CN100337956C - Overglaze capable of automatically forming vertical cob-webbing, fish scale webbing or lateral cob-webbing and is use - Google Patents

Overglaze capable of automatically forming vertical cob-webbing, fish scale webbing or lateral cob-webbing and is use Download PDF

Info

Publication number
CN100337956C
CN100337956C CNB2005100312409A CN200510031240A CN100337956C CN 100337956 C CN100337956 C CN 100337956C CN B2005100312409 A CNB2005100312409 A CN B2005100312409A CN 200510031240 A CN200510031240 A CN 200510031240A CN 100337956 C CN100337956 C CN 100337956C
Authority
CN
China
Prior art keywords
cover
reticulate pattern
coat enamel
oxide
horizontal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100312409A
Other languages
Chinese (zh)
Other versions
CN1683285A (en
Inventor
何昌楚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd
Original Assignee
HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd filed Critical HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd
Priority to CNB2005100312409A priority Critical patent/CN100337956C/en
Publication of CN1683285A publication Critical patent/CN1683285A/en
Application granted granted Critical
Publication of CN100337956C publication Critical patent/CN100337956C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to overglaze capable of automatically forming vertical net stripes, fish scale stripes or transversal net stripes. The overglaze is characterized in that the overglaze is composed of the following raw materials: 8 to 13% of quartz, 25 to 35% of calcite, 2 to 4% of alumina, 8% of iron oxide, 3 to 6% of barium carbonate, 1% of oxidation jewel, 30 to 40% of clay and 6 to 13% of frit. The overglaze forms irregular vertical stripe net patterns when being applied to a smooth porcelain blank. The overglaze is applied to a concave and convex forming porcelain blank to form irregular fish scale stripes or transversal net stripes. The overglaze provided according to a technical scheme is applied to a blank coated with base glaze, and a finished product after burning can present irregular vertical net stripes, concave and convex fish scale stripes or transversal net stripes. Thus, patterns on the porcelain blank are natural and beautiful.

