CA2686703C - Asymmetric type bf3 complex as a solvent for an electrolyte solution - Google Patents
Asymmetric type bf3 complex as a solvent for an electrolyte solution Download PDFInfo
- Publication number
- CA2686703C CA2686703C CA2686703A CA2686703A CA2686703C CA 2686703 C CA2686703 C CA 2686703C CA 2686703 A CA2686703 A CA 2686703A CA 2686703 A CA2686703 A CA 2686703A CA 2686703 C CA2686703 C CA 2686703C
- Authority
- CA
- Canada
- Prior art keywords
- complex
- liquid electrolyte
- electrochemical device
- asymmetric type
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A main object of the present invention is to provide an asymmetric type BF3 complex which is useful as a solvent for a liquid electrolyte for electrochemical device, in which the liquid electrolyte has a wide potential window and is particularly excellent in oxidation resistance. To attain the object, the present invention provides an asymmetric type BF3 complex represented by the following general formula (1): (see formula 1) (in the general formula (1), each of R1 and R2 is an alkyl group having 1 to 6 carbon atoms and may be the same or different, and R1 and R2 may be branched or may form a ring).
Description
DESCRIPTION
AN ELECTROLYTE SOLUTION
Technical Field [0001]
The present invention relates to an asymmetric type BF3 complex which can provide a liquid electrolyte for electrochemical device, in which the liquid electrolyte has a wide potential window and is particularly excellent in oxidation resistance.
Background Art
AN ELECTROLYTE SOLUTION
Technical Field [0001]
The present invention relates to an asymmetric type BF3 complex which can provide a liquid electrolyte for electrochemical device, in which the liquid electrolyte has a wide potential window and is particularly excellent in oxidation resistance.
Background Art
[0002]
Conventionally, liquid electrolytes having a lithium salt dissolved in a non-aqueous solvent have been used as liquid electrolytes used in lithium secondary batteries. Furthermore, mixed solvents of ethylene carbonate, propylene carbonate, diethyl carbonates etc. are generally used as the non-aqueous solvent.
Conventionally, liquid electrolytes having a lithium salt dissolved in a non-aqueous solvent have been used as liquid electrolytes used in lithium secondary batteries. Furthermore, mixed solvents of ethylene carbonate, propylene carbonate, diethyl carbonates etc. are generally used as the non-aqueous solvent.
[0003]
These carbonate-based solvents are generally used as the non-aqueous solvent, but suffer from a problem of poor oxidation resistance. Accordingly, there is a demand for hardly oxidized liquid electrolytes, from the viewpoint of improving the performance of lithium secondary batteries. Generally, liquid electrolytes are preferably those hardly undergoing oxidation .......... ............ ............. ...................... ..__.............
Y r and reduction; in order words, liquid electrolytes with a wide potential window are desired.
These carbonate-based solvents are generally used as the non-aqueous solvent, but suffer from a problem of poor oxidation resistance. Accordingly, there is a demand for hardly oxidized liquid electrolytes, from the viewpoint of improving the performance of lithium secondary batteries. Generally, liquid electrolytes are preferably those hardly undergoing oxidation .......... ............ ............. ...................... ..__.............
Y r and reduction; in order words, liquid electrolytes with a wide potential window are desired.
[0004]
On the other hand, lithium secondary batteries having a BF3 complex added to a liquid electrolyte are known. For example, Patent Document 1 discloses a non-aqueous lithium battery using a BF3 complex as a capacity reduction rate-suppressing additive.
Patent Document 1 addresses prevention of a lithium secondary battery from reducing its capacity caused during long-term use by using a BF3 complex as an additive. Patent Document 2 discloses a non-aqueous electrolyte secondary battery comprising a Werner-type complex of boron trifluoride. Patent Document 2 aims at preventing a film of lithium halide such as LiF from generating on the surface of an anode by using a BF3 complex as an additive, thereby suppressing an increase in battery impedance.
On the other hand, lithium secondary batteries having a BF3 complex added to a liquid electrolyte are known. For example, Patent Document 1 discloses a non-aqueous lithium battery using a BF3 complex as a capacity reduction rate-suppressing additive.
Patent Document 1 addresses prevention of a lithium secondary battery from reducing its capacity caused during long-term use by using a BF3 complex as an additive. Patent Document 2 discloses a non-aqueous electrolyte secondary battery comprising a Werner-type complex of boron trifluoride. Patent Document 2 aims at preventing a film of lithium halide such as LiF from generating on the surface of an anode by using a BF3 complex as an additive, thereby suppressing an increase in battery impedance.
[0005]
In both of Patent Documents 1 and 2, however, the BF3 complex is used absolutely as an additive, and the amount of the complex used is very small. Specifically, the amount of the BF3 complex is about 1 to 5% by weight based on the electrolyte in Patent Document 1, and the amount of the BF3 complex is about 0.5 to 5% by weight based on the whole of the liquid electrolyte in Patent Document 2. Furthermore, in Patent Documents 1 and 2, there is absolutely no description to the effect that the performance of the lithium secondary battery is improved by widening the potential window of the liquid electrolyte.
In both of Patent Documents 1 and 2, however, the BF3 complex is used absolutely as an additive, and the amount of the complex used is very small. Specifically, the amount of the BF3 complex is about 1 to 5% by weight based on the electrolyte in Patent Document 1, and the amount of the BF3 complex is about 0.5 to 5% by weight based on the whole of the liquid electrolyte in Patent Document 2. Furthermore, in Patent Documents 1 and 2, there is absolutely no description to the effect that the performance of the lithium secondary battery is improved by widening the potential window of the liquid electrolyte.
[0006]
............ ......_............... .....
4 s Patent Document 3 discloses an electrode active material for lithium secondary battery, which further comprises an amphoteric compound such as a BF3 complex in an electrode active material.
Patent Document 1: Japanese Patent Application Laid-Open (JP-A) No. H11-149943 Patent Document 2: JP-A No. 2000-138072 Patent Document 3: JP-A No. 2005-510017 Disclosure of the Invention Problems to be solved by the invention
............ ......_............... .....
4 s Patent Document 3 discloses an electrode active material for lithium secondary battery, which further comprises an amphoteric compound such as a BF3 complex in an electrode active material.
Patent Document 1: Japanese Patent Application Laid-Open (JP-A) No. H11-149943 Patent Document 2: JP-A No. 2000-138072 Patent Document 3: JP-A No. 2005-510017 Disclosure of the Invention Problems to be solved by the invention
[0007]
The present invention is achieved in view of the above-mentioned situation. A main object of the present invention is to provide an asymmetric type BF3 complex which is useful as a solvent for a liquid electrolyte for electrochemical device, in which the liquid electrolyte has a wide potential window and is particularly excellent in oxidation resistance.
