CN100523090C - 用于ogfc的复合改性沥青及其制备方法 - Google Patents

用于ogfc的复合改性沥青及其制备方法 Download PDF

Info

Publication number
CN100523090C
CN100523090C CNB2005101123156A CN200510112315A CN100523090C CN 100523090 C CN100523090 C CN 100523090C CN B2005101123156 A CNB2005101123156 A CN B2005101123156A CN 200510112315 A CN200510112315 A CN 200510112315A CN 100523090 C CN100523090 C CN 100523090C
Authority
CN
China
Prior art keywords
modified asphalt
composite modified
asphalt
0gfc
petroleum resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005101123156A
Other languages
English (en)
Other versions
CN1990568A (zh
Inventor
黄卫东
孙立军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongji University
Original Assignee
Tongji University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongji University filed Critical Tongji University
Priority to CNB2005101123156A priority Critical patent/CN100523090C/zh
Publication of CN1990568A publication Critical patent/CN1990568A/zh
Application granted granted Critical
Publication of CN100523090C publication Critical patent/CN100523090C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种透水性路面用高粘度改性沥青。本发明所述的用于OGFC的高粘度复合改性沥青，其各组分的重量分数如下：沥青100、苯乙烯-乙烯/丁烯-苯乙烯嵌段共聚物3～12、石油树脂5～30和聚乙烯蜡1～6。本发明在沥青中掺入苯乙烯-乙烯/丁烯-苯乙烯嵌段共聚物和石油树脂及聚乙烯蜡，不仅粘度很高，而且分散性和稳定性也很好，PG分级达到82-28，属于高性能的改性沥青，可用于一般的渗水性路面，也可以用于桥面铺装和应力吸收层等特殊场合。

Description

用于OGFC的复合改性沥青及其制备方法
技术领域
本发明涉及一种用于OGFC的高粘度改性沥青。
背景技术
高粘度沥青是指60℃粘度大于2万Pa.s的沥青，适合于交通路面和排水路面的铺摊。高粘度沥青目前主要通过在石油沥青中添加聚合物改性制得。添加聚合物对石油沥青进行改性，可明显改善沥青的高、低温性能，提供沥青路面的高温抗车辙、低温抗开裂能力。但是，由于聚合物与沥青之间存在分子量、粘度等差异，使聚合物改性沥青分散困难；同时，由于大多数聚合物与沥青能完全相容，并且存在密度差，导致改性沥青体系在高温下存储稳定性不好，容易分层，影响沥青质量及正常施工。
为解决高粘度沥青分散困难的问题，中国专利cn1089349c报道了采用先将聚合物与沥青及其它配合剂共混，制备成易在沥青中分散的母料，再将此母料分散在沥青中，制备改性沥青。
为解决改性沥青的高温存储稳定性问题，美国专利us3,634,293提出了用聚合物改性沥青时，加入过氧化物，硫磺等交联剂的方法；国际专利wo45，488提出了将SB两嵌段与SBS三嵌段共聚物并用，加入少量的交联剂的方法；中国专利cn1386790A公开了通过先将聚合物与碳黑共混再改性沥青的方法。
但分散性和稳定性都很好的透水性路面用改性沥青还未见报道。
发明内容
本发明的目的是提供一种新的高粘度改性沥青，这种沥青不仅容易分散，而且还有较好的高温存储稳定性。
为达到上述目的，本发明采取的技术方案是：
一种用于OGFC的高粘度复合改性沥青，其含有如下组分：沥青100、苯乙烯-乙烯/丁烯-苯乙烯嵌段共聚物(SEBS)3～12、石油树脂5～30、聚乙烯蜡1～6(以上均为重量份数)。
所述的SEBS是苯乙烯(S)-乙烯(E)/丁烯(B)-苯乙烯(S)构成的嵌段共聚物，它将聚苯乙烯的热塑性特征和乙烯-丁烯共聚物的弹性体特征结合在同一聚合物中，其分子构型为A-B-A型的三嵌段共聚物。由于SEBS中弹性体嵌段已完全氢化，因此SEBS具有优良的耐老化性并能在高温下进行加工。其分子量在3～35万时效果较好，优选为10～25万。
所述的石油树脂优选为软化点在70～150℃的石油树脂，最优选为90～115℃的石油树脂。
所述的聚乙烯蜡的平均分子量为500～15000，优选为3000～6000。软化点为90～160℃，优选为120～150℃。
本发明所述的用于OGFC的高粘度复合改性沥青的制备方法是：先将沥青加热到流动态，然后依次加入苯乙烯-乙烯/丁烯-苯乙烯嵌段共聚物、石油树脂和聚乙烯蜡，强力搅拌即可。
本发明的有益效果：本发明在沥青中掺入聚乙烯蜡和石油树脂，不仅粘度很高，而且分散性和稳定性也很好，PG分级达到82—28，属于高性能的改性沥青，可用于一般的渗水性路面，也可以用于桥面铺装和应力吸收层等特殊场合。
具体实施方式
取针入度为300的基础沥青100公斤，加热到180℃，依次加入苯乙烯-乙烯/丁烯-苯乙烯嵌段共聚物(SEBS)(平均分子量为16万)8公斤、石油树脂(软化点为105℃)8公斤和聚乙烯蜡2公斤，采用强力搅拌机以200转/分的搅拌速度进行搅拌6小时，制备出改性沥青，结果见表一。
表一
 
改性沥青的指标
针入度25℃，dmm 70
延度5℃，5cm/min(cm) 26
软化点T<sub>R&amp;B</sub>(℃) 90
运动粘度135℃(Pa.s) 2.7
弹性恢复25℃(％) 92
RTFOT后延度5℃，5cm/min(cm) 19
粘度60℃(10000Pa.s) 4.1
PG分级 82—28
从表中可以看出，制备出高性能的改性沥青，60度粘度大于2万Pa.s，PG分级达到82～28，高性能的改性沥青可以用于OGFC，此外也可以用于桥面铺装、应力吸收层等特殊场合。

Claims (8)

1、一种用于0GFC的复合改性沥青，其各组分的重量份数如下：沥青100、SEBS3～12、石油树脂5～40、聚乙烯蜡1～6。
2、如权利要求1所述的用于0GFC的复合改性沥青，其特征在于：SEBS的分子量在3～35万之间。
3、如权利要求2所述的用于0GFC的复合改性沥青，其特征在于：SEBS的分子量在10～25万之间。
4、如权利要求1所述的用于0GFC的复合改性沥青，其特征在于：石油树脂的软化点为70～150℃。
5、如权利要求4所述的用于0GFC的复合改性沥青，其特征在于：石油树脂的软化点为90～115℃。
6、如权利要求1所述的用于0GFC的复合改性沥青，其特征在于：聚乙烯蜡的平均分子量为500～15000，软化点为90～160℃。
7、如权利要求6所述的用于0GFC的复合改性沥青，其特征在于：聚乙烯蜡的平均分子量为3000～6000，软化点为120～150℃。
8、权利要求1～7所述的任一用于0GFC的复合改性沥青的制备方法，该方法是：先将沥青加热到流动态，然后依次加入SEBS、石油树脂和聚乙烯蜡，采用强力搅拌机以200转/分的搅拌速度进行搅拌6小时。
CNB2005101123156A 2005-12-29 2005-12-29 用于ogfc的复合改性沥青及其制备方法 Expired - Fee Related CN100523090C (zh)