CN101396841A - 铸造废砂路面砖制造方法 - Google Patents
铸造废砂路面砖制造方法 Download PDFInfo
- Publication number
- CN101396841A CN101396841A CNA2007100561063A CN200710056106A CN101396841A CN 101396841 A CN101396841 A CN 101396841A CN A2007100561063 A CNA2007100561063 A CN A2007100561063A CN 200710056106 A CN200710056106 A CN 200710056106A CN 101396841 A CN101396841 A CN 101396841A
- Authority
- CN
- China
- Prior art keywords
- sand
- waste
- sands
- bricks
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
铸造废砂路面砖制造方法，其特征为：先将废砂过6目筛，再依次加入重量比为15％的冲天炉水渣、20％的水泥，混合好的废砂待用，将重量比为70％、粒度尺寸为0.212mm－0.106mm的细干砂，28％的白水泥，1％的染料，1％的光亮剂混合作为面砂，将面砂先加入模具中，再加入混合好的废砂，在30－50MPa压力下成型，在路面砖成型后，养生28天，在第一周内每天浇水两次，以后每天浇水一次，用苫布盖严，温度控制在15℃以上。本发明可将80％以上的铸造固体废物处理掉，提高了废砂砖的强度，降低了路面砖的成本。
Description
技术领域
本发明属于建筑材料的技术领域，特别涉及一种铸造废砂路面砖制造方法。
背景技术
铸造废砂和废炉渣占铸造固体废弃物80％以上。过去，有很多人尝试利用废砂制路面砖，但都因所制的产品强度较低而失败。造成这一问题的主要原因一是废砂粒度较细，需要较多的水泥粘结剂；二是废砂中的粉尘对水泥强度有一定影响。铸造旧砂中二氧化硅约占85％，颗粒尺寸大多在0.3mm—0.15mm之间，一般制路面砖的河砂颗粒尺寸大多在3mm—0.5mm。再加上旧砂中的灰份，使混合料的表面积加大，在同样水泥粘结剂加入量下，如不加入其它材料，路面砖的强度会下降。
发明内容
本发明的目的就是针对上述材料配比及其制造方法的不足，提供一种铸造废砂路面砖制造方法。
本发明的技术方案是这样实现的：
铸造废砂路面砖制造方法，其特征为：
该制造方法的步骤为：
先将废砂过6目筛，再依次加入重量比为15％的冲天炉水渣、20％的水泥，混合好的废砂待用，将重量比为70％、粒度尺寸为0.212mm—0.106mm的细干砂，28％的白水泥，1％的染料，1％的光亮剂混合作为面砂，将面砂先加入模具中，再加入混合好的废砂，在30—50MPa压力下成型，在路面砖成型后，养生28天，在第一周内每天浇水两次，以后每天浇水一次，用苫布盖严，温度控制在15℃以上。
本发明可将80％以上的铸造固体废物处理掉，提高了废砂砖的强度，降低了路面砖的成本。
具体实施方案
下面详细说明本发明的具体技术方案。
本发明是先将废砂过6目筛，再依次加入重量比为15％的冲天炉水渣、20％的水泥，混合好的废砂待用，将重量比为70％、粒度尺寸为0.212mm—0.106mm的细干砂，28％的白水泥，1％的染料，1％的光亮剂混合作为面砂，将面砂先加入模具中，再加入混好的废砂，在30—50MPa压力下成型，养生28天，在第一周内每天浇水两次，以后每天浇水一次，用苫布盖严，温度控制在15℃以上。
实施例：
步道砖尺寸：100×200×(80～60)，颜色：红或按客户要求。
将废砂过6目筛，再依次加入冲天炉水渣15％、水泥20％，混合后待用，将粒度尺寸在0.212mm—0.106mm的细干砂70％，白水泥28％，红染料氧化铁红1％，光亮剂三聚氰胺1％混合作为面砂，将面砂先加入模具中，再加入混好的废砂，30—50MPa压力下成型后，养生28天；养生方法和一般路面砖相同，在第一周内每天浇水两次，以后每天浇水一次，用苫布盖严，温度控制在15℃以上。
通过调整粒度和各组分的加入量、添加冲天炉水渣等添加剂，并通过严格的各种检测和数据分析，优选出了较理想的配方，有效保证了该砖的各项力学性能，使该砖达到了国标路面砖的各项力学指标。本发明除水泥和废砂外，添加冲天炉水渣、清理氧化铁皮等废弃材料。经使用证明，这些材料对于提高砖的强度和耐磨性具有非常良好的作用。
本发明使用的染料不同时，可以制成不同颜色的路面砖。如黄色、绿色或黑色等颜色的路面砖。
Claims (1)
1、铸造废砂路面砖制造方法，其特征为：
该制造方法的步骤为：
先将废砂过6目筛，再依次加入重量比为15％的冲天炉水渣、20％的水泥，混合好的废砂待用，将重量比为70％、粒度尺寸为0.212mm—0.106mm的细干砂，28％的白水泥，1％的染料，1％的光亮剂混合作为面砂，将面砂先加入模具中，再加入混好的废砂，在30—50MPa压力下成型，在路面砖成型后，养生28天，在第一周内每天浇水两次，以后每天浇水一次，用苫布盖严，温度控制在15℃以上。