CN100554510C - 激光快速成形专用铁基粉料 - Google Patents

激光快速成形专用铁基粉料 Download PDF

Info

Publication number
CN100554510C
CN100554510C CN 200710113214 CN200710113214A CN100554510C CN 100554510 C CN100554510 C CN 100554510C CN 200710113214 CN200710113214 CN 200710113214 CN 200710113214 A CN200710113214 A CN 200710113214A CN 100554510 C CN100554510 C CN 100554510C
Authority
CN
China
Prior art keywords
iron
powder
special
fast forming
base powder
Prior art date
Application number
CN 200710113214
Other languages
English (en)
Other versions
CN101122018A (zh
Inventor
边秀房
付春霞
Original Assignee
山东大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 山东大学 filed Critical 山东大学
Priority to CN 200710113214 priority Critical patent/CN100554510C/zh
Publication of CN101122018A publication Critical patent/CN101122018A/zh
Application granted granted Critical
Publication of CN100554510C publication Critical patent/CN100554510C/zh

Abstract

本发明涉及一种激光快速成形专用铁基粉料,属于金属材料粉料领域。该铁基粉料化学成份为(质量百分比):Cr:15-25%;Ni:8-15%;Mo:1.5-2.5%;Si:1.2-1.8%;B:0.1-1.0%;MgO≤1%;CaF2≤2%;C、Nb、Co其重量百分比≤2%;CeO2、Y3O2、La2O3其中之一或组合≤1%;Fe:余量。各种金属粉末按成分配比入混料机中充分混合。将该粉料在无任何预热和缓冷前后处理的条件下在45#钢基体表面进行激光熔覆,得到表面光滑、平整、无裂纹、厚度达到10mm以上的激光熔覆层,其硬度在HRC28-30之间。利用本发明形成的熔覆层成形性良好。组织致密、成分均匀、无裂纹。

