CN101173090B - 一种pc/abs合金 - Google Patents

一种pc/abs合金 Download PDF

Info

Publication number
CN101173090B
CN101173090B CN2006101231846A CN200610123184A CN101173090B CN 101173090 B CN101173090 B CN 101173090B CN 2006101231846 A CN2006101231846 A CN 2006101231846A CN 200610123184 A CN200610123184 A CN 200610123184A CN 101173090 B CN101173090 B CN 101173090B
Authority
CN
China
Prior art keywords
abs
styrene
butadiene
abs alloy
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2006101231846A
Other languages
English (en)
Other versions
CN101173090A (zh
Inventor
汪克风
杨得志
姚其海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CN2006101231846A priority Critical patent/CN101173090B/zh
Publication of CN101173090A publication Critical patent/CN101173090A/zh
Application granted granted Critical
Publication of CN101173090B publication Critical patent/CN101173090B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种PC/ABS合金，其主要包括以下组分，以重量份数表示为：聚碳酸酯(PC)54～76、丙烯腈-丁二烯-苯乙烯共聚物(ABS)7～14、相容剂2～5、增韧剂3～8、磷酸酯类阻燃剂10～18、氢氧化镁1～2、聚四氟乙烯0.2～0.5、抗氧剂0.1～0.3。本发明提供的该种无卤阻燃PC/ABS合金，其采用磷酸酯类阻燃剂对PC/ABS合金进行阻燃改性，在提高PC/ABS合金阻燃性能的同时，也大大改善了PC/ABS的加工流动性。

Description

一种PC/ABS合金
技术领域
本发明涉及高分子技术领域，特别是涉及一种PC/ABS合金配方。
背景技术
PC/ABS(聚碳酸酯/丙烯腈-丁二烯-苯乙烯共聚物)合金是一种综合性能较好的工程塑料，兼有PC和ABS的优点，既具有优良的机械性能和热性能，又具有成型性好，耐应力开裂能力好的特点，适合于成型大型薄壁的制件。PC/ABS合金广泛应用于汽车工业、家用电器、通讯设备如移动电话等、办公设备如计算器和打印机等等。
当PC/ABS合金用于制造电子零构件时，往往要求材料具有阻燃性能，对此，人们通常采用添加阻燃剂的方法来改善材料的阻燃性能。而常用于阻燃PC/ABS合金的阻燃剂主要有十(或八)溴二苯醚、四溴双酚A、含溴碳酸酯齐聚物等卤系阻燃剂。一方面，使用含卤阻燃存在安全环保问题，另一方面含卤阻燃材料热裂解时产生的腐蚀性气体(HCl、HBr等)，即使浓度甚低，也可能使电子/电气设备中的关键部件受损而导致整套设备失灵。开发无卤阻燃PC/ABS合金是未来的发展趋势。
发明内容
鉴于以上需求，本发明的主要目的在于提供一种PC/ABS合金，该合金不使用卤系阻燃剂，有利于环保。
为达到上述目的，本发明提供的该种PC/ABS合金，其主要包括以下组分，以重量份数表示为：
聚碳酸酯(PC)                    54～76；
丙烯腈-丁二烯-苯乙烯共聚物(ABS) 7～14；
相容剂                          2～5；
增韧剂                          3～8；
磷酸酯类阻燃剂                  10～18；
氢氧化镁                        1～2；
聚四氟乙烯                      0.2～0.5；
抗氧剂                          0.1～0.3。
其中，所述兼容剂可为苯乙烯-马来酸酐共聚物(SMA)、马来酸酐接枝苯乙烯-丁二烯-丙烯腈三元共聚物(ABS-g-MAH)等。
所述增韧剂可优选为丙烯酸酯类共聚物等，例如丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)。
所述磷酸酯类阻燃剂可为磷酸三苯酯、亚磷酸三苯酯等。
所述抗氧剂可为抗氧剂2921、抗氧剂1076等。
优选地，本发明提供的PC/ABS合金，按重量份数计算包括以下组分：
聚碳酸酯(PC)                            54；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)         14；
苯乙烯-马来酸酐共聚物(SMA)              4；
丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)   8；
磷酸三苯酯                              18；
氢氧化镁                                2；
聚四氟乙烯                              0.5；
抗氧剂2921                              0.3。
优选地，本发明提供的PC/ABS合金，按重量份数计算包括以下组分：
聚碳酸酯(PC)                            68；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)         10；
苯乙烯-马来酸酐共聚物(SMA)              3；
丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)   5；
磷酸三苯酯                              12；
氢氧化镁                                2；
聚四氟乙烯                              0.3；
抗氧剂2921                              0.3。
优选地，本发明提供的PC/ABS合金，按重量份数计算包括以下组分：
聚碳酸酯(PC)                        76；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)     7；
苯乙烯-马来酸酐共聚物(SMA)          2；
丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)3；
磷酸三苯酯                          10；
氢氧化镁                            2；
聚四氟乙烯                          0.2；
抗氧剂2921                          0.3。
本发明提供的无卤阻燃PC/ABS合金，其采用磷酸酯类阻燃剂对PC/ABS合金进行阻燃改性，在提高PC/ABS合金阻燃性能的同时，也大大改善了PC/ABS的加工流动性。
具体实施方式
实施例1
按比例称取下列材料：
聚碳酸酯(PC)                           54；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)        14；
苯乙烯-马来酸酐共聚物(SMA)             4；
丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)  8；
磷酸三苯酯                             18；
氢氧化镁                               2；
聚四氟乙烯                             0.5；
抗氧剂2921                             0.3。
再将该共混料通过挤出机中混炼造粒，所得混炼造粒经注射成型制成成品，然后测试其性能，其结果如表1所示：
表1：实施例1所得成品测试结果
Figure GSB00000382775500031
实施例2
按比例称取下列材料：
聚碳酸酯(PC)                            68；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)         10；
苯乙烯-马来酸酐共聚物(SMA)              3；
丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)   5；
磷酸三苯酯                              12；
氢氧化镁                                2；
聚四氟乙烯                              0.3；
抗氧剂2921                              0.3。
再将该共混料通过挤出机中混炼造粒，所得混炼造粒经注射成型制成成品，然后测试其性能，其结果如表2所示：
表2：实施例2所得成品测试结果
Figure GSB00000382775500041
实施例3
按比例称取下列材料：
聚碳酸酯(PC)                         76；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)      7；
苯乙烯-马来酸酐共聚物(SMA)           2；
丙烯酸酯-苯乙烯-丁二烯三元共聚物(MBS)3；
磷酸三苯酯                           10；
氢氧化镁                             2；
聚四氟乙烯                           0.2；
抗氧剂2921                           0.3。
再将该共混料通过挤出机中混炼造粒，所得混炼造粒经注射成型制成成品，然后测试其性能，其结果如表3所示：
表3：实施例3所得成品测试结果
Figure GSB00000382775500042
以上具体实施方式，是对本发明所作的详细说明。注意这些实施方式并非用以限定本发明，对于本领域的熟练技术人员，在不背离本发明精神的情况下所做出的改进和补充，应该视为在本发明的保护范围之内。

