CN101348336A - 复合型预拌砂浆专用水泥 - Google Patents
复合型预拌砂浆专用水泥 Download PDFInfo
- Publication number
- CN101348336A CN101348336A CNA2008101963769A CN200810196376A CN101348336A CN 101348336 A CN101348336 A CN 101348336A CN A2008101963769 A CNA2008101963769 A CN A2008101963769A CN 200810196376 A CN200810196376 A CN 200810196376A CN 101348336 A CN101348336 A CN 101348336A
- Authority
- CN
- China
- Prior art keywords
- cement
- special
- ready
- mixed mortar
- composite type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
预拌砂浆专用水泥是一种在预拌砂浆的成产与应用中,可以降低预拌砂浆成本的一种复合型专用干粉料。该专用水泥以硅酸盐水泥为主,加上复合型保水增稠剂、I级和II级F类粉煤灰(或者矿粉等矿物掺合料)组成,其中硅酸盐水泥占专用水泥的50.0%~80.0%,复合型保水增稠剂占专用水泥总质量的1.3%~5.0%,矿物掺合料(粉煤灰、矿粉等)占专用水泥总质量的15.0%~48.7%。外加剂中的减水剂为萘系或聚羧酸系粉剂减水剂,纤维素醚为羟丙基甲基纤维素醚。
Description
技术领域
本发明是一种在预拌砂浆的生产与应用中,在保证预拌砂浆基本性能满足现行标准要求的同时能够显著降低预拌砂浆成本的复合型胶凝材料,属于预拌砂浆建筑制品领域。
背景技术
目前,还没有预拌砂浆专用水泥的公开报道。在类似报道中,同济大学的张雄的《建筑砂浆粉工业化生产技术路线》一文中引入了建筑砂浆粉这一概念。建筑砂浆粉是将干粉砂浆中的砂与胶结料分离,将胶结料作为独立的产品命名为建筑砂浆粉。
发明内容
技术问题:本发明的目的是针对预拌砂浆的制备过程中工序较多、成本过高等问题,提供一种预拌砂浆专用水泥。该专用水泥制备出的预拌砂浆能在满足现行标准规范的条件下,大幅度降低预拌砂浆的成本。
技术方案:本发明的复合型预拌砂浆专用水泥由硅酸盐水泥、保水增稠剂、矿物掺合料组成,其中硅酸盐水泥占专用水泥的50.0%~80.0%,复合型保水增稠剂占专用水泥总质量的1.3%~5.0%,粉煤灰、矿粉、石粉等占专用水泥总质量的15.0%~48.7%。
用于预拌砂浆专用水泥中的硅酸盐水泥可以为普通硅酸盐水泥、粉煤灰硅酸盐水泥、复合硅酸盐水泥、矿渣硅酸盐水泥,水泥的品质要求应符合GB175-2007《通用硅酸水泥》标准要求,水泥用量占专用水泥总质量的50%~80%。
用于预拌砂浆中的复合型保水增稠剂,是由消泡剂、凹凸棒石粘土或膨润土、纤维素醚、减水剂和活性矿物掺合料(粉煤灰、矿渣等)组成,其中消泡剂质量分数为0.1%~1.0%,凹凸棒石粘土或膨润土质量分数为0.3%~1.0%,纤维素醚质量分数为5.0%~8.0%,减水剂质量分数为22.0%~30.0%,活性矿物掺合料(粉煤灰、矿渣等)质量分数为60.0%~72.0%。
活性矿物掺合料主要包括粉煤灰和矿渣,粉煤灰采用符合GB/T 1596-2005《用于水泥和混凝土中的粉煤灰》中规定的I级和II级F类粉煤灰。矿粉采用符合GB/T 18046-2000《用于水泥和混凝土中的粒化高炉矿渣粉》中规定的S95及其以上级别的矿粉。
减水剂为萘系或聚羧酸系粉剂减水剂,其质量要求应复合厂家出厂要求。纤维素醚为羟丙基甲基纤维素醚。
