CN101100801A - Non-ironing post-finishing technique for cotton fabric - Google Patents

Non-ironing post-finishing technique for cotton fabric Download PDF

Info

Publication number
CN101100801A
CN101100801A CNA2007100430902A CN200710043090A CN101100801A CN 101100801 A CN101100801 A CN 101100801A CN A2007100430902 A CNA2007100430902 A CN A2007100430902A CN 200710043090 A CN200710043090 A CN 200710043090A CN 101100801 A CN101100801 A CN 101100801A
Authority
CN
China
Prior art keywords
resin
cotton fabric
controlled
temperature
minute
Prior art date
Application number
CNA2007100430902A
Other languages
Chinese (zh)
Other versions
CN100549271C (en
Inventor
徐军
顾永星
张国平
Original Assignee
上海白玉兰染整有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 上海白玉兰染整有限公司 filed Critical 上海白玉兰染整有限公司
Priority to CNB2007100430902A priority Critical patent/CN100549271C/en
Publication of CN101100801A publication Critical patent/CN101100801A/en
Application granted granted Critical
Publication of CN100549271C publication Critical patent/CN100549271C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to weaving cotton fabric no ironing post collating technology. It includes the following steps: face fabric preparation; padding resin; framing drying; baking; pre-shrinking; winding. The face fabric preparation includes gray cloth seaming, singeing, de-sizing, alkali mercerization, dying, framing forming, liquid ammonia collating. The padding resin includes two times. The above technology can make the cotton fabric have good feeling, gas permeability, moisture absorption, and increase wrinkle resistance, greatly reduce formaldehyde residual, energy resource consumption, sewage discharge.

Description

The non-ironing post-finishing technique of COTTON FABRIC
Technical field
The present invention relates to the finishing technique of fabric, relate in particular to the non-ironing post-finishing technique of woven COTTON FABRIC.
Background technology
Pure cotton fabric is strong, soft, comfortable and easy to wear because of good permeability, hygroscopicity for a long time, is subjected to consumer's welcome deeply always.But the clothes of pure cotton fabric are wrinkling easily, not well-pressed in dress and washing, and it is attractive in appearance that easily the clothes made of the pure cotton fabric of wrinkle have influenced people's dress.Obviously, the natural attribute of the easy wrinkle of pure cotton fabric affects the use range of this fabric significantly.
The process route of no-ironing finishing of pure cotton textile has two kinds: the one, before bake method, be that the fabric open width is padded resin, flat curings etc. all operation are finished by printing and dyeing mill, this is traditional process route, its weak point is that processing brings certain degree of difficulty to clothes, be difficult to give its a little gofferings and apparel modeling, so it is only applicable to the arrangement processing of cloth to clothes; The 2nd, adopt to bake method after now widely popular, according to the mode difference of padding resin, can be divided into again that grey cloth pads and two kinds of clothes dippings.The former pads resin and oven dry for pure cotton fabric in printing and dyeing mill, but resin crosslinks reaction is stayed and just finished after putting into baking oven after the garment sewing; The latter is dried and is baked after spraying with clothes immersion dressing liquid or with spray gun.Clothes are through after baking, and crosslinked resin just makes the goffering of clothes and smooth outward appearance be fixed up, and clothes are after the dress washing, and fiber always tries hard to be returned to the state when crosslinked.Clothes after durable press finish, have soft, characteristics such as goffering is lasting.
The various in recent years technologies around no-ironing finishing of pure cotton textile constantly occur, but there is two large problems all the time in iron-free finishing process:
One, the fabric strength of handling through iron-free finishing process, ABRASION RESISTANCE reduce, the clothes cracky that the fabric that its clothes of making were not handled through iron-free finishing process is made;
Two, the residual height of handling through iron-free finishing process of fabric formaldehyde.
CN 1189617C discloses a kind of " method for no-ironing finishing of pure cotton textile ", and its technology is that lining is prepared, and is pre-soft; the tide crosslinking coagent, storage reaction, washing; stentering forming, calendering, preshrunk; test technological processes such as dress; its defective is that technological process is long, must be through water-washing step, and this step need be with a large amount of water; consumed great amount of water resources, sewage discharge is unfavorable for the protection of environment.And the content of formaldehyde of the pure cotton fabric that obtains through this noniron finish method is higher, just reaches international environmental protection standard 75ppm.
