CN100385042C - 钕铁硼磁性材料表面除油去污清洗剂及使用方法 - Google Patents

钕铁硼磁性材料表面除油去污清洗剂及使用方法 Download PDF

Info

Publication number
CN100385042C
CN100385042C CNB2006100502484A CN200610050248A CN100385042C CN 100385042 C CN100385042 C CN 100385042C CN B2006100502484 A CNB2006100502484 A CN B2006100502484A CN 200610050248 A CN200610050248 A CN 200610050248A CN 100385042 C CN100385042 C CN 100385042C
Authority
CN
China
Prior art keywords
detergent
ndfeb
clean
cleaning
oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100502484A
Other languages
English (en)
Other versions
CN1847459A (zh
Inventor
严密
应华根
罗伟
吴进明
贺雪峰
吴磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang University ZJU
Original Assignee
Zhejiang University ZJU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang University ZJU filed Critical Zhejiang University ZJU
Priority to CNB2006100502484A priority Critical patent/CN100385042C/zh
Publication of CN1847459A publication Critical patent/CN1847459A/zh
Application granted granted Critical
Publication of CN100385042C publication Critical patent/CN100385042C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种钕铁硼磁性材料表面除油去污清洗剂及使用方法,它是由氢氧化钠,碳酸钠,磷酸三钠,焦磷酸钠,OP-10乳化剂,十二烷基硫酸钠和硫脲组成。本发明清洗剂化学性能稳定,使用周期长,使用该清洗剂时所需的设备简单,在30-50℃下用浸泡法在10-15分钟内即可实现彻底除油,如使用超声波除油则所需时间更短,缩短了钕铁硼磁性材料前处理所需的时间,减小了材料在前处理中的腐蚀。经处理后的表面可直接进行电镀、化学镀或喷涂,增加了镀(涂)层的结合力,提高防护层的质量。

