CN101435079A - 镀锌复合钝化液及其制备方法 - Google Patents
镀锌复合钝化液及其制备方法 Download PDFInfo
- Publication number
- CN101435079A CN101435079A CNA2007100481035A CN200710048103A CN101435079A CN 101435079 A CN101435079 A CN 101435079A CN A2007100481035 A CNA2007100481035 A CN A2007100481035A CN 200710048103 A CN200710048103 A CN 200710048103A CN 101435079 A CN101435079 A CN 101435079A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- preparation
- alcohol
- passivation solution
- composite passivation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及金属钝化液领域,特别涉及一种用于镀锌产品上的复合钝化液及其制备方法。该镀锌复合钝化液的组分和配比为:95%酒精135-165L;三乙醇胺20.7-25.3kg;苯甲酸钠10.8-13.2kg;亚硝酸钠7.2-8.8kg;聚乙烯醇5.4-6.6kg;硅酸钠4-8kg;羟基乙叉二磷酸5.4-6.6kg;水144-176L。本发明还提供了上述符合钝化液的制备方法。由于采用了上述的技术解决方案,完全解决了当前电镀产品Cr6+的环保与盐雾实验时间短相矛盾问题,使目前蓝白锌的电镀产品的盐雾实验时间显著延长,而蓝白锌的电镀产品不含Cr6+,从而符合了欧盟的ROSH指令的标准达到环保的要求。
Description
技术领域
本发明涉及金属钝化液领域,特别涉及一种用于镀锌产品上的复合钝化液及其制备方法。
背景技术
金属制件的合金层或镀锌层常需要对其表面进行钝化处理,以增加耐腐蚀性和装饰性。目前的镀锌产品分为彩锌产品(俗称黄锌)和蓝白锌产品。随着欧盟的ROSH指令不允许在镀锌产品中存在Cr6+的规定出台和当前环保的需要,含Cr6+的彩锌产品(俗称黄锌)由于不符合ROSH指令,其市场就受到空前的制约。而蓝白锌与Cr3+彩锌钝化虽没有Cr6+,但是盐雾试验时间不长,储存期短,存在着质量隐患。因此市场非常需要能解决电镀产品Cr6+的环保与盐雾实验时间短相矛盾问题的方法。
发明内容
本发明的目的在于提供一种能解决上述电镀产品Cr6+的环保与盐雾实验时间短相矛盾问题的复合钝化液。
本发明的另一目的在于提供上述符合钝化液的制备方法。
实现本发明目的技术方案是:一种镀锌复合钝化液,其组分和配比为:
95%酒精 135-165L;
三乙醇胺 20.7-25.3kg;
苯甲酸钠 10.8-13.2kg;
亚硝酸钠 7.2-8.8kg;
聚乙烯醇 5.4-6.6kg;
硅酸钠 4-8kg;
羟基乙叉二磷酸 5.4-6.6kg;
水 144-176L。
一种上述的镀锌复合钝化液的制备方法,包括如下步骤:
1)将聚乙烯醇浸入适量水中,放置12-24小时;
2)加热已经充分溶胀的聚乙烯醇至95-105℃,聚乙烯醇开始溶解,加热搅拌至少2小时以使聚乙烯醇完全溶解;
3)缓慢加入酒精,搅拌均匀;
4)将其他组分在搅拌中缓慢加入并搅匀;
5)控制温度40-50℃,待用。
由于采用了上述的技术解决方案,完全解决了当前电镀产品Cr6+的环保与盐雾实验时间短相矛盾问题,使目前蓝白锌的电镀产品的盐雾实验时间显著延长,而蓝白锌的电镀产品不含Cr6+,从而符合了欧盟的ROSH指令的标准达到环保的要求。
具体实施方式
下面对本发明作进一步的详细说明。
一种镀锌复合钝化液,其组分和配比为:
95%酒精 135-165L;
三乙醇胺 20.7-25.3kg;
苯甲酸钠 10.8-13.2kg;
亚硝酸钠 7.2-8.8kg;
聚乙烯醇 5.4-6.6kg;
硅酸钠 4-8kg;
羟基乙叉二磷酸 5.4-6.6kg;
