CN101508125A - Production method of plywood for container bottom board - Google Patents

Production method of plywood for container bottom board Download PDF

Info

Publication number
CN101508125A
CN101508125A CNA2009101315243A CN200910131524A CN101508125A CN 101508125 A CN101508125 A CN 101508125A CN A2009101315243 A CNA2009101315243 A CN A2009101315243A CN 200910131524 A CN200910131524 A CN 200910131524A CN 101508125 A CN101508125 A CN 101508125A
Authority
CN
China
Prior art keywords
plate
board
container
length
brachymedial
Prior art date
Application number
CNA2009101315243A
Other languages
Chinese (zh)
Other versions
CN101508125B (en
Inventor
廖志远
Original Assignee
黄庆邦
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 黄庆邦 filed Critical 黄庆邦
Priority to CN2009101315243A priority Critical patent/CN101508125B/en
Publication of CN101508125A publication Critical patent/CN101508125A/en
Application granted granted Critical
Publication of CN101508125B publication Critical patent/CN101508125B/en

Abstract

The invention provides a method for manufacturing a plywood used for a bottom board of a container, which relates to the technical field of plates. The invention provides the method for manufacturing the plywood used for the bottom board of the container and a novel composite plywood by key technology of 'scientific material selection and matching-based scientific structure'. The method comprises the following steps of log pruning, boiling, veneer rotary cutting, drying, sorting, matching, gluing, bonding, plate blanking, prepressing, hot press, thermal stacking, trimming, graveling, printing and packaging so as to manufacture a finished product of the bottom board of the container. The bottom board is applied to containers, doors and windows, furniture, automobile, ships and other aspects. The method is simple, and the product has the advantages of reasonable structure, good quality, high strength, good elasticity, no deformation, no foaming, strong pressure resisting capability, low cost, long service life and wide range of application, and can be printed with the required patterns on the surface and has beautiful appearance.

