CN100473739C - Manufacturing method for high-strength straight welding oil annular tube steel - Google Patents

Manufacturing method for high-strength straight welding oil annular tube steel Download PDF

Info

Publication number
CN100473739C
CN100473739C CNB2006100282516A CN200610028251A CN100473739C CN 100473739 C CN100473739 C CN 100473739C CN B2006100282516 A CNB2006100282516 A CN B2006100282516A CN 200610028251 A CN200610028251 A CN 200610028251A CN 100473739 C CN100473739 C CN 100473739C
Authority
CN
China
Prior art keywords
steel
manufacturing
intensity
straight welding
coiled sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2006100282516A
Other languages
Chinese (zh)
Other versions
CN101096737A (en
Inventor
殷光虹
陆明和
杨峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baoshan Iron and Steel Co Ltd
Original Assignee
Baoshan Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoshan Iron and Steel Co Ltd filed Critical Baoshan Iron and Steel Co Ltd
Priority to CNB2006100282516A priority Critical patent/CN100473739C/en
Publication of CN101096737A publication Critical patent/CN101096737A/en
Application granted granted Critical
Publication of CN100473739C publication Critical patent/CN100473739C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a petroleum pipe casing steel and the manufacturing method in particular to a high-intensity straight welding petroleum pipe casing steel and the manufacturing method, which solves the low welding property technique problem of the high-intensity straight welding petroleum pipe casing steel and the technique problem of lack of the coil intensity homogeneousness. The high-intensity straight welding petroleum pipe casing steel comprises the following parts: 0.2-0.3%C, 0.1%-0.5% Si, 0.8%-1.5% Mn, P<=0.02%, S<=0.01%, 0.005%-0.050% Al, 0.1%-0.3%Mo, 0.01%-0.1%V, the rest Fe and unavoidable impurity. The method comprises the following steps: smelting; making billet; hot-rolling; cooling laminar flow; winding. The method is characterized by the following: smelting the steel liquid with the revolving furnace or the electric furnace according to the proportion; rolling the casting billet into the plate belt by heating at 1200-1300Deg. C; controlling the final temperature at 800-900Deg. C; cooling the layer flow of the rolled plate belt to 500-600Deg. C; winding into the coil. The acceptable N80 welded pipe is acquired according to the proportion and the manufacturing technique.

