CN101758739A - Method for producing high wear-resistant interbedded crystalline decorating plate - Google Patents
Method for producing high wear-resistant interbedded crystalline decorating plate Download PDFInfo
- Publication number
- CN101758739A CN101758739A CN201010045811A CN201010045811A CN101758739A CN 101758739 A CN101758739 A CN 101758739A CN 201010045811 A CN201010045811 A CN 201010045811A CN 201010045811 A CN201010045811 A CN 201010045811A CN 101758739 A CN101758739 A CN 101758739A
- Authority
- CN
- China
- Prior art keywords
- film
- transparent
- clear sheet
- resin
- crystalline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing a high wear-resistant interbedded crystalline decorating plate, comprising the following steps: processing the upper surface and/or the lower surface of a transparent sheet to obtain an upper surface layer and/or a lower surface layer, and fixing transparent resin protection films and foaming sponges with release paper on the upper surface layer and/or the lower surface layer. Various films have the surfaces of various colors, figures and patterns such as the leather grain surface, the wood grain surface, the cloth grain surface, the marble surface, the high gloss surface, the polished surface and the like, thus the produced crystalline decorating plate is attractive, luxury and clean, has high quality, strong stereoscopic sense, strong market competitiveness, smooth surface, light weight, high strength and low installation cost, can resist water, moisture and dust, does not need to be painted on site and is easy and convenient to construct and install.
Description
Technical field
The present invention relates to construction material, especially relate to a kind of preparation method of high wear-resistant interbedded crystalline decorating plate.
Background technology
Because people are more and more higher to the aesthetical standard of U.S., be that the city or the building constructions in rural area all want advanced luggage to repair at present, could use then that decorative panel also is applied to fit up metope, furniture and various door more and more.The traditional decoration plate all is to handle at the outer surface of substrate, and inner surface is not handled, promptly the outer surface at substrate is fixed with layer of transparent paint, to play light, attractive in appearance and transparent function, but this clean oil enamelled coating is easy to be scratched, stay cut, destroyed pattern, very ugly.
Summary of the invention
The preparation method who the object of the present invention is to provide a kind of handling ease, makes simple high wear-resistant interbedded crystalline decorating plate, by a process for preparing the decorative panel that comes have beautiful, surfacing attractive in appearance, the market competitiveness strong, high-grade luxurious, do not need field painting, waterproof and dampproof, light weight, intensity height, handling ease, construction and installation simple, quick, save advantage such as installation cost.
The object of the present invention is achieved like this:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate, feature is:
A, by resin extruded machine with resin extruded in mould, obtain flat clear sheet after the cooling;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, obtain upper surface layer;
C, upper surface layer and clear sheet are carried out compound, make upper surface layer be fixed on clear sheet above;
D, at the upper surface layer of clear sheet fixing layer of transparent resin protection film again, promptly obtain finished product: quartzy decorative panel.
Described sheet material upper surface processing is the transparent wearproof paint of upper surface brushing at last transparent resin film, at the transparent conventional seccotine of the lower surface brushing of last transparent resin film; Or described sheet material upper surface processing is the transparent wearproof paint of upper surface brushing at clear sheet; Or it is upper surface printer belt pattern, the color at clear sheet, the teleblem of decorative pattern that described sheet material upper surface is handled, at the transparent wearproof paint of upper surface brushing of teleblem; Or, described sheet material upper surface processing is the transparent wearproof paint of upper surface brushing at last transparent resin film, at the teleblem of the first printer belt pattern of the lower surface of last transparent resin film, color, decorative pattern, brush transparent conventional seccotine again, will go up transparent resin film then and be fixed on the sheet material upper surface.
In step B, carry out the sheet material upper surface at upper surface and handle clear sheet, when obtaining upper surface layer, the lower surface of clear sheet is carried out the sheet material lower surface handle, obtain undersurface layer.
In step C, carry out compoundly with clear sheet upper surface layer and undersurface layer together, make upper surface layer and undersurface layer be separately fixed at the upper surface and the lower surface of clear sheet.