Description

The preparation method of composite board for bottom board of container
Technical field
The preparation method of composite board for bottom board of container of the present invention relates to the sheet material technical field; Be particularly related to the sheet material technical field that is applied to container; Relate in particular to the sheet material technical field that not only can be applicable to container bottom board but also can be applicable to the each side such as special glued board that furniture, automobile case uses with base plate, vessel; Be specifically related to the preparation method technical field of composite board for bottom board of container.
Background technology
With regard to sheet material, everybody is not strange, just be applied to the sheet material of container, though also be to constitute by multilayer, but no matter be wood raw material selection, or long in the mutual collocation of plate and brachymedial plate, exist all that structure owes reasonable, of poor quality, intensity is low, poor flexibility, panel and base plate is all yielding, easily foaming of surface, anti-pressure ability are poor, cost height, the life-span is short, range of application is little deficiency, defective and drawback.In view of applicant and designer's professional knowledge with the rich experiences of being engaged in industry work and to the excelsior unremitting pursue of cause, the present invention is exactly on conscientious and sufficient investigation, understanding, analysis, the above-mentioned existing known technology present situation of summary basis, with the key technology of " collocation of science selection and science and realize scientific structure ", for overcoming and solving that many deficiencies, defective and the drawback of existing known technology existence succeed in developing.Of the present invention succeeding in developing also can be applicable to each side such as furniture, automobile, vessel, can effectively enlarge range of application, can effectively reduce the container plate import, can effectively reduce cost.
Summary of the invention
The present invention is the key technology with " science selection and science are arranged in pairs or groups and the realization scientific structure ", and a kind of preparation method and composite plywood new product of composite board for bottom board of container is provided; Its operating procedure be with log cross cut saw, boiling, rotary cut venner, drying, sorting, collocation, gluing, bonding, slab, precompressed, hot pressing, thermal reactor put, edging, sanding, printing, packing and be made into the container bottom board finished product.
The purpose that reaches by the present invention is: make rational in infrastructure, Functionality, quality and appealing design, intensity height, good springiness, the panel of composite plywood new product and base plate is all indeformable, the surface is non-foaming, anti-pressure ability is strong, cost is low, the life-span is long, applied range, both can be applicable to container, can be applicable to various aspects such as door and window, furniture, automobile, vessel again, both can effectively enlarge range of application, the import of container plate can be effectively reduced again, also cost can be effectively reduced.
The present invention can accomplish the end in view.
For achieving the above object, technical scheme provided by the invention is:
A kind of preparation method of composite board for bottom board of container, operating procedure be with log cross cut saw, boiling, rotary cut venner, drying, sorting, collocation, gluing, bonding, slab, precompressed, hot pressing, thermal reactor put, edging, sanding, printing, packing and be made into the container bottom board finished product;
Described log is wooden with a kind of or A Bidong in the permutation and combination method mix and match by the hardwood of A Bidong wood, import, white Eucalyptus, homemade hardwood for selecting, a kind of in the hardwood of import, white Eucalyptus, the homemade hardwood;
Described rotary cut venner is to be peeled into plate and brachymedial plate in the length of sheet structure, and plate is a lines sheet structure forward in the described length, and described brachymedial plate is the horizontal sheet structure of lines, and the thickness of plate and brachymedial plate is the 1.0-2.5 millimeter in the described length;
Employed adhesive is for selecting a kind of in phenolic resins, the melmac during described gluing, and the glue-spread during described gluing is every square metre a two-sided 340-400 gram;
The temperature of described hot pressing is 125-150 ℃, and the pressure of described hot pressing is every square centimeter of 1.6-2.0mpa, and the time of described hot pressing is 35-55 minute;
Described sanding will polish smooth through the material behind the edging in the mode of friction for using sand paper or sandbag;
Described printing is the material surface printed patterns that is polishing smooth;
The composite plywood shape structure of described container bottom board finished product for being made into through being coated with glue bond and hot pressing by the base plate of plate in plate, the described brachymedial plate of one deck, the described length of one deck in plate in plate in the described brachymedial plate of panel, one deck of plate in the described length of one deck, the five layers of described length, the described brachymedial plate of one deck, three layers to the five layers described length, the described brachymedial plate of one deck, the five layers of described length successively.
The preparation method of described composite board for bottom board of container, in the described length panel of plate and long in the base plate of plate be a kind of by in plate, the impregnated paper in the described length of the wooden one-tenth of A Bidong of selection.
The preparation method of described composite board for bottom board of container, it is dry and make after flooding that described impregnated paper is put into phenolic resin glue with paper.
Owing to adopted technical scheme provided by the present invention; Be key technology, a kind of preparation method and composite plywood new product of composite board for bottom board of container is provided with " science selection and science are arranged in pairs or groups and the realization scientific structure "; Owing to operating procedure of the present invention be with log cross cut saw, boiling, rotary cut venner, drying, sorting, collocation, gluing, bonding, slab, precompressed, hot pressing, thermal reactor put, edging, sanding, printing, packing be made into the container bottom board finished product; Make the present invention compare with existing known technology, the beneficial effect that obtains is: make the rational in infrastructure of composite plywood new product of the present invention, Functionality, quality and appealing design, the intensity height, good springiness, panel and base plate are all indeformable, the surface is non-foaming, anti-pressure ability is strong, cost is low, life-span is long, applied range, both can be applicable to container, can be applicable to door and window again, furniture, automobile, various aspects such as vessel, both can effectively enlarge range of application, can effectively reduce the import of container plate again, also can effectively reduce cost, particularly can be and elegant in appearance at the needed various patterns of its surface printing client, have good resistance to impact simultaneously, wearability, resistance tocrocking, environmental protection and wholesome outstanding feature.
Description of drawings
Fig. 1 is the technological process window schematic diagram of the specific embodiment of the invention.
Fig. 2 is one of the structure of composite plywood new product in a specific embodiment of the invention schematic diagram.
Fig. 3 is two schematic diagrames of the structure of composite plywood new product in the specific embodiment of the invention.
Fig. 4 is one of the structure of a prior art glued board schematic diagram.As with contrast figure of the present invention.
Fig. 5 is two schematic diagrames of the structure of prior art glued board.Conduct and contrast figure of the present invention too.
Label among the figure: the panel of plate in 1, long, 2, the brachymedial plate, 3, long in plate, 4, long in the base plate of plate.
The specific embodiment
Below in conjunction with Figure of description, the present invention is described in detail.Shown in Figure of description 1,2,3:
A kind of preparation method of composite board for bottom board of container, operating procedure be with log cross cut saw, boiling, rotary cut venner, drying, sorting, collocation, gluing, bonding, slab, precompressed, hot pressing, thermal reactor put, edging, sanding, printing, packing and be made into the container bottom board finished product;
Described log is wooden with a kind of or A Bidong in the permutation and combination method mix and match by the hardwood of A Bidong wood, import, white Eucalyptus, homemade hardwood for selecting, a kind of in the hardwood of import, white Eucalyptus, the homemade hardwood;
Described rotary cut venner is to be peeled into plate and brachymedial plate in the length of sheet structure, and plate is a lines sheet structure forward in the described length, and described brachymedial plate is the horizontal sheet structure of lines, and the thickness of plate and brachymedial plate is the 1.0-2.5 millimeter in the described length;
Employed adhesive is for selecting a kind of in phenolic resins, the melmac during described gluing, and the glue-spread during described gluing is every square metre a two-sided 340-400 gram;
The temperature of described hot pressing is 125-150 ℃, and the pressure of described hot pressing is every square centimeter of 1.6-2.0mpa, and the time of described hot pressing is 35-55 minute;
Described sanding will polish smooth through the material behind the edging in the mode of friction for using sand paper or sandbag;
Described printing is the material surface printed patterns that is polishing smooth;
The composite plywood shape structure of described container bottom board finished product for being made into through being coated with glue bond and hot pressing by the base plate of plate in plate, the described brachymedial plate of one deck, the described length of one deck in plate in plate in the described brachymedial plate of panel, one deck of plate in the described length of one deck, the five layers of described length, the described brachymedial plate of one deck, three layers to the five layers described length, the described brachymedial plate of one deck, the five layers of described length successively.
The preparation method of described composite board for bottom board of container, in the described length panel of plate and long in the base plate of plate be a kind of by in plate, the impregnated paper in the described length of the wooden one-tenth of A Bidong of selection.
The preparation method of described composite board for bottom board of container, it is dry and make after flooding that described impregnated paper is put into phenolic resin glue with paper.
In above-mentioned specific implementation process: described log is implemented with the hardwood of A Bidong wood, import, white Eucalyptus, homemade hardwood respectively; Thickness to plate in the described length and brachymedial plate is implemented with 1.0,1.1,1.2,1.3,1.4,1.5,1.6,1.7,1.8,1.9,2.0,2.1,2.2,2.3,2.4,2.5 millimeters respectively; Employed adhesive is implemented with phenolic resins, melmac respectively during to described gluing; Glue-spread during to described gluing is implemented with every square metre two-sided 340,345,350,360,365,370,375,380,385,390,395,400 grams respectively; Temperature to described hot pressing is implemented with 125,130,135,140,145,150 ℃ respectively; The pressure of described hot pressing is implemented with every square centimeter 1.6,1.7,1.8,1.9,2.0mpa respectively; Time to described hot pressing implemented with 35,40,45,50,55 minutes respectively; Implement with five layers long middle plates in intermediate layer to the described finished product of container bottom board as shown in Figure 2; Implement with three layers long middle plates in intermediate layer to the described finished product of container bottom board as shown in Figure 3; All received the good result of expection.
The present invention has carried out property on probation examination after making and finishing, through trying out the various aspects of using with base plate, vessel in container bottom board, furniture, automobile case such as special glued board, effectively enlarge range of application, effectively reduced import to container plate, effectively reduced the cost of manufacture of container; By to of the present invention on probation, reached international fully to making the quality requirement of sheet material that container uses, also reached the quality requirement of each sheet material such as special glued board that making furniture, automobile case are used with base plate, vessel fully; Product particularly of the present invention can be at the needed various patterns of its surface printing client and elegant in appearance, and product of the present invention has good resistance to impact, wearability, resistance tocrocking, environmental protection and wholesome outstanding feature simultaneously.Through examination on probation, obtained the good result of expection.
The above is preferred embodiment of the present invention only, is not that the present invention is done any pro forma restriction; The those of ordinary skill of all industry, but all shown in the by specification accompanying drawing and the above, and implement the present invention swimmingly; But all those skilled in the art in not breaking away from the technical solution of the present invention scope, when can utilizing the above technology contents that discloses, and a little change of making, modify the equivalent variations with differentiation, are equivalent embodiment of the present invention; Simultaneously, all foundations essence technology of the present invention all still belongs in the scope of technical scheme of the present invention change, modification and the differentiation etc. of any equivalent variations that above embodiment did.