Summary of the invention
The object of the present invention is to provide a kind of non-ironing post-finishing technique that can overcome the COTTON FABRIC of above-mentioned defective workmanship, this technology makes feel, gas permeability, the hygroscopicity of COTTON FABRIC continue to keep the characteristic of COTTON FABRIC, wrinkle resistance, fabric strength, ABRASION RESISTANCE greatly improve, and formaldehyde is residual to be reduced greatly.
The technical scheme that realizes the object of the invention is: a kind of non-ironing post-finishing technique of COTTON FABRIC, comprise that lining prepares, pads that resin, tentering are dried, baked, preshrunk, clot step, wherein lining prepare to comprise that grey cloth sews up, singes, destarch, alkali mercerized, dyeing, stentering forming and liquid ammonia finishing step, wherein, also comprise pad behind the resin and the tentering oven dry before ventilative step.
The described resin steps of padding comprises and pads resin steps twice, the prescription that pads the resin of resin steps for this twice is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, dimethyl urea glyoxal 60-120g/L, dicyandiamide 1-5g/L, catalyst 5-50g/L, softener 5-100g/L, wetting agent 0.1-5g/L, all the other are water in every liter of volume, and the ventilative time is controlled at 30-80 second in the ventilative step.
Preferably, the described prescription that pads the resin of resin steps for twice is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, dimethyl urea glyoxal 60-120g/L, dicyandiamide 2g/L, catalyst 40g/L, polyethylene softener 20g/L, silicone softening agent 30g/L, non-ionic wetting agent 1g/L, all the other are water in every liter of volume, the ventilative time is controlled at 30-80 second in the ventilative step.
Preferably, described to pad the pick-up that pads resin in the resin steps for the first time for twice be 75-80%, the speed of a motor vehicle be 30-60 rice/minute, the pick-up that pads resin for the second time is 68-70%, the speed of a motor vehicle be 30-60 rice/minute.
During preparing, described lining carries out liquefied ammonia open washing step after the liquid ammonia finishing step, this step is open washing in four times five the ten lattice flat wash troughs on every lattice flat wash trough deflector roll is, 80-90 ℃ of the liquefied ammonia temperature control of 1-6 lattice flat wash trough, the 7th lattice add acetic acid, and pH value is controlled at 3-4 in this groove, and temperature is controlled at 50-60 ℃, the 8th lattice temperature is controlled at 80-90 ℃, the 9th and 10 lattice temperature are controlled at 30-40 ℃, and cropping cloth cover pH value is controlled at 6-7, speed of a motor vehicle 30-60 rice/minute.Described tentering baking step is for carrying out 80 ℃ of preceding four joint drying room temperature, 90 ℃ of five-six joint drying room temperature in eight joint drying rooms, 100 ℃ of temperature oven dry of seven-eight joint drying rooms, cropping cloth surface temperature is controlled at 30 ℃ ± 5 ℃, cloth surface humidity 6-8%, the speed of a motor vehicle be 30-60 rice/minute.The described step condition that bakes is 160 ℃ of temperature, 1 minute 45 seconds-3 minutes time.In the described stentering forming step speed of a motor vehicle 30-65 rice/minute, 150 ℃ of temperature.Described catalyst is the Catalyst531 of commercially available Ou Nuofa company or the plain N in Kangding of BASF AG.
Owing to adopted above-mentioned technical solution, solved the contradiction between cotton fabric crease-shedding performance and fabric strength, the ABRASION RESISTANCE fully, make the feel, gas permeability, hygroscopicity of COTTON FABRIC continue to keep the characteristic of COTTON FABRIC, wrinkle resistance greatly improves, formaldehyde is residual to be reduced greatly, can also reduce energy resource consumption and sewage emissions.
The specific embodiment
The present invention is described in further detail below in conjunction with embodiment.
