CN100457421C - 一种纯塑防渗氧管及其制备方法 - Google Patents
一种纯塑防渗氧管及其制备方法 Download PDFInfo
- Publication number
- CN100457421C CN100457421C CNB2004100215245A CN200410021524A CN100457421C CN 100457421 C CN100457421 C CN 100457421C CN B2004100215245 A CNB2004100215245 A CN B2004100215245A CN 200410021524 A CN200410021524 A CN 200410021524A CN 100457421 C CN100457421 C CN 100457421C
- Authority
- CN
- China
- Prior art keywords
- moulding
- aeration pipe
- pipe
- pure
- quality
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种纯塑防渗氧管及其制备方法,在耐高温聚乙烯管(PE-RT)、无规共聚聚丙烯(PP-R)管或聚丁烯(PB)管材上增加了防渗氧层,防渗氧层为乙烯—乙烯醇共聚物(EVOH),制备采用三层共挤复合挤出机组,由主挤出机挤出聚乙烯层、无规共聚聚丙烯层或聚丁烯层,加工温度控制在重100~280℃之间;两台辅挤出机分别挤出热熔胶层和防渗氧层(乙烯—乙烯醇共聚物(EVOH)),加工温度控制在180~250℃之间:三层物料在熔融状态于共挤出机头内复合共挤出。
Description
技术领域
本发明涉及一种防渗氧管及其制备方法。
背景技术
耐高温聚乙烯(PE-RT)管、无规共聚聚丙烯管及聚丁烯管因具有耐热、耐水压、耐化学腐蚀、安装方便可靠等优点,被广泛应用于普通水暖工程和低温地面辐射采暖以及给水等领域。但是由于在使用过程中,大气中的氧气容易通过管壁渗入管道系统内部,而使与上述管材相连的金属材料制造的管件、设备锈蚀;并且由于氧气的渗入而导致了微生物的滋生,对输送的水质造成不良影响,也容易形成积垢而阻塞管路。
发明内容
本发明的目的在于提供一种防渗氧的管材及其制备方法。
一种纯塑防渗氧管及其制备方法,在耐高温聚乙烯管、无规共聚聚丙烯管或聚丁烯管材上增加了防渗氧层,防渗氧层为乙烯-乙烯醇共聚物(EVOH)。
纯塑防渗氧管及其制备方法,防渗氧层与耐高温聚乙烯管、无规共聚聚丙烯管或聚丁烯管通过改性乙烯-醋酸共聚物(EVA)热熔胶连接。
纯塑防渗氧管及其制备方法,防渗氧层在最外层。
纯塑防渗氧管及其制备方法,防渗氧层的质量占纯塑防渗氧管质量的4~20%,优选为4~5%。
纯塑防渗氧管及其制备方法,热熔胶的质量占纯塑防渗氧管质量的3~10%,优选为3~5%。
一种纯塑防渗氧管及其制备方法,制备采用三层共挤复合挤出机组,其特征在于:由主挤出机挤出聚乙烯层、无规共聚聚丙烯层或聚丁烯层,加工温度控制在100~280℃之间:两台辅挤出机分别挤出热熔胶层和防渗氧层(乙烯-乙烯醇共聚物(EVOH)),加工温度控制在180~250℃之间:三层物料在熔融状态于共挤出机头内复合共挤出。
本发明耐高温聚乙烯防渗氧管中,所用的耐高温聚乙烯(PE-RT)为中密度聚乙烯DOWLEX*2344E。
本发明无规共聚聚丙烯防渗氧管中,所用的无规共聚聚丙烯(PP-R)为RA130E。
本发明聚丁烯防渗氧管中,所用的聚丁烯(PB)为美国壳牌Shell公司生产。
