CN101126271A - 一种水泥装饰板及其制备方法 - Google Patents

一种水泥装饰板及其制备方法 Download PDF

Info

Publication number
CN101126271A
CN101126271A CNA2007100153971A CN200710015397A CN101126271A CN 101126271 A CN101126271 A CN 101126271A CN A2007100153971 A CNA2007100153971 A CN A2007100153971A CN 200710015397 A CN200710015397 A CN 200710015397A CN 101126271 A CN101126271 A CN 101126271A
Authority
CN
China
Prior art keywords
cement
decorative plate
surface layer
wire
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007100153971A
Other languages
English (en)
Other versions
CN100494603C (zh
Inventor
张莉莉
苏允桥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jinan University
University of Jinan
Original Assignee
University of Jinan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Jinan filed Critical University of Jinan
Priority to CNB2007100153971A priority Critical patent/CN100494603C/zh
Publication of CN101126271A publication Critical patent/CN101126271A/zh
Application granted granted Critical
Publication of CN100494603C publication Critical patent/CN100494603C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于建筑装饰板的技术领域,特别涉及一种具有质感和美感、价廉物美的水泥装饰板,以及它的制备方法。本发明涉及一种水泥装饰板,是由面层和底层构成,底层是由水泥沙浆制成,面层是由水泥、水溶性有机树脂、颜料和外加剂为原料制成,面层的外表面内嵌有呈一定图案的金属丝。该装饰板材具有良好的耐水耐酸碱性的性能,较强的抗药和抗折强度,不变形、不褪色。其颜色和金属丝的造型、材质可以根据需要进行设计,具有成本低、环保、符合可持续发展的产业政策等优点。可广泛应用于墙面、地面、家具表面等的装饰。本发明的制作方法,具有简单易学,制作方便。

