CN101407915A - 环保型金属除锈防锈喷涂液 - Google Patents

环保型金属除锈防锈喷涂液 Download PDF

Info

Publication number
CN101407915A
CN101407915A CNA2008102310242A CN200810231024A CN101407915A CN 101407915 A CN101407915 A CN 101407915A CN A2008102310242 A CNA2008102310242 A CN A2008102310242A CN 200810231024 A CN200810231024 A CN 200810231024A CN 101407915 A CN101407915 A CN 101407915A
Authority
CN
China
Prior art keywords
rust
parts
environment
sodium
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008102310242A
Other languages
English (en)
Other versions
CN101407915B (zh
Inventor
夏光甫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHIJIAZHUANG ZHENGREN ENVIRONMENTAL PROTECTION TECHNOLOGY CO., LTD.
Original Assignee
夏光甫
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 夏光甫 filed Critical 夏光甫
Priority to CN2008102310242A priority Critical patent/CN101407915B/zh
Publication of CN101407915A publication Critical patent/CN101407915A/zh
Application granted granted Critical
Publication of CN101407915B publication Critical patent/CN101407915B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种对金属材料和金属制品的表面进行预处理的环保型金属除锈防锈喷涂液,它是由下列原料配制而成:磷酸、三聚磷酸钠、硅酸钠、高分子活性剂、苯甲酸钠、尿素。该喷涂液与金属表面的反应,可实现对污物、锈蚀物、氧化皮的溶解、逆转,形成高抗蚀性的牢固的保护层,最后形成光亮的黑色磷化膜。而且不含任何强酸、强碱和有机溶剂,无毒,无腐蚀,性能稳定,不燃不爆,具有使用简便,安全可靠,没有烟雾和气味挥发,也不存在废液排放,对环境和人员无任何损害,节省成本等优点。