In step D; earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again; then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
Described sheet material lower surface processing is at the transparent conventional seccotine of upper surface brushing that descends transparent resin film, at the counterdie of the lower surface printer belt pattern that descends transparent resin film, color, decorative pattern; Or it is lower surface printer belt pattern, the color at clear sheet, the counterdie of decorative pattern that described sheet material lower surface is handled.
Described resin is a kind of in polyvinyl resin (PE resin), polystyrene resin (PS resin), Corvic (polyvinyl chloride resin), polycarbonate resin (PC resin), plexiglass (PMMA resin), acrylonitrile--butadiene--styrene resin (ABS resin) or the polyphenyl dioctyl phthalate glycol ester resin (PET resin).
Describedly go up transparent resin film, transparent resin film, teleblem, counterdie, transparent protective resin film are a kind of in polyethylene film (PE film), polystyrene film (PS film), polychloroethylene film (PVC film), polycarbonate membrane (PC film), polymethyl methacrylate film (PMMA film), acrylonitrile--butadiene--styrene film (ABS film) or the polyphenyl dioctyl phthalate glycol ester film (PET film) down.
The present invention carries out surface treatment by upper surface and/or the lower surface to clear sheet, obtains upper surface layer, undersurface layer, is fixed with the foam sponge of transparent protective resin film and band release liners more respectively at upper surface layer and/or undersurface layer, gets product.Described resin is a kind of in polyvinyl resin (PE resin), polystyrene resin (PS resin), Corvic (polyvinyl chloride resin), polycarbonate resin (PC resin), plexiglass (PMMA resin), acrylonitrile--butadiene--styrene resin (ABS resin) or the polyphenyl dioctyl phthalate glycol ester resin (PET resin).The described transparent resin film of going up; following transparent resin film; teleblem; counterdie; the transparent protective resin film is polyethylene film (PE film); polystyrene film (PS film); polychloroethylene film (PVC film); polycarbonate membrane (PC film); polymethyl methacrylate film (PMMA film); a kind of in acrylonitrile--butadiene--styrene film (ABS film) or the polyphenyl dioctyl phthalate glycol ester film (PET film); and the pattern of various films is (as the dermatoglyph face; the wood grain face; textured surface; marble surface; high light face or sanding face etc.); color; decorative pattern can be diversified; the quartzy decorative panel that comes out of made is attractive in appearance beautiful like this; the third dimension and the market competitiveness are strong, and be high-grade luxurious.Decorative panel again can water proof and dust proof, and is also attractive in appearance beautiful, clean.Therefore, the present invention have beautiful, surfacing attractive in appearance, the market competitiveness strong, high-grade luxurious, do not need field painting, waterproof and dampproof, light weight, intensity height, handling ease, construction and installation simple, quick, save advantage such as installation cost.
The specific embodiment
Below in conjunction with embodiment and contrast accompanying drawing the present invention is described in further detail.
Embodiment 1:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A, polyvinyl resin (PE resin) is expressed in the mould, obtains flat clear sheet after the cooling by resin extruded machine;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, promptly at the teleblem of the upper surface printer belt pattern of clear sheet, color, decorative pattern: polystyrene film (PS film), the transparent wearproof paint of upper surface brushing at teleblem obtains upper surface layer;
C, upper surface layer and clear sheet are carried out compound, make upper surface layer be fixed on clear sheet above;
D, at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: polychloroethylene film (PVC film) promptly obtains finished product: quartzy decorative panel.