Description

一种水泥装饰板及其制备方法(一) 技术领域本发明属于建筑装饰板的技术领域,特别涉及一种具有质感和美感、 价廉物美的水泥装饰板,以及它的制备方法。(二) 背景技术随着国家经济生活的发展,室内设计所使用的材料己涉及到钢铁、有 色金属、化工、纺织、木材、陶瓷、塑料、玻璃等多种行业。人们对于室 内设计的主题精神的强调与重视,也需要极具个性又成本适中的新型材料 来实现。单就贴面装饰一项,可选用的板材种类众多,比如陶瓷釉面砖、 大理石,花岗岩饰面砖等,但上述板材在装饰效果上难以有新的突破,并 且造价偏高。研制造价低廉、性能良好、具有环保的特点,符合国家发展 政策的装饰板材是相当有必要的。(三) 发明内容本发明的目的在于提供一种具有质感和美感的价廉物美的水泥装饰 板,以替代天然大理石、人造大理石、瓷砖、水磨石等材料,用于装饰柱 子、墙面和室内地面。本发明的另一目的在于提供上述水泥装饰板的制备方法。本发明是通过以下措施来实现的:本发明涉及一种水泥装饰板,是由面层和底层构成,其特别之处在于: 底层是由水泥沙浆制成,面层是由水泥、水溶性有机树脂、颜料和外加剂 为原料制成,面层的外表面内嵌有呈一定图案的金属丝。上述本发明的水泥装饰板,底料是由以下重量配比的原料制成:硫铝酸盐水泥15-25%、沙20-35%、石子20-35%、辅料0-15%,水10-20%; 面料是由以下重量配比的原料制成:硫铝酸盐水泥25-40%、沙15-30%、 玻璃纤维1.5-2%、颜料5-15%、水溶性树脂5-10%,水20-30%。其中颜料为氧化铁红、氧化铬绿、群青、钛白粉、金粉、银粉等无机 颜料,这些颜料可单独使用,也可混合使用。上述本发明的水泥装饰板,所述的金属丝为铜丝、铝丝、银丝、金丝 和不锈钢丝的一种或一种以上。
上述本发明的水泥装饰板的制备方法,包括以下步骤:
(1) 制备底层料浆;
(2) 制备面层料浆
(3) 模具内壁刷涂脱模剂,然后把金属丝摆放在模具表面预先制好的
槽内,适当固定,随即将搅拌均匀的面层料浆注入模具2〜3毫 米厚,振平;再注入充分搅拌的底层料浆,振平;随后静置2小 时让其初步凝结,初凝后养护3天,最后脱模,晾干8天即可。
本发明的有益效果是,该装饰板材具有良好的耐水耐酸碱性的性能, 较强的抗药和抗折强度,不变形、不褪色。其颜色和金属丝的造型、材质 可以根据需要进行设计,具有成本低、环保、符合可持续发展的产业政策 等优点。可广泛应用于墙面、地面、家具表面等的装饰。
本发明的制作方法,具有简单易学,制作方便。
(四) 附图说明
图1是本发明的结构分解示意图 图2是本发明的剖面结构示意图。 图3是本发明的平面结构示意图。 图中:l金属丝、2面层、3底层。
(五) 具体实施方式 下面结合附图和具体实施例对本发明进一步说明。
实施例1:
本实施例的结构如图l-图3所示,是由面层2和底层3构成,面层3 的外表面内嵌有5根金属丝1。
制备方法如下:
制备底层料浆:称取以下重量配比的原料,搅拌均匀制成底层料浆。
硫铝酸盐水泥22%、沙30%、石子28%、水15%、工业废渣5%。
制备面层料浆:称取以下重量配比的原料,搅拌均匀制成面层料浆。
硫铝酸盐水泥36%、沙22%、玻璃纤维2%、水24%、颜料为氧化铬绿和
金粉共计8%、水溶性树脂8%。
模具内壁刷涂脱模剂,然后将5根铜丝制成的金属丝,摆放在模具表
面预先制好的槽内,适当固定,随即将搅拌均匀的面层料浆注入模具约2〜 3毫米厚,振平;再注入充分搅拌的底层料浆,振平;随后静置2小时让
其初歩凝结,初凝后养护3天,最后脱模,晾干8天即可。
实施例2:
本实施例的结构与实施例1基本相同。
制备方法如下:
制备底层料浆:称取以下重量配比的原料,搅拌均匀制成底层料浆。
硫铝酸盐水泥25%、沙33%、石子24%、水18%。
制备面层料浆:称取以下重量配比的原料,搅拌均匀制成面层料浆。
硫铝酸盐水泥30%、沙30%、玻璃纤维1.5%、水22%、颜料为金粉和银 粉8.5%、水溶性树脂8%。
用玻璃制成模具,模具内壁刷涂脱模剂,然后将铜丝和铝丝制成金属 丝,摆放在模具表面预先制好的槽内,适当固定,随即将搅拌均匀的面层 料浆注入模具约3毫米厚,振平;再注入充分搅拌的底层料浆,约5毫米 厚,然后振平;随后静置2小时让其初步凝结,初凝后养护3天,最后脱 模,晾干8天即可。

Claims (5)

1、一种水泥装饰板,是由面层和底层构成,其特征在于:底层是由水泥沙浆制成,面层是由水泥、水溶性有机树脂、颜料和外加剂为原料制成,面层的外表面内嵌有呈一定图案的金属丝。
2、 根据权利要求1所述的水泥装饰板,其特征在于: 底料是由以下重量配比的原料制成:硫铝酸盐水泥15-25%、沙20-35%、石子20-35%、辅料0-15%,水10-20%;面料是由以下重量配比的原料制成:硫铝酸盐水泥25-40%、沙 15-30%、玻璃纤维1.5-2%、颜料5-15%、水溶性树脂5-20%,水20-30%。
3、 根据权利要求1或2所述的水泥装饰板,其特征在于:所述的金属 丝为铜丝、铝丝、银丝、金丝和不锈钢丝的一种或一种以上。
4、 根据权利要求1或2所述的水泥装饰板,其特征在于:所述的颜料 为氧化铁红、氧化铬绿、群青、钛白粉、金粉和银粉的一种或一种 以上。
5、 一种权利要求1所述的水泥装饰板的制备方法,其特征在于包括以下步骤:(1) 制备底层料浆;(2) 制备面层料浆;(3) 模具内壁刷涂脱模剂,然后把金属丝摆放在模具表面预先制好的 槽内,适当固定,随即将搅拌均匀的面层料桨注入模具2〜3毫 米厚,振平;再注入充分搅拌的底层料浆,振平;随后静置2小 时让其初步凝结,初凝后养护3天,最后脱模,晾干8天即可。
CNB2007100153971A 2007-07-20 2007-07-20 一种水泥装饰板及其制备方法 Expired - Fee Related CN100494603C (zh)