CN100432291C - 金属表面处理液及处理工艺 - Google Patents

金属表面处理液及处理工艺 Download PDF

Info

Publication number
CN100432291C
CN100432291C CNB2006101519618A CN200610151961A CN100432291C CN 100432291 C CN100432291 C CN 100432291C CN B2006101519618 A CNB2006101519618 A CN B2006101519618A CN 200610151961 A CN200610151961 A CN 200610151961A CN 100432291 C CN100432291 C CN 100432291C
Authority
CN
China
Prior art keywords
treatment
treating
film
metal surface
treating liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006101519618A
Other languages
English (en)
Other versions
CN1916236A (zh
Inventor
张苏平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia Qingyang Mining Co., Ltd.
Original Assignee
ZHENGDA HI-TECH ELECTRONIC (NEIMENGGU) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENGDA HI-TECH ELECTRONIC (NEIMENGGU) Co Ltd filed Critical ZHENGDA HI-TECH ELECTRONIC (NEIMENGGU) Co Ltd
Priority to CNB2006101519618A priority Critical patent/CN100432291C/zh
Publication of CN1916236A publication Critical patent/CN1916236A/zh
Application granted granted Critical
Publication of CN100432291C publication Critical patent/CN100432291C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种新型环保金属表面处理液及处理工艺，属于冶金领域。配方：磷酸二氢锌40-60g/L、硝酸锌90-120g/L、硝酸镍或硝酸钙5-10g/L、亚硝酸钠1-3g/L、酒石酸6-9g/L、OP-10：10-12g/L、水余量。工艺如下：将被处理的金属放在一个处理槽中，加入上述处理液，处理液的总酸度为75-90点，游离酸度为3-5点，处理时间为3min，处理温度为40-60℃，脱脂、除锈、磷化同步完成。本发明处理液处理的金属制品，磷化膜的厚度为3μm，颜色为深灰色，结晶致密、连续均匀，耐硫酸铜溶液的点滴大于40S。经使用证实，磷化膜成膜迅速与阴极电泳漆结合力强，无溶膜现象出现。

Description

金属表面处理液及处理工艺
一、技术领域：
本发明涉及一种金属表面处理液及处理工艺，属于冶金领域。
二、现有技术：
在涂装生产线中，它的工艺流程一般是：脱脂→水洗→除锈→水洗→磷化→水洗→烘干→涂装→烘干。工序多，处理时间长，生产效率低，环境污染严重，劳动强度大。如果采用一般的三合一或四合一处理液(脱脂、除锈、磷化)生产成本高，处理工艺都是采用浸渍法，且处理时间都高于5min，处理时间长，生产效率低，特别是在自动化生产线上，处理时间多1min，就意味着整个生产线将推迟1min出产品，使生产量大幅度降低。而且后线的电泳生产线处理时间短，不超过3min，前线的处理工艺不能满足后线的需求。
三、发明内容
本发明解决的技术问题是：简化了生产工艺，提高了前处理的生产效率，节能降耗，减少、降低环境污染，降低生产成本。
技术解决方案：本发明处理液配方：
磷酸二氢锌        40-60g/L
硝酸锌            90-120g/L
硝酸镍(硝酸钙)    5-10g/L
亚硝酸钠          1-3g/L
酒石酸            6-9g/L
OP-10        10-12g/L
水余量。
处理工艺如下：
将被处理的金属放在一个处理槽中，加入上述处理液，处理液的总酸度为75-90点，游离酸度为3-5点，处理时间为3min，处理温度为40-60℃，脱脂、除锈、磷化同步完成。
处理方式为喷射法，喷射压力为0.1MPa，喷嘴的规格为0.1MPa的压力下，流量为10.4-18.6L/min。
本发明效果：
由于本发明将脱脂、除锈、磷化三大工序在一个处理槽中同步完成，简化了工艺，节能降耗；处理液所采用的原材料对人体无害，对环境污染小；因处理液中采用的是比草酸还弱的磷酸，所以对钢铁体不会产生过腐蚀的现象；因在处理液中加入了络合剂，能与铁离子形成络合物，使溶液不发生沉淀，可长期使用。因此也不需经常排放和处理，环境污染小。
经本发明处理液处理的金属制品，磷化膜的厚度为3μm，磷膜的颜色为深灰色，磷化膜的结晶致密，连续均匀，磷化膜的耐硫酸铜溶液的点滴大于40s。磷化膜的成膜迅速，与阴极电泳漆结合力强，无溶膜现象出现。
本发明处理工艺应用到电泳涂装自动生产线上，生产量比传统的工艺增加2倍。产品出口美国，经外商对产品的检测，合格率达到100％，得到顾客的赞誉。
四、具体实施方式
实施例1
钢铁工件、锌合金的处理液配方：
磷酸二氢锌40-60g/L、硝酸锌90-120g/L、硝酸镍5-10g/L、亚硝酸钠1-3g/L、酒石酸6-9g/L、OP-1010-12g/L其余为水，处理液总酸度75-90点，游离酸度3-5点，处理时间3min，处理温度40-60℃。
处理工艺：将被处理的金属放在一个处理槽中，加入上述处理液，处理液的总酸度为75-90点，游离酸度为3-5点，处理时间为3min，处理温度为40-60℃，脱脂、除锈、磷化同步完成；
处理方式为喷射法，喷射压力为0.1MPa，喷嘴的规格为0.1MPa的压力下，流量为10.4-18.6L/min。
实施例2
本发明采用了脱脂、除锈、磷化三合一综合处理工艺，处理方式为喷射法，喷射压力0.1MPa，喷嘴规格为0.1MPa下流量为10.4-18.6L/min，输送链的线速度为3m/min，喷射时间为2min，处理温度为40-60℃，处理液的配方为：Zn(H2PO4)245g/L、Zn(NO3)2120g/L、Ni(NO3)210g/L、C4H6O68g/L、NaNO22g/L、OP-1010g/L，总酸度75-90点，游离酸度3-5点。经喷射处理后的产品，进入水洗工序和烘干工序烘干后，下线检测表面处理的结果，将产品放在光线良好的地方，用肉眼观察，磷化膜均匀完整，附着牢固有光泽，磷化膜的颜色为灰白色。经测定磷化膜的重量为2.4g/m2，P比89％，晶粒度为9μm，镍含量28mg/m2，很适宜与阴极电泳配合。用硫酸铜溶液对磷化膜进行滴定，在磷化膜的表面不同部位检查3次，取其变色的平均值，磷化膜的变色时间为42s。

Claims (3)

1、金属表面处理液，其特征在于：其配方组分如下，单位为克/升：
磷酸二氢锌        40-60g/L
硝酸锌            90-120g/L
硝酸镍或硝酸钙    5-10g/L
亚硝酸钠          1-3g/L
酒石酸            6-9
OP-10             10-12g/L
水余量。
2、金属表面处理工艺，其特征在于：工艺步骤如下：将被处理的金属放在一个处理槽中，加入上述处理液，处理液的总酸度为75-90点，游离酸度为3-5点，处理时间为3min，处理温度为40-60℃，脱脂、除锈、磷化同步完成。
3、根据权利要求2所述的金属表面处理工艺，其特征在于：上述工艺采用喷射法，喷射压力为0.1MPa，喷嘴的规格为0.1MPa的压力下，流量为10.4-18.6L/min。
CNB2006101519618A 2006-09-03 2006-09-03 金属表面处理液及处理工艺 Expired - Fee Related CN100432291C (zh)