Description

激光快速成形专用铁基粉料
技术领域
本发明属于金属材料粉料领域,特别是涉及一种激光快速成形专用铁基粉料。 背景技术
快速成形技术是20世纪80年代末发展起来的先进制造技术,它是一种由计算机辅助 制图模型直接驱动的快速制造复杂形状实体的技术。由于它采用离散/堆积原理,因此理论 上快速成形可以制造任意复杂形状的实体。快速成形能显著縮短新产品开发时间、降低开 发费用。对于激光快速成形技术国内外研究者作了很多工作,取得了大量有价值的研究成 果,并得到一定规模的应用。然而利用金属粉料生产机械零部件的实际工程应用却有待于 开发和推广,主要原因是激光快速成形过程中工件常会产生裂纹、气孔等缺陷。
目前,国内外用于激光快速成形的粉料材料主要沿用传统的热喷涂系列合金粉料,常 用激光熔覆材料主要包括镍基合金、铁基合金、钴基自熔合金,以及上述合金与碳化物(WC、 TiC、 SiC等)颗粒组成的金属陶瓷复合粉料,这类金属粉料成形后普遍存在合金层之间结 合强度低,耐磨性差以及残余应力大,出现气孔和裂纹等问题。其中,最为棘手的问题是 工件中存在的裂纹与气孔。
激光快速成形专用的金属粉料在国内外尚未有所报道,而传统的热喷涂系列合金已不 能满足激光快速成形技术快速发展的需要,因此必须开发出激光快速成形专用的金属粉料, 解决激光快速成形过程中产生的裂纹问题。
发明内容
针对现有技术的不足,本发明提供一种激光快速成形专用铁基粉料,解决激光快速成 形过程中产生的裂纹问题。
本发明的激光快速成形专用铁基粉料,是在铁粉中,添加以下元素中的至少一种进行 强化而得到的:C、 Cr、 Mo、 Ni、 Nb或Co。
上述的激光快速成形专用铁基粉料,其特点在于,还添加有B、 Si和微量稀土氧化物。 所述的微量稀土氧化物选自下列之一或组合:Ce02、 丫302或La203,添加的稀土氧化物总量 按重量百分比《1%粉料总重量。
通过添加适量B、 Si和微量稀土氧化物并调节各元素比例,铁基合金在凝固后形成以 奥氏体为基体,其上分布少量的碳化物的组织,使合金在具有良好的韧性,降低合金熔点 的同时还使凝固层具有一定硬度和强度的要求。从根本上保证并提高了合金粉料在激光快 速成形过程中的抗裂性、成形性、工艺稳定性和成分均匀性。
优选的,上述激光快速成形专用铁基粉料中,C、 Nb、 Co总重量百分比《2%粉料总重
旦 里o本发明激光快速成形专用铁基粉料,其特征在于,所述材料中还含有Mg0,重量百分 比《1%粉料总重量。
本发明激光快速成形专用铁基粉料,其特征在于,所述材料中还含有CaF2,重量百分 比《2%粉料总重量。
本发明激光快速成形专用铁基粉料,优选的组成按重量百分比如下: Cr: 15-25%; Ni: 8-15%; Mo: 1.5-2.5%; Si: 1.2-1.8%; B: 0.1-1.0%; C、 Nb和Co 总量《2%; MgO《l%; CaF2《2%; Ce02、 Y302、 1^203其中之一或组合《1%; Fe:余量。
本发明激光快速成形专用铁基粉料硬度在HRC28-30之间。
本发明激光快速成形专用铁基粉料的制备方法,将上述组分原料按成分配比,放入混 料机中充分混合即可,混合时间2-5小时。
本发明激光快速成形专用铁基粉料主要应用在大型零件的尺寸修复,还可应用于汽车、 轮椅、摩托车、客车、叉车、卡车、电脑类产品、照相机、摄像机、医疗设备等行业,特
别在模具行业中有着广泛的应用。
本发明的优点在于:在利用C、 Cr、 Mo、 Ni、 Nb、 Co等元素强化的铁基合金基础上, 通过调节各元素比例及添加适量的B、 Si和微量稀土氧化物使合金在凝固后形成以奥氏体 为基体,其上分布少量的碳化物的组织,使合金在具有良好的韧性,降低合金熔点的同时 还使凝固层具有一定硬度和强度的要求,增加了耐磨性能。本发明的激光快速成形专用铁 基金属粉料,其成分配比合理。该金属粉料有良好的润湿性及自熔性,塑、韧性大,能够 阻止裂纹的产生,从根本上保证并提高了合金粉料的激光快速成形中的抗裂性、成形性、 工艺稳定性和成分均匀性。
具体实施方式
一种激光快速成形专用铁基粉料,在铁基上至少利用以下元素中的一种成分强化而得: C、 Cr、 Mo、 Ni、 Nb、 Co;并在该铁基合金基础上添加B、 Si和微量稀土氧化物组成,所述 材料中添加的微量的稀土氧化物是Ce02、 Y302、 LaA其中的一种或任意一种组,合,其总量 按重量百分比《粉料总重量的1%;所述材料中还有按重量百分比《"/。的MgO和按重量百分 比《2W的CaF2。具体实施例如下:
实施例1
一种激光快速成形专用铁基粉料,组成按重量百分比为:Cr: 25%; Mo: 1.5%; Ni: 10%;
Si: 1.5%; B: 0.1%; Y203: 0.5%; C:0.5%、 Nb: 0.5%、 Co: 0.5%: CaF2: 1%; MgO: 0.4%; Fe:余量。
将以上各种金属粉末按成分配比配制,放入混料机中充分混合,混合时间2-5小时。 将所得专用铁基粉料应用于某碱业公司阴、阳转子轴颈修复:转子重量约为WOOKg' 工作温度15(TC左右,工作介质是碱性蒸汽'轴颈部分磨损严重。用机加工去处表层后'用研制的铁基合金粉进行修复,采用4000W横流高压连续CO2激光器,应用所述材料进行 激光熔覆,操作的工艺参数为:功率:2000W;光斑直径3ram;扫描速度:60mm/min;焦距: 320mm。再经机加工复形。经无损探伤检测,发现没有空洞、夹杂、裂纹等缺陷,轴颈尺寸 合格,整体无变形,硬度均匀,性能稳定。厂家回装后运转稳定,使用正常。 实施例2
一种激光快速成形专用铁基粉料,组成按重量百分比为:
Cr: 18%; Mo: 1.2%; Ni: 8%; Si: 1.2%; B: 0.3%; Ce02: 0.3%; Y203: 0.3%; C:O. 7%、 Nb: 0,8%、 Co: 0.5%; CaF2: 2%; MgO: 0.1%; Fe:余量。
各种金属粉末按成分配比配制,放入混料机中充分混合,混合时间2-5小时。
采用5000W横流高压连续C02激光器,应用将所得专用铁基粉料在无任何预热和缓冷 处理的45tt钢基体表面进行单道多层的熔覆试验,最后得到长140mm,高25mm的熔覆层。 工艺参数为:功率:1300W;焦距375mra;光斑直径3mm;扫描速度:300腿/min。经渗透法 检测,没有发现裂纹,经组织观察没有发现空洞、夹杂等缺陷,硬度均匀,服C28-30。
实施例3
一种激光快速成形专用铁基粉料,组成按重量百分比为:
Cr: 20%; Mo: 1.2%; Ni: 8%; Si: 1.8%; B: 0.5%; Y203: 0.5%; C:0.5%、 Nb: 0.4%、 Co: 0.3%; CaF2: 0.5%; MgO: 0.2%; Fe:余量。各种金属粉末按成分配比配制,放入混料 机中充分混合,混合时间2-5小时。
采用德国Rof in公司制造的ROFIN TR050型快轴流C02激光器,应用所述粉料在无预 热和缓冷的条件下40tt钢基体表面进行成形实验,最后得到壁厚2mm,高40咖,外圆直径 30mm的圆筒。工艺参数为:750W;焦距460mm;光斑直径2ram;扫描速度:350mra/min。送 粉速度4deg/s,成形层厚0.4mm/s经渗透法检测,没有发现裂纹,经组织观察没有发现空 洞、夹杂等缺陷,硬度均匀。

Claims (1)

1、一种激光快速成形专用铁基粉料,其特征在于是在铁粉中添加以下元素进行强化而得到的:C、Cr、Mo、Ni、Nb、Co、B和Si,还添加有微量稀土氧化物、MgO和CaF2,所述的微量稀土氧化物选自下列之一或组合:CeO2、Y3O2或La2O3,所述铁基粉料组成重量百分比如下: Cr:15-25%;Ni:8-15%;Mo:1.5-2.5%;Si:1.2-1.8%;B:0.1-1.0%;C、Nb和Co总量≤2%;微量稀土氧化物总量≤1%,MgO≤1%,CaF2≤2%,Fe:余量。
CN 200710113214 2007-09-29 2007-09-29 激光快速成形专用铁基粉料 CN100554510C (zh)