CN101838510A - 一种高效树脂型灌缝胶及其制备 - Google Patents

一种高效树脂型灌缝胶及其制备 Download PDF

Info

Publication number
CN101838510A
CN101838510A CN201010189080A CN201010189080A CN101838510A CN 101838510 A CN101838510 A CN 101838510A CN 201010189080 A CN201010189080 A CN 201010189080A CN 201010189080 A CN201010189080 A CN 201010189080A CN 101838510 A CN101838510 A CN 101838510A
Authority
CN
China
Prior art keywords
resin
percent
fissures
pitch
heavy traffic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201010189080A
Other languages
English (en)
Other versions
CN101838510B (zh
Inventor
刘杨军
李国涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SANDI BITUMINOUS MATERIAL CO LTD
Original Assignee
ANHUI SANDI BITUMINOUS MATERIAL CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SANDI BITUMINOUS MATERIAL CO LTD filed Critical ANHUI SANDI BITUMINOUS MATERIAL CO LTD
Priority to CN2010101890801A priority Critical patent/CN101838510B/zh
Publication of CN101838510A publication Critical patent/CN101838510A/zh
Application granted granted Critical
Publication of CN101838510B publication Critical patent/CN101838510B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用于沥青、水泥路面灌缝的高效树脂型灌缝胶，其组分的质量百分比为：芳烃10％-15％、改性剂3％-10％、增强剂1％-3％、助溶剂3％-10％、树脂混合物30％-60％、重交沥青10％-20％，先将芳烃加热至60℃～70℃，然后加入改性剂搅拌约30分钟；再逐步缓慢加如增强剂和助熔剂；最后将树脂与沥青加入，保温120℃，在搅拌的情况下保持30分钟，即可生产出性能优越的树脂型灌缝胶。本发明中的芳烃用于将改性剂、树脂与沥青之间形成一个稳定的均匀混合物，使得树脂基团和沥青基团在改性剂等的作用下桥接；而树脂用在路面时，发挥了高黏结性等特点。改性剂用于改善路用性能，如提高软化点、低温延度等，同时也是很好的胶粘材料。

