CN101193982A - 具有改善的流动性的聚酰胺模塑材料及其制备和用途 - Google Patents
具有改善的流动性的聚酰胺模塑材料及其制备和用途 Download PDFInfo
- Publication number
- CN101193982A CN101193982A CNA2006800172938A CN200680017293A CN101193982A CN 101193982 A CN101193982 A CN 101193982A CN A2006800172938 A CNA2006800172938 A CN A2006800172938A CN 200680017293 A CN200680017293 A CN 200680017293A CN 101193982 A CN101193982 A CN 101193982A
- Authority
- CN
- China
- Prior art keywords
- mold plastic
- polyamide
- polyamide mold
- weight
- end group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
聚酰胺类型 | 相对粘度(间甲酚中0.5%) | 体积流动速率(MVR)(275℃/5kg(cm3/10min)) |
PA12Grilamid L20*) | 1,9 | 75-100 |
Grilamid TR70*) | 1,4-1.5 | 5-10 |
炭黑类型 | BET(ASTMD3037),[m2/g] | DBP(ASTM D2414)[mL/100g] |
Ensaco 250比利时Timcal公司的商品 | 65 | 190 |
科琴黑EC-600 JDAkzo Nobel公司的商品 | 1270 | 480-510 |
聚酰胺类型 | 相对粘度(间甲酚中0.5%) | 端基浓度 | 摩尔质量(g/mol) |
PA12-低聚物 | 1.1 | NH2/COOH20/50 | 2000 |
名称 | 组成 | 生产商/供应商 |
Microtalk ITextra | 硅酸镁 | Norwegian Talc.B.V. |
Microcarb-OG | 重质碳酸钙 | OMYA AG(瑞士) |
Socal U1 | 沉淀碳酸钙 | Solvay AdvancedFunctional Materials(意大利) |
高岭土(瓷土) | 硅酸铝 | ECC InternationalLtd.(UK-Cornwall) |
组成 | ||||||
成分 | 条件 | 单位 | VB1 | B1 | B2 | B3 |
Grilamid L20(聚酰胺12) | 重量% | 62,65 | 57,65 | 52,65 | 47,65 | |
PA12-低聚物 | 重量% | 0 | 5,00 | 10,00 | 15,00 | |
玻璃纤维 | 重量% | 20,00 | 20,00 | 20,00 | 20,00 | |
炭黑ENSACO 250 | 重量% | 17,00 | 17,00 | 17,00 | 17,00 | |
HOSTANOXPAR 24 | 重量% | 0,10 | 0,10 | 0,10 | 0,10 | |
IRGANOX 245 | 重量% | 0,25 | 0,25 | 0,25 | 0,25 | |
聚酰胺模塑料的性质 | ||||||
H2O-含量 | 重量% | 0,003 | 0,05 | 0,02 | 0,04 | |
MVR | 275℃;10kg | cm3/10min | 26 | 49 | 81 | 213 |
流程 | mm | 152 | 188 | 219 | 257 | |
拉伸E模量 | - | MPa | 5400 | 5200 | 5000 | 5000 |
屈服应力 | - | MPa | 93 | 93 | 92 | 92 |
屈服伸长 | - | % | 3,7 | 3,9 | 4,1 | 4 |
断裂应力 | - | MPa | 90 | 92 | 91 | 91 |
断裂伸长 | - | % | 5,7 | 5,2 | 5,3 | 4,6 |
SZ | 23℃ | kJ/m2 | 66 | 68 | 63 | 52 |
SZ | -30℃ | kJ/m2 | 50 | 46 | 38 | 30 |
KSZ | 23℃ | kJ/m2 | 11,4 | 10 | 7,7 | 6,8 |
KSZ | -30℃ | kJ/m2 | 5,7 | 5,6 | 5,4 | 5,2 |
OWS | - | Ohm | 2,60E+05 | 1,50E+04 | 1,00E+04 | 9,60E+03 |
酸气(%) | +62 | +56 | +45 | +30 |
组成 | |||||
成分 | 条件 | 单位 | VB2 | B4 | B5 |
Grilamid L20(聚酰胺 12) | 重量% | 62.65 | 57.65 | 52.65 | |
PA12-低聚物 | 重量% | 0 | 5.00 | 10.00 | |
玻璃纤维 | 重量% | 30.00 | 30.00 | 30.00 | |
炭黑科琴黑EC-600 JD | 重量% | 7.00 | 7.00 | 7.00 | |
HOSTANOXPAR24 | 重量% | 0.10 | 0.10 | 0.10 | |
IRGANOX 245 | 重量% | 0.25 | 0.25 | 0.25 | |
聚酰胺模塑料的性质 | |||||
H2O含量 | 重量% | 0.08 | 0.03 | 0.03 | |
MVR | 275℃/21.6kg | cm3/10min | 27 | 37 | 66 |