Embodiment 2:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A, polystyrene resin (PS resin) is expressed in the mould, obtains flat clear sheet after the cooling by resin extruded machine;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, promptly at the teleblem of the upper surface printer belt pattern of clear sheet, color, decorative pattern: polyethylene film (PE film), the transparent wearproof paint of upper surface brushing at teleblem obtains upper surface layer;
C, upper surface layer and clear sheet are carried out compound, make upper surface layer be fixed on clear sheet above;
D, earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: polystyrene film (PS film); then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
Embodiment 3:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A, Corvic (polyvinyl chloride resin) is expressed in the mould, obtains flat clear sheet after the cooling by resin extruded machine;
B, upper surface to clear sheet carries out the processing of sheet material upper surface respectively, promptly at last transparent resin film: the transparent wearproof paint of upper surface brushing of polymethyl methacrylate film (PMMA film), at the transparent conventional seccotine of the lower surface brushing of last transparent resin film, obtain upper surface layer, lower surface to clear sheet carries out the processing of sheet material lower surface again, promptly at following transparent resin film: the transparent conventional seccotine of upper surface brushing of polyphenyl dioctyl phthalate glycol ester film (PET film), lower surface printer belt pattern at following transparent resin film, color, the counterdie of decorative pattern: acrylonitrile--butadiene--styrene film (ABS film) will descend transparent resin film to be fixed on the sheet material lower surface then; Obtain undersurface layer;
C, to carry out high temperature under the conditions of 100 degree compound with clear sheet together with upper surface layer and undersurface layer, makes upper surface layer and undersurface layer be separately fixed at the upper surface and the lower surface of clear sheet;
D, earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: acrylonitrile--butadiene--styrene film (ABS film); then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
Embodiment 4:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A,--butadiene--styrene resin (ABS resin) is expressed in the mould with acrylonitrile by resin extruded machine, obtains flat clear sheet after the cooling;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, it is the transparent wearproof paint of upper surface brushing of clear sheet, obtain upper surface layer, lower surface to clear sheet carries out the processing of sheet material lower surface again, promptly at the counterdie of the lower surface printer belt pattern of clear sheet, color, decorative pattern: polymethyl methacrylate film (PMMA film) obtains undersurface layer;
C, carry out compoundly with clear sheet upper surface layer and undersurface layer together, make upper surface layer and undersurface layer be separately fixed at the upper surface and the lower surface of clear sheet;
D, earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: polycarbonate membrane (PC film); then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
Embodiment 5:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A, polycarbonate resin (PC resin) is expressed in the mould, obtains flat clear sheet after the cooling by resin extruded machine;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, promptly at last transparent resin film: the transparent wearproof paint of upper surface brushing of polyethylene film (PE film), teleblem at the first printer belt pattern of the lower surface of last transparent resin film, color, decorative pattern: polycarbonate membrane (PC film), brush transparent conventional seccotine again, obtain upper surface layer;
C, upper surface layer and clear sheet are carried out high temperature under the conditions of 180 degree compound, make upper surface layer be fixed on clear sheet above;
D, earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: polystyrene film (PS film); then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
Embodiment 6:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A, plexiglass (PMMA resin) is expressed in the mould, obtains flat clear sheet after the cooling by resin extruded machine;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, promptly at last transparent resin film: the transparent wearproof paint of upper surface brushing of polymethyl methacrylate film (PMMA film), at the transparent conventional seccotine of the lower surface brushing of last transparent resin film, obtain upper surface layer, lower surface to clear sheet carries out the processing of sheet material lower surface again, promptly at the counterdie of the lower surface printer belt pattern of clear sheet, color, decorative pattern: polymethyl methacrylate film (PMMA film) obtains undersurface layer;
C, to carry out high temperature under the conditions of 200 degree compound with clear sheet together with upper surface layer and undersurface layer, makes upper surface layer and undersurface layer be separately fixed at the upper surface and the lower surface of clear sheet;
D, at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: polymethyl methacrylate film (PMMA film) promptly obtains finished product: quartzy decorative panel.