Description

环保型金属除锈防锈喷涂液
技术领域
本发明属于金属表面处理技术领域,是一种用于对金属材料和金属制品 的表面进行预处理的环保型金属除锈防锈喷涂液。 背景技术
金属表面的除锈防锈一直是广为关注的技术难题,在公知的技术中,传 统的方法基本有两种, 一种是利用人工进行油污的清洗以及用刀刮或金属刷 子刮刷的方式进行除锈,不仅劳动强度大,需要的人力多,效率低,而且除 锈造成的锈尘到处飞扬,对周围的环境造成污染。此种方式仅适于油污和锈 斑不太严重的金属表面的预处理,而对于金属表面粘附有大量的油污和锈斑, 就很难清除干净。另一种方法是利用强碱除油,强酸除锈的两道清洗工序来 完成,该方法一是需要建造两个作业池,占用的场地大;二是清洗麻烦、速 度慢、效率低;三是在清洗时,必须小心谨慎,因为强碱和强酸的使用,均 对人体有害,存在不安全的隐患。尤其是使用高强度的盐酸具有有害毒素的 酸味,对人体有强烈的剌激感,而且产生的酸雾严重污染空气;四是废酸水 的排放严重污染水资源,影响和破坏了水资源的可持续发展。五是经高浓度 盐酸清洗后的金属表面在大气中一般停留3分钟后即可产生二次氧化锈蚀, 因此,只能起到暂时性的缓蚀作用。近时期以来,国内外出现有很多种对金 属材料的化学除油除锈剂,大多是直接使用无机酸或氨的生物为主料,配以 表面活性剂、缓蚀剂等添加敷料制成的。如:专利公告号为CN86407238A公 开的一种除油除锈剂,其所用原料的组成为:铝粉、氢氧化钠、六次甲基四胺、聚氧乙烯脂肪醇醚、环氧乙烷、水、磷酸,并按照一定的比例配制成的, 这种除油除锈剂虽然效率较高,但因为原料中的环氧乙烷性质不稳定,又有 毒性,生产过程不安全,对环境的污染较严重,而且生产成本很高。公告号
为CN1004429A公开的一种除锈钝化剂,是由磷酸、磷酸二氢锌、草酸、硝 酸锌、聚乙二醇辛基烷基醚、水按照一定比例混合而成,但是由于醚类物质 性质不稳定,所以产品的保存时间短,容易失效,而且除锈效果并不十分理 想。上述技术不仅工艺复杂、除锈效果较差,而且必须在除锈之后立即进行 干燥,并涂复专门的防锈底漆或其它防护层。特别是大型设备、桥梁以及建 筑物除锈,不仅需要人工或喷砂工艺,生产效率低,处理成本高,而且其角 落、隐蔽处的锈层无法清除,造成锈蚀隐患,这些问题一直未得到较好的解 决。
发明目的
本发明的目的是提供一种能够对金属表面的锈层、氧化皮、有机无机污 垢进行一次性彻底清除,且能够在常温下使用,操作简便,安全可靠、无环 境污染、对人体和金属无刺激、无损害的环保型金属除锈防锈喷涂液。
实现本发明的目的所采取的技术方案是:本发明的金属除锈防锈液,是由
下列重量份的原料配制而成:磷酸10〜35份、三聚磷酸钠5〜15份、硅酸钠 1〜5份、高分子活性剂5〜10份、苯甲酸钠2〜7份、尿素2〜8份。
所述高分子活性剂按重量百分比由:磷酸三钠60〜80% 、三乙醇胺3〜5% 份、DX渗透剂3〜20%和十二烷基苯磺酸钠3〜20%配制而成。
本发明选用上述原料进行组合,可使各原料功效产生协同作用,可在金 属表面形成一层封闭薄膜,防止外界水分、氧气浸入,避免形成新的锈蚀。其次,各原料反应形成的成膜物质在渗入锈层内部后,通过物理粘结和化学 转化,使之形成一个坚韧致密的黑色保护膜,从而使原来有害的锈层转变为 有利的保护层。另外,原料反应的另一些成分则均匀分布在无锈金属表面, 并与之反应,形成一个对水、氧等浸蚀因素不敏感的钝化层。因此,能够一 次性快速有效地进行除油、除锈,而且通过封闭薄膜、锈层转化保护层及钝 化层三道防线的叠加效应,使防锈功能大大增强,可以完全取代防锈底漆。 各原料的功能作用分别为-
磷酸:呈弱酸性,具有除锈、除氧化皮的作用,而且对金属表面具有一定 的磷化作用,形成细密的磷化膜,保护金属表面,防止锈蚀,适用于金属表 面处理剂。
三聚磷酸钠:可用作络合助剂,能够软化水质、分散污垢、缓冲碱性,有 利于酸性污垢的祛除。
硅酸钠:具有强碱性,可中和酸性污物,使脂肪和油类乳化,对无机物和 有机物有反絮凝能力,对金属有防腐蚀能力,对PH值有缓冲能力,具有除垢、 乳化、分散、湿润和渗透等性能。
苯甲酸钠:具有较强的亲油性,适用于钢铁除锈。
尿素:呈微碱性,能与酸作用生成盐,可用于制取高分子合成材料、三聚 氧胺树脂等。
