CN100423808C - 凹凸棒陶粒滤料的生产方法 - Google Patents

凹凸棒陶粒滤料的生产方法 Download PDF

Info

Publication number
CN100423808C
CN100423808C CNB200510094569XA CN200510094569A CN100423808C CN 100423808 C CN100423808 C CN 100423808C CN B200510094569X A CNB200510094569X A CN B200510094569XA CN 200510094569 A CN200510094569 A CN 200510094569A CN 100423808 C CN100423808 C CN 100423808C
Authority
CN
China
Prior art keywords
attapulgite
hadite
production
filtering materials
ceramic grain
Prior art date
Application number
CNB200510094569XA
Other languages
English (en)
Other versions
CN1762540A (zh
Inventor
许庆华
Original Assignee
许盛英
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 许盛英 filed Critical 许盛英
Priority to CNB200510094569XA priority Critical patent/CN100423808C/zh
Publication of CN1762540A publication Critical patent/CN1762540A/zh
Application granted granted Critical
Publication of CN100423808C publication Critical patent/CN100423808C/zh

Abstract

本发明公开了一种凹凸棒陶粒滤料的生产方法,其技术方案的要点是,凹凸棒陶粒滤料的生产方法是:配料、磨粉、造粒、焙烧、筛分、包装为成品。凹凸棒陶粒滤料是由凹凸棒石粘土、煤矸石和火山灰组成。凹凸棒陶粒滤料表面粗糙不结釉,挂膜性能良好,水流阻力小,耐水冲刷,不会造成堵塞,具有较好的稳定性和吸附性能,而且易于再生,反冲洗容易进行,能耗低。凹凸棒陶粒滤料生产方法简单,所采用的原料价格低廉,焙烧温度低,可以节约大量的能源,降低生产成本,物化性能稳定,不向水体释放有毒有害物等特性,无二次污染。凹凸棒陶粒滤料是一种廉价的吸附过滤剂,适用于水质净化处理。