Means for solving the problems
The present invention is achieved in view of the above-mentioned situation. A main object of the present invention is to provide an asymmetric type BF3 complex which is useful as a solvent for a liquid electrolyte for electrochemical device, in which the liquid electrolyte has a wide potential window and is particularly excellent in oxidation resistance.
Means for solving the problems
[0008]
To solve the above-mentioned problems, the present invention provides an asymmetric type BF3 complex represented by the following general formula (1):
To solve the above-mentioned problems, the present invention provides an asymmetric type BF3 complex represented by the following general formula (1):
[0009]
[Chemical Formula 1]
Rl,-o R2 General Formula (1) F
F
[Chemical Formula 1]
Rl,-o R2 General Formula (1) F
F
[0010]
(in the general formula (1) , each of R1 and R2 is an alkyl group having 1 to 6 carbon atoms and may be the same or different, and R1 and R2 may be branched or may form a ring).
In the present invention, an organic molecule (ester) which coordinates to an unoccupied orbital of boron of BF3 has an asymmetric structure to a B-0 binding. Thus, a crystal structure is unlikely to be formed, and a complex having a lower melting point and a lower heat of fusion compare to those of similar symmetric type BF3 complex can be obtained. Thus, the asymmetric type BF3 complex of the present invention is useful, for example, as a solvent for a liquid electrolyte for electrochemical device.
(in the general formula (1) , each of R1 and R2 is an alkyl group having 1 to 6 carbon atoms and may be the same or different, and R1 and R2 may be branched or may form a ring).
In the present invention, an organic molecule (ester) which coordinates to an unoccupied orbital of boron of BF3 has an asymmetric structure to a B-0 binding. Thus, a crystal structure is unlikely to be formed, and a complex having a lower melting point and a lower heat of fusion compare to those of similar symmetric type BF3 complex can be obtained. Thus, the asymmetric type BF3 complex of the present invention is useful, for example, as a solvent for a liquid electrolyte for electrochemical device.
[0011) In the above-mentioned invention, the asymmetric type BF3 complex is preferably a kind of complex selected from the group consisting of the following structural formulae (la) to (lc).
This is because such asymmetric type BF3 complex is useful as a solvent for a liquid electrolyte for electrochemical device.
This is because such asymmetric type BF3 complex is useful as a solvent for a liquid electrolyte for electrochemical device.
[0012]
[Chemical Formula 2]
......................
f Y
F''B
{ { I
F F F
Structural Structural Structural Formula (1 a) Formula (1 b) Formula (1 c)
[Chemical Formula 2]
......................
f Y
F''B
{ { I
F F F
Structural Structural Structural Formula (1 a) Formula (1 b) Formula (1 c)
[0013]
Further, the present invention provides a liquid electrolyte for electrochemical device which comprises the above-mentioned asymmetric type BF3 complex as a solvent.
According to the present invention, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent .
Further, the present invention provides a liquid electrolyte for electrochemical device which comprises the above-mentioned asymmetric type BF3 complex as a solvent.
According to the present invention, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent .
[0014]
Moreover, the present invention provides a liquid electrolyte for electrochemical device comprising an asymmetric type BF3 complex represented by the following general formula (2) as a solvent:
-[0015]
[Chemical Formula 3]
~R4 General Formula (2) F'~B'`'F
F
t r (0016]
(in the general formula (2), each of R3 and R4 is an alkyl group having 1 to 5 carbon atoms and is a different alkyl group).
According to the present invention, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent.
[0017]
In the above-mentioned invention, the asymmetric type BF3 complex is preferably a complex represented by the below-mentioned structural formula (2a). This is because such asymmetric type BF3 complex is useful as a solvent for a liquid electrolyte for electrochemical device.
[0018]
[Chemical Formula 4]
Off/
O Y
O
F
F
Structural Formula (2a) [0019]
Further, the present invention provides a lithium secondary battery comprising: a cathode layer containing a cathode active material, an anode layer containing an anode active material, a separator provided between the cathode layer and the anode layer, and a liquid electrolyte impregnated at least with the ti ......... .... ... .......... ....
separator, characterized in that the liquid electrolyte is the above-explained liquid electrolyte for electrochemical device.
[0020]
According to the present invention, a lithium secondary battery which can be used at a high voltage can be obtained by using a liquid electrolyte comprising the above-mentioned asymmetric type BF3 complex as a solvent.
Effects of the Present Invention [0021]
The present invention attains an effect of providing an asymmetric type BF3 complex which is useful as a solvent for a liquid electrolyte for electrochemical device.
Brief Description of the Drawings [0022]
FIG. 1 shows the results of BF3-GBL Complex obtained by using a DSC.
FIG. 2 shows the results of BF3-EP Complex obtained by using a DSC.
FIG. 3 shows the results of BF3-EMC Complex obtained by using a DSC.
FIG. 4 shows LSV curves of the liquid electrolytes for electrochemical device obtained in Example 2-1 and Comparative Example 2-1.
FIG. 5 shows LSV curves of the liquid electrolytes for electrochemical device obtained in Example 2-2 and Comparative Example 2-2.
FIG. 6 shows LSV curves of the liquid electrolytes for electrochemical device obtained in Example 2-3 and Comparative Example 2-3.
Best Mode for Carrying Out the Invention [0023]
Hereinafter, an asymmetric type BF3 complex, liquid electrolyte for electrochemical device, and a lithium secondary battery of the present invention will be explained.
[0024]
A. Asymmetric Type BF3 Complex First, an asymmetric type BF3 complex of the present invention will be explained. The asymmetric type BF3 complex of the present invention is represented by the above-mentioned general formula (1).
[0025]
In the present invention, an organic molecule (ester) which coordinates to an unoccupied orbital of boron of BF3 has an asymmetric structure to a B-O binding. Thus, a crystal structure is unlikely to be formed, and a complex having a lower melting point and a lower heat of fusion compare to those of similar symmetric type BF3 complex can be obtained. Therefore, the asymmetric type BF3 complex of the present invention is useful, for example, as a solvent for a liquid electrolyte for electrochemical device.
