CN101314703A - 一种纳米改性花炮底座胶及其制备方法 - Google Patents

一种纳米改性花炮底座胶及其制备方法 Download PDF

Info

Publication number
CN101314703A
CN101314703A CNA2007100350293A CN200710035029A CN101314703A CN 101314703 A CN101314703 A CN 101314703A CN A2007100350293 A CNA2007100350293 A CN A2007100350293A CN 200710035029 A CN200710035029 A CN 200710035029A CN 101314703 A CN101314703 A CN 101314703A
Authority
CN
China
Prior art keywords
nano
modified
base plate
resin
environmentally friendly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100350293A
Other languages
English (en)
Inventor
袁宏伟
李冬月
颜珍琼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN SHENLI INDUSTRIAL Co Ltd
Original Assignee
HUNAN SHENLI INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN SHENLI INDUSTRIAL Co Ltd filed Critical HUNAN SHENLI INDUSTRIAL Co Ltd
Priority to CNA2007100350293A priority Critical patent/CN101314703A/zh
Publication of CN101314703A publication Critical patent/CN101314703A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种纳米改性花炮底座胶及其制备方法。它以SBS弹性体为主体材料,选择环保溶剂,加入纳米材料、增粘树脂、稳定剂溶解混合而成。该产品符合国家环保标准,增大了花炮纸筒和底座间的粘接强度,配方合理、科学,生产工艺简单。

Description

一种纳米改性花炮底座胶及其制备方法
技术领域
本发明涉及一种纳米改性花炮底座胶及其制备方法,尤其涉及一种用于花炮筒体和底座间粘接的纳米改性SBS胶粘剂及其制备方法。
背景技术
花炮系列产品中的小炮弹、烟花、盆花均是将发射药装入纸筒,再将纸筒固定在底座上,使其可以平稳地放在地上燃放,受冲击振动不摇摆和歪倒,烟花能笔直升上天空形成绚丽多彩的美丽画面。花炮底座胶主要起到粘接纸筒和底座的作用。
随着花炮产业的不断进步,花炮底座的材料也多种多样,有人造木屑底座,有纸板底座,还有难粘的PP、PE塑料底座。纸筒与底座吻合得不够好,往往只能依靠纸筒底端环形截面与底座对应平面之间的胶粘来完成纸筒与底座的组装。花炮底座胶曾使用过聚醋酸乙烯乳液,俗称白乳液,普通溶剂胶,如以SBS为主体树脂的溶剂型胶粘剂。白乳液是水基胶,干燥速度慢,对PP、PE塑料底座,粘附力差;普通溶剂胶,干燥速度比较快,对PE、PP塑料底座粘附力也较好,但仍不能完全满足纸筒与塑料底座粘接牢度的要求。现在,一筒多发,即一个纸筒内装有多发炮弹,按程序逐一发射,已成为主流产品,纸筒与底座之间的胶层需经受多次冲击性负荷,现有的胶粘剂不能保证花炮的质量。
发明内容
本发明的目的是提供一种纳米改性花炮底座胶及其制备方法,克服现有胶粘剂性能的不足。本发明设计制备的花炮底座胶,主体树脂选择SBS弹性体,增粘树脂选用石油树脂、萜烯树脂、改性松香树脂,溶剂选用了环保溶剂,纳米材料选用了粒度为30~80nm的二氧化硅,还选用了稳定剂,所制备的纳米改性花炮底座胶的粘接强度、刚性、成本、稳定性都达到了本发明的目的。
本发明的技术方案如下:
纳米改性花炮底座胶各组份的重量百分比组成为:
SBS弹性体                   18~25%
纳米二氧化硅;30nm~80nm    1~5%
石油树脂                    8~15%
萜烯树脂        4~8%
改性松香树脂    4~8%
环保溶剂        50~64%
稳定剂264       0.1%~0.5%
花炮底座胶各组份的重量百分数之和为100%。环保溶剂是上海东和胶粘剂厂生产。
本发明的制备方法如下:
1、称取规定配比量的环保溶剂,加入带搅拌器的反应釜中,调温至20~35℃,开动搅拌,加入配比量的石油树脂、萜烯树脂、改性松香树脂,搅拌2小时,再加入SBS弹性体,搅拌4~6小时,直至物料完全溶解,过滤出料。
2、将上述滤液加入分散机中,开动搅拌,转速为1000~2000转/分,慢慢加入纳米二氧化硅,搅拌1小时,再加入稳定剂,搅拌30~60分钟,取样检验,产品合格后进行灌装。
本发明和现有产品相比的有益效果是:在SBS和树脂中加入纳米材料,粘接强度提高,胶层既有韧性又有足够的刚性,T型剥离强度提高了32%以上,实物抽查合格率提高了12%以上。整套配方搭配巧妙,先进合理,生产工艺简单。
具体实施方式
本发明纳米改性花炮底座胶,通过下述实施例加以说明,但不受这些实施例的限制,实施例1~2及对照例各组份的重量份数见表1。
实施例1
称取58份环保溶剂,加入带搅拌的反应釜中,调温至20~25℃,开动搅拌。加入8份石油树脂,7份萜烯树脂,4份改性松香树脂,搅拌2小时后,再加入18份SBS,搅拌4小时,过滤出料。
将上述滤液加入分散机中,开启搅拌,转速为2000转/分,慢慢加入3.0份50nm纳米二氧化硅,搅拌1小时,再加入稳定剂0.3份,搅拌40分钟,出料包装。
实施例2和对照例制备方法同实施例1。
表1
  组份名称   实施例1   实施例2   对照例
  SBS   18份   21份   24份
  纳米二氧化硅   3.0份(50nm)   1.5份(65nm)   /
  石油树脂   8份   10份   14份
  萜烯树脂   7份   6份   4份
  改性松香树脂   4份   7份   5份
  环保溶剂   58份   55份   50份
  稳定剂   0.3份   0.2份   0.4份
将实施例1、实施例2、对照例样品参照GB/T2791-1995标准,试片选择帆布-帆布,检测25℃时的T型剥离强度,另各制带塑料底座发射筒100个,装药做发射试验,纸筒与底座之胶接破坏为不合格,结果见表2。
表2
  样品名称   实施例1   实施例2   对照例
  T型剥离强度25℃帆布-帆布N/2.5cm 135 124 94
  实物抽查合格率%   100   99   87