Description

A kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily
Technical field
The present invention relates to a kind ofly can generate vertical reticulate pattern, scalelike mark or the horizontal cover-coat enamel of reticulate pattern automatically, belong to ceramic glaze prescription class, refer in particular to and be used for the cover-coat enamel that the secondary glazing is used.
Background technology
Color and pattern on the various domestic ceramics utensils have several different methods to make, general they all be on the porcelain base after the moulding, to fire and form by applying different glaze colours pigment, also useful handwritten drawings method is drawn a picture on base substrate or the utensil that has been fired into color glaze, then reburns and makes merit.The above-mentioned multiple mode operation that applies cover-coat enamel is various; And its formed patterns is generally all more stiff, lacks Art Imagination power and infectivity.
Summary of the invention
Purpose of the present invention: be to provide a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily; Make the goods after burning till have more Art Imagination power and infectivity.
This cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily is characterized in that: the raw material of described cover-coat enamel following (by weight percentage): quartz 8~13%, calcite 25~35%, aluminum oxide 2~4%, ferric oxide 8%, barium carbonate 3~6%, oxidation brill 1%, frit 6~13%, clay 30~37%.
Its particle diameter accounts for the raw material total amount more than 98% less than 200 purpose granule materials in the described various raw material.
Described cover-coat enamel, its firing temperature is at 1200~1260 ℃.
Described cover-coat enamel forms irregular vertical reticulate pattern when using on smooth porcelain base substrate.
Described cover-coat enamel forms irregular scalelike mark on concavo-convex porcelain base.
Described cover-coat enamel forms the horizontal reticulate pattern that the ring-type decorative pattern combines with vertical reticulate pattern on horizontal local ring-type step porcelain base substrate.
This cover-coat enamel according to above technical scheme proposes is imposing on it on molding blank of going up ground-coat enamel, can manifest irregular vertical reticulate pattern, concavo-convex scalelike mark or horizontal reticulate pattern on the finished product after fired, make decorative pattern on the body more natural, have more aesthetic feeling.
Description of drawings
Accompanying drawing 1 is for using the design sketch of the formed vertical reticulate pattern of this cover-coat enamel;
Accompanying drawing 2 is for using the design sketch of the formed concavo-convex fish phosphorus line of this cover-coat enamel;
Accompanying drawing 3 is for using the design sketch of the formed horizontal reticulate pattern of this cover-coat enamel.
Among the figure: 1, vertical reticulate pattern 2, fish phosphorus line 3, horizontal reticulate pattern
Embodiment (by weight percentage)
Example 1 Example 2 Example 3
Quartzy calcite aluminium oxide iron oxide brium carbonate cobalt oxide frit clay ??8 ??35 ??2 ??8 ??3 ??1 ??6 ??37 ??10.5 ??30 ??3 ??8 ??4.5 ??1 ??9.5 ??33.5 ??13 ??25 ??4 ??8 ??6 ??1 ??13 ??30
Actual use as above-mentioned cover-coat enamel has following characteristics:
The first, the firing temperature of cover-coat enamel should be controlled at 1200 ℃-1260 ℃;
The second, after applying this cover-coat enamel on the ground-coat enamel of the different colours of smooth porcelain base, will form the irregular vertical reticulate pattern formula decorative pattern of different colours;
The 3rd, after applying this cover-coat enamel on the ground-coat enamel of the different colours of concavo-convex porcelain base, form irregular scalelike mark, perhaps horizontal netted decorative pattern.
Above-mentioned cover-coat enamel is burnt till the discussion of mechanism according to the inventor, recognize: be applied to the porcelain molding blank and (both referred to smooth base substrate, also comprise the concave-convex type base substrate) on this cover-coat enamel, cohesion and on the molding blank that porcelain mud is made, form irregular perpendicular line reticulate pattern, scalelike mark gradually in the furnace heating-up process, perhaps horizontal reticulate pattern.The formation of these three kinds of form decorative patterns, in fact the surface finish with the forming process of ceramics base substrate is closely related: one, when the forming process of ceramics billet surface was smooth shiny surface, this kind cover-coat enamel promptly formed vertical reticulate pattern 1 as shown in Figure 1; Simultaneously in the forming process of this decorative pattern, because the cohesion of cover-coat enamel is finished gradually, under action of gravity, form and drip the effect of dropping down downwards, this vertical reticulate pattern 1 that the porcelain surface is formed has that the top color is slightly shallow, streakline is slightly thin, and deepen gradually to the bottom, the natural beauty phenomenon of chap.
Its two, when the porcelain base substrate that is adopted, when making rough fish phosphorus hole shape, described this cover-coat enamel is cohesion and form scalelike mark as shown in Figure 22 in a compact mass on the molding blank that porcelain mud is made gradually in the furnace heating-up process;
They are three years old, when the porcelain base substrate that is adopted, when making horizontal local circular step, described this cover-coat enamel is cohesion and form the horizontal reticulate pattern 3 that horizontal ring-type decorative pattern as shown in Figure 3 combines with vertical reticulate pattern on the molding blank that porcelain mud is made gradually in the furnace heating-up process.
The frit that adopts among the present invention program is the general a kind of material of the industry, come from professional production producer, this molten fast constitutive material is as follows: silicon-dioxide 58.3%, aluminium sesquioxide 10.17%, ferric oxide 0.08%, calcium oxide 10.44%, magnesium oxide 0.12%, potassium oxide 6.96%, sodium oxide 4.36%, Lithium Oxide 98min 0.29%, boron oxide 9.27%.

Claims (6)

1, a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily is characterized in that: the raw material of described cover-coat enamel following (by weight percentage): quartz 8~13%, calcite 25~35%, aluminum oxide 2~4%, ferric oxide 8%, barium carbonate 3~6%, cobalt oxide 1%, frit 6~13%, clay 30~37%; Wherein the constitutive material of frit is: silicon-dioxide 58.3%, aluminium sesquioxide 10.17%, ferric oxide 0.08%, calcium oxide 10.44%, magnesium oxide 0.12%, potassium oxide 6.96%, sodium oxide 4.36%, Lithium Oxide 98min 0.29%, boron oxide 9.27%.
2, a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily as claimed in claim 1, it is characterized in that: in the various raw materials of described cover-coat enamel, particle diameter accounts for more than 98% of raw material gross weight less than 200 purpose granule materials.
3, a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily as claimed in claim 1, it is characterized in that: the firing temperature of described cover-coat enamel is at 1200~1260 ℃.
4, a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily as claimed in claim 1, it is characterized in that: described cover-coat enamel forms irregular vertical reticulate pattern (1) when using on smooth porcelain base substrate.
5, a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily as claimed in claim 1, it is characterized in that: described cover-coat enamel then forms irregular scalelike mark (2) on concavo-convex moulding porcelain base.
6, a kind of cover-coat enamel that can generate vertical reticulate pattern, scalelike mark or horizontal reticulate pattern voluntarily as claimed in claim 1, it is characterized in that: described cover-coat enamel forms the horizontal reticulate pattern (3) that the ring-type decorative pattern combines with vertical reticulate pattern on horizontal local ring-type step porcelain base substrate.
CNB2005100312409A 2005-02-02 2005-02-02 Overglaze capable of automatically forming vertical cob-webbing, fish scale webbing or lateral cob-webbing and is use Expired - Fee Related CN100337956C (en)