CN101050329A - Coating material for high anticorrosive pack, and preparation method - Google Patents
Coating material for high anticorrosive pack, and preparation method Download PDFInfo
- Publication number
- CN101050329A CN101050329A CN 200710106977 CN200710106977A CN101050329A CN 101050329 A CN101050329 A CN 101050329A CN 200710106977 CN200710106977 CN 200710106977 CN 200710106977 A CN200710106977 A CN 200710106977A CN 101050329 A CN101050329 A CN 101050329A
- Authority
- CN
- China
- Prior art keywords
- resin
- agent
- antirust
- coating
- pack
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention discloses a high-strength antirust packaging paint, which is composed of: ethylene resin, epoxy resin, polyurethane alkyd resin, rosin-modified resin, acrylate resin, cadmium stearate, lanoline, diphenyl amine, barium petroleum sulfonate, essence, antirust oil, plasticizer, heat stabilizer, antirust agent, diluting agent, adhesion promoter, leveling agent, UV absorbent, dispersant, defoamer and flame retardant. The packaging paint can be directly sprayed, soak-coated or brush-coated onto objects with any shape or appearance. A bright and smooth protective film is formed several minutes later. The protective film has high antirust performance, and can be stripped off for recycling.
Description
Technical field:
The present invention relates to a kind of composition of coating, relate in particular to a kind of rust proof paint.It is to be main film forming substance with multiple macromolecule copolymer resin, is equipped with the wrapping material of a kind of high anticorrosives of synthetic such as softening agent, stablizer, rust-preventive agent, fire retardant.
Background technology:
General in the market rush-resisting material does not possess strippability after the film forming, after mostly needing to apply, add housing material (as anti-tarnish paper, plastics bag etc.) and can not reclaim, and can not reuse.
Summary of the invention:
At above-mentioned situation, the objective of the invention is to: no matter with a kind of coating object shape how, outward appearance how, all can directly spray, soak or brush, behind the several minutes, the level and smooth protective membrane of one deck light can form.The rust-proof effect of its existing brute force is simultaneously also as housing material.With the standardized osculum of protective membrane, promptly available hand is peelled off, and the protective membrane that peels is put into molten Ji, still can use.
This product is with the comprehensive advantage of its " effect is strong, multi-functional, use factory ", is this coating that also all do not possess simultaneously of traditional coating product in the market.
The present invention is achieved in that what coating was made up of following component weight ratio: ethenoid resin 40-60g, Resins, epoxy 5-30g, Polyurethane Synolac 20-50g, modified rosin resin 30-70g, acrylic resin 10-40g, stearic acid is every 2-10g, lanolin 30-100g, pentanoic 2-5g, barium mahogany sulfonate 20-60g, thinner 600-800g, softening agent 4-20g, flow agent 5-30g, slushing oil 30-60g, dispersion agent 5-20g, fire retardant 5-20g, sticking power promotor 4-18g, defoamer 4-20g, ultraviolet absorbers 4-20g, thermo-stabilizer 10-30g, essence 5-20g.A kind of preparation method of powerful rust package coating: above-mentioned materials is blended in the container by weight proportion dissolves, stirring at normal temperature with the filtration of 360 orders, is poured in the container of differing capacities after 30 minutes at last, packs then.
The invention has the advantages that:
1, the main base-material of this product is a high molecular polymer, itself has good chemical resistance, weathering resistance and strippability, and mate mutually with multiple tree film, make every physicochemical property of rete reach the ideal effect.
2, this product can be infiltrated between each electrode of metallic surface, form high insulation resistance, effectively intercept the decay corrosion current and flow, bonding reaction makes the metallic surface not have the lowest point and the long-pending point of water, simultaneously this product is miscible rust-preventive agent efficiently, makes that the corrosive internal cause is greatly contained.The densification of this product rete molecular structure, force of cohesion is big, and therefore strong adhesion effectively intercepts the infiltration that particle is expected in moisture in the outside atmosphere, oxygen and corrosion, to reach the purpose that efficiently prevents corrosion.
3, this product strong absorption ultraviolet optionally, and convert thereof into harmless heat energy or other low-energy radiation, consume or release energy, the absorption of carrying out energy and the conversion that so go round and begin again, thereby make ultraviolet energy no longer endanger the molecular linkage of filmogen, reach splendid weathering resistance.
4, this product rete has suitable thickness (one deck dip-coating can reach 45 μ) snappiness good, the unit elongation height, and impact resistance is strong, and level and smooth light has good anti-efflorescence, protects light, tint retention.Three anti-effect is indoor reaches 10 years,, outdoor more than 5 years.No matter body form how, outward appearance how, all can directly spray.Soak or brush, behind the several minutes, the level and smooth protective membrane of one deck light can form, and it promptly can have the high anticorrosive effect, also can make housing material, and this protective membrane has strippability, and the protective membrane that peels is put into solvent, and is still reusable.
5, be main film forming substance with multiple macromolecule copolymer resin.Being equipped with the antirust and outer packaging of synthetic collection such as plasticising material stuff, stablizer, rust-preventive agent, fire retardant is the coating of one.It has strippability,
6, main base-material is a high molecular polymer, and with various kinds of resin phase interworking coupling, the characteristics of various resins is brought into play, makes it have good chemical resistance, weathering resistance and strippability.Because main base-material is a vinyl resin, other is acrylic resin, Resins, epoxy, natural rosin modified resin, resol.
7, significantly improve the various characteristics of coating, because main auxiliary agent is: softening agent, froth breaking Ji, flow agent, dispersion agent, sticking power promotor, ultraviolet absorption agent etc.
8, can dissolve and dispersion paints in filmogen, form liquid coating.Because primary solvent is ester class, ketone and high boiling point aromatic hydrocarbons mixed solvent.
Embodiment:
Above-mentioned three embodiment are put in mixed dissolution in the container with material earlier, and stirring at normal temperature is after 30 minutes, and finally sealed becomes product in the container of differing capacities with irritating after the filtration of 360 orders again.
Claims (2)
1, a kind of coating material for high anticorrosive pack is characterized in that: this coating is made up of following component weight ratio:
Ethenoid resin 40-60g, Resins, epoxy 5-30g, Polyurethane Synolac 20-50g, modified rosin resin 30-70g, acrylic resin 10-40g, stearic acid be every 2-10g, lanolin 30-100g, pentanoic 2-5g, barium mahogany sulfonate 20-60g, thinner 600-800g, softening agent 4-20g, flow agent 5-30g, slushing oil 30-60g, dispersion agent 5-20g, fire retardant 5-20g, sticking power promotor 4-18g, defoamer 4-20g, ultraviolet absorbers 4-20g, thermo-stabilizer 10-30g, essence 5-20g.
2, a kind of preparation method of powerful rust package coating is characterized in that: above-mentioned materials is blended in the container by weight proportion dissolves, stirring at normal temperature was filtered with 360 orders after 30 minutes, was poured at last in the container of differing capacities, packed then.