磷酸三钠:能与水中易结垢的可溶性f丐盐、镁盐等作用,生成不溶性的磷 酸钙、磷酸镁等沉淀物悬浮在水中,能使金属表面的结垢松软脱落,而且磷 酸盐没有粘性,能防止金属表面的结垢,还具有渗透性和乳化作用,可用作 阻垢缓蚀剂、金属除垢防锈剂、金属洁净剂等。三乙醇胺:具有碱性,能与有机酸和无机酸反应生成盐,能和高级脂肪酸 反应形成脂,能保护金属表面,防止氧化,可用作活性剂、缓蚀剂。
DX渗透剂:是由特殊高分子物质及表面活性剂组成,含有强力渗透表面 活性剂和特殊的绣抑制剂,极易祛除机械设备、金属表面的油污、灰尘、油 脂、石蜡、碳迹等。
十二烷基苯磺酸钠:呈中性,不易氧化,起泡力强,去污力高,对颗粒污 垢、蛋白污垢和油性污垢有显著的去污效果,易与各种助剂复配,是一种很 好的表面活性剂。
按照上述原料配制的环保型金属除锈防锈喷涂液,可对金属表面通过渗 透层与形成锈斑的媒介物质发生化学反应,经表面活性剂乳化、分解,能迅 速的破坏、分解、剥落金属表面上的油污、锈层和除氧化皮,并形成一层牢 固、封闭的保护膜,从而达到除锈、防锈一次完成,取代现有技术的除锈、 防锈、磷化、发黑、增光、底漆涂复等多道工艺,与现有技术相比,具有以 下有益效果-
1、 可以对金属表面的尘垢、油污和锈层进行彻底有效的清除,并自然形 成附着牢固的保护层,无须再涂复防锈底漆。
2、 使用方法简便,喷涂、刷涂、浸泡均可达到良好的除锈、防锈效果, 适用于大、中、小型各类器械、器皿的全部或部分金属表面的清洗、防护处 理。
3、 该除锈防锈液溶液内不含任何强酸、强碱和有机溶剂,无毒,无腐蚀, 性能稳定,不燃不爆,使用安全可靠,而且没有烟雾和气味挥发,也不存在 废液排放,对环境和人员无任何损害。4、 经本除锈防锈液处理的金属表面形成黑色光亮的保护表层,不仅美观, 其有效防护期可达两年以上。
5、 与现有技术相比,处理成本可大大降低,其除锈液、防锈的总费用,
仅为底漆单项材料成本的70%。
6、 该除锈防锈液具有较长的保存有效期, 一般可达两年以上不变质,使 用效果依然良好。
具体实施方式
在本发明中,各原料的用量是经过发明人进行大量摸索总结得出的,其 用量在下述重量份配比范围内都具有较好的功效:磷酸10〜35份、三聚磷酸 钠5〜15份、硅酸钠1〜5份、高分子活性剂5〜10份、苯甲酸钠2〜7份、 尿素2〜8份,其中高分子活性剂按重量百分比由磷酸三钠60〜80% 、三乙醇 胺3〜5%份、DX渗透剂3〜20%和十二烷基苯磺酸钠3〜20%混合制成。
实施例一
所述各原料的重量份配比可以是:磷酸10份、三聚磷酸钠5份、硅酸钠 l份、高分子活性剂5份、苯甲酸钠2份、尿素2份,其中高分子活性剂按重 量百分比由重量百分比由磷酸三钠60°/。、三乙醇胺5%份、DX渗透剂20%和 十二烷基苯磺酸钠10%混合制成。
实施例二
所述各原料的重量份配比也可以是:磷酸22份、三聚磷酸钠10份、硅 酸钠3份、高分子活性剂7份、苯甲酸钠5份、尿素5份,其中高分子活性 剂按重量百分比由磷酸三钠73% 、三乙醇胺4%份、DX渗透剂3。/。和十二烷基 苯磺酸钠20%混合制成。实施例三
所述各原料的重量份配比还可以是:磷酸35份、三聚磷酸钠15份、硅
酸钠5份、高分子活性剂10份、苯甲酸钠7份、尿素8份,其中高分子活性 剂按重量百分比由磷酸三钠80% 、三乙醇胺3%份、DX渗透剂14°/。和十二烷 基苯磺酸钠3%混合制成。
本发明的喷涂液在使用时,可以薄层喷涂或刷涂在待处理的设备或器具表 面,以不流为原则,然后让其自然干燥,随着喷涂液与金属表面的反应,实 现对污物、锈蚀物、氧化皮的溶解、逆转,形成高抗蚀性的牢固的保护层, 最后形成光亮的黑色磷化膜。待涂层变黑和完全干燥后,可在其表面刷或喷 两道面漆,以增强表面的亮度和美观。

Claims (2)

1、一种环保型金属除锈防锈喷涂液,其特征在于:本发明的可取代底漆的多用环保型金属除锈防锈液,是由下列重量份的原料配制而成:磷酸10~35份、三聚磷酸钠5~15份、硅酸钠1~5份、高分子活性剂5~10份、苯甲酸钠2~7份、尿素2~8份。
2、 根据权利要求1所述的环保型金属除锈防锈喷涂液,其特征在于:所述高分子活性剂按重量百分比由磷酸三钠60〜80% 、三乙醇胺3〜5%份、DX 渗透剂3〜20%和十二烷基苯磺酸钠3〜20%配制而成。
CN2008102310242A 2008-11-24 2008-11-24 环保型金属除锈防锈喷涂液 Expired - Fee Related CN101407915B (zh)