Claims (3)

1, a kind of preparation method of composite board for bottom board of container is characterized in that: operating procedure be with log cross cut saw, boiling, rotary cut venner, drying, sorting, collocation, gluing, bonding, slab, precompressed, hot pressing, thermal reactor put, edging, sanding, printing, packing and be made into the container bottom board finished product;
Described log is wooden with a kind of or A Bidong in the permutation and combination method mix and match by the hardwood of A Bidong wood, import, white Eucalyptus, homemade hardwood for selecting, a kind of in the hardwood of import, white Eucalyptus, the homemade hardwood;
Described rotary cut venner is to be peeled into plate and brachymedial plate in the length of sheet structure, and plate is a lines sheet structure forward in the described length, and described brachymedial plate is the horizontal sheet structure of lines, and the thickness of plate and brachymedial plate is the 1.0-2.5 millimeter in the described length;
Employed adhesive is for selecting a kind of in phenolic resins, the melmac during described gluing, and the glue-spread during described gluing is every square metre a two-sided 340-400 gram;
The temperature of described hot pressing is 125-150 ℃, and the pressure of described hot pressing is every square centimeter of 1.6-2.0mpa, and the time of described hot pressing is 35-55 minute;
Described sanding will polish smooth through the material behind the edging in the mode of friction for using sand paper or sandbag;
Described printing is the material surface printed patterns that is polishing smooth;
The composite plywood shape structure of described container bottom board finished product for being made into through being coated with glue bond and hot pressing by the base plate of plate in plate, the described brachymedial plate of one deck, the described length of one deck in plate in plate in the described brachymedial plate of panel, one deck of plate in the described length of one deck, the five layers of described length, the described brachymedial plate of one deck, three layers to the five layers described length, the described brachymedial plate of one deck, the five layers of described length successively.
2, the preparation method of composite board for bottom board of container according to claim 1 is characterized in that: in the described length panel of plate and long in the base plate of plate be a kind of by in plate, the impregnated paper in the described length of the wooden one-tenth of A Bidong of selection.
3, the preparation method of composite board for bottom board of container according to claim 2 is characterized in that: it is dry and make after flooding that described impregnated paper is put into phenolic resin glue with paper.
CN2009101315243A 2009-04-07 2009-04-07 Production method of plywood for container bottom board CN101508125B (en)