[0026]
r In general, BF3 complexes coordinated with organic molecules at BF3 are solid at room temperature for most cases, and it is necessary to mix the complexes with other organic solvents to use the complexes as solvents for liquid electrolyte for electrochemical devices. At that time, when a melting point is high and a melting energy is strong for a BF3 complex, it is necessary to mix a large amount of organic solvents in order to obtain a liquid mixed solvent at room temperature. Thus, there is a problem of lowering an electrochemical stability, which is a feature of a BF3 complex. In the present invention, an asymmetric type BF3 complex in which symmetric properties of an organic molecule is intentionally broken is used in order to make the formation of a crystal structure difficult. Thereby, it becomes possible to lower a melting point and heat of fusion of the asymmetric type BF3 complex compare to those of similar symmetric type BF3 complex. As a result, an asymmetric type BF3 complex which can be singularly used as a solvent, or an asymmetric type BF3 complex which becomes a liquid by adding a small amount of an organic solvent can be obtained.
[0027]
That is, the asymmetric type BF3 complex of the present invention is very useful as a solvent for a liquid electrolyte for electrochemical device. Therefore, in the present invention, it is possible to provide a solvent for a liquid electrolyte for electrochemical device represented by the above-mentioned general formula (1).
[00281 In the general formula (1), each of R, and R2 is generally an alkyl group having 1 to 6 carbon atoms. The number of the carbon atoms is preferably within the range of 1 to 3, and more preferably within the range of 1 to 2. Each of R, and R2 may be an alkyl group not branched or a branched alkyl group, but an alkyl group not branched is preferable. Further, R, and R2 may be the same of different. In the present invention, R1 and R2 maybe branched or may forma ring. In particular, it is preferable in the present invention that an ester molecule which coordinates to BF3 has a five-membered ring or six- membered ring.
[0029]
In the present invention, the ester molecule which coordinates to BF3 may be a cyclic ester or a chain ester. As examples of the cyclic ester, gamma-butyrolactone (GBL) and gamma-valerolactone (GVL) can be cited. As examples of the chain ester, ethyl propionate (EP), methyl propionate (MP), ethyl acetate (EA), and methyl acetate (MA) can be cited.
[0030]
In the present invention, the asymmetric type BF3 complex is a kind of complex selected from the group consisting of the following structural formulae (la) to (lc) . This is because such asymmetric type BF3 complex is particularly useful as a solvent for a liquid electrolyte for electrochemical device. In the present invention, the structural formula (la) may be referred to "BF3-GBL complex", the structural formula (lb) maybe referred to "BF3-EP complex", and the structural formula (lc) may be referred to "BF3-MP complex".
[0031]
[Chemical Formula 5]
O N"~"'O O
O O O
F----B-,F F----B-IF F''B`'F
F F F
Structural Structural Structural Formula (1 a) Formula (1 b) Formula (1 c) [0032]
A method of producing an asymmetric type BF3 complex of the present invention is not particularly limited. As an example, a method of aerate a BF3 gas to a raw material ester can be cited.
The asymmetric type BF3 complex can be identified, for example, by a carbon-nuclear magnetic resonance method (13C-NMR method) and a hydrogen-nuclear magnetic resonance method (1H-NMRmethod) .
[0033]
B. Liquid Electrolyte for Electrochemical Device Next, a liquid electrolyte for electrochemical device of the present embodiment will be explained. The liquid electrolyte for electrochemical device of the present invention comprises the asymmetric type BF3 complex as a solvent. The liquid electrolyte for electrochemical device can be roughly divided into two embodiments according to the technical structure of the asymmetric type BF3 complex. Hereinafter, the liquid electrolyte for electrochemical device of the present invention will be explained by way of the first and second embodiments.
[0034]
1. First Embodiment First, a first embodiment of the liquid electrolyte for electrochemical device of the present invention will be explained.
A liquid electrolyte for electrochemical device of the present embodiment comprises the asymmetric type BF3 complex represented by the above-mentioned general formula (1) as a solvent.
[0035]
According to the present embodiment, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent.
As an acidity of the BF3 part is very strong in the asymmetric type BF3 complex used in the present embodiment, an electron of a coordinating organic molecule (ester) is pulled to the BF3 part.
Thus, an oxidation resistance of the organic molecule part in the complex improves and a liquid electrolyte having a wide potential window can be obtained.
[0036]
Moreover, as explained in the above-mentioned section of "A. Asymmetric Type BF3 Complex", the asymmetric type BF3 complex used in the present embodiment has an asymmetric structure. Thus, it is possible to lower a melting point and heat of fusion of the asymmetric type BF3 complex compare to those of similar symmetric type BF3 complex. Accordingly, for example, even if the asymmetric type BF3 complex is solid at room temperature, the complex can be made to a liquid by adding a small amount ........ _.... ...._._ of an organic solvent. Therefore, it has an advantage of providing a wide selection in the solvent composition.
[0037]
The liquid electrolyte for electrochemical device of the present embodiment comprises the above-mentioned asymmetric type BF3 complex represented by the general formula (1) as a solvent.
In the present embodiment, the asymmetric type BF3 complex is contained by, generally 10 % by weight or more to all of the solvent, preferably 20 % by weight or more, and more preferably 50 % by weight or more.
Hereinafter, the liquid electrolyte for electrochemical device of the present embodiment will be explained by each technical structure.
[0038]
(1) Asymmetric Type BF3 Complex An asymmetric type BF3 complex used in the present embodiment is similar to that explained in the above-mentioned section of "A. Asymmetric Type BF3 Complex".
[0039]
In particular, in the present embodiment, an ester molecule which coordinates to BF3 of the asymmetric type BF3 complex is preferably a cyclic ester. Specifically, the cyclic ester is preferably GBL or GVL, and more preferably GBL. In other words, in the present embodiment, the asymmetric type BF3 complex is preferably BF3-GBL complex (a complex presented by the above-mentioned structural formula (1a)). Thereby, a liquid electrolyte for electrochemical device significantly excellent in oxidation resistance can be obtained. Specifically, as it will be explained later, an oxidation resistance of the liquid electrolyte for electrochemical device obtained significantly improves when a mixed solvent of DEC and BF3-GBL complex is used compare to a case when a mixed solvent of diethyl carbonate (DEC) and ethylene carbonate (EC) is used.
[0040]
Further, in the present embodiment, the asymmetric type BF3 complex is preferably a BF3-MP complex (complex represented by the above-mentioned structural formula (ic)). Thereby, a liquid electrolyte for electrochemical device excellent not only in an oxidation resistance but also in reduction-resistance can be obtained. The reason of having excellent reduction-resistance is not necessarily clear, but is thought that the asymmetric type BF3 complex forms a good film by being reducted and decomposed. Substance MP (methyl propionate) becomes a complex by coordinating to BF3 and its oxidation resistance is significantly improved. When the oxidation resistance is improved, the reduction-resistance may sometimes be relatively lowered. However, when a BF3-MP complex is used, a unique effect of improving also the reduction-resistance can be attained.