A kind of non-ironing post-finishing technique of COTTON FABRIC comprises: lining prepare, pad resin, ventilative, tentering is dried, bake, preshrunk, clot step.Be specially:
(1) lining is prepared
Steps such as lining prepares to comprise that grey cloth sews up, singes, destarch, alkali mercerized, liquid ammonia finishing.
1, grey cloth sews up
It is with the positive and negative unanimity that grey cloth sews up, and the grey cloth that margin to seam is firm is made connection, guarantees serialization production.
2, singe
Four burners, two positive two counter to reach the cloth cover filoplume clean, lining 80-400 gram/square metre speed be 70-140 rice/minute.
3, destarch
Destarch is moved back only, guarantees that the destarch rate is more than 99%.
4, alkali mercerized
Caustic soda concentration 240-260 grams per liter.
5, dyeing/stamp
6, stentering forming
The speed of a motor vehicle 20-80 rice/minute, temperature 80-200 ℃.
7, liquid ammonia finishing
Fabric pads in pure liquid ammonia (33 ℃) lining, and is expanded internally during evaporation, discharges inherent strain, increases gloss, brute force and the elasticity etc. of cellulose fibre, the more plentiful softness of feel, and speed of a motor vehicle 20-80 rice/minute.
8, liquefied ammonia open washing
Ten lattice flat wash trough open washings, every lattice flat wash trough deflector roll is last four times five, 80-90 ℃ of the liquefied ammonia temperature control of 1-6 lattice flat wash trough, the 7th lattice add acetic acid, pH value is controlled at 3-4 in this groove, and temperature is controlled at 50-60 ℃, and the 8th lattice temperature is controlled at 80-90 ℃, 9th, 10 lattice temperature are controlled at 30-40 ℃, and cropping cloth cover pH value is controlled at 6-7.Speed of a motor vehicle 30-60 rice/minute.
(2) pad resin
In order to guarantee that resin fully permeates, the left, center, right is even, and padding resin is secondary, and secondary pads the prescription unanimity of resin.
For the first time pad resin, pick-up is 75-80%, the speed of a motor vehicle be 30-60 rice/minute.
The prescription of resin is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, dimethyl urea glyoxal (DNUG resin) 60-120g/L, dicyandiamide 1-5g/L, catalyst 5-50g/L, softener 5-100g/L, wetting agent 0.1-5g/L, all the other are water.
According to the cloth brute force, modification 2D resin is that dihydroxymethyl dihydroxy ethylene base urea can be controlled in 60-120g/L, and the DNUG resin is at 60-120g/L.
For the second time pad resin, pick-up is 68-70%, the speed of a motor vehicle be 30-60 rice/minute.
The prescription of resin is formed: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, dimethyl urea glyoxal 60-120g/L, and dicyandiamide 1-5g/L, catalyst 5-50g/L, softener 5-100g/L, wetting agent 0.1-5g/L, all the other are water.
According to the cloth brute force, above-mentioned catalyst, softener, wetting agent are selected from the known reagent of this area.For example catalyst is a magnesium chloride etc., and softener is polyethylene softener and silicone softening agent, and wetting agent is a non-ionic wetting agent.
(3) ventilative
The ventilative time is controlled at 30-80 second.
This step guarantees that resin fully is penetrated into fibrous inside.
(4) tentering oven dry
The oven dry of 80-100 ℃ of temperature, cropping temperature be at 30 ℃ ± 5 ℃, cloth cover contain damp rate at 6-8%.
(5) bake
160 ℃, 1 minute 45 seconds-3 minutes, resin and cellulose fibre at high temperature carried out the interlinkage reaction, reach non-ironing effect.
(6) preshrunk
Improve the DIMENSIONAL STABILITY and the feel of fabric.
(7) clot
The clot finished product.
The component of above-mentioned resin formula is all from commercially available.
Modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea source: the flat F-ECO of clothes silk of BASF AG or the Permafresh TG of Ou Nuofa company; DNUG resin source: the flat NF of clothes silk of BASF AG.
Catalyst source: the plain N in the Catalyst531 of Ou Nuofa company or the Kangding of BASF AG.
