CN101401676A - 陶瓷首饰的制作方法 - Google Patents

陶瓷首饰的制作方法 Download PDF

Info

Publication number
CN101401676A
CN101401676A CNA2008101991010A CN200810199101A CN101401676A CN 101401676 A CN101401676 A CN 101401676A CN A2008101991010 A CNA2008101991010 A CN A2008101991010A CN 200810199101 A CN200810199101 A CN 200810199101A CN 101401676 A CN101401676 A CN 101401676A
Authority
CN
China
Prior art keywords
ceramic
bead blanks
blanks
ceramic bead
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008101991010A
Other languages
English (en)
Inventor
梁春光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2008101991010A priority Critical patent/CN101401676A/zh
Publication of CN101401676A publication Critical patent/CN101401676A/zh
Pending legal-status Critical Current

Abstract

本发明公开了陶瓷首饰的制作方法，其特征在于如下步骤：A.用泥料做出瓷珠坯体；B.风干瓷珠坯体；C.对瓷珠坯体进行上釉处理；D.用耐高温的丝条将上好釉的瓷珠坯体串起来；E.将串起来的瓷珠坯体送进窑炉内吊烧，使釉与泥料烧结；F.将烧好的瓷珠按照一定的造型串联起来。瓷珠坯体的形状可预先制造，本发明是直接对瓷珠坯体进行全面上釉，然后送到窑炉内进行吊烧，由于采用吊烧工艺，所以在对瓷珠坯体进行上釉处理时，可全面上釉，而且瓷珠坯体受热均匀，从而使烧出来的瓷珠各个表面具有均匀艳丽的色彩；再把瓷珠配合各种线绳或金属等部件按照一定的造型串联起来，就构成一件具有特色的陶瓷首饰。