[0041]
(2) Solvent for Liquid Electrolyte for Electrochemical Device In the present embodiment, the asymmetric type BF3 complex represented by the above-mentioned general formula (1) is used as a solvent. For example, when a melting point of the asymmetric type BF3 complex is sufficiently low, solvents used for the liquid electrolyte for electrochemical device may all be asymmetric type BF3 complexes. On the other hand, when a melting point of the asymmetric type BF3 complex is higher than room temperature, solvents other than the asymmetric type BF3 complex is generally used. As the asymmetric type BF3 complex used in the present embodiment has a low heat of fusion, it has an advantage of providing a wide selection in the solvent composition. The preferable solvent composition is the same as those explained above.
[0042]
As examples of solvents other than the asymmetric type BF3 complex, carbonates such as ethylene carbonate (EC) , propylene carbonate (PC),dimethyl carbonate (DMC),diethyl carbonate (DEC), and ethylmethyl carbonate (EMC); ethers such as dimethyl ether, diethyl ether, tetrahydrofuran (THF), and methyltetrahydrofuran; nitriles such as methoxypropionitrile and acetonitrile; esters such as methyl acetate; amines such as triethylamine; alcohols such as methanol; and ketones such as acetone, can be cited. Among them, carbonates are preferable.
Further, an organic molecule which coordinates to BF3 of the asymmetric type BF3 complex can be used as solvents other than the asymmetric type BF3 complex.
[0043) (3) Electrolyte of Liquid Electrolyte for Electrochemical Device An electrolyte used in the present embodiment is not _............. .................. .................. ........ ..... .... ....
...
particularly limited as long as it is dissolved in a solvent which contains the asymmetric type BF3 complex. The type of the electrolyte varies depending on the use of the liquid electrolyte.
As examples, Li salts, Na salts, and quaternary ammonia salts can be cited, and Li salts are preferable among them. This is because they can be used in lithium secondary batteries.
[0044]
As the Li salts, a general Li salts may be used and not particularly limited. For example, LiN (SO2CF3) 2 (in some cases also referred to LiTFSI), LiN(S02C2F5)2 (in some cases also referred to LiBETI) , LiC104, LiBF4, and LiPF6 can be cited. Among them, LiN (S02CF3) 2 and LiN (S02C2F5) 2 are preferable. This is because the lithium imide salts such as LiTFSI and LiBETI have high decomposition temperature and can restrain the generation of hydrogen fluoride (HF).
[0045]
A density of the electrolyte of the liquid electrolyte for electrochemical device is not particularly limited, and it is the same as the density of a general electrolyte. Although it is not particularly limited, it is normally about 1 mol/L.
[0046]
(4) Others As examples of an application of the liquid electrolyte for electrochemical device of the present embodiment, a secondary battery, capacitor, or sensor can be cited. Among them, a secondary battery and capacitor are preferable, and a secondary battery is particularly preferable. Further, even among the secondary batteries, it is preferable to use the liquid electrolyte for electrochemical device of the present embodiment as a lithium secondary battery.
[0047]
2. Second Embodiment Next, a second embodiment of a liquid electrolyte for electrochemical device of the present invention will be explained.
The liquid electrolyte for electrochemical device of the present embodiment comprises an asymmetric type BF3 complex represented by the below-mentioned general formula (2) as a solvent:
[0048]
(Chemical Formula 6]
Q~_' General Formula(2) FB-_F
F
[0049]
(in the general formula (2), each of R3 and R4 is an alkyl group having 1 to 5 carbon atoms and is a different alkyl group).
According to the present embodiment, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent.
As an acidity of the BF3 part is very strong in the asymmetric type BF3 complex used in the present embodiment, an electron of a coordinating organic molecule (carbonate) is pulled to the ... ... _... _........ ..... ..._ ..... _ ......
BF3 part. Thus, an oxidation resistance of the organic molecule part in the complex improves and a liquid electrolyte having a wide potential window can be obtained.
[0050]
Moreover, as explained in the above-mentioned section of "A. Asymmetric Type BF3 Complex", the asymmetric type BF3 complex used in the present embodiment also has an asymmetric structure.
Thus, it is possible to lower a melting point and heat of fusion of the asymmetric type BF3 complex compare to those of similar symmetric type BF3 complex. Accordingly, for example, even if the asymmetric type BF3 complex is solid at room temperature, the complex can be made to liquid by adding a small amount of an organic solvent. Therefore, it has an advantage of providing a wide selection in the solvent composition.
[0051]
The liquid electrolyte for electrochemical device of the present embodiment comprises the above-mentioned asymmetric type BF3 complex represented by the general formula (2) as a solvent.
In the present embodiment, the asymmetric type BF3 complex is contained by, generally 10 % by weight or more to all of the solvent, preferably 20 % by weight or more, and more preferably 50 % by weight or more.
Hereinafter, the liquid electrolyte for electrochemical device of the present embodiment will be explained by each technical structure.
[0052) (1) Asymmetric Type BF3 Complex First, an asymmetric type BF3 complex used in the present embodiment will be explained. The asymmetric type BF3 complex used in the present embodiment is represented by the above-mentioned general formula (2) . As the asymmetric type BF3 complex used in the present embodiment has an asymmetric structure, it is very useful as a solvent for a liquid electrolyte for electrochemical device similarly to the case of the above-explained first embodiment. Therefore, it is possible in the present embodiment to provide the solvent for a liquid electrolyte for electrochemical device represented by the above-mentioned general formula (2).
[0053]
In the general formula (2), each of R3 and R4 is generally an alkyl group having 1 to 5 carbon atoms. The number of the carbon atoms is preferably within the range of 1 to 3, and more preferably within the range of 1 to 2. Each of R3 and R4 may be an alkyl group not branched or a branched alkyl group, but an alkyl group not branched is preferable. Further, R3 and R4 are different alkyl group. This is because, if they are the same alkyl group, the asymmetric type BF3 complex cannot have an asymmetric structure.
[0054]
In particular, in the present embodiment, the asymmetric type BF3 complex is preferably a complex represented by the below-mentioned structural formula (2a). This is because such asymmetric type BF3 complex is useful as a solvent for a liquid .............. ............ _.._..........