Description

凹凸棒陶粒滤料的生产方法技术领域:本发明涉及滤料,具体涉及一种凹凸棒陶粒滤料的生产方法。 背条技术:在水质净化处理工艺中,常使用大量的陶粒滤料,传统使用的陶粒滤料是 采用陶土、粘土等原料,经造粒后烧结而成,浪费了大量的土地资源。近几年 来,以粉煤灰、煤矸石为主要原料生产的陶粒不断研制成功,投入生产和使用, 但是,以粉煤灰、煤矸石为主要原料生产的陶粒需要较高的烧结温度,烧结温 度大多都在110 0〜1 2 0 (TC之间,消耗大量的能源,而且以粉煤灰、煤矸 石为主要原料生产的陶粒,质脆易碎,陶粒表面在高温烧结的情况下容易结釉, 挂胰和吸附性能比较差。粉煤灰、煤矸石为主要原料生产的陶粒,应用于混凝 土、陶粒空心砌块和钢筋砼等建筑工程中,而很少应用于水质净化处理工艺。中国专利公开号CN 1486773,公开曰为2004年4月7日,名称为"一种奥粘过滤陶粒及制作方法",它公开了 "一种奥粘过滤陶粒及制作方法,由凹凸棒 土、木炭粉、粘土 (红壤土)、瓷泥、硅藻土这五种原料制配而成,其特征在于: 它的重量组份为凹凸棒土 1 9 一 3 5 ,木炭粉1一5,瓷泥3 — 5,粘土35 —7 0,硅藻土7 —1 5,其最佳主量组份是:凹凸土2 9,木炭粉2 ,粘土 6 0,瓷泥3 ,硅藻土 1 0 ,其工艺是:配料——粉碎——搅拌——团粒—— 烘千——烧结等工序,粉碎度为O. 15—2. 2 5mm,加水团粒后,烘干 温度为8 0〜1 2 (TC,烧结温度为9 0 0〜1 2 0 (TC。其优点:1 、原料 易得;2、制作工艺简单,3、重量轻、微孔多,过滤效果好;4、能广泛应 用于工业废水过滤。"上述发明的不足之处是,1、原料"粉碎度为O. 15 — 2. 25mm", 其颗斧立度太大,"加水团粒后",颗粒之间不能形成一种紧密的结合,造成颗粒 强度较低。
2、凹凸棒土经过"烧结温度为9 0 0〜1 2 0 0 °C",会破坏凹凸棒土特 殊的晶体结构,陶粒表面在高温烧结的情况下容易结釉,挂膜和吸附性能比较 差,影响其产品的整体性能。
发明内容:
本发明的目的是克服现有技术中不足之处,提供一种操作简单,充分利用 自然资源,强度髙、吸附和过滤效果好的凹凸棒陶粒滤料的生产方法。
凹凸棒陶粒滤料的生产方法是:配料、磨粉、造粒、焙烧、筛分、包装为 成品力
凹凸棒陶粒滤料是由凹凸棒石粘土、煤矸石和火山灰组成。
凹凸棒石粘土是一种具链层状结构的含水富镁硅酸盐粘土r"物,由于凹凸 棒石独特的晶体结构,使之具有许多特殊的物化及工艺性能。主要物化性能和
工艺性能有:阳离子可交换性、吸水性、吸附脱色性和大的比表面积,凹凸棒
石粘土粘结性能好,在含水的情况下具有较高的可塑性。
煤矸石是一种含碳矿物,单独使用煤矸石生产的陶粒滤料,质脆易碎,煤 矸石是低热值燃料,在本发明的四凸棒陶粒滤料焙烧过程中,不但可以节省燃
料,而且煤矸石在焙烧中,能生成活性碳和大量的微孔,煤矸石中Al203的含量
比较高,能提高F1凸棒陶粒滤料的强度;我国目前煤矸石的利用率还处乎较低 水平,综合利用煤矸石,不仅可以减少资源浪费,还能取得了较好的社会效益 和生态效益。
火山灰是火山喷发溢流形成的一禾t粗糙、轻质、多孔和吸水率较高的矿石,火山灰主要成分是活性硅土 (Si02)和氧化鋁(AlA),火山灰在本发明的凹凸 棒陶粒滤料中可以增加其活性,提高吸附挂膜的性能。我国火山灰的储量比较 丰富,目前仅使用在水泥生产中。
本发明通过下述技术方案予以实现-
1、 凹凸棒陶粒滤料的配料,按重量百分比包括下列组分:凹凸棒石粘土 25〜 50%、煤犴石20〜45%和火山灰15〜30%。
2、 将上述ia料浪舍后输送到磨机中进行磨粉,颗粒细度应《0.074毫米。
3、 用磨粉后的混合料,输入造粒机进行造粒,颗粒度控制在L5〜15亳米。
4、 造粒后的颗粒,送入焙烧炉中进行焙烧,焙烧温度控制在350〜500'C。
5、 焙'瓶的颗粒应进行筛分,颗粒度控帝帖1.5〜15毫米,包装为成品。
凹凸棒陶粒滤料是一种轻质球形陶粒,粒度均匀,表面多微孔。凹凸棒陶 粒滤料颗粒强度髙耐摩擦,5毫米的凹凸棒陶粒滤料,30颗的颗粒强度平均值 》80N。
凹凸棒陶粒滤料表面粗糙不结釉,挂膜性能良好,水流阻力小,射水冲刷, 不会造成堵塞,具有较好的稳定性和吸附性能,而且易于再生,反冲洗容易进行, 能耗低。
凹凸棒陶粒滤料生产方法简单,所采用的原料价格低廉,焙烧温度低,可 以节约大量的能源,降低生产成本,物化性能稳定,不向水体释放有毒有害物 等特性,无二次污染。
凹凸棒陶粒滤料是一种廉价的吸附过滤剂,适用于水质净化处理。 具体实施方式:
下面结合实施例,对本发明作进一步的描述:实施例1:用于处理生活用水的凹凸棒陶粒滤料的生产方法是,凹凸棒陶粒 滤料配料按重量百分比包括下列组分:凹凸棒石粘土40%、煤矸石35%和火山灰25%;将卜.述配料混合后输送到磨机中进行磨粉,颗粒细度应《0.074亳米;用磨粉后的混合料,输入造粒机进行造粒,颗粒度控制在2〜10毫米;经造粒后的颗粒,送入焙烧炉中进行焙烧,焙烧温度控制在45(TC;焙烧后的颗粒应进 行筛分,颗粒度控制在2〜10毫米,包装为成品。实施例2:用于处理工业污水的凹凸棒陶粒滤料的生产方法是,凹凸棒陶粒滤料配料按重量百分比包括下列组分:凹凸棒石粘十50%、煤矸石35%和火山 灰15%。将上述配料混合后输送到磨机中进行磨粉,颗粒细度应《0.074毫米;用磨粉后的混合料,输入造粒机进行造粒,颗粒度控制在4〜15亳米;经造粒后的颗粒,送入焙烧炉中进行焙烧,焙烧温度控制在50(TC;,后的颗粒应进 行筛分,颗粒度控制在4〜15毫米,包装为成品。

Claims (1)

1. 一种凹凸棒陶粒滤料的生产方法,其特征在于,凹凸棒陶粒滤料的配料,按重量百分比由下列组分组成:凹凸棒石粘土25~50%、煤矸石20~45%和火山灰15~30%;将上述配料混合后输送到磨机中进行磨粉,颗粒细度应≤0.074毫米;用磨粉后的混合料,输入造粒机进行造粒,颗粒度控制在1.5~15毫米;造粒后的颗粒,送入焙烧炉中进行焙烧,焙烧温度控制在350~500℃;焙烧后的颗粒应进行筛分,颗粒度控制在1.5~15毫米,包装为成品。
CNB200510094569XA 2005-09-28 2005-09-28 凹凸棒陶粒滤料的生产方法 CN100423808C (zh)