Description

A kind of manufacture method of high-strength straight welding oil annular tube steel
Technical field: the present invention relates to a kind of manufacture method of oil casing steel, particularly a kind of manufacture method of high-strength straight welding oil annular tube steel, casing steel intensity can reach the APIN80 grade of steel.
Background technology: the API standard code, can make petroleum casing pipe with seamless tube and longitudinal welded pipe.With regard to the straight weld sleeve pipe, traditional production technique is: according to the needs of sleeve pipe performance, design suitable chemical ingredients; Smelting also rolls into hot-rolled sheet coil; Coiled sheet is made the pipe material by moulding and vertical masonry joint resistance welding mode; Steel pipe seam or steel pipe integral are heat-treated; And pipe end is carried out suitable screw thread process, final production goes out qualified petroleum casing pipe.
With regard to the N80 steel level oil bushing, standard code: the yield strength of body between 552~758MPa, tensile strength 〉=689MPa.
If after the tubulation moulding, only butt welded seam carries out online thermal treatment, and the hot-rolled sheet coil performance that provides so just should reach above-mentioned standard code.But after considering that tubulation is shaped, because the effect of work hardening, tube body performance is compared with the coiled sheet performance, yield strength can increase, tensile strength is constant substantially, and therefore the coiled sheet yield strength that provides should be controlled at about 600MPa, and tensile strength should be controlled at more than the 750MPa.
For obtaining this high tensile strength hot rolled coiled sheet, and suitably control its yield strength, consider, should adopt the normal carbon manganese steel of higher carbon from the composition design angle.But for welded tube production,, also need two coiled sheets are carried out the CO2 shielded welding between end to end, so that realize the multireel continuous production except needs carry out the electrical induction heating fusing back extruding welding the plate flanging part.Therefore, from soldering angle, must the carbon equivalent of coiled sheet be limited to some extent.In order well to carry out coiled sheet butt welding end to end, generally all the carbon equivalent of coiled sheet is controlled at below 0.40.In order to obtain higher-strength than under the low-carbon-equivalent, the present invention will add alloying element and address this problem in material.
In addition, should about 500~600 ℃, batch after hot-rolled sheet coil generally rolls.Batch at lesser temps below 500 ℃, bigger because coiled sheet intensity is higher to the influence of reeling machine equipment, therefore when the higher coiled sheet of production intensity, should suitably improve coiling temperature.Yet, after comparatively high temps batches more than 600 ℃, under the condition of naturally cooling, be equivalent to that coiled sheet is carried out long term annealing and handle, at this moment the annealing speed of cooling of coiled sheet outer ring will be much higher than coiled sheet inside.For this high-strength steel of N80 grade of steel, if only contain carbon, manganese element in the material, coiled sheet is inner because the annealing speed of cooling is slower, and intensity will have bigger reduction.When serious, the inside and outside intensity difference of coiled sheet can reach more than the 100MPa, has a strong impact on the homogeneity of steel tube performance behind the tubulation.Therefore the present invention is by adding suitable alloying element, to guarantee the homogeneity of coiled sheet performance.
At present external resistance welding (ERW) the N80 sleeve pipe of producing has dual mode: a kind of is to be the POST WELD HEAT TREATMENT OF ENTIRE mode of representative with U.S. Lone Star Iron And Steel Company and NKK and Japan Kobe Iron And Steel Company, and another kind is to be the postwelding weld seam heat treatment mode of representative with Japanese Nippon Steel and NKK and Kobe Steel.
Each producer sees Table 1 with the ERW N80 sleeve pipe composition design of postwelding weld seam heat treatment mode production.
Table 1 ERW N80 petroleum casing pipe chemical ingredients %
Producer C Si Mn P S Cr Al Nb V Ti
Nippon Steel 0.19 0.21 1.64 0.010 0.004 - - 0.043 0.003
NKK 0.24 0.25 1.41 0.019 0.004 0.13 0.036 <0.01 <0.030 <0.030
Kobe Steel 0.28 0.21 1.34 0.016 0.003 0.027 0.041
The listed steel grades mentality of designing of table 1 is mainly by adding Nb, V, Ti microalloy element, to improve the intensity of material in carbon manganese steel.
By retrieval, find 2 pieces of patents of producing the ERW welding petroleum sheath, its chemical ingredients proportioning sees Table 2
Table 2 ERW petroleum casing pipe patent composition %
The patent No. C Si Mn Nb V Ti Technology
JP 60187663 ≤ 0.19 ≤ 0.5 1.0- 2.0 ≤ 0.05 ≤ 0.05 ≤ 0.04 Batch below 500 ℃
US4772771 0.08- 0.26 0.1- 0.5 0.8- 1.9 ≤ 0.05 ≤ 0.05 ≤ 0.03 Batch below 500 ℃
The welded tube yield strength of this patented invention can be used as the K55 sleeve pipe, but its coiling temperature is lower about 500MPa, after then requiring to roll speed of cooling is faster arranged, and is difficult to the homogeneity of control coiled sheet temperature during actual production.
Summary of the invention: the purpose of this invention is to provide a kind of high-strength straight welding oil annular tube steel and manufacture method thereof, mainly solve the not enough technical problem of coiled sheet intensity homogeneity that the welding property that has high-strength straight welding oil annular tube steel now is relatively poor and obtain.
Technical scheme of the present invention is: a kind of high-strength straight welding oil annular tube steel, and the weight percent of its moiety is:
C:0.2~0.3%
