CN101007712A - Construction method of constructing endured wall or architecture using mud - Google Patents

Construction method of constructing endured wall or architecture using mud Download PDF

Info

Publication number
CN101007712A
CN101007712A CN 200610004330 CN200610004330A CN101007712A CN 101007712 A CN101007712 A CN 101007712A CN 200610004330 CN200610004330 CN 200610004330 CN 200610004330 A CN200610004330 A CN 200610004330A CN 101007712 A CN101007712 A CN 101007712A
Authority
CN
China
Prior art keywords
building
earth
constructional
construction
mud
Prior art date
Application number
CN 200610004330
Other languages
Chinese (zh)
Inventor
河元台
金元宪
Original Assignee
河元台
金元宪
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 河元台, 金元宪 filed Critical 河元台
Priority to CN 200610004330 priority Critical patent/CN101007712A/en
Publication of CN101007712A publication Critical patent/CN101007712A/en

Abstract

The invention discloses a constructing method to build wall of good permanence and building with mud, wherein the key point of technology is using nature mud with H.K.-1.000 inorganic ionic hardener. The composite material maintains solidifying force, which possesses certain elasticity to be reserved for a long time.

Description

Utilize earth to construct the constructional method of strong wall of persistence or building

Technical field

The invention belongs to workers and peasants' technical field of buildings, specifically a kind of constructional method of utilizing earth to construct strong wall of persistence or building.

Background technology

As everyone knows, the earth wall in the past or the emphasis point of construction techniques are to utilize earth, sandy soil, lime (CaCo 3) wait and shorten argillous pore layer and tomography, utilize lime and argillous hydration reaction to make clay solidifying.When adopting in the past constructional method to construct the earth wall for this reason according to temperature variation, the alcohol series that the absorption of moisture and earth are entrained, coal series produces reaction, and very fast generation weathering is so the part of earth wall or building is easy to sustain damage.

Summary of the invention

The purpose of this invention is to provide and a kind ofly construct the constructional method of strong wall of persistence or building as the earth that utilizes of additive with H.K-1.000 mineral ion cured body and earth intensity reinforcing agent.

The object of the present invention is achieved like this: the earth wall construction method that utilizes the soil application H.K-1.000 mineral ion solidifying agent of nature.

The present invention strengthens for the tension force that makes wall or building and maximizes, and then uses the constructional method that strengthens tension force and wall is maximized in the lump with reinforcing bar.

The present invention also in order to prevent wall or building suction, adopts the inorganic pressing mold agent of DEED-H to carry out the technology of pressing mold WATER REPELLENT on the outside surface of wall or building.

The present invention adds in mixing material can keep curing power after H.K-1.000 mineral ion cured body solidifies mixing material for a long time, also has certain elasticity when keeping very high intensity when constructing the earth wall, but so mixing material structures prolonged preservation.The pouring concrete construction method that constructional method of the present invention is used, conveniently advances equipment and technology supervision of construction etc. at the shortening time.The present invention has prevented weathering, makes the surface of wall or building not have nature and falls the fall phenomenon of ash of sand, has protected environment.

Description of drawings

Fig. 1 is construction process figure of the present invention

Embodiment

By shown in Figure 1, after used earth physical properties being confirmed experiment, pass through mechanical means, personnel placement, material is prepared, metering earth, cement, inorganic solidified body of H.K-1.000 and material mixing are than confirming project scale, utilize electron microscope method and simple hydro-tester to confirm the combined amount and the construction of demonstrating, mix earth according to the material mixing ratio, cement, H.K-1.000, materials such as soft rock get mixing material, according to the working-yard needs mould is set, for the tension force that makes wall or building strengthens and maximization, then in mould, be provided with reinforcing bar, in this mould, drop into mixing material, two seasons of summer in winter carry out removing mould after the health according to temperature contrast, adopt the inorganic pressing mold agent of DEED-H to carry out the technology of pressing mold WATER REPELLENT on the outside surface of wall or building.

The inorganic solidified body of above-mentioned H.K-1.000 is composed as follows:

The reinforcing bar requirement is according to the length of wall, width, and differences such as height are adjusted.Below with 1m 3The cubes structures be that the illustration model calculates the reinforcing bar requirement:

1m 3The surperficial parallel cut 1m of cubes structures 2Square, the long reinforcing bar of 6 1m can be set, that is: 1m * 6=6m on this face

1m 3Cubes structures muscle requirement (except the top layer) then is: 6m * 3=18m

Concrete construction process: at normal temperatures earth 80~90%, cement 10~20%, H.K-1.000 (below 1%) puts in the concrete mixer moisture (water ratio) is adjusted into 18~22%, and the shape of constructing wall with certain mould drops into.Simultaneously the material that H.K-1.000 is constructed with 1% ratio takes out mould after through 3~4 days conditioned time.

Various projects and experimental value after the health during through 27 days

Experimental project The result Laboratory strength (kgf/cm 3) ????79 Compressive strength (kgf/cm 3) ????230 Adhesion strength (kgf/cm 3) ????30 Specific absorption (%) ????7 Permeability rate (g) ????6 Tensile velocity of variation (%) ????1089

Can find out that from last note result structures can keep very strong compressive strength etc.The time of this health is generally, 4~5 days winters and cannot construct 1~2 day summer below-5 ℃.

Earth wall or building are made up of grogs, even if be cured, health also has the tendency that is easy to absorb moisture after the drying.

To this, the method for preventing is to use the inorganic press mold agent of DEED-H that the surface portion of wall is carried out press mold after the health.Realize purpose of the present invention in sum.

Claims (3)

1, a kind of constructional method of utilizing earth to construct strong wall of persistence or building is characterized in that: the earth wall construction method that utilizes the soil application H.K.-1.000 mineral ion solidifying agent of nature.
2, the constructional method of utilizing earth to construct strong wall of persistence or building according to claim 1 is characterized in that: use the constructional method that strengthens tension force and wall is maximized in the lump with reinforcing bar.
3, the constructional method of utilizing earth to construct strong wall of persistence or building according to claim 1 is characterized in that: adopt the inorganic pressing mold agent of DEED-H to carry out the technology of pressing mold WATER REPELLENT on the outside surface of wall or building.
CN 200610004330 2006-01-24 2006-01-24 Construction method of constructing endured wall or architecture using mud CN101007712A (en)