Description

一种高效树脂型灌缝胶及其制备
技术领域
本发明涉及一种公路路面用的树脂型灌缝胶，尤其涉及一种用于沥青、水泥路面灌缝的高效树脂型灌缝胶。
背景技术
公路路面大量采用沥青或者水泥作为路面胶凝材料。而沥青或者水泥作为胶凝材料的路面，由于在自然界的阳光、风、水的侵蚀作用会产生一定的性能老化问题；同时由于材料固有的特性，水泥无法抗拒热胀冷缩，沥青无法抗拒比较大的、比较集中的压力。因此，在公路路面上我们经常可以看到有或大或小的裂缝。现有的施工为用改性沥青直接灌缝，而改性沥青灌缝由于黏结力不足，常常产生三月施工五月坏、一年到头路上修，越修越补缝越宽的窘况。
中国专利申请网上未有同类产品。
发明内容
本发明的目的在于提供一种高效的树脂型灌缝胶，解决用改性沥青灌缝产生的施工难度大、使用时间短、且对缝有扩大作用的问题。
本发明解决其技术问题所采用的技术方案：
一种高效树脂型灌缝胶，其特征在于：其组分的质量百分比为：
芳烃              10％-15％
改性剂            3％-10％
增强剂            1％-3％
助溶剂            3％-10％
树脂混合物        30％-60％
重交沥青          10％-20％
其中，所述的重交沥青为符合JTG F40-2004标准要求的道路石油沥青；
所述的树脂混合物为石油树脂混合物；所述的改性剂选自SBS、SBR、SIS、PE中的一种或多种；所述的助熔剂选自无机氯系化合物中的一种或多种；所述的增强剂选自有机硫系化合物中的一种或多种。
一种高效树脂型灌缝胶的制备方法，包括如下步骤：
1)将芳烃加热到60℃～70℃；
2)将改性剂加入热的芳香烃里并搅拌至液体，然后加增强剂、助熔剂；
3)将重交沥青加热到100℃-170℃并逐步加入增塑剂，步骤2)形成的液体加热到60℃～70℃；将重交沥青与一种或多种树脂混合物形成的液体、步骤2)形成的液体混合，通过的机械搅拌形成均匀稳定的混合物，充分搅拌，冷却到常温储存即得。
本冷树脂型灌缝胶的物理指标为：5℃延度：大于25厘米。软化点：大于70℃。弹性恢复：大于75％。老化后指标：5℃延度：大于30厘米。软化点：大于70℃。弹性恢复：大于75％。
本发明的有益效果：
本发明中的芳烃解决了将改性剂、树脂与沥青之间形成一个稳定的均匀混合物，使得树脂基团和沥青基团在改性剂等的作用下桥接。而树脂用在路面时，发挥了高黏结性等特点。改性剂用于改善路用性能，如提高软化点、低温延度等，同时也是很好的胶粘材料。
以下实施例来进一步描述本发明的技术效果，应理解为这些实施例仅用于例证的目的，不限制本发明的范围，同时本领域普通技术人员根据本发明所做的显而易见的改变和修饰也包含在本发明范围之内。
具体实施方式
实施例1：一种高效树脂型灌缝胶的制备
组分：以质量百分比计，芳烃：20％；重交沥青：16％，改性剂：10％，石油树脂：50％，增强剂：2％，助熔剂：2％。
制备方法：
1)将芳烃加热到60℃；
2)将改性剂加入并搅拌至液体，然后加增强剂、助熔剂；
3)将重交沥青加热到120℃并逐步加入一种或者多种树脂混合物，步骤2)形成的液体加热到60℃；将重交沥青与一种或多种树脂混合物形成的液体、步骤2)形成的液体混合，通过的机械搅拌形成均匀稳定的混合物，充分搅拌，冷却到常温储存即得。
实施例2：
1：一种高效树脂型灌缝胶的制备
组分：以重量百分比计，芳烃：20％；重交沥青：17％，改性剂：6％，石油树脂：53％，增强剂：2％，助熔剂：2％。
制备方法：
1)将芳烃加热到65℃；
2)将改性剂加入并搅拌至液体，然后加增强剂、助熔剂；
3)将重交沥青加热到115℃并逐步加入一种或者多种树脂混合物，步骤2)形成的液体加热到65℃；将重交沥青与一种或多种树脂混合物形成的液体、步骤2)形成的液体混合，通过的机械搅拌形成均匀稳定的混合物，充分搅拌，冷却到常温储存即得。
实施例3：
1：一种高效树脂型灌缝胶的制备
组分：以重量百分比计，芳烃：18％；重交沥青：17％，改性剂：7％，石油树脂：55％，增强剂：1％，助熔剂：2％。
制备方法：
1)将芳烃加热到60℃；
2)将改性剂加入并搅拌至液体，然后加增强剂、助熔剂；
3)将重交沥青加热到130℃并逐步加入一种或者多种树脂混合物，步骤2)形成的液体加热到60℃；将重交沥青与一种或多种树脂混合物形成的液体、步骤2)形成的液体混合，通过的机械搅拌形成均匀稳定的混合物，充分搅拌，冷却到常温储存即得。
试验检测：按中华人民共和国行业标准：公路工程沥青及沥青混合料试验规程JTJ 052-2000中的T0605-1993、T0606-2000、T0662-2000、T0616-1993标准进行检测结果如下：
  试验项目  5℃延度   软化点   弹性恢复   粘附性
  实施例1  24厘米   54℃   77％   5级
  实施例2  25厘米   55℃   76％   5级
  实施例3  25厘米   54℃   77％   5级

Claims (2)

1.一种高效树脂型灌缝胶，其特征在于：其组分的质量百分比为：
芳烃                    10％-15％
改性剂                  3％-10％
增强剂                  1％-3％
助溶剂                  3％-10％
树脂混合物              30％-60％
重交沥青                10％-20％
其中，所述的重交沥青为符合JTG F40-2004标准要求的道路石油沥青；
所述的树脂混合物为石油树脂混合物；所述的改性剂选自SBS、SBR、SIS、PE中的一种或多种；所述的助熔剂选自无机氯系化合物中的一种或多种；所述的增强剂选自有机硫系化合物中的一种或多种。
2.一种制备权利要求1所述的高效树脂型灌缝胶的方法，包括如下步骤：
1)将芳烃加热到60℃～70℃；
2)将改性剂加入并搅拌至液体，然后加增强剂、助熔剂；
3)将重交沥青加热到100℃-170℃并逐步加入一种或者多种树脂混合物，步骤2)形成的液体加热到60℃～70℃；将重交沥青与一种或多种树脂混合物形成的液体、步骤2)形成的液体混合，通过的机械搅拌形成均匀稳定的混合物，充分搅拌，冷却到常温储存即得。
CN2010101890801A 2010-06-02 2010-06-02 一种树脂型灌缝胶及其制备 Expired - Fee Related CN101838510B (zh)