Description

钕铁硼磁性材料表面除油去污清洗剂及使用方法技术领域本发明涉及一种钕铁硼(NdFeB)磁性材料表面除油去污清洗剂及使用方法, 属于化学法金属材料清洗技术领域。 背景技术NdFeB作为一种永磁材料以其优异的磁性能和高的性价比被广泛应用于计 算机、工业自动化、家电、通讯以及各种电声器件上,NdFeB磁性材料有力地 促进了现代科学技术与信息产业化的发展,是促进当代技术与社会进步的重要 物质基础之一,为新型产业的出现提供了物质保证。NdFeB磁性材料由三个相 组成,即主相、富钕相和富硼相,由于富钕相和富硼相一般都分布在晶界处, 而富钕相极易被氧化,所以NdFeB磁性材料极易发生晶间腐蚀;另外,由于富 钕相的腐蚀电位较低,容易发生电化学腐蚀。所以必须对NdFeB磁性材料进行 表面防护处理,目前较常用的保护方法主要有:喷涂、电泳、电镀和化学镀等。 不管采用哪种防护方法,为了使镀(涂层)层与基体结合良好,必须在进行防 护前对材料基体进行除油、除锈等前处理。而在取得良好的除油效果的同时尽 量减少处理液对基体的腐蚀是非常有必要的。现有的材料表面清洗剂主要是针对钢铁材料或锌、锡、铝、铜等金属或合金 而开发的,在这些材料表面能取得很好除油去污效果的清洗剂用在钕铁硼材料 表面并不能取得预期的效果。首先,NdFeB磁性材料表面疏松多孔,普通的清洗剂难以去除孔隙中的油污;其次,清洗剂一般为强碱性溶液,清洗温度较高, 一般在5(TC以上,容易腐蚀NdFeB基体,造成材料的浪费或破坏。发明内容本发明的目的是提供一种钕铁硼磁性材料表面除油去污清洗剂及使用方 法。这种清洗剂使用温度比较低,除油所需时间比较短,因而对NdFeB磁性材 料基体的腐蚀比较小,同时清洗剂的存储稳定性较好。钕铁硼磁性材料表面除油去污清洗剂:每升溶液中氢氧化钠为5-10g、碳酸 钠为15-30g、磷酸三钠为30-50g、焦磷酸钠为10-15g、 OP-10乳化剂为l-3g、 十二烷基硫酸钠为l-2g、硫脲为0.5-1.5g。钕铁硼磁性材料表面除油去污清洗剂的使用方法:清洗温度为30-50'C,用 浸泡法清洗需10—15min,用超声波清洗需3-6min。与现有技术相比,本发明有如下优点: 1. 效果好。该清洗剂可有效去除NdFeB磁性材料表面和孔隙中的油污,为后续工序提供洁净的表面;2. 工艺简单,使用方便,只需将工件浸泡在清洗剂中并搅拌或釆用超声波清 洗即可实现彻底除油-,3. 使用安全,无毒无味,不燃不爆,清洗温度低,清洗时间短,不对基体产 生过腐蚀;4. 性能稳定,可长期存储而不影响使用效果。 具体实施方式本发明利用皂化作用和乳化作用原理,使用皂化剂和乳化剂,配合一些表 面活性剂和缓蚀剂组成适用于NdFeB磁性材料的表面除油去污清洗剂。材料表 面的油脂与除油液中的皂化物质发生皂化反应,使不溶于水的皂化性油脂变成 能溶于水的肥皂和甘油而除去;材料表面的非皂化性油脂与乳化剂作用,变成 微细的油珠与材料表面分离,并均匀分布到溶液中,成为乳浊液,实现除油目 的。表面活性剂能溶于水中,即有亲水性,另一方面性,在除油过程中能吸附 油污,即有一定的亲油性,表面活性剂的亲油作用有利于降低除油温度;缓蚀 剂在溶液中能降低基体材料的腐蚀速度,防止基体的过腐蚀。本发明的钕铁硼磁性材料表面除油去污清洗剂是由氢氧化钠,碳酸钠,磷酸 三钠,焦磷酸钠,OP-10乳化剂,十二垸基硫酸钠和硫脲组成。以1升计,溶液 中氢氧化钠含量为5-10g,碳酸钠含量为15-30g,磷酸三钠含量为30-50g,焦磷 酸钠含量为10-15g, OP-10乳化剂含量为l-3g,十二烷基硫酸钠含量为l-2g,硫 脲含量为0.5-1.5g,其余为水。上述成分中,氢氧化钠主要起皂化作用;碳酸钠 和磷酸三钠有一定的皂化能力和缓冲作用,且磷酸三钠还起一定的乳化作用;焦 磷酸钠缓冲性良好,有一定的表面活性作用,而且还具有一定的鳌合作用,可以 防止基体材料表面生成不溶性的硬皂化膜;OP-10乳化剂主要起乳化作用,去除 非皂化性油脂;十二烷基硫酸钠和硫脲分别起表面活性剂和缓蚀剂的作用。上述钕铁硼磁性材料表面除油去污清洗剂的使用方法是在温度为30-50°C 时,用浸泡法清洗10-15min,或用超声波清洗法清洗3-6min,即可达到较好的 除油去污效果。下面结合具体实施例对本发明的内容进行详细描述,首先配制不同配方的 清洗剂溶液,具体成分如表1所示。然后将O10mmX3mm的NdFeB磁体按下面各实施例的工艺方法进行清洗。
表l.不同成分光亮剂配方表 <table>table see original document page 5</column></row> <table>实施例1:取配方1成分清洗剂60ml,在3(TC用浸泡法清洗10min,在清洗时不断搅拌。 实施例2:取配方1成分清洗剂60ml,在3(TC超声波清洗法清洗3min。 实施例3:取配方2成分清洗剂60ml,在4(TC用浸泡法清洗12min,在清洗时不断搅拌。 实施例4:取配方2成分清洗剂60ml,在5(TC超声波清洗法清洗5min。实施例5:取配方3成分清洗剂60ml,在5(TC用浸泡法清洗15min,在清洗时不断搅拌。 实施例6:取配方3成分清洗剂60ml,在4(TC超声波清洗法清洗6min。 实施例7:取配方4成分清洗剂60ml,在30'C用浸泡法清洗10min,在清洗时不断搅拌。 实施例8:取配方4成分清洗剂60ml,在3(TC超声波清洗法清洗3min。 实施例9:取配方5成分清洗剂60ml,在4(TC用浸泡法清洗12min,在清洗时不断搅拌。实施例10:取配方5成分清洗剂60ml,在4(TC超声波清洗法清洗4min。 实施例11 :取配方6成分清洗剂60ml,在5(TC用浸泡法清洗15min,在清洗时不断搅拌。实施例10:
取配方6成分清洗剂60ml,在5(TC超声波清洗6min法清洗。 采用水膜破裂检验法和水润湿检验法检验各实施例中NdFeB磁体清洗后表 面的清洁度。水膜破裂检验法:清洗后将零件取出,发现NdFeB磁体表面均匀覆盖水膜, 无水珠或表面水膜破裂。再用水润湿检验法检验:将NdFeB磁体烘干后,将水 珠滴在磁体表面,发现水滴散布在表面呈水膜状,表面倾斜时无水滴滚落。以上检测结果表明采用实施例中各配方对NdFeB磁体进行清洗时,表面油污去除彻底,清洗干净。经观测,磁体表面未被腐蚀,表明清洗液对磁体的腐 蚀率极小。将清洗后的各实施例中的NdFeB磁体和未经本发明方法处理的NdFeB磁体 按常规方法电镀镍,然后进行划痕试验检测镀层的结合力。发现未经本发明方 法处理的NdFeB磁体表面镀层脱落,而经清洗处理的各实施例中的NdFeB磁体 的镀层结合良好,经划痕试验不起皮或脱落。进一步表明本发明清洗剂有很好 的除油去污效果。

Claims (2)

1.一种钕铁硼磁性材料表面除油去污清洗剂,其特征在于每升溶液中氢氧化钠为5-10g、碳酸钠为15-30g、磷酸三钠为30-50g、焦磷酸钠为10-15g、OP-10乳化剂为1-3g、十二烷基硫酸钠为1-2g、硫脲为0.5-1.5g。
2. —种如权利要求1所述钕铁硼磁性材料表面除油去污清洗剂的使用方 法,其特征在于清洗温度为30-5(TC,用浸泡法清洗需10—15min,或用超声波 清洗需3-6min。
CNB2006100502484A 2006-04-07 2006-04-07 钕铁硼磁性材料表面除油去污清洗剂及使用方法 Expired - Fee Related CN100385042C (zh)