..........._..........._...........,_......_........... .
electrolyte for electrochemical device. In the present embodiment, the structural formula (2a) may sometimes be referred as "BF3-EMC complex".
[0055]
[Chemical Formula 7]
0 Y 0,,,,,-O
F---B-'`F
F
Structural Formula (2a) [0056]
A method of producing an asymmetric type BF3 complex of the present embodiment is not particularly limited. As an example, a method of aerate a BF3 gas to a raw material carbonate can be cited. The asymmetric type BF3 complex can be identified, for example, by a carbon-nuclear magnetic resonance method (13C-NMR
method) and a hydrogen-nuclear magnetic resonance method (1H-NMR
method).
[0057]
(2) Solvent for Liquid Electrolyte for Electrochemical Device In the present embodiment, an asymmetric type BF3 complex represented by the above-mentioned general formula (2) is used as a solvent. For example, when a melting point of the asymmetric type BF3 complex is sufficiently low, solvents used for the liquid electrolyte for electrochemical device may all be asymmetric type BF3 complexes. On the other hand, when a melting point of the asymmetric type BF3 complex is higher than room temperature, solvents other than the asymmetric type BF3 complex is generally used. As the asymmetric type BF3 complex used in the present embodiment has a low heat of fusion, it has an advantage of providing a wide selection in the solvent composition. The preferable solvent composition is the same those as explained above.
[0058]
As solvents other than the asymmetric type BF3 complex is the same to those explained in the above-mentioned section of "1. First Embodiment", explanation here is omitted. Further, the electrolyte, the application of the liquid electrolyte for electrochemical device, and other factors of the present embodiment are the same to those explained in the above-mentioned section of "1. First Embodiment", explanation here is omitted.
[00591 C. Lithium Secondary Battery Next, a lithium secondary battery of the present invention will be explained. The lithium secondary battery of the present invention comprises: a cathode layer containing a cathode active material, an anode layer containing an anode active material, a separator provided between the cathode layer and the anode layer, and a liquid electrolyte impregnated at least with the separator, characterized in that the liquid electrolyte is the liquid electrolyte for electrochemical device explained above.
[0060]
According to the present invention, a lithium secondary battery which can be used at a high voltage can be obtained by using a liquid electrolyte comprising the above-mentioned asymmetric type BF3 complex as a solvent.
[0061]
The lithium secondary battery of the present invention comprises at least a cathode layer, an anode layer, a separator, and a liquid electrolyte. As the liquid electrolyte is the same to that explained in the above-mentioned section of "B. Liquid Electrolyte for Electrochemical Device", explanation here is omitted.
[0062]
The cathode layer used in the present invention contains at least a cathode active material. As examples of the cathode active material, LiCoO2, LiMn2O4, LiNi02, LiNi0 8Coo.202, LiNi1/3Mn1/3Co1/302r LiNio.5Mno.502, LiNio.5Mni.504, LiCoPO4, LiMnPO4r LiFePO4 can be cited. Among them, LiCo02 is preferable. Further, the cathode active material generally contains a conductive material and a binder. As examples of the conductive material, carbon black and acetylene black can be cited. As examples of thebinder, fluorine--based resins such as polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), and ethylenetetrafluoroethylene (ETFE) can be cited. Further, the lithium secondary battery of the present invention generally comprises a cathode active material which corrects current of a cathode layer. As examples of a material for the cathode current collector, aluminum, stainless, nickel, iron, and titanium can be cited.
[0063]
The anode layer used in the present invention contains at least an anode active material. As examples of the anode active material, metal lithium, a lithium alloy, metal oxide, metal sulfide, metal nitride, and carbon material such as graphite can be cited. Among them, graphite is preferable. The anode layer may contain a conductive material and a binder as needed.
As for the conductive material and the binder, the same materials as the cathode layer can be used. Further, the lithium secondary battery of the present invention normally comprises an anode current collector which corrects currents of the anode layer.
As examples of a material for the anode current collector, copper, stainless, and nickel can be cited.
[0064]
As for the separator used in the present invention, the same materials as the separator substrates used in general lithium secondary batteries can be used, and thus, not particularly limited. For example, resins such as polyethylene (PE), polypropylene (PP), polyester, cellulose, and polyamide can be cited. Among them, polyethylene and polypropylene are preferable . Further, a shape of a battery case used in the present invention is not particularly limited as long as it can store the above-mentioned cathode layer, anode layer, and a separator.
As specific example, a cylindrical type, a square type, a coin type, and a laminate type can be cited.
[0065) EXAMPLES
[0066]
The present invention will be further specifically explained by way of examples.
[Example 1-1]
Prepared as a raw material ester was gamma -butyrolactone (GBL) and it was aerated with a BF3 gas in 0 C nitrogen atmosphere for 20 minutes or longer. A white liquid was obtained consequently. The obtained liquid was filtered and a solid was removed, and thereby, a white BF3-GBL complex was obtained.
Next, a melting point and a heat of fusion of the obtained BF3-GBL complex were measured. Measurement was conducted by sealing the BF3-GBL complex in a SUS closed container, using a differential scanning calorimeter (DSC), and setting the temperature rising conditions to 2 C/minute and the upper limit of the temperature to 180 C. As a result, as shown in FIG. 1, a melting point of the BF3-GBL complex was 70.23 C, and a heat of fusion thereof was 54.16 J/g.
[0067]
[Example 1-2]
A BF3-EP complex was obtained in the same manner as in Example 1-1 except that ethyl propionate (EP) was used as a raw material ester.
Next, a melting point and a heat of fusion of the obtained BF3-EP complex were measured in the same manner as in Example 1-1. As shown in FIG. 2, a melting point of the BF3-EP complex was 43.06 C, and a heat of fusion thereof was 76.30 J/g.
[0068]
[Example 1-3]
A BF3-MP complex was synthesized in the same manner as in Example 1-1 except that methyl propionate (MP) was used as a raw material ester. In the present example, the obtained liquid was filtered while it was cooled down after aerated with a BF3 gas, and a solid was removed. The obtained BF3-MP complex was liquid at room temperature.
[0069]
[Example 1-4]
A BF3-EMC complex was obtained in the same manner as in Example 1-1 except that ethyl methyl carbonate (EMC) was used as a raw material carbonate instead of raw material ester.
Next, a melting point and a heat of fusion of the obtained BF3-EMC complex were measured in the same manner as in Example 1-1. As shown in FIG. 3, a melting point of the BF3-EMC complex was 65.43 C, and a heat of fusion thereof was 63.98 J/g.