水 144-176L,
其中,羟基乙叉二磷酸的化学结构式为:
上述的镀锌复合钝化液的制备方法,步骤为:
1)将聚乙烯醇浸入适量水中,放置12-24小时;
2)加热已经充分溶胀的聚乙烯醇至95-105℃,聚乙烯醇开始溶解,加热搅拌至少2小时以使聚乙烯醇完全溶解;
3)缓慢加入酒精,搅拌均匀;
4)将其他组分在搅拌中缓慢加入并搅匀;
5)控制温度40-50℃,待用。
实施例1
95%酒精 150L;
三乙醇胺 23kg;
苯甲酸钠 12kg;
亚硝酸钠 8kg;
聚乙烯醇 6kg;
硅酸钠 4-8kg;
羟基乙叉二磷酸 6kg;
水 160L。
上述复合钝化液制备步骤为:
1、将6kg聚乙烯醇浸入约160升水,放置12-24小时。
2、加热已经充分溶胀的聚乙烯醇,升高至95-105℃,加以搅拌,聚乙烯醇开始溶解,溶解至少2小时,以完全溶解为准。
3、缓慢加入150L酒精,搅拌均匀。
4、将其他组分在搅拌中缓慢加入并搅匀。
5、控制温度40-50℃,待用。
实施例2
一种镀锌复合钝化液,其组分和配比为:
95%酒精 135L;
三乙醇胺 20.7kg;
苯甲酸钠 10.8kg;
亚硝酸钠 7.2kg;
聚乙烯醇 5.4kg;
硅酸钠 4kg;
羟基乙叉二磷酸 5.4kg;
水 144L。
该镀锌复合钝化液的制备方法为:
1、将5.4kg聚乙烯醇浸入144升水,放置12-24小时。
2、加热已经充分溶胀的聚乙烯醇,升高至95-105℃,加以搅拌,聚乙烯醇开始溶解,溶解至少2小时,以完全溶解为准。
3、缓慢加入135L酒精,搅拌均匀。
4、将其他组分在搅拌中缓慢加入并搅匀。
5、控制温度40-50℃,待用。
实施例3
一种镀锌复合钝化液,其组分和配比为:
95%酒精 165L;
三乙醇胺 25.3kg;
苯甲酸钠 13.2kg;
亚硝酸钠 8.8kg;
聚乙烯醇 6.6kg;
硅酸钠 8kg;
羟基乙叉二磷酸 6.6kg;
水 176L。
该镀锌复合钝化液的制备方法为:
1、将6.6kg聚乙烯醇浸入176升水,放置12-24小时。
2、加热已经充分溶胀的聚乙烯醇,升高至95-105℃,加以搅拌,聚乙烯醇开始溶解,溶解至少2小时,以完全溶解为准。
3、缓慢加入165L酒精,搅拌均匀。
4、将其他组分在搅拌中缓慢加入并搅匀。
5、控制温度40-50℃,待用。
上述镀锌复合钝化液因为添加了硅酸钠,使上述镀锌复合钝化液在蓝白锌产品上的钝化效果有了显著地提高。在蓝白锌产品实验室实验效果非常良好:白锈时间普遍在72小时以上,最长达到120小时,红锈都在240小时以上。
本发明的镀锌复合钝化液的优点在于:
1、加工处理时间短,1分钟以内处理完毕,生产效能高;
2、工艺简单成本低:正常连续生产的吨成本可控制在100元以下,目前单批次生产的吨成本能控制在300元以下;
3、黄锌、白锌都能通用,盐雾试验都能有很大提高;实验数据见下表:
4、不同于封闭剂物理吸附成膜,这是一种复合钝化的化学反应膜,结合牢度大大提高;
5、项目研发成本低,在小批量的生产过程中不断改进工艺,除了盐雾试验费用外,没有其他的研发费用投入。
6、ROSH检测:只含有Cr3+,不含Cr6+(<0.1PPM),符合环保要求。
以上实施例仅供说明本发明之用,而非对本发明的限制,有关技术领域的技术人员,在不脱离本发明的精神和范围的情况下,还可以作出各种变换或变型,因此所有等同的技术方案也应该属于本发明的范畴,应由各权利要求所限定。
Claims (2)
1、一种镀锌复合钝化液,其特征在于,其组分和配比为:
95%酒精 135-165L;
三乙醇胺 20.7-25.3kg;
苯甲酸钠 10.8-13.2kg;
亚硝酸钠 7.2-8.8kg;
聚乙烯醇 5.4-6.6kg;
硅酸钠 4-8kg;
羟基乙叉二磷酸 5.4-6.6kg;
水 144-176L。
2、根据权利要求1所述的镀锌复合钝化液的制备方法,其特征在于,包括如下步骤:
1)将聚乙烯醇浸入适量水中,放置12-24小时;
2)加热已经充分溶胀的聚乙烯醇至95-105℃,聚乙烯醇开始溶解,加热搅拌至少2小时以使聚乙烯醇完全溶解;
3)缓慢加入酒精,搅拌均匀;
4)将其他组分在搅拌中缓慢加入并搅匀;
5)控制温度40-50℃,待用。