The concocting method of above-mentioned resin formula is conventional collocation method, concocting method such as above-mentioned resin formula is followed successively by: 300ml water, add nonionic wetting agent 0.1-5g/L, adding modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, adds DNUG resin 60-120g/L, adds polyethylene softener 20g/L, add organic silicone softener 30g/L, add catalyst 40g/L, add dicyandiamide 2g/L, add water and cause 1L.
The technique effect of technology of the present invention is as follows:
1, improves flat deflection.
Press AATCC124-2001 test, report number: STJ0032588 (once padding)/STJ0081470 (secondary pads+lets in air) through Intertek company
Show:
Pad number of times Pick-up Flat deflection
Once pad ????70% ????2.8-3.2
Secondary pads+lets in air ????70% ????3.5-4.0
2, the present invention has improved the brute force of the COTTON FABRIC after the noniron finish, has reduced residual formaldehyde, has reduced the water consumption of this technology.
Press the AATCC124-2001 test through Intertek company, report number: STJ0226659 shows: (with 40*40, the 130*90 Cotton Colored Woven Fabric is an example)
Tensile strength (N) Tearing brute force (N) Water consumption (ton/myriametre) Flat deflection Content of formaldehyde
Tide is crosslinked 240 ??8 ??80 ?3.5-4.0 ??≤75
Common resins 260 ??7 ??40 ?2.0-3.0 ??≤75
The present invention's prescription 290 ??10 ??0 ?3.5-4.0 ??≤40
3, improved the ABRASION RESISTANCE of the COTTON FABRIC after the noniron finish.
Through the test of american cotton company, with 20*16, the purplish blue look of 128*60 is an example, and the data of testing with Martin Dell wear resistant instrument are:
7000 change 10000 change 15000 change 20000 change
Normal dyeing ??/ ???/ Wearing and tearing are arranged
Tide is crosslinked ??/ Wearing and tearing are arranged Worn out
Common resins Wearing and tearing are arranged Worn out
The present invention's prescription ??/ ???/ ??/ Wearing and tearing are arranged
Above-mentionedly roll low formaldehyde no-ironing resin and carry out on framing shaping machine, equipment has two padding machines through transforming, and evenly soaks on fabric to guarantee low formaldehyde no-ironing resin, and ventilative technology guarantees that resin fully is penetrated into fibrous inside.
Embodiment 1
With the pure cotton dyeing poplin cloth is example, this poplin cloth number 40*40, and specification 130*80, grammes per square metre 110 grams/square metre.
(1) lining is prepared
1. grey cloth sews up
It is with the positive and negative unanimity that grey cloth sews up, and the grey cloth that margin to seam is firm is made connection, guarantees serialization production.
2. singe
Four burners, two positive two counter to reach the cloth cover filoplume clean, lining 110 grams/square metre, speed is 110 meters/minute.
3. destarch
Destarch is moved back only, guarantees that the destarch rate is more than 99%.
4. alkali mercerized
Caustic soda concentration 240-260 grams per liter.
5. dyeing
6. stentering forming
The speed of a motor vehicle is at 65 meters/minute, 150 ℃ of temperature.
7. liquid ammonia finishing
Fabric pads in pure liquid ammonia (33 ℃) lining, and is expanded internally during evaporation, discharges inherent strain, increases gloss, brute force and the elasticity etc. of cellulose fibre, the more plentiful softness of feel, 65 meters/minute of the speed of a motor vehicle.
8. liquefied ammonia open washing
Ten lattice flat wash trough open washings, every lattice flat wash trough deflector roll is last four times five, 80-90 ℃ of the temperature control of 1-6 lattice flat wash trough, the 7th lattice add acetic acid, pH value is controlled at 3-4 in this groove, and temperature is controlled at 50-60 ℃, and the 8th lattice temperature is controlled at 80-90 ℃, 9th, 10 lattice temperature are controlled at 30-40 ℃, and cropping cloth cover pH value is controlled at 6-7.60 meters/minute of the speed of a motor vehicle.
(2) pad resin
In order to guarantee that resin fully permeates, the left, center, right is even, and padding resin is secondary.
For the first time pad resin, pick-up is 75-80%, and the speed of a motor vehicle is 60 meters/minute.