流程 | mm | 124 | 146 | 172 | |
拉伸E模量 | - | MPa | 7200 | 7200 | 7100 |
断裂应力 | - | MPa | 120 | 120 | 120 |
断裂伸长 | - | % | 6.5 | 5.7 | 5.5 |
SZ | 23℃ | kJ/m2 | 90 | 80 | 80 |
SZ | -30℃ | kJ/m2 | 90 | 85 | 65 |
KSZ | 23℃ | kJ/m2 | 15 | 13 | 11 |
KSZ | -30℃ | kJ/m2 | 13 | 9 | 8 |
OWS | - | Ohm | 110 | 180 | 180 |
酸气(%) | +15 | +25 | +15 |
组成 | ||||||
成分 | 条件 | 单位 | VB3 | B6 | VB4 | B7 |
Grilamid L20(聚酰胺 12) | 重量% | 34,7 | 33.19 | 26.075 | 23.465 | |
PA12-低聚物 | 重量% | 0 | 1.735 | 0 | 3.47 | |
玻璃纤维 | 重量% | 65 | 65 | 65 | 65 | |
Grilamid TR70 | 重量% | 0 | 0 | 8.675 | 7.82 | |
HOSTANOXPAR 24 | 重量% | 0,05 | 0,05 | 0 | 0 | |
IRGANOX 245 | 重量% | 0,25 | 0,025 | 0,25 | 0,25 | |
聚酰胺模塑料的性质 | ||||||
H2O-含量 | 重量% | 0,02 | 0,03 | 0,02 | 0,01 | |
MVR | 275℃;5kg | cm3/10min | 52 | 112 | 5.4 | 9.7 |
流程 | mm | 146 | 163 | 133 | 182 | |
拉伸E模量 | - | MPa | 17000 | 17000 | 18200 | 18500 |
断裂应力 | - | MPa | 171 | 171 | 189 | 184 |
断裂伸长 | - | % | 4.5 | 4 | 3.4 | 2.6 |
SZ | 23℃ | kJ/m2 | 61 | 61 | 67 | 52 |
SZ | -30℃ | kJ/m2 | 75 | 64 | 74 | 55 |
KSZ | 23℃ | kJ/m2 | 21 | 19 | 17 | 14 |
KSZ | -30℃ | kJ/m2 | 17 | 16 | 14 | 11 |
组成 | ||||||||||||
成分 | 单位 | B8 | B9 | B10 | B11 | B12 | B13 | B14 | B15 | VB5 | VB6 | VB7 |
PA MACM12 | 重量% | 63 | 45 | 36 | 36 | 36 | 36 | 36 | ||||
PA 6I6T(30∶70) | 重量% | 47 | ||||||||||
PA 66 | 40 | 45 | ||||||||||
PA 12低聚物 | 重量% | 7 | 5 | 4 | 4 | 4 | 4 | 4 | 3 | 0 | 0 | 50 |
玻璃纤维 | 重量% | 30 | 50 | 50 | 40 | 30 | 40 | 40 | 40 | 30 | 50 | 0 |
Millicarb | 重量% | 10 | 20 | 10 | 5 | 40 | ||||||
高岭土 | 重量% | 30 | 5 | 10 | ||||||||
Socal U1 | 重量% | 20 | 30 | |||||||||
Mikrotalk ITextra | 重量% | 20 | ||||||||||
聚酰胺模塑料的性质 | ||||||||||||
水含量 | 重量% | 0.03 | 0.03 | 0.02 | 0.03 | 0.03 | 0.03 | 0.03 | 0.02 | 0.02 | 0.02 | 0.02 |
MVR(275 ℃/5kg) | ccm/10min | 56 | 27 | 13 | 14 | 15 | 16 | 14 | 25 | 14 | 12 | 22 |
变形 | % | 1.6 | 2.0 | 2.0 | 1.8 | 1.5 | 1.6 | 1.9 | 1.3 | 5.1 | 5.1 | 5.3 |
组成 | |||||||||
成分 | 单位 | B8 | B9 | B10 | B11 | B12 | B13 | B14 | B15 |
PA MACM12 | 重量% | 63 | 45 | 36 | 36 | 36 | 36 | 36 | |
PA 6I6T(30∶70) | 重量% | 47 | |||||||
PA 12低聚物 | 重量% | 7 | 5 | 4 | 4 | 4 | 4 | 4 | 3 |
玻璃纤维 | 重量% | 30 | 50 | 50 | 40 | 30 | 40 | 40 | 40 |
Millicarb | 重量% | 10 | 20 | 10 | |||||
高岭土 | 重量% | 30 | |||||||
Socal U1 | 重量% | 20 | |||||||
Mikrotalk IT extra | 重量% | 20 | |||||||
聚酰胺模塑料的性质 | |||||||||
水含量 | 重量% | 0.03 | 0.03 | 0.02 | 0.03 | 0.03 | 0.03 | 0.03 | 0.02 |
MVR(275℃/5kg) | ccm/10min | 56 | 27 | 13 | 14 | 15 | 16 | 14 | 25 |
变形 | % | 1.6 | 2.0 | 2.0 | 1.8 | 1.5 | 1.6 | 1.9 | 1.3 |
Claims (34)