[0070]
[Comparative Example 1-1]
A BF3-DMC complex was obtained in the same manner as in Example 1-1 except that diethyl carbonate (DMC) was used as a symmetric type organic molecule.
Next, a melting point and a heat of fusion of the obtained BF3-DMC complex were measured in the same manner as in Example 1-1. A melting point of the BF3-DMC complex was 110.79 t, and a heat of fusion thereof was 125.5 J/g.
[0071]
[Comparative Example 1-2]
A BF3-DEC complex was obtained in the same manner as in Example 1-1 except that diethyl carbonate (DMC) was used as a symmetric type organic molecule.
Next, a melting point and a heat of fusion of the obtained BF3-DEC complex were measured in the same manner as in Example 1-1. A melting point of the BF3-DEC complex was 58.45 C, and a heat of fusion thereof was 156.4 J/g.
The above-mentioned results are shown in below Table 1.
[0072]
[Table 13 Melting Point Heat of Fusion Complex ( C) (J/g) Example 1-1 BF3-GBL 70.23 54.16 Example 1-2 BF3-EP 43.06 76.30 Room Example 1-3 BF3-MP Temperature or -Lower Example 1-4 BF3-EMC 65.43 63.98 Comparative BF3-DMC 110.79 125.5 Example 1-1 Comparative BF3-DEC 58.45 156.4 Example 1-2 [0073]
As apparent fromTable 1, all complexes obtained in examples showed low melting points and heat of fusion. In contrast, the symmetric type organic molecule of Comparative Example 1-1 showed high value in both of melting point and heat of fusion. Further, the symmetric type organic molecule of Comparative Example 1-2 showed low melting point, but also showed high heat of fusion, so that it was necessary to add a large amount of other organic solvent to obtain a liquid electrolyte in a liquid state at room temperature.
[0074]
[Example 2-1]
A BF3-GBL complex obtained in Example 1-1 and diethyl carbonate (DEC) was mixed so as the mol ratio thereof becomes $
1:1, and a homogenous mixed solvent was obtained. Subsequently, LiPF6was dissolved by 1M to the obtained mixed solvent and a liquid electrolyte for electrochemical device was obtained.
[0075]
[Comparative Example 2-1]
A liquid electrolyte for electrochemical device was obtained in the same manner as in Example 2-1 except that ethylene carbonate (EC) was used instead of a BF3-GBL complex.
[0076]
[Evaluation]
The oxidation potential of the respective liquid electrolyte for electrochemical device obtained in Example 2-1 and Comparative Example 2-1 were measured. Measurement was conducted by using a three electrode cell provided with glassy carbon for a working electrode, lithium metals for a counter electrode and a reference electrode, and under a linear sweep voltammetric technique. At the time of measuring, potential of the working electrode was swept from the immersed potential to the high potential side. The sweep speed was 5 mVsec-1.
The results (LSV curves) are shown in FIG. 4. As shown in FIG. 4, with the liquid electrolyte for electrochemical device of Comparative Example 2-1, elevation in current value were confirmed from the potential of about 6.5 VvsLi/Li+. When glassy carbon is used for a working electrode, no particularly active RedOx series is present in electrodes and a solution. Thus, the current confirmed here is thought to be caused by oxidative decomposition of the liquid electrolyte itself. In contrast, with the liquid electrolyte for electrochemical device of Comparative Example 2-1, no substantial current was flowing even at potentials higher than 6.5 VvsLi/Li+. Thus, the liquid electrolyte for electrochemical device of the present invention was found excellent in oxidation resistance.
[0077]
[Example 2-2]
A BF3-MP complex obtained in Example 1-3 and diethyl carbonate (DEC) was mixed so as the mol ratio thereof becomes 1:1, and a homogenous mixed solvent was obtained. Subsequently, LiPF6 was dissolved by 1M to the obtained mixed solvent and a liquid electrolyte for electrochemical device was obtained.
[0078]
[Comparative Example 2-21 A liquid electrolyte for electrochemical device was obtained in the same manner as Example 2-2 except that ethylene carbonate (EC) was used instead of a BF3-MP complex.
[0079]
[Evaluation]
The reduction potential of the respective liquid electrolyte for electrochemical device obtained in Example 2-2 and Comparative Example 2-2 were measured. Measurement was conducted by using a three electrode cell provided with glassy carbon for a working electrode, lithium metals for a counter electrode and a reference electrode, and under a linear sweep voltammetric technique. At the time of measuring, potential of the working electrode was swept from the immersed potential to the low potential side. The sweep speed was 5 mVsec-1.
The results (LSV curves) are shown in FIG. 5. As shown in FIG. 5, with the liquid electrolyte for electrochemical device of Comparative Example 2-2, reduction current were confirmed from the potential of about 0.5 VvsLi/Li+. This is thought to be caused by reductive degradation of the liquid electrolyte itself. In contrast, with the liquid electrolyte for electrochemical device of Comparative Example 2-2, no substantial current was flowing until 0.2 VvsLi/Li+. Thus, it was confirmed that the reduction-resistance of the liquid electrolyte was improved.
[0080]
[Example 2-3]
A BF3-EMC complex obtained in Example 1-4 and EMC was mixed so as the mol ratio thereof becomes 1: 1, and a homogenous mixed solvent was obtained. Subsequently, LiTFSI was dissolved by 1M
to the obtained mixed solvent and a liquid electrolyte for electrochemical device was obtained.
[0081]
[Comparative Example 2-3]
A liquid electrolyte for electrochemical device was obtained in the same manner as Example 2-3 except that only EMC
was used as a solvent.
[0082]
[Evaluation]
The oxidation potential of the respective liquid electrolyte for electrochemical device obtained in Example 2-3 and Comparative Example 2-3 were measured. Measurement was conducted by using a three electrode cell provided with glassy carbon for a working electrode, lithium metals for a counter electrode and a reference electrode, and under a linear sweep voltammetric technique. At the time of measuring, potential of the working electrode was swept from the immersed potential to the high potential side. The sweep speed was 5 mVsec-1.
The results (LSV curves) are shown in FIG. 6. As shown in FIG. 6, with the liquid electrolyte for electrochemical device of Comparative Example 2-3, elevation in current value were confirmed from the potential of about 5. 2 VvsLi /Li+. In contrast, with the liquid electrolyte for electrochemical device of Example 2-3, no substantial current was flowing until about 5.6 VvsLi/Li+.
Thus, the liquid electrolyte for electrochemical device of the present invention was found excellent in oxidation resistance.