Claims (7)

1.一种PC/ABS合金，其特征在于，主要包括以下组分，以重量份数表示为：
聚碳酸酯(PC)                    54～76；
丙烯腈-丁二烯-苯乙烯共聚物(ABS) 7～14；
相容剂                          2～5；
增韧剂                          3～8；
磷酸酯类阻燃剂                  10～18；
氢氧化镁                        1～2；
聚四氟乙烯                      0.2～0.5；
抗氧剂                          0.1～0.3；
其中，所述磷酸酯类阻燃剂为磷酸三苯酯、亚磷酸三苯酯。
2.根据权利要求1所述的PC/ABS合金，其特征在于，所述相容剂为苯乙烯-马来酸酐共聚物(SMA)、马来酸酐接枝苯乙烯-丁二烯-丙烯腈三元共聚物(ABS-g-MAH)。
3.根据权利要求1所述的PC/ABS合金，其特征在于，所述增韧剂为丙烯酸酯类共聚物。
4.根据权利要求1所述的PC/ABS合金，其特征在于，所述抗氧剂为抗氧剂2921、抗氧剂1076。
5.根据权利要求1-4任意一项所述的PC/ABS合金，其特征在于，其配方按重量份数计算包括以下组分：
聚碳酸酯(PC)                                54；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)             14；
苯乙烯-马来酸酐共聚物(SMA)                  4；
甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物(MBS) 8；
磷酸三苯酯                                  18；
氢氧化镁                                    2；
聚四氟乙烯                                  0.5；
抗氧剂2921                                  0.3。
6.根据权利要求1-4任意一项所述的PC/ABS合金，其特征在于，其配方按重量份数计算包括以下组分：
聚碳酸酯(PC)                                68；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)             10；
苯乙烯-马来酸酐共聚物(SMA)                  3；
甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物(MBS) 5；
磷酸三苯酯        12；
氢氧化镁          2；
聚四氟乙烯        0.3；
抗氧剂2921        0.3。
7.根据权利要求1-4任意一项所述的PC/ABS合金，其特征在于，其配方按重量份数计算包括以下组分：
聚碳酸酯(PC)                                76；
丙烯腈-丁二烯-苯乙烯共聚物(ABS)             7.；
苯乙烯-马来酸酐共聚物(SMA)                  2；
甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物(MBS) 3；
磷酸三苯酯                                  10；
氢氧化镁                                    2；
聚四氟乙烯                                  0.2；
抗氧剂2921                                  0.3。
CN2006101231846A 2006-10-31 2006-10-31 一种pc/abs合金 Expired - Fee Related CN101173090B (zh)