Embodiment 7:
A kind of preparation method of high wear-resistant interbedded crystalline decorating plate,
A, polyphenyl dioctyl phthalate glycol ester resin (PET resin) is expressed in the mould, obtains flat clear sheet after the cooling by resin extruded machine;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, promptly at last transparent resin film: the transparent wearproof paint of upper surface brushing of polyphenyl dioctyl phthalate glycol ester film (PET film), at the transparent conventional seccotine of the lower surface brushing of last transparent resin film, obtain upper surface layer, lower surface to clear sheet carries out the processing of sheet material lower surface again, promptly at the counterdie of the lower surface printer belt pattern of clear sheet, color, decorative pattern: polyphenyl dioctyl phthalate glycol ester film (PET film) obtains undersurface layer;
C, to carry out high temperature under the conditions of 280 degree compound with clear sheet together with upper surface layer and undersurface layer, makes upper surface layer and undersurface layer be separately fixed at the upper surface and the lower surface of clear sheet;
D, earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again: polyphenyl dioctyl phthalate glycol ester film (PET film); then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
Claims (9)
1. the preparation method of a high wear-resistant interbedded crystalline decorating plate is characterized in that:
A, by resin extruded machine with resin extruded in mould, obtain flat clear sheet after the cooling;
B, the upper surface of clear sheet is carried out the sheet material upper surface respectively handle, obtain upper surface layer;
C, upper surface layer and clear sheet are carried out compound, make upper surface layer be fixed on clear sheet above;
D, at the upper surface layer of clear sheet fixing layer of transparent resin protection film again, promptly obtain finished product: quartzy decorative panel.
2. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 1, it is characterized in that: described sheet material upper surface processing is the transparent wearproof paint of upper surface brushing at last transparent resin film, at the transparent conventional seccotine of the lower surface brushing of last transparent resin film; Or described sheet material upper surface processing is the transparent wearproof paint of upper surface brushing at clear sheet; Or it is upper surface printer belt pattern, the color at clear sheet, the teleblem of decorative pattern that described sheet material upper surface is handled, at the transparent wearproof paint of upper surface brushing of teleblem; Or, described sheet material upper surface processing is the transparent wearproof paint of upper surface brushing at last transparent resin film, at the teleblem of the first printer belt pattern of the lower surface of last transparent resin film, color, decorative pattern, brush transparent conventional seccotine again, will go up transparent resin film then and be fixed on the sheet material upper surface.
3. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 1, it is characterized in that: in step B, carrying out the sheet material upper surface at the upper surface to clear sheet handles, when obtaining upper surface layer, lower surface to clear sheet carries out the processing of sheet material lower surface, obtains undersurface layer.
4. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 3, it is characterized in that: in step C, carry out compoundly with clear sheet upper surface layer and undersurface layer together, make upper surface layer and undersurface layer be separately fixed at the upper surface and the lower surface of clear sheet.
5. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 4; it is characterized in that: in step D; earlier at the upper surface layer of clear sheet fixing layer of transparent resin protection film again; then at the transparent conventional seccotine of the upper and lower surface brushing of plate foam sponge; again foam sponge is fixed on the lower surface of clear sheet; stickup release liners below foam sponge promptly obtains finished product: quartzy decorative panel at last.
6. as the preparation method of claim 3 or 4 or 5 described high wear-resistant interbedded crystalline decorating plates, it is characterized in that: described sheet material lower surface processing is at the transparent conventional seccotine of upper surface brushing that descends transparent resin film, at the counterdie of the lower surface printer belt pattern that descends transparent resin film, color, decorative pattern; Or it is lower surface printer belt pattern, the color at clear sheet, the counterdie of decorative pattern that described sheet material lower surface is handled.
7. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 1 is characterized in that: described resin is a kind of in polyvinyl resin, polystyrene resin, Corvic, polycarbonate resin, plexiglass, acrylonitrile--butadiene--styrene resin or the polyphenyl dioctyl phthalate glycol ester resin; The transparent protective resin film is a kind of in polyethylene film, polystyrene film, polychloroethylene film, polycarbonate membrane, polymethyl methacrylate film, acrylonitrile--butadiene--styrene film or the polyphenyl dioctyl phthalate glycol ester film.
8. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 3 is characterized in that: describedly go up a kind of in transparent resin film and teleblem--butadiene--styrene film that is polyethylene film, polystyrene film, polychloroethylene film, polycarbonate membrane, polymethyl methacrylate film, acrylonitrile or the polyphenyl dioctyl phthalate glycol ester film.
9. the preparation method of high wear-resistant interbedded crystalline decorating plate as claimed in claim 3 is characterized in that: a kind of in described transparent resin film down and counterdie are polyethylene film, polystyrene film, polychloroethylene film, polycarbonate membrane, polymethyl methacrylate film, acrylonitrile--butadiene--styrene film or the polyphenyl dioctyl phthalate glycol ester film.