The prescription of resin is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 80g/L, DNUG resin 80g/L, and dicyandiamide 2g/L, catalyst 35g/L, polyethylene softener 20g/L, silicone softening agent 30g/L, wetting agent 1g/L, all the other are water.
For the second time pad resin, pick-up is 68-70%, and the speed of a motor vehicle is 60 meters/minute.
The prescription that pads for the second time resin is with padding for the first time resin formula.
(3) ventilative
The ventilative time was controlled at 40 seconds.
(4) tentering oven dry
Eight joint drying rooms are arranged, 80 ℃ at preceding four joints, 90 ℃ at five-six joints, 100 ℃ of temperature oven dry of seven-eight joints, cropping cloth surface temperature is controlled at 30 ℃ ± 5 ℃, cloth surface humidity 6-8%.The speed of a motor vehicle is 60 meters/minute.
(5) bake
Bake 160 ℃, 1 minute and 45 seconds.
(6) preshrunk
Improve the DIMENSIONAL STABILITY and the feel of fabric.
(7) clot
Embodiment 2
With the Cotton Colored Woven Fabric is example, this Cotton Colored Woven Fabric number 40*40, and specification 130*90, grammes per square metre 140 grams/square metre.
(1) lining is prepared
Steps such as lining prepares to comprise that grey cloth sews up, singes, destarch, alkali mercerized, liquid ammonia finishing.Lining comprises yarn-dyed fabric, stained clot-h, calico
9. grey cloth sews up
It is with the positive and negative unanimity that grey cloth sews up, and the grey cloth that margin to seam is firm is made connection, guarantees serialization production.
10. singe
Four burners, two positive two counter to reach the cloth cover filoplume clean, lining 140 grams/square metre, speed is 100 meters/minute.
11. destarch
Destarch is moved back only, guarantees that the destarch rate is more than 99%.
12. it is alkali mercerized
Caustic soda concentration 240-260 grams per liter.
13. stentering forming
The speed of a motor vehicle is at 60 meters/minute, 150 ℃ of temperature.
14. liquid ammonia finishing
Fabric pads in pure liquid ammonia (33 ℃) lining, and is expanded internally during evaporation, discharges inherent strain, increases gloss, brute force and the elasticity etc. of cellulose fibre, the more plentiful softness of feel, 60 meters/minute of the speed of a motor vehicle.
15. liquefied ammonia open washing
Ten lattice flat wash trough open washings, every lattice flat wash trough deflector roll is last four times five, 80-90 ℃ of the temperature control of 1-6 lattice flat wash trough, the 7th lattice add acetic acid, this tank pH value is controlled at 3-4, and temperature is controlled at 50-60 ℃, and the 8th lattice temperature is controlled at 80-90 ℃, 9th, 10 lattice temperature are controlled at 30-40 ℃, and cropping cloth cover pH value is controlled at 6-7.50 meters/minute of the speed of a motor vehicle.
(2) pad resin
In order to guarantee that resin fully permeates, the left, center, right is even, and padding resin is secondary.
For the first time pad resin, pick-up is 75-80%, and the speed of a motor vehicle is 45 meters/minute.
The prescription of resin is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 80g/L, DNUG resin 100g/L, and dicyandiamide 2g/L, catalyst 40g/L, polyethylene softener 20g/L, silicone softening agent 30g/L, wetting agent 0.1g/L, all the other are water.
For the second time pad resin, pick-up is 68-70%, and the speed of a motor vehicle is 45 meters/minute.
The prescription that pads for the second time resin is with padding for the first time resin formula.
(3) ventilative
The ventilative time was controlled at 53 seconds.
(4) tentering oven dry
Eight joint drying rooms are arranged, 80 ℃ at preceding four joints, 90 ℃ at five-six joints, 100 ℃ of temperature oven dry of seven-eight joints, cropping cloth surface temperature is controlled at 30 ℃ ± 5 ℃, cloth surface humidity 6-8%.The speed of a motor vehicle is 45 meters/minute.
(5) bake
Bake 160 ℃, 2 minutes.
(6) preshrunk
Improve the DIMENSIONAL STABILITY and the feel of fabric.
