CN101580396B - Furnace body insulating material for quartz continuous melting furnace - Google Patents

Furnace body insulating material for quartz continuous melting furnace Download PDF

Info

Publication number
CN101580396B
CN101580396B CN2009100335502A CN200910033550A CN101580396B CN 101580396 B CN101580396 B CN 101580396B CN 2009100335502 A CN2009100335502 A CN 2009100335502A CN 200910033550 A CN200910033550 A CN 200910033550A CN 101580396 B CN101580396 B CN 101580396B
Authority
CN
China
Prior art keywords
furnace body
insulating material
furnace
continuous melting
portions
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2009100335502A
Other languages
Chinese (zh)
Other versions
CN101580396A (en
Inventor
孙国方
李玉生
Original Assignee
李玉生
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 李玉生 filed Critical 李玉生
Priority to CN2009100335502A priority Critical patent/CN101580396B/en
Publication of CN101580396A publication Critical patent/CN101580396A/en
Application granted granted Critical
Publication of CN101580396B publication Critical patent/CN101580396B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a furnace body insulating material for a quartz continuous melting furnace, which is characterized in that the furnace body insulating material is prepared from the following raw materials in portion by weight: 0.8 to 1.2 portions of alumina, 1.8 to 2.2 portions of zirconia hollow ball, 1.2 to 1.8 portions of aluminum silicate, and 0.8 to 1.2 portions of perlite. The furnace body insulating material is a novel composite furnace body insulating material; and the insulating material has good insulating effect and little furnace temperature loss, and does not need to be cooled by a furnace body water jacket during use. Measured by a conventional method, the surface temperature of a furnace body made of the insulating material is low, generally about 60 DEG C; the manufacturing cost of the furnace body is low and can be saved by about 15 percent; the service life of the furnace body can be prolonged by about 3 years; the electricity is saved by about 15 percent; andthe water is saved by about 200 tons every year.

Description

Furnace body insulating material for quartz continuous melting furnace
Technical field
The present invention relates to a kind of quartz continuous melting furnace, particularly a kind of furnace body insulating material for quartz continuous melting furnace.
Background technology
The single zirconium white lagging material of the general employing of the lagging material of common continuous induction melting furnace body of heater of the prior art, its heat insulation effect is relatively poor, and the furnace temperature loss is serious, need adopt overcoat to add recirculated cooling water during use, and stove table temperature just can be guaranteed about 85 ℃.
Summary of the invention
Technical problem to be solved by this invention is the deficiency to prior art, and a kind of furnace body insulating material for quartz continuous melting furnace reasonable, high insulating effect of filling a prescription is provided.
Technical problem to be solved by this invention is to realize through following technical scheme.The present invention is a kind of furnace body insulating material for quartz continuous melting furnace, is characterized in, it is to be processed by following materials of weight proportions:
Aluminum oxide 0.8-1.2 zirconium white hollow ball 1.8-2.2
Pure aluminium silicate 1.2-1.8 perlite 0.8-1.2.
In the above-described furnace body insulating material for quartz continuous melting furnace, the preferred weight proportioning of each raw material is:
Aluminum oxide 1 zirconium white hollow ball 2
Pure aluminium silicate 1.5 perlites 1.
Compared with prior art, the present invention is a kind of NEW TYPE OF COMPOSITE furnace insulation material, this lagging material high insulating effect, and the furnace temperature loss is few, need not during use to cool off with furnace water jacket again.Through by ordinary method measuring and calculating, the body of heater table temperature of using lagging material of the present invention to process is low, and generally about 60 ℃, and body of heater cost cost is low, can save about 15%, and body of heater can prolong about 3 years work-ing life, and it is about 15% to economize on electricity, and year economizes on water about 200 tons.
Embodiment
Below further describe concrete technical scheme of the present invention,, and do not constitute restriction its right so that those skilled in the art understands the present invention further.
Embodiment 1, a kind of furnace body insulating material for quartz continuous melting furnace, and it is to be processed by following materials of weight proportions:
Aluminum oxide 0.8 zirconium white hollow ball 1.8
Pure aluminium silicate 1.2 perlites 0.8.
Embodiment 2, a kind of furnace body insulating material for quartz continuous melting furnace, and it is to be processed by following materials of weight proportions:
Aluminum oxide 1.2 zirconium white hollow balls 2.2
Pure aluminium silicate 1.8 perlites 1.2.
Embodiment 3, a kind of furnace body insulating material for quartz continuous melting furnace, and it is to be processed by following materials of weight proportions:
Aluminum oxide 1 zirconium white hollow ball 2
Pure aluminium silicate 1.5 perlites 1.
Embodiment 4, a kind of furnace body insulating material for quartz continuous melting furnace, and it is to be processed by following materials of weight proportions:
Aluminum oxide 0.9 zirconium white hollow ball 2.1
Pure aluminium silicate 1.7 perlites 1.1.
Embodiment 5, a kind of furnace body insulating material for quartz continuous melting furnace, and it is to be processed by following materials of weight proportions:
Aluminum oxide 1.1 zirconium white hollow balls 1.9
Pure aluminium silicate 1.4 perlites 0.9.

Claims (2)

1. a furnace body insulating material for quartz continuous melting furnace is characterized in that, it is to be processed by following materials of weight proportions:
Aluminum oxide 0.8-1.2 zirconium white hollow ball 1.8-2.2
Pure aluminium silicate 1.2-1.8 perlite 0.8-1.2.
2. furnace body insulating material for quartz continuous melting furnace according to claim 1 is characterized in that, the weight proportion of each raw material is:
Aluminum oxide 1 zirconium white hollow ball 2
Pure aluminium silicate 1.5 perlites 1.
CN2009100335502A 2009-06-23 2009-06-23 Furnace body insulating material for quartz continuous melting furnace Active CN101580396B (en)