Si:0.1~0.5%
Mn:0.8~1.5%
P:≤0.02%
S:≤0.01%
Al:0.005~0.050%
Mo:0.1~0.3%
V:0.01~0.1%
Surplus is Fe and unavoidable impurities.
For increasing the intensity and the toughness of steel, also can on the basis of mentioned component, add among Nb and the Ti one or both, weight percentage is: 0.01 ~ 0.08%.
A kind of manufacture method of high-strength straight welding oil annular tube steel comprises smelting, base, hot rolling, laminar flow cooling and batches step, obtain molten steel through converter or electrosmelting by said ratio, and slab is made in casting.Slab rolls into strip after 1200~1300 ℃ of heating, the finishing temperature of strip is between 800~900 ℃, and strip is cooled to 500~600 ℃ through laminar flow and coils into coiled sheet after rolling.The hot rolled coil that rolls into by above-mentioned requirements can provide manufacturing N80 welded tube.
Adopt steel grade of the present invention, under 800 ~ 900 ℃ finish to gauge condition, within rolling in back 10 seconds, dynamic and static recrystallize can not take place, the rolling deformation of crystal grain only can take place.Be cooled to steel pipe rapidly batch below 600 ℃ this moment, helps thinning microstructure, production high-performance petroleum casing pipe.
Introduce the effect of each alloying element below respectively:
C:0.2 ~ 0.3 (wt%, below each element identical), C is a carbide forming element, can improve the intensity of steel, DeGrain when too low, too Gao Shihui reduces the welding property of steel greatly.
Mn:0.8 ~ 1.5, Mn is an austenite former, can improve the hardening capacity of steel, and content is not obvious less than effect in 0.8 o'clock, and content increased the microstructure segregation in the steel greatly greater than 1.5 o'clock, influenced the homogeneity of hot rolling microstructure.
Mo:0.1 ~ 0.3 mainly is intensity and the temper resistance that improves steel by carbide and solution strengthening form, and too high levels can reduce the toughness of steel.
V:0.01 ~ 0.1 can crystal grain thinning, forms carbide, improves the intensity and the toughness of steel.But when content reached a certain amount of, its effect increase was just not obvious, simultaneously because price is very high, so want prohibitive amount.
Among Nb and the Ti one or both: 0.01 ~ 0.08, can crystal grain thinning, form carbide, improve the intensity and the toughness of steel.But when content reached a certain amount of, its effect increase was just not obvious, simultaneously because price is very high, so want prohibitive amount.
Above-mentioned coiled sheet adopts CO2 shielded welding mode to carry out coiled sheet butt welding end to end.Carry out 100~200 ℃ of preheatings according to the different thickness specification before the butt welding, postwelding is carrying out stress relief annealing below 200 ℃.
Coiled sheet carries out online weld seam thermal treatment to welded tube behind continuously shaped, resistance welding (ERW).The weld seam thermal treatment process can be that normalizing also can be to quench to add the tempering processing.
The invention has the beneficial effects as follows that the present invention compares with the listed steel grade of table 1, the main difference part has been to add 0.1 ~ 0.3% Mo element, and it mainly acts on is the stability that improves whole coiled sheet performance.Since coiled sheet 500~600 ℃ batch after, be equivalent to whole coiled sheet and in this temperature range, carry out anneal.Because the coiled sheet outer ring is faster than the inner speed of cooling of coiled sheet, cause the inside and outside strength difference of coiled sheet, outer ring intensity is higher, differs about 100MPa sometimes.And the Mo element can improve temper resistance, helps reducing the inside and outside intensity difference of coiled sheet, improves the homogeneity of the inside and outside performance of coiled sheet, thereby improves the performance uniformity of welded tube.JP60187663 compares with US4772771 with the contrast patent, and the present invention batches in 500~600 ℃ of scopes, is in reeling machine optimal working temp scope, is easy to realize production operation, can obtain qualified N80 welded tube.
Embodiment: the embodiment of the invention 1-5 its chemical ingredientss see Table 3, and composition all is weight percentage.They are rolled into hot-rolled sheet coil in rolling, the coiling temperature scope of regulation, its mechanical property the results are shown in Table 4.By table 4 as seen, adopt steel grade of the present invention and technology, the yield strength of rolling the back coiled sheet can satisfy the performance requriements of N80 tubing and casing all greater than 600MPa.
Table 3 test steel chemical composition %
Numbering C Si Mn Mo V Nb Ti P S Al
B1 0.20 0.26 1.35 0.29 0.07 0.018 0.008 0.007
B2 0.29 0.27 0.81 0.14 0.01 0.05 0.03 0.015 0.005 0.045
B3 0.26 0.15 1.15 0.13 0.05 0.05 0.007 0.007 0.016
B4 0.23 0.29 1.49 0.10 0.03 0.03 0.01 0.010 0.010 0.018
B5 0.24 0.45 1.05 0.21 0.010 0.01 0.009 0.009 0.019
Table 4 mechanical property

Claims (1)

1, a kind of manufacture method of high-strength straight welding oil annular tube steel, comprise smelting, base, hot rolling, laminar flow cooling and batch step, it is characterized in that, weight percent by following moiety obtains molten steel: C:0.2~0.3%, Si:0.1~0.5%, Mn:0.8~1.5%, P :≤0.02%, S :≤0.01%, Al:0.005~0.050%, Mo:0.1~0.3%, one or both among Nb and the Ti: 0.01~0.08%, V:0.01~0.1%, surplus are Fe and unavoidable impurities; Molten steel rolls into strip through converter or electrosmelting and the slab of making of casting after 1200~1300 ℃ of heating, the finishing temperature of strip is between 800~900 ℃, and strip is cooled to 500~600 ℃ through laminar flow and coils into coiled sheet after rolling.
CNB2006100282516A 2006-06-28 2006-06-28 Manufacturing method for high-strength straight welding oil annular tube steel Active CN100473739C (en)