CN100999334A - Manufacturing method of antimony trioxide parent particle - Google Patents
Manufacturing method of antimony trioxide parent particle Download PDFInfo
- Publication number
- CN100999334A CN100999334A CN 200710000830 CN200710000830A CN100999334A CN 100999334 A CN100999334 A CN 100999334A CN 200710000830 CN200710000830 CN 200710000830 CN 200710000830 A CN200710000830 A CN 200710000830A CN 100999334 A CN100999334 A CN 100999334A
- Authority
- CN
- China
- Prior art keywords
- antimony trioxide
- coupling agent
- master batch
- agent
- carrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Prescription | ABS/ % | Decabromodiphynly oxide/% | Antimonous oxide powder/% | Master batch/the % of antimonous oxide content 90% |
1 2 | 84 84 | 12 12 | 4 - | - 4 |
Performance | Operative norm | ABS04 | ABS07 |
Elongation at break/% tensile strength/MPa simply supported beam non-notch resistance to impact shock/kJm -2The socle girder breach is towards intensity/kJm -2Melt flow rate (MFR)/g10 min -1Plastics combustionproperty UL94 (3.0mm) plastics combustionproperty oxygen index method | GB/T1040-1992 GB/T1040-1992 GB/T1043-1993 GB/T1843-1996 GB/T3682-2000 GB/T2408-1996 GB/T2406-1993 | 21 42.0 59.3 8.0 1.86 V-0 26.7 | 24 41.8 61.2 8.6 1.91 V-0 27.6 |
Claims (3)