本发明耐高温聚乙烯防渗氧管中,所用的EVA热熔胶为牌号为SoamolDT2903、SoamolDC3203、DFDS6498、V3510K等牌号。
本发明耐高温聚乙烯防渗氧管中,所用的EVOH为F104W、E105和XEP398等牌号。
本发明提供的防渗氧管,其防渗氧效果好,其制备工艺简单,生产成本低。
具体实施方式:
实施例1:
主体层材料,中密度聚乙烯重量100kg(PE-RT 2344E 陶氏化工)。将上述中密度聚乙烯材料加入挤出机组中主挤出机的料斗内,经干燥后挤出,加工温度在195~235℃之间进行。
热熔胶层改性乙烯-醋酸乙烯共聚物(EVA)重量5.56kg(SoamoIDT2903美国Nichimen公司)。将上述改性乙烯-醋酸乙烯共聚物(EVA)加入挤出机组中辅挤出机1的料斗内,加工温度在195~235℃之间进行。
防渗氧层材料乙烯-乙烯醇共聚物(EVOH)重量5.56kg(XEP398日本可乐丽欧洲公司)。将上述乙烯-乙烯醇共聚物(EVOH)加入挤出机组中辅挤出机2的料斗内,加工温度在195~235℃之间进行。以上3台挤出机共用一个复合成型机头,上述3种材料熔融后同时进入机头复合成型,生产管径为¢16,挤出速度在10-12米/分,再经过定径、冷却、卷取、包装后成成品。
实施例2
主体层材料,中密度聚乙烯重量100kg(PE-RT 2344E 陶氏化工)。将上述中密度聚乙烯材料加入挤出机组中主挤出机的料斗内,经干燥后挤出,加工温度在200~240℃之间进行。
热熔胶层改性乙烯-醋酸乙烯共聚物(EVA)重量3.23kg(SoamolDC3203美国Nichimen公司)。将上述改性乙烯-醋酸乙烯共聚物(EVA)加入挤出机组中辅挤出机1的料斗内,加工温度在200~235℃之间进行。
防渗氧层材料乙烯-乙烯醇共聚物(EVOH)重量4.30kg(F104W日本可乐丽欧洲公司)。将上述乙烯-乙烯醇共聚物(EVOH)加入挤出机组中辅挤出机2的料斗内,加工温度在200~235℃之间进行。以上3台挤出机共用一个复合成型机头,上述3种材料熔融后同时进入机头复合成型,生产管径为¢20,挤出速度在9-12米/分,再经过定径、冷却、卷取、包装后成成品。
实施例3
主体层材料无规共聚聚丙烯重量100kg(PP-R RA130E 北欧化工)。将上述无规共聚聚丙烯材料加入挤出机组中主挤出机的料斗内,经干燥后挤出,加工温度在190~260℃之间进行。
热熔胶层改性乙烯-醋酸乙烯共聚物(EVA)重量4.32kg(DFDS6498芬兰萘斯特化学公司)。将上述改性乙烯-醋酸乙烯共聚物(EVA)加入挤出机组中辅挤出机1的料斗内,加工温度在195~235℃之间进行。
防渗氧层材料乙烯-乙烯醇共聚物(EVOH)重量5.20kg(日本合成化学公司)。将上述乙烯-乙烯醇共聚物(EVOH)加入挤出机组中辅挤出机2的料斗内,加工温度在195~235℃之间进行。以上3台挤出机共用一个复合成型机头,上述3种材料熔融后同时进入机头复合成型,生产管径为¢16,挤出速度在10-12米/分,再经过定径、冷却、卷取、包装后成成品。
实施例4
主体层材料聚丁烯重量100kg(PB美国壳牌Shell公司)。将上述聚丁烯材料加入挤出机组中主挤出机的料斗内,经干燥后挤出,加工温度在130~210℃之间进行。
热熔胶层改性乙烯-醋酸乙烯共聚物(EVA)重量3.18kg(V3510K德国巴斯夫公司)。将上述改性乙烯-醋酸乙烯共聚物(EVA)加入挤出机组中辅挤出机1的料斗内,加工温度在195~235℃之间进行。
防渗氧层材料乙烯-乙烯醇共聚物(EVOH)重量4.36kg(XEP398日本可乐丽欧洲公司)。将上述乙烯-乙烯醇共聚物(EVOH)加入挤出机组中辅挤出机2的料斗内,加工温度在195~235℃之间进行。以上3台挤出机共用一个复合成型机头,上述3种材料熔融后同时进入机头复合成型,生产管径为¢20,挤出速度在8-10米/分,再经过定径、冷却、卷取、包装后成成品。