Moreover, the present invention provides a liquid electrolyte for electrochemical device comprising an asymmetric type BF3 complex represented by the following general formula (2) as a solvent:
-[0015]
[Chemical Formula 3]
~R4 General Formula (2) F'~B'`'F
F
t r (0016]
(in the general formula (2), each of R3 and R4 is an alkyl group having 1 to 5 carbon atoms and is a different alkyl group).
According to the present invention, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent.
[0017]
In the above-mentioned invention, the asymmetric type BF3 complex is preferably a complex represented by the below-mentioned structural formula (2a). This is because such asymmetric type BF3 complex is useful as a solvent for a liquid electrolyte for electrochemical device.
[0018]
[Chemical Formula 4]
Off/
O Y
O
F
F
Structural Formula (2a) [0019]
Further, the present invention provides a lithium secondary battery comprising: a cathode layer containing a cathode active material, an anode layer containing an anode active material, a separator provided between the cathode layer and the anode layer, and a liquid electrolyte impregnated at least with the ti ......... .... ... .......... ....
separator, characterized in that the liquid electrolyte is the above-explained liquid electrolyte for electrochemical device.
[0020]
According to the present invention, a lithium secondary battery which can be used at a high voltage can be obtained by using a liquid electrolyte comprising the above-mentioned asymmetric type BF3 complex as a solvent.
Effects of the Present Invention [0021]
The present invention attains an effect of providing an asymmetric type BF3 complex which is useful as a solvent for a liquid electrolyte for electrochemical device.
Brief Description of the Drawings [0022]
FIG. 1 shows the results of BF3-GBL Complex obtained by using a DSC.
FIG. 2 shows the results of BF3-EP Complex obtained by using a DSC.
FIG. 3 shows the results of BF3-EMC Complex obtained by using a DSC.
FIG. 4 shows LSV curves of the liquid electrolytes for electrochemical device obtained in Example 2-1 and Comparative Example 2-1.
FIG. 5 shows LSV curves of the liquid electrolytes for electrochemical device obtained in Example 2-2 and Comparative Example 2-2.
FIG. 6 shows LSV curves of the liquid electrolytes for electrochemical device obtained in Example 2-3 and Comparative Example 2-3.
Best Mode for Carrying Out the Invention [0023]
Hereinafter, an asymmetric type BF3 complex, liquid electrolyte for electrochemical device, and a lithium secondary battery of the present invention will be explained.
[0024]
A. Asymmetric Type BF3 Complex First, an asymmetric type BF3 complex of the present invention will be explained. The asymmetric type BF3 complex of the present invention is represented by the above-mentioned general formula (1).
[0025]
In the present invention, an organic molecule (ester) which coordinates to an unoccupied orbital of boron of BF3 has an asymmetric structure to a B-O binding. Thus, a crystal structure is unlikely to be formed, and a complex having a lower melting point and a lower heat of fusion compare to those of similar symmetric type BF3 complex can be obtained. Therefore, the asymmetric type BF3 complex of the present invention is useful, for example, as a solvent for a liquid electrolyte for electrochemical device.
[0026]
r In general, BF3 complexes coordinated with organic molecules at BF3 are solid at room temperature for most cases, and it is necessary to mix the complexes with other organic solvents to use the complexes as solvents for liquid electrolyte for electrochemical devices. At that time, when a melting point is high and a melting energy is strong for a BF3 complex, it is necessary to mix a large amount of organic solvents in order to obtain a liquid mixed solvent at room temperature. Thus, there is a problem of lowering an electrochemical stability, which is a feature of a BF3 complex. In the present invention, an asymmetric type BF3 complex in which symmetric properties of an organic molecule is intentionally broken is used in order to make the formation of a crystal structure difficult. Thereby, it becomes possible to lower a melting point and heat of fusion of the asymmetric type BF3 complex compare to those of similar symmetric type BF3 complex. As a result, an asymmetric type BF3 complex which can be singularly used as a solvent, or an asymmetric type BF3 complex which becomes a liquid by adding a small amount of an organic solvent can be obtained.
[0027]
That is, the asymmetric type BF3 complex of the present invention is very useful as a solvent for a liquid electrolyte for electrochemical device. Therefore, in the present invention, it is possible to provide a solvent for a liquid electrolyte for electrochemical device represented by the above-mentioned general formula (1).
[00281 In the general formula (1), each of R, and R2 is generally an alkyl group having 1 to 6 carbon atoms. The number of the carbon atoms is preferably within the range of 1 to 3, and more preferably within the range of 1 to 2. Each of R, and R2 may be an alkyl group not branched or a branched alkyl group, but an alkyl group not branched is preferable. Further, R, and R2 may be the same of different. In the present invention, R1 and R2 maybe branched or may forma ring. In particular, it is preferable in the present invention that an ester molecule which coordinates to BF3 has a five-membered ring or six- membered ring.
[0029]
In the present invention, the ester molecule which coordinates to BF3 may be a cyclic ester or a chain ester. As examples of the cyclic ester, gamma-butyrolactone (GBL) and gamma-valerolactone (GVL) can be cited. As examples of the chain ester, ethyl propionate (EP), methyl propionate (MP), ethyl acetate (EA), and methyl acetate (MA) can be cited.
[0030]
In the present invention, the asymmetric type BF3 complex is a kind of complex selected from the group consisting of the following structural formulae (la) to (lc) . This is because such asymmetric type BF3 complex is particularly useful as a solvent for a liquid electrolyte for electrochemical device. In the present invention, the structural formula (la) may be referred to "BF3-GBL complex", the structural formula (lb) maybe referred to "BF3-EP complex", and the structural formula (lc) may be referred to "BF3-MP complex".
[0031]
[Chemical Formula 5]
O N"~"'O O
O O O
F----B-,F F----B-IF F''B`'F
F F F
Structural Structural Structural Formula (1 a) Formula (1 b) Formula (1 c) [0032]
A method of producing an asymmetric type BF3 complex of the present invention is not particularly limited. As an example, a method of aerate a BF3 gas to a raw material ester can be cited.
The asymmetric type BF3 complex can be identified, for example, by a carbon-nuclear magnetic resonance method (13C-NMR method) and a hydrogen-nuclear magnetic resonance method (1H-NMRmethod) .
[0033]
B. Liquid Electrolyte for Electrochemical Device Next, a liquid electrolyte for electrochemical device of the present embodiment will be explained. The liquid electrolyte for electrochemical device of the present invention comprises the asymmetric type BF3 complex as a solvent. The liquid electrolyte for electrochemical device can be roughly divided into two embodiments according to the technical structure of the asymmetric type BF3 complex. Hereinafter, the liquid electrolyte for electrochemical device of the present invention will be explained by way of the first and second embodiments.