Claims (4)

1、一种纳米改性花炮底座胶,其特征在于它是由重量百分数为18~25%的SBS弹性体、1~5%的纳米二氧化硅、8~15%的石油树脂、4~8%的萜烯树脂、4~8%的改性松香树脂、0.1%~0.5%的稳定剂、50~64%的环保溶剂组成,各组份的重量百分数之和为100%。
2、如权利要求1所述的纳米改性花炮底座胶,其特征在于石油树脂是C9石油树脂、C5石油树脂。
3、根据权利要求1所述的纳米改性花炮底座胶,其特征在于环保溶剂是环保溶剂405和环保溶剂401。
4、根据权利要求1所述的纳米改性花炮底座胶的制备方法,其特征在于它是按下述工艺过程制备的:
(1)称取规定配比量的环保溶剂,加入带搅拌器的反应釜中,温度控制在20~35℃,开动搅拌,加入配比量的石油树脂、萜烯树脂、改性松香树脂,搅拌2小时,再加入SBS,搅拌4~6小时,直至物料完全溶解,过滤出料。
(2)将上述滤液加入分散机中,开启搅拌,转速为1000~2000转/分,慢慢加入纳米二氧化硅,搅拌1~2小时,再加入稳定剂,搅拌30~60分钟,即为本发明产品。
CNA2007100350293A 2007-05-31 2007-05-31 一种纳米改性花炮底座胶及其制备方法 Pending CN101314703A (zh)