实施例5:
主体层材料,中密度聚乙烯重量100kg(PE-RT 2344E 陶氏化工)。将上述中密度聚乙烯材料加入挤出机组中主挤出机的料斗内,经干燥后挤出,加工温度在195~235℃之间进行。
热熔胶层改性乙烯-醋酸乙烯共聚物(EVA)重量7.8kg(SoamolDT2903美国Nichimen公司)。将上述改性乙烯-醋酸乙烯共聚物(EVA)加入挤出机组中辅挤出机1的料斗内,加工温度在195~235℃之间进行。
防渗氧层材料乙烯-乙烯醇共聚物(EVOH)重量5.56kg(XEP398日本可乐丽欧洲公司)。将上述乙烯-乙烯醇共聚物(EVOH)加入挤出机组中辅挤出机2的料斗内,加工温度在195~235℃之间进行。以上3台挤出机共用一个复合成型机头,上述3种材料熔融后同时进入机头复合成型,生产管径为¢16,挤出速度在10-12米/分,再经过定径、冷却、卷取、包装后成成品。
实施例6:
主体层材料,中密度聚乙烯重量100kg(PE-RT 2344E 陶氏化工)。将上述中密度聚乙烯材料加入挤出机组中主挤出机的料斗内,经干燥后挤出,加工温度在195~235℃之间进行。
热熔胶层改性乙烯-醋酸乙烯共聚物(EVA)重量5.56kg(SoamolDT2903美国Nichimen公司)。将上述改性乙烯-醋酸乙烯共聚物(EVA)加入挤出机组中辅挤出机1的料斗内,加工温度在195~235℃之间进行。
防渗氧层材料乙烯-乙烯醇共聚物(EVOH)重量14.44kg(XEP398日本可乐丽欧洲公司)。将上述乙烯-乙烯醇共聚物(EVOH)加入挤出机组中辅挤出机2的料斗内,加工温度在195~235℃之间进行。以上3台挤出机共用一个复合成型机头,上述3种材料熔融后同时进入机头复合成型,生产管径为¢16,挤出速度在10-12米/分,再经过定径、冷却、卷取、包装后成成品。
Claims (9)
1、一种纯塑防渗氧管,在耐高温聚乙烯(PE-RT)管、无规共聚聚丙烯(PP-R)管或聚丁烯(PB)管材上增加了防渗氧层,防渗氧层为乙烯一乙烯醇共聚物(EVOH),防渗氧层与耐高温聚乙烯管、无规共聚聚丙烯管或聚丁烯管通过改性乙烯-醋酸共聚物(EVA)热熔胶粘接,其特征在于:所述热熔胶为SoamolDT2903、SoamolDC3203、DFDS6498或V3510K。
2、按照权利要求1所述纯塑防渗氧管,其特征在于:所述防渗氧层在最外层。
3、按照权利要求1所述纯塑防渗氧管,其特征在于:所述防渗氧层的质量占纯塑防渗氧管质量的4~20%,热熔胶的质量占纯塑防渗氧管质量的3~10%。
4、按照权利要求3所述纯塑防渗氧管,其特征在于:所述防渗氧层的质量占纯塑防渗氧管质量的4~5%。
5、按照权利要求3所述纯塑防渗氧管,其特征在于:所述热熔胶的质量占纯塑防渗氧管质量的3~5%。
6、按照权利要求1所述纯塑防渗氧管,其特征在于:所述耐高温聚乙烯(PE-RT)为中密度聚乙烯DOWLEX*2344E。
7、按照权利要求1所述纯塑防渗氧管,其特征在于:所述无规共聚聚丙烯(PP-R)为RA130E。
8、按照权利要求1所述纯塑防渗氧管,其特征在于:所述聚丁烯(PB)为美国壳牌Shell公司生产。
9、制备权利要求1所述的纯塑防渗氧管的方法,制备采用三层共挤复合挤出机组,其特征在于:由主挤出机挤出聚乙烯层、无规共聚聚丙烯层或聚丁烯层,加工温度控制在100~280℃之间;两台辅挤出机分别挤出热熔胶层和防渗氧层,加工温度控制在180~250℃之间:三层物料在熔融状态于共挤出机头内复合共挤出。