimeter in above-mentioned mixed solution, and it is stirred, and it is subsequent use to make radium-shine powder coating; Butyl acrylate is soluble in butyl ester, and butyl ester can be with the resin bed dissolving that is printed on picture and text on the radium-shine powder;
(b) in the printing element of printing machine, printing-ink bottom on paper 3, and oven dry in the baking oven 5 of printing machine as shown in Figure 1, the average longitudinal tensile strain rate of paper is 3.6%, tensile strength is 2.7kn/m;
(c) the radium-shine powder coating that makes in the step (a) is put into feeding box 6, stir 7 pairs of radium-shine powder coatings of bar with motor-driven and stir, radium-shine powder is fully mixed with the butyl ester solvent; Do not produce deposition or layering; When stirring, with water pump radium-shine powder coating is pumped in the charging tray 1 of coater unit of printing machine, the printing machine coater unit is as shown in Figure 1, comprises applicator roll 2, roller platen 4 and charging tray 1; Applicator roll 2 rolls with roller platen 4 and contacts, and applicator roll 2 is immersed in the radium-shine powder coating in the hopper 1;
(d) in the coater unit of printing machine; The paper that is printed with ink bottom layer in the step (b) is passed between the applicator roll 2 of coater unit and roller platen 4; Ink lay on the paper 3 is over against applicator roll 2; Applicator roll 2 dips in from hopper 1 gets radium-shine powder coating, when applicator roll 2 turns to when contacting with roller platen 4 radium-shine powder coating is stamped on the ink lay of paper 3, then paper is cooled off after the drying in oven of printing machine.
Claims (3)
1. the production method of a crystal decorative paper, it is characterized in that: this method may further comprise the steps:
(a) get 100 weight portion adhering resins, it is dissolved in the organic solvent of 60-70 weight portion, and in above-mentioned mixed solution, add radium-shine powder 8-12 weight portion, it is stirred, it is subsequent use to make radium-shine powder coating;
Said radium-shine powder directly is the 0.1-1 millimeter, and adhering resin is a butyl acrylate, and organic solvent is a butyl ester;
(b) in the printing element of printing machine, printing-ink bottom on paper is then with the drying in oven of paper at printing machine;
(c) the radium-shine powder coating that makes in the step (a) is put into feeding box, while stirring it is pumped in the charging tray of coater unit of printing machine;
(d) in the coater unit of printing machine; The paper that is printed with ink bottom layer in the step (b) is passed between the applicator roll of coater unit and roller platen; Applicator roll is transferred to the radium-shine powder coating in the charging tray on the ink bottom layer of paper, then paper is cooled off after the drying in oven of printing machine.
2. the production method of a kind of crystal decorative paper according to claim 1 is characterized in that:
Get 100 parts by weight of acrylic acid butyl esters in the said step (a), it is dissolved in the butyl ester of 65 weight portions, and in above-mentioned mixed solution, add radium-shine powder 10 weight portions, it is stirred, it is subsequent use to make radium-shine powder coating.
3. the production method of a kind of crystal decorative paper according to claim 2 is characterized in that:
In the said step (b), the average longitudinal tensile strain rate of paper is 3.6%, and tensile strength is 2.7kn/m.