(7) clot
Press the AATCC124-2001 test through Intertek company, report number: STJ00226659 Cotton Colored Woven Fabric 40*40,130*90, grammes per square metre 150 gram/square metre test datas are:
Formaldehyde Flat deflection
After washing five times 30ppm 4.0
Embodiment 3
With textile cloth is example, this cotton textiles cloth number 40/2 * 40/2, and specification 138 * 66, grammes per square metre 360 grams/square metre.
(1) lining is prepared
Steps such as lining prepares to comprise that grey cloth sews up, singes, destarch, alkali mercerized, liquid ammonia finishing.Lining comprises yarn-dyed fabric, stained clot-h, calico
1. grey cloth sews up
It is with the positive and negative unanimity that grey cloth sews up, and the grey cloth that margin to seam is firm is made connection, guarantees serialization production.
2. singe
Four burners, two positive two counter to reach the cloth cover filoplume clean, lining 360 grams/square metre, speed is 85 meters/minute.
3. destarch
Destarch is moved back only, guarantees that the destarch rate is more than 99%.
4. alkali mercerized
Caustic soda concentration 240-260 grams per liter.
5. dyeing
6. stentering forming
The speed of a motor vehicle is at 30 meters/minute, 150 ℃ of temperature.
7. liquid ammonia finishing
Fabric pads in pure liquid ammonia (33 ℃) lining, and is expanded internally during evaporation, discharges inherent strain, increases gloss, brute force and the elasticity etc. of cellulose fibre, the more plentiful softness of feel, 30 meters/minute of the speed of a motor vehicle.
8. liquefied ammonia open washing
Ten lattice flat wash trough open washings, every lattice flat wash trough deflector roll is last four times five, 80-90 ℃ of the temperature control of 1-6 lattice flat wash trough, the 7th lattice add acetic acid, pH value is controlled at 3-4 in this groove, and temperature is controlled at 50-60 ℃, and the 8th lattice temperature is controlled at 80-90 ℃ 2,9th, 10 lattice temperature are controlled at 30-40 ℃, and cropping cloth cover pH value is controlled at 6-7.
(2) pad resin
In order to guarantee that resin fully permeates, the left, center, right is even, and padding resin is secondary.
For the first time pad resin, pick-up is 75-80%, and the speed of a motor vehicle is 30 meters/minute.
The prescription of resin is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 100g/L, DNUG resin 120g/L, dicyandiamide 2g/L, the mixture 40g/L of magnesium chloride and citric acid equal proportion, polyethylene softener 20g/L, silicone softening agent 30g/L, wetting agent 5g/L, all the other are water.
For the second time pad resin, pick-up is 68-70%, and the speed of a motor vehicle is 30 meters/minute.
The prescription that pads for the second time resin is with padding for the first time resin formula.
(3) ventilative
The ventilative time was controlled at 80 seconds.
(4) tentering oven dry
Eight joint drying rooms are arranged, 80 ℃ at preceding four joints, 90 ℃ at five-six joints, 100 ℃ of temperature oven dry of seven-A joint, cropping cloth surface temperature is controlled at 30 ℃ ± 5 ℃, cloth surface humidity 6-8%, the speed of a motor vehicle is 30 meters/minute.
(5) bake
Bake 160 ℃, 3 minutes.
(6) preshrunk
Improve the DIMENSIONAL STABILITY and the feel of fabric.
(7) clot → finished product
Press the AATCC124-2001 test through Intertek company, report number: STJ0110866, Cotton Colored Woven Fabric 40/2 * 40/2,138 * 66, grammes per square metre 360 gram/square metre test datas:
Flat deflection
After washing once ????3.7
After giving a baby a bath on the third day after its birth time ????3.5
Owing to adopt the anti wrinkling agent of low formaldehyde, use and bake technology, reduced energy resource consumption and sewage emissions, improved productivity ratio.Owing to adopted above-mentioned technical solution, solved the contradiction between cotton fabric crease-shedding performance and fabric strength, the ABRASION RESISTANCE fully, make the feel, gas permeability, hygroscopicity of COTTON FABRIC continue to keep the characteristic of COTTON FABRIC, wrinkle resistance greatly improves, and formaldehyde is residual to be reduced greatly.
