CN101607359A - 一种无内胎变截面等强度车轮轮辋备坯成形工艺 - Google Patents

一种无内胎变截面等强度车轮轮辋备坯成形工艺 Download PDF

Info

Publication number
CN101607359A
CN101607359A CNA2008101267103A CN200810126710A CN101607359A CN 101607359 A CN101607359 A CN 101607359A CN A2008101267103 A CNA2008101267103 A CN A2008101267103A CN 200810126710 A CN200810126710 A CN 200810126710A CN 101607359 A CN101607359 A CN 101607359A
Authority
CN
China
Prior art keywords
billet
inner tube
wheel
section
bulging
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008101267103A
Other languages
English (en)
Inventor
钟志平
张建荣
张小光
边翊
高军
王志科
翟月雯
彭冲
闫红艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SITONG WHEEL MAKING CO Ltd JIAXING
Beijing Research Institute of Mechanical and Electrical Technology
Original Assignee
SITONG WHEEL MAKING CO Ltd JIAXING
Beijing Research Institute of Mechanical and Electrical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SITONG WHEEL MAKING CO Ltd JIAXING, Beijing Research Institute of Mechanical and Electrical Technology filed Critical SITONG WHEEL MAKING CO Ltd JIAXING
Priority to CNA2008101267103A priority Critical patent/CN101607359A/zh
Publication of CN101607359A publication Critical patent/CN101607359A/zh
Pending legal-status Critical Current

Abstract

一种无内胎变截面等强度车轮轮辋备坯成形工艺,其步骤为:将铸造钢坯棒料经加热、穿孔、下料、热辗环、定径涨形、去氧化皮工序完成备坯。本工艺由于采用铸造钢坯棒料作为原材料,使成本降低。在热辗环加工过程中,铸造钢坯的铸态组织将被改变成锻造组织。随后进行的定径涨形为冷加工,不但可以提高车轮轮辋的备坯精度,而且通过冷加工可以提高车轮轮辋强度约百分之二十。用这种工艺制造的车轮轮辋没有焊缝,制成的车轮在使用过程中不会漏气,可以用于高速重载运输车辆的无内胎车轮,具有安全可靠、节约油耗等优点。所用的加热设备、穿孔设备、辗环设备、定径涨形设备皆有国产设备可供选用。本工艺是一种投资少、生产成本低的无内胎变截面等强度车轮轮辋备坯成形工艺。

Description

一种无内胎变截面等强度车轮轮辋备坯成形工艺
技术领域
本发明涉及载重汽车无内胎钢制车轮的制造技术,一种无内胎变截面等强度车轮轮辋备坯成形工艺。
背景技术
钢制车轮是目前广泛应用于汽车上的车轮,特别是在载重汽车上。钢制车轮一般由轮辐和轮辋两部分组成,分别制造,然后再焊接在一起。其中轮辋是轮胎的载体部件,轮辐是车轮与汽车的连接部件。目前国内外大批量生产车轮轮辋的备坯工艺归纳起来有下列两种方案:1、采用钢带轧制为型钢,下料后卷焊备坯;2、采用钢带卷焊后,滚型备坯。这两种方案所制造的轮辋是用型钢或带钢卷焊而成的,轮辋上都有一条贯通的焊缝。采用这种有焊缝的轮辋制造的车轮,在使用过程中很难保证轮辋上的焊缝在频繁的交变应力作用下不漏气。这类车轮用于轻载汽车的无内胎车轮或中载汽车的有内胎车轮上时,安全隐患并不明显,而用于载重汽车的有内胎车轮时,则漏气、爆胎现象时有发生。
发明内容
本发明的目的是提出一种无内胎变截面等强度车轮轮辋备坯成形工艺,可以使用价格低廉的原材料和投资较少的国产设备,批量生产无焊缝车轮轮辋。
这种无内胎变截面等强度车轮轮辋备坯成形工艺的步骤为:将铸造钢坯棒料经加热、穿孔、下料、热辗环、定径涨形、去氧化皮工序完成备坯。本工艺由于采用铸造钢坯棒料作为原材料,使成本降低。在热辗环加工过程中,铸造钢坯的铸态组织将被改变成锻造组织。随后进行的定径涨形为冷加工,不但可以提高车轮轮辋的备坯精度,而且通过冷加工可以提高车轮轮辋强度约百分之二十。用这种工艺制造的车轮轮辋没有焊缝,制成的车轮在使用过程中不会漏气,可以用于高速重载运输车辆的无内胎车轮,具有安全可靠、节约油耗等优点。所用的加热设备、穿孔设备、辗环设备、定径涨形设备皆有国产设备可供选用。因此,本工艺是一种投资少、生产成本低的无内胎变截面等强度车轮轮辋备坯成形工艺。
附图说明
附图为这种无内胎变截面等强度车轮轮辋备坯成形工艺的工艺路线示意图。
具体实施方式
如附图所示,这种无内胎变截面等强度车轮轮辋备坯成形工艺的步骤为:(a)加热→(b)穿孔→(c)下料→(d)热辗环→(e)定径涨形→(f)去氧化皮。
(a)加热:用加热炉将铸造钢坯棒料加热到锻造温度。
(b)穿孔:由推料机推动铸造钢坯棒料送入穿孔机进行穿孔,制成管坯。
(c)下料:用锯床将穿孔后的管坯按体积不变的原则截成管段。
(d)热辗环:用加热炉将管段加热到锻造温度,用辗环机将加热后的管段辗扩到中间坯尺寸。热辗环过程中,铸态组织被改性成锻造组织。
(e)定径涨形:用液压机和涨形模具将热辗环得到的中间坯定径涨形至轮辋坯料尺寸。
(f)去氧化皮:用抛丸机去除轮辋坯料上的氧化皮,完成车轮轮辋备坯工序。

Claims (3)

1、一种无内胎变截面等强度车轮轮辋备坯成形工艺,其步骤为:将铸造钢坯棒料经加热、穿孔、下料、热辗环、定径涨形、去氧化皮工序完成备坯,其特征是所述的钢坯棒料为铸造组织。
2、如权利要求1所述的无内胎变截面等强度车轮轮辋备坯成形工艺,其特征是所述的下料工序中,按体积不变原则将管坯截成管段,然后将管段加热到锻造温度,用辗环机热辗扩制成中间坯,热辗环过程中铸态组织被改性成锻造组织。
3、如权利要求1所述的无内胎变截面等强度车轮轮辋备坯成形工艺,其特征是所述的定径涨形工序中,所用的涨形模具从直径最小处分为两半,两半模具从中间坯的两端插入,相合在一起,然后用液压机压下,定径涨形至轮辋坯料尺寸。
CNA2008101267103A 2008-06-20 2008-06-20 一种无内胎变截面等强度车轮轮辋备坯成形工艺 Pending CN101607359A (zh)