Description

陶瓷首饰的制作方法
技术领域
本发明涉及一种陶瓷首饰的制作方法。
背景技术
现有的传统陶瓷首饰是在白色瓷珠上贴上花纸，然后将瓷珠简单地串联而成，所述瓷珠的形状比较单一，首饰的设计造型比较单调。而瓷珠的烧制方法方面，目前所采用的是平烧方式，就是将瓷珠坯体平放在窑炉内进行烧制，这样瓷珠坯体的受热不均匀，而且底面不能上釉，所以当制造形状复杂的瓷珠时，就只能采用除底面外的单面上釉处理，从而限制了产品的款式，而且这样制作出来的瓷珠表面比较粗糙，不够美观。
发明内容
为了克服现有技术的不足，本发明的目的在于提供一种实用可靠的陶瓷首饰的制作方法，这样的制作方法可制作出立体感强，色彩艳丽，富有光泽，形状各异，美观大方的陶瓷首饰。
本发明解决其技术问题所采用的技术方案是：陶瓷首饰的制作方法，其特征在于如下步骤：
A、用泥料做出瓷珠坯体；
B、风干瓷珠坯体；
C、对瓷珠坯体进行上釉处理；
D、用耐高温的丝条将上好釉的瓷珠坯体串起来；
E、将串起来的瓷珠坯体送进窑炉内吊烧，使釉与泥料烧结；
F、将烧好的瓷珠按照一定的造型串联起来。
其中，对瓷珠坯体进行多面上釉处理。
其中，所述丝条为铌金属条。
其中，对串起来的瓷珠坯体进行烧制的窑炉为电窑炉。
其中，所述上釉处理指沾上各种颜色的釉料或花釉、手绘青花、手绘粉彩、金水、微雕刻等工艺。
其中，所述吊烧的温度为1200℃-1400℃，时间为4-5小时。
其中，所述吊烧的温度为1250℃，时间为4.5小时。
本发明的有益效果是：瓷珠坯体的形状可预先制造，而且本发明是直接对瓷珠坯体进行全面上釉，然后送到窑炉内进行吊烧，由于采用吊烧工艺，所以在对瓷珠坯体进行上釉处理时，可全面上釉，而且瓷珠坯体受热均匀，从而使烧出来的瓷珠各个表面具有均匀艳丽的色彩；然后再把这些瓷珠配合各种线绳或金属等其他材质的部件按照一定的造型串联起来，就构成一件具有特色的陶瓷首饰。这样的陶瓷首饰具有立体感强，色彩艳丽，富有光泽，形状各异，美观大方的优点。
具体实施方式
陶瓷首饰的制作方法，步骤如下：
A、首先按产品形状要求用泥料做出瓷珠坯体；
B、将瓷珠坯体进行风干处理；
C、对风干后的瓷珠坯体进行全面上釉处理；
D、用耐高温的铌金属丝条将上好釉的瓷珠坯体串起来；
E、将串好的瓷珠坯体送进窑炉内吊烧，使釉与泥料烧结；
F、将烧好的瓷珠按照一定的造型串联起来。
其中，瓷珠坯体的形状可根据产品要求预先制造，而且本发明是直接对瓷珠坯体进行全面上釉，然后送到窑炉内进行吊烧，由于采用吊烧工艺，所以在对瓷珠坯体进行上釉处理时，可全面上釉，而且瓷珠坯体受热均匀，从而使烧出来的瓷珠各个表面具有均匀艳丽的色彩；然后再把这些瓷珠配合各种线绳或金属等其他材质的部件按照一定的造型串联起来，就构成一件具有特色的陶瓷首饰。这样的陶瓷首饰具有立体感强，色彩艳丽，富有光泽，形状各异，美观大方的优点。
为了使釉料均匀全面地覆盖瓷珠坯体，可对瓷珠坯体进行多面上釉；同时结合吊烧的工艺，可使烧出来的瓷珠装饰面更具光泽、美观。
为了防止耐高温的丝条在烧制的过程中被烧断，所述丝条采用耐高温能力比较强的铌金属条来制造。
为了保证烧制出来的效果，对串起来的瓷珠坯体进行烧制的窑炉为电窑炉，其吊烧的温度为1250℃，时间为4.5个小时。当然，所述瓷珠坯体也可以用燃气窑炉来烧制，烧制的温度就要达到1330℃。另外，准确的具体的吊烧温度和时间要根据上的釉料来定，一般的吊烧的温度为1200℃-1400℃，时间为4-5小时。
还有，所述上釉处理指沾上各种颜色的釉料或花釉、手绘青花、手绘粉彩、金水、微雕刻等工艺，上述工艺可单独或采用一种或一种以上结合起来对瓷珠坯体进行处理，其要求根据具体的产品要求来定。
当然，本发明并不限于上述的实施例，与本发明的等同或变劣的实施例也属于本发明的保护范围。

Claims (7)

1.陶瓷首饰的制作方法，其特征在于如下步骤：
A、用泥料做出瓷珠坯体；
B、风干瓷珠坯体；
C、对瓷珠坯体进行上釉处理；
D、用耐高温的丝条将上好釉的瓷珠坯体串起来；
E、将串起来的瓷珠坯体送进窑炉内吊烧，使釉与泥料烧结；
F、将烧好的瓷珠按照一定的造型串联起来。
2.根据权利要求1所述的陶瓷首饰的制作方法，其特征在于：对瓷珠坯体进行多面上釉处理。
3.根据权利要求1所述的陶瓷首饰的制作方法，其特征在于：所述丝条为铌金属条。
4.根据权利要求1所述的陶瓷首饰的制作方法，其特征在于：对串起来的瓷珠坯体进行烧制的窑炉为电窑炉。
5.根据权利要求1所述的陶瓷首饰的制作方法，其特征在于：所述上釉处理指沾上各种颜色的釉料或花釉、手绘青花、手绘粉彩、金水、微雕刻等工艺。
6.根据权利要求1、2、3、4或5所述的陶瓷首饰的制作方法，其特征在于：所述吊烧的温度为1200℃-1400℃，时间为4-5小时。
7.根据权利要求6所述的陶瓷首饰的制作方法，其特征在于：所述吊烧的温度为1250℃，时间为4.5小时。
CNA2008101991010A 2008-10-14 2008-10-14 陶瓷首饰的制作方法 Pending CN101401676A (zh)