Above embodiment is only for the usefulness that the present invention is described, but not limitation of the present invention, person skilled in the relevant technique, under the situation that does not break away from the spirit and scope of the present invention, can also make various conversion or modification, therefore all technical schemes that are equal to also should belong to category of the present invention, should be limited by each claim.

Claims (9)

1, a kind of non-ironing post-finishing technique of COTTON FABRIC, comprise that lining prepares, pads that resin, tentering are dried, baked, preshrunk, clot step, wherein lining prepare to comprise that grey cloth sews up, singes, destarch, alkali mercerized, dyeing, stentering forming and liquid ammonia finishing step, it is characterized in that, also comprise and pad behind the resin and tentering oven dry ventilative step before.
2, the non-ironing post-finishing technique of COTTON FABRIC according to claim 1, it is characterized in that, the described resin steps of padding comprises and pads resin steps twice, the prescription that pads the resin of resin steps for this twice is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, dimethyl urea glyoxal 60-120g/L, dicyandiamide 1-5g/L, catalyst 5-50g/L, softener 5-100g/L, wetting agent 0.1-5g/L, all the other are water in every liter of volume, and the ventilative time is controlled at 30-80 second in the ventilative step.
3, the non-ironing post-finishing technique of COTTON FABRIC according to claim 1, it is characterized in that, the described prescription that pads the resin of resin steps for twice is: modification 2D resin is dihydroxymethyl dihydroxy ethylene base urea 60-120g/L, dimethyl urea glyoxal 60-120g/L, dicyandiamide 2g/L, catalyst 40g/L, polyethylene softener 20g/L, silicone softening agent 30g/L, non-ionic wetting agent 1g/L, all the other are water in every liter of volume, and the ventilative time is controlled at 30-80 second in the ventilative step.
4, according to the non-ironing post-finishing technique of the described COTTON FABRIC of each claim of claim 1-3, it is characterized in that, it is described that to pad the pick-up that pads resin in the resin steps for the first time for twice be 75-80%, the speed of a motor vehicle be 30-60 rice/minute, the pick-up that pads for the second time resin is 68-70%, the speed of a motor vehicle be 30-60 rice/minute.
5, the non-ironing post-finishing technique of COTTON FABRIC according to claim 4, it is characterized in that, during preparing, described lining carries out liquefied ammonia open washing step after the liquid ammonia finishing step, this step is open washing in four times five the ten lattice flat wash troughs on every lattice flat wash trough deflector roll is, 80-90 ℃ of the liquefied ammonia temperature control of 1-6 lattice flat wash trough, the 7th lattice add acetic acid, pH value is controlled at 3-4 in this groove, temperature is controlled at 50-60 ℃, the 8th lattice temperature is controlled at 80-90 ℃, the 9th and 10 lattice temperature are controlled at 30-40 ℃, and cropping cloth cover pH value is controlled at 6-7, speed of a motor vehicle 30-60 rice/minute.
6, the non-ironing post-finishing technique of COTTON FABRIC according to claim 5, it is characterized in that, described tentering baking step is for carrying out in eight joint drying rooms, 80 ℃ of preceding four joint drying room temperature, 90 ℃ of five-six joint drying room temperature, 100 ℃ of temperature oven dry of seven-eight joint drying rooms, cropping cloth surface temperature is controlled at 30 ℃ ± 5 ℃, cloth surface humidity 6-8%, the speed of a motor vehicle be 30-60 rice/minute.
7, the non-ironing post-finishing technique of COTTON FABRIC according to claim 6 is characterized in that, the described step condition that bakes is 160 ℃ of temperature, 1 minute 45 seconds-3 minutes time.
8, the non-ironing post-finishing technique of COTTON FABRIC according to claim 7 is characterized in that, in the described stentering forming step speed of a motor vehicle 30-65 rice/minute, 150 ℃ of temperature.
9, the non-ironing post-finishing technique of COTTON FABRIC according to claim 2 is characterized in that, described catalyst is the Catalyst531 of commercially available Ou Nuofa company or the plain N in Kangding of BASF AG.
CNB2007100430902A 2007-06-29 2007-06-29 The non-ironing post-finishing technique of COTTON FABRIC Expired - Fee Related CN100549271C (en)