CN101045545A - 用蛋壳生产轻质碳酸钙的技术 - Google Patents
用蛋壳生产轻质碳酸钙的技术 Download PDFInfo
- Publication number
- CN101045545A CN101045545A CN 200710027669 CN200710027669A CN101045545A CN 101045545 A CN101045545 A CN 101045545A CN 200710027669 CN200710027669 CN 200710027669 CN 200710027669 A CN200710027669 A CN 200710027669A CN 101045545 A CN101045545 A CN 101045545A
- Authority
- CN
- China
- Prior art keywords
- eggshell
- kiln
- calcium carbonate
- light calcium
- technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用蛋壳生产轻质碳酸钙的技术，以蛋壳为原料，将蛋壳在煅烧炉内进行煅烧，生成CO2和CaO，煅烧温度控制在800～1400℃的温度范围内，然后将CaO与水反应生成Ca(OH)2，再将Ca(OH)2与煅烧工段产生的CO2气体反应生成轻质碳酸钙。本发明选用各种蛋壳为原料生产轻质碳酸钙，由于用蛋壳做原料，杂质含量少，省去了杂质分离工序，同时对蛋壳资源进行再生和综合利用，能有效地保护环境。
Description
【技术领域】
本发明涉及一种用蛋壳为原料生产轻质碳酸钙，属于轻质碳酸钙的生产方法。
【背景技术】
轻质碳酸钙的传统生产方法是用石灰石为原料，将石灰石与煤混在一起或分层装入竖式煅烧窑中锻烧，将所生成的产物经水化和碳化作用，最后制得轻质碳酸钙。这种制造方法采用天然矿石做原料，而天然矿物原料往往含杂质较多，矿石与煤之间的反应也往往不够完全，需要一个分离除杂工序，以除去原矿中的杂质、未反应的矿石和碳素。
在日常生活中，人们扔弃的大量蛋壳给环境带来了严重污染，而蛋壳是一种可再生的资源，如果不对蛋壳进行资源化深加工，也造成了资源的浪费。
【发明内容】
为了克服现有技术的上述缺点，本发明提供一种能对蛋壳资源进行再生和综合利用、并能有效地保护环境的用蛋壳生产轻质碳酸钙技术。
本发明解决其技术问题所采用的技术方案是：一种用蛋壳生产轻质碳酸钙的技术，以蛋壳为原料，将蛋壳在煅烧炉内进行煅烧，生成CO2和CaO，煅烧温度控制在800～1400℃的温度范围内，然后将CaO与水反应生成Ca(OH)2，再将Ca(OH)2与煅烧工段产生的CO2气体反应生成轻质碳酸钙。
所述煅烧炉为竖式煅烧窑或燃气窑炉或电炉。
煅烧所用燃料采用煤或焦炭或气体燃料或采用电作为热源。
采用竖式煅烧窑进行煅烧，采用煤或者焦炭为燃料，将蛋壳碎片与燃料混合或者分层堆积在竖式煅烧窑中，竖式煅烧窑中燃料与蛋壳碎片的重量配比为1∶4～1∶5。
采用燃气窑炉或电炉时，将蛋壳碎片盛放在托盘中，然后将盛有蛋壳碎片的托盘置于窑车的各层隔板上，再将窑车置于窑炉内煅烧。
本发明的有益效果是：选用各种蛋壳为原料生产轻质碳酸钙，由于用蛋壳做原料，杂质含量少，省去了杂质分离工序，同时对蛋壳资源进行再生和综合利用，能有效地保护环境。
【具体实施方式】
下面结合实施例对本发明进一步说明。
一种用蛋壳生产轻质碳酸钙的技术，采用各种蛋壳为原料，用机械或者人工将蛋壳粉碎成碎片，燃料采用煤或焦炭或液化气或天然气或煤气或煤气发生气，然后将蛋壳碎片在洗涤装置中清洗掉粘附在蛋壳上的蛋清残液和泥土等杂质，再将清洗干净的蛋壳碎片晾晒以去除附着在蛋壳表面上的水分，或者用热风烘干、蒸汽烘干、电热烘干、微波干燥等方法干燥蛋壳碎片。
采用竖式煅烧窑进行煅烧时，将蛋壳碎片置于竖式煅烧窑中锻烧，蛋壳碎片在800～1400℃的温度范围内进行煅烧，蛋壳碎片发生分解生成CaO和CO2，在煅烧窑中煤或者焦炭与蛋壳碎片的重量配比为1∶4～1∶5，蛋壳碎片与煤或者焦炭混合或者分层堆积，在800～1400℃的温度下煅烧。采用燃气窑炉进行煅烧时，燃气窑炉窑的四壁用耐火材料砌成，窑车的架子上有隔板，将盛有蛋壳碎片的托盘置于窑车的各层隔板上，气体燃料在窑炉中均匀燃烧。采用电炉进行煅烧时，电窑的四壁用耐火材料砌成，窑车的架子上有隔板，将盛有蛋壳碎片的托盘置于窑车的各层隔板上，蛋壳碎片在800～1400℃的温度范围内煅烧。
Claims (5)
1、一种用蛋壳生产轻质碳酸钙的技术，其特征是：以蛋壳为原料，将蛋壳在煅烧炉内进行煅烧，生成CO2和CaO，煅烧温度控制在800～1400℃的温度范围内，然后将CaO与水反应生成Ca(OH)2，再将Ca(OH)2与煅烧工段产生的CO2气体反应生成轻质碳酸钙。
2、如权利要求1所述的用蛋壳生产轻质碳酸钙的技术，其特征是：所述煅烧炉为竖式煅烧窑或燃气窑炉或电炉。
3、如权利要求1所述的用蛋壳生产轻质碳酸钙的技术，其特征是：煅烧所用燃料采用煤或焦炭或气体燃料或采用电作为热源。
4、如权利要求2所述的用蛋壳生产轻质碳酸钙的技术，其特征是：采用竖式煅烧窑进行煅烧，采用煤或者焦炭为燃料，将蛋壳碎片与燃料混合或者分层堆积在竖式煅烧窑中，竖式煅烧窑中燃料与蛋壳碎片的重量配比为1∶4～1∶5。
5、如权利要求2所述的用蛋壳生产轻质碳酸钙的技术，其特征是：采用燃气窑炉或电炉时，将蛋壳碎片盛放在托盘中，然后将盛有蛋壳碎片的托盘置于窑车的各层隔板上，再将窑车置于窑炉内煅烧。