CN100558936C - 镁合金化成处理液 - Google Patents
镁合金化成处理液 Download PDFInfo
- Publication number
- CN100558936C CN100558936C CNB2007100195137A CN200710019513A CN100558936C CN 100558936 C CN100558936 C CN 100558936C CN B2007100195137 A CNB2007100195137 A CN B2007100195137A CN 200710019513 A CN200710019513 A CN 200710019513A CN 100558936 C CN100558936 C CN 100558936C
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- treatment liquid
- chemical synthesis
- synthesis treatment
- alloy chemical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种镁合金化成处理液，每升该镁合金化成处理液中包含以下物质溶于水：10-30g钼酸根化合物、2-10ml磷酸、0.1-5g钨酸根化合物以及0.1-5g偏钒酸根化合物。使用步骤如下：将表调后的镁合金在该镁合金化成处理液中浸泡45秒-5分钟，工作温度为35-45℃，取出后经二次纯水清洗以及一次烘烤，则该合金表面形成一层耐腐蚀以及低阻抗的防护膜。该配方对环境污染小，且不会对生产人员产生毒害，成本低廉。
Description
【技术领域】
本发明属于金属表面处理领域，具体涉及镁合金表面的磷化防护处理领域，由此在镁合金上产生具有极佳耐蚀性和防锈性的化学防护膜。
【背景技术】
镁合金因为比重低、强度足够且适于回收使用，所以被广泛地用于汽车和电器设备，但由于镁合金化学反应性高，在大气中其表面迅速形成一层氧化物，造成腐蚀，因此在使用前需要对该镁合金进行防护性处理，其中化成处理工序中通常采用铬酸盐或磷酸盐，以形成一层增强镁合金耐蚀性的保护膜：由于铬化物的使用会造成水源及土壤污染，不符合环保的要求，因此目前本领域大都采用磷酸盐体系来处理，但是，使用磷酸盐在镁合金表面所形成的保护膜的质量较差，增强镁合金耐腐性的能力有限，因此，镁合金的无铬且不降低保护膜质量的化成处理技术的研发已成为镁合金表面防护技术发展的一个重要方向和亟待解决的问题。
因此，实有必要提出一种镁合金化成处理液，既不减弱镁合金的化成处理效果又较少污染环境。
【发明内容】
因此，本发明的目的在于提供一种镁合金化成处理液，能在镁合金表面形成一层质量好的防护膜，且较少污染环境。
为达成上述目的，本发明的镁合金化成处理液，包含钼酸根离子、磷酸、钨酸根离子和偏钒酸根离子，且作为钼酸根离子源的水溶性化合物的浓度是10-30g/L，磷酸溶液的浓度是2-10ml/L，作为钨酸根离子源的水溶性化合物的浓度是0.1-5g/L以及作为偏钒酸根离子源的水溶性化合物的浓度是0.1-5g/L。
使用该化成处理液的步骤如下：
将表调后的镁合金在包含10-30g/L的钼酸盐、2-10ml/L的磷酸、0.1-5g/L的钨酸盐和0.1-5g/L的偏钒酸盐的溶液中浸泡45秒-5分钟，工作温度为35-45℃，取出后经二次纯水清洗以及一次烘烤，则该合金表面形成一层外观为灰白色的防护膜。
从成膜性能测试结果可知，经过处理后的镁合金经过中性盐雾实验8小时表面仍无明显腐蚀，且在该防护膜上量取距离≤5cm的两测试点，它们之间的阻抗＜2欧姆，完全符合镁合金的耐腐蚀以及低阻抗的要求。
另外，相较于现有技术，本发明的镁合金化成处理液不含六价铬，对环境污染小，且该化成处理液中的物质皆为无毒或低毒物质，在使用该配方进行大批量生产时，不会对生产人员产生毒害，且成本低廉；又，该化成处理液可以在中温条件下使用，能耗小。
【具体实施方式】
该镁合金化成处理液包含作为成膜主剂的钼酸根离子和磷酸，其中提供钼酸根离子的化合物浓度为10-30g/L，磷酸的浓度为2-10ml/L。
优选地，每升该镁合金化成处理液中包含：
钼酸根化合物 10-30g；
磷酸 2-10ml；
钨酸根化合物 0.1-5g；
偏钒酸根化合物 0.1-5g。
其中，该钼酸根化合物、钨酸根化合物以及偏钒酸根化合物皆溶于水(较佳为纯水)，且较优地，该钼酸根化合物、钨酸根化合物以及偏钒酸根化合物分别包含钠离子或铵离子。
钼酸根化合物、磷酸、钨酸根化合物以及偏钒酸根化合物的溶液浓度并不限于上述范围内，因为它取决于欲形成防护膜的厚度及浸泡时间。
优选地，该镁合金化成处理液pH值介于2至3.5之间，主要通过添加磷酸溶液对pH值进行控制。如果pH值低于2，镁合金的溶解作用过于活泼，以致损害其表面；如果pH值高于3.5，则无法为钼酸盐提供一个游离的酸环境。
使用该镁合金化成处理液的二较佳实施例如下：
实施例1：
将表调(合金经过脱脂、酸洗后，再使用PS-F01系表面调整剂进行处理，在合金磷化时能促进磷化膜晶核产生，从而缩短合金表面磷化膜的形成时间，使磷化膜薄而均匀、致密，提高合金的防锈性能，其中该表面调整剂的配制方法：每吨清水中加1-2千克表面调整剂，搅拌均匀后即可使用，且该表面调整剂溶液PH值为7.5-9)后的镁合金在包含10g/L钼酸盐、9ml/L磷酸、0.2g/L钨酸盐和5g/L偏钒酸盐的该镁合金化成处理液中浸泡45秒，工作温度35℃，取出后经一次纯水清洗以及一次烘烤，则该合金表面粘附一层外表为灰白色的防护膜。
实施例2：
将表调后的镁合金在包含30g/L钼酸盐、2ml/L磷酸、5g/L钨酸盐和0.1g/L偏钒酸盐的该镁合金化成处理液中浸泡5分钟，工作温度45℃，取出后经一次纯水清洗以及一次烘烤，则该合金表面粘附一层外表为灰白色的防护膜。
以上镁合金化成处理液的工作温度以及时间并不限于上述范围内，因为它取决于欲形成防护膜的厚度。
Claims (6)
1、一种镁合金化成处理液，其特征在于：每升该镁合金化成处理液中包含以下物质溶于水：
钼酸根化合物 10-30g；
磷酸 2-10ml；
钨酸根化合物 0.1-5g；
偏钒酸根化合物 0.1-5g。
2、如权利要求1所述的镁合金化成处理液，其特征在于：该钼酸根化合物、钨酸根化合物和偏钒酸根化合物还包含钠离子或铵离子。
3、如权利要求2所述的镁合金化成处理液，其特征在于：该镁合金化成处理液的pH值介于2与3.5之间。
4、如权利要求1所述的镁合金化成处理液，其特征在于：该镁合金化成处理液的工作时间为45秒-5分钟。
5、如权利要求1所述的镁合金化成处理液，其特征在于：该镁合金化成处理液的工作温度为35-45℃。
6、如权利要求1所述的镁合金化成处理液，其特征在于：所述水为纯水。