本发明的复合型胶凝材料技术要点是:引入预拌砂浆中的一个新的概念——专用水泥,专用水泥是将通用水泥、保水增稠剂、矿物掺合料(工业废料废渣,如粉煤灰、矿渣粉和石粉等)按照一定的比例混合搅拌制成的复合型胶凝材料,可利用现有水泥企业生产线生产,也可利用水泥熟料粉磨站、矿粉产品粉磨站工艺设备生产,该专用水泥可直接运送到施工现场与一定比例的砂、水拌合施工使用,从而大大节约了能耗,提高了施工效率。
本发明的专用水泥以通用水泥为主,加上保水增稠剂、矿物掺合料(粉煤灰或矿粉或石粉等)组成。
有益效果:本发明所配制的专用水泥制备预拌砂浆后,能在满足现行标准规范的条件下,提高砂浆产品质量并大幅度的降低预拌砂浆的成本。该专用水泥可以根据不同强度等级的需要,改变其组分配方,从而制备出不同品种(主要为砌筑、抹面和地面砂浆)和强度等级的砂浆。
此外,该专用水泥也可用于现有预拌砂浆厂配制各种干拌砂浆和湿拌砂浆,也可用于现场采用传统方法拌制各种建筑砂浆。从而可以适用于我国各个地区、各种工艺拌制建筑砂浆,并提高产品质量、降低成本。
具体实施方式
本发明的复合型预拌砂浆专用水泥由硅酸盐水泥、保水增稠剂、矿物掺合料组成,其中硅酸盐水泥占专用水泥的50.0%~80.0%,复合型保水增稠剂占专用水泥总质量的1.3%~5.0%,粉煤灰、矿粉、石粉等占专用水泥总质量的15.0%~48.7%。
用于预拌砂浆专用水泥中的硅酸盐水泥可以为普通硅酸盐水泥、粉煤灰硅酸盐水泥、复合硅酸盐水泥、矿渣硅酸盐水泥,水泥的品质要求应符合GB175-2007《通用硅酸盐水泥》标准要求,水泥用量占专用水泥总质量的50%~80%。
用于预拌砂浆中的复合型保水增稠剂,是由消泡剂、凹凸棒石粘土或膨润土、纤维素醚、减水剂和活性矿物掺合料(粉煤灰、矿渣等)组成,其中消泡剂质量分数为0.1%~1.0%,凹凸棒石粘土或膨润土质量分数为0.3%~1.0%,纤维素醚质量分数为5.0%~8.0%,减水剂质量分数为22.0%~30.0%,活性矿物掺合料(粉煤灰、矿渣等)质量分数为60.0%~72.0%。
活性矿物掺合料主要包括粉煤灰和矿渣,粉煤灰采用符合GBT1596-2005《用于水泥和混凝土中的粉煤灰》中规定的I级和II级F类粉煤灰。矿粉采用符合GB/T18046-2000《用于水泥和混凝土中的粒化高炉矿渣粉》中规定的S95及其以上级别的矿粉。
减水剂为萘系或聚羧酸系粉剂减水剂,其质量要求应复合厂家出厂要求。
纤维素醚为羟丙基甲基纤维素醚。
本发明的专用水泥配方如下表1所示。
表1专用水泥的组成及比例
专用水泥所配制的预拌砂浆的性能如下表2所示。
表2专用水泥配制各强度等级的预拌砂浆性能
Claims (6)
1.一种复合型预拌砂浆专用水泥,其特征在于该专用水泥由硅酸盐水泥、保水增稠剂、矿物掺合料组成,其中硅酸盐水泥占专用水泥的50.0%~80.0%,复合型保水增稠剂占专用水泥总质量的1.3%~5.0%,粉煤灰、矿粉、石粉等占专用水泥总质量的15.0%~48.7%。
2.根据权利要求1所述的复合型预拌砂浆专用水泥,其特征在于用于预拌砂浆专用水泥中的硅酸盐水泥为普通硅酸盐水泥、粉煤灰硅酸盐水泥、复合硅酸盐水泥、矿渣硅酸盐水泥。
3.根据权利要求1所述的复合型预拌砂浆专用水泥,其特征在于用于预拌砂浆中的复合型保水增稠剂,是由消泡剂、凹凸棒石粘土或膨润土、纤维素醚、减水剂和活性矿物掺合料组成,其中消泡剂质量分数为0.1%~1.0%,凹凸棒石粘土或膨润土质量分数为0.3%~1.0%,纤维素醚质量分数为5.0%~8.0%,减水剂质量分数为22.0%~30.0%,活性矿物掺合料质量分数为60.0%~72.0%。
4.根据权利要求1所述的复合型预拌砂浆专用水泥,其特征在于活性矿物掺合料主要包括粉煤灰、和矿渣。
5.根据权利要求1所述的复合型预拌砂浆专用水泥,其特征在于减水剂为萘系或聚羧酸系粉剂减水剂。
6.根据权利要求3所述的复合型预拌砂浆专用水泥,其特征在于纤维素醚为羟丙基甲基纤维素醚。