[0034]
1. First Embodiment First, a first embodiment of the liquid electrolyte for electrochemical device of the present invention will be explained.
A liquid electrolyte for electrochemical device of the present embodiment comprises the asymmetric type BF3 complex represented by the above-mentioned general formula (1) as a solvent.
[0035]
According to the present embodiment, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent.
As an acidity of the BF3 part is very strong in the asymmetric type BF3 complex used in the present embodiment, an electron of a coordinating organic molecule (ester) is pulled to the BF3 part.
Thus, an oxidation resistance of the organic molecule part in the complex improves and a liquid electrolyte having a wide potential window can be obtained.
[0036]
Moreover, as explained in the above-mentioned section of "A. Asymmetric Type BF3 Complex", the asymmetric type BF3 complex used in the present embodiment has an asymmetric structure. Thus, it is possible to lower a melting point and heat of fusion of the asymmetric type BF3 complex compare to those of similar symmetric type BF3 complex. Accordingly, for example, even if the asymmetric type BF3 complex is solid at room temperature, the complex can be made to a liquid by adding a small amount ........ _.... ...._._ of an organic solvent. Therefore, it has an advantage of providing a wide selection in the solvent composition.
[0037]
The liquid electrolyte for electrochemical device of the present embodiment comprises the above-mentioned asymmetric type BF3 complex represented by the general formula (1) as a solvent.
In the present embodiment, the asymmetric type BF3 complex is contained by, generally 10 % by weight or more to all of the solvent, preferably 20 % by weight or more, and more preferably 50 % by weight or more.
Hereinafter, the liquid electrolyte for electrochemical device of the present embodiment will be explained by each technical structure.
[0038]
(1) Asymmetric Type BF3 Complex An asymmetric type BF3 complex used in the present embodiment is similar to that explained in the above-mentioned section of "A. Asymmetric Type BF3 Complex".
[0039]
In particular, in the present embodiment, an ester molecule which coordinates to BF3 of the asymmetric type BF3 complex is preferably a cyclic ester. Specifically, the cyclic ester is preferably GBL or GVL, and more preferably GBL. In other words, in the present embodiment, the asymmetric type BF3 complex is preferably BF3-GBL complex (a complex presented by the above-mentioned structural formula (1a)). Thereby, a liquid electrolyte for electrochemical device significantly excellent in oxidation resistance can be obtained. Specifically, as it will be explained later, an oxidation resistance of the liquid electrolyte for electrochemical device obtained significantly improves when a mixed solvent of DEC and BF3-GBL complex is used compare to a case when a mixed solvent of diethyl carbonate (DEC) and ethylene carbonate (EC) is used.
[0040]
Further, in the present embodiment, the asymmetric type BF3 complex is preferably a BF3-MP complex (complex represented by the above-mentioned structural formula (ic)). Thereby, a liquid electrolyte for electrochemical device excellent not only in an oxidation resistance but also in reduction-resistance can be obtained. The reason of having excellent reduction-resistance is not necessarily clear, but is thought that the asymmetric type BF3 complex forms a good film by being reducted and decomposed. Substance MP (methyl propionate) becomes a complex by coordinating to BF3 and its oxidation resistance is significantly improved. When the oxidation resistance is improved, the reduction-resistance may sometimes be relatively lowered. However, when a BF3-MP complex is used, a unique effect of improving also the reduction-resistance can be attained.
[0041]
(2) Solvent for Liquid Electrolyte for Electrochemical Device In the present embodiment, the asymmetric type BF3 complex represented by the above-mentioned general formula (1) is used as a solvent. For example, when a melting point of the asymmetric type BF3 complex is sufficiently low, solvents used for the liquid electrolyte for electrochemical device may all be asymmetric type BF3 complexes. On the other hand, when a melting point of the asymmetric type BF3 complex is higher than room temperature, solvents other than the asymmetric type BF3 complex is generally used. As the asymmetric type BF3 complex used in the present embodiment has a low heat of fusion, it has an advantage of providing a wide selection in the solvent composition. The preferable solvent composition is the same as those explained above.
[0042]
As examples of solvents other than the asymmetric type BF3 complex, carbonates such as ethylene carbonate (EC) , propylene carbonate (PC),dimethyl carbonate (DMC),diethyl carbonate (DEC), and ethylmethyl carbonate (EMC); ethers such as dimethyl ether, diethyl ether, tetrahydrofuran (THF), and methyltetrahydrofuran; nitriles such as methoxypropionitrile and acetonitrile; esters such as methyl acetate; amines such as triethylamine; alcohols such as methanol; and ketones such as acetone, can be cited. Among them, carbonates are preferable.
Further, an organic molecule which coordinates to BF3 of the asymmetric type BF3 complex can be used as solvents other than the asymmetric type BF3 complex.
[0043) (3) Electrolyte of Liquid Electrolyte for Electrochemical Device An electrolyte used in the present embodiment is not _............. .................. .................. ........ ..... .... ....
...
particularly limited as long as it is dissolved in a solvent which contains the asymmetric type BF3 complex. The type of the electrolyte varies depending on the use of the liquid electrolyte.
As examples, Li salts, Na salts, and quaternary ammonia salts can be cited, and Li salts are preferable among them. This is because they can be used in lithium secondary batteries.
[0044]
As the Li salts, a general Li salts may be used and not particularly limited. For example, LiN (SO2CF3) 2 (in some cases also referred to LiTFSI), LiN(S02C2F5)2 (in some cases also referred to LiBETI) , LiC104, LiBF4, and LiPF6 can be cited. Among them, LiN (S02CF3) 2 and LiN (S02C2F5) 2 are preferable. This is because the lithium imide salts such as LiTFSI and LiBETI have high decomposition temperature and can restrain the generation of hydrogen fluoride (HF).
[0045]
A density of the electrolyte of the liquid electrolyte for electrochemical device is not particularly limited, and it is the same as the density of a general electrolyte. Although it is not particularly limited, it is normally about 1 mol/L.
[0046]
(4) Others As examples of an application of the liquid electrolyte for electrochemical device of the present embodiment, a secondary battery, capacitor, or sensor can be cited. Among them, a secondary battery and capacitor are preferable, and a secondary battery is particularly preferable. Further, even among the secondary batteries, it is preferable to use the liquid electrolyte for electrochemical device of the present embodiment as a lithium secondary battery.
[0047]
2. Second Embodiment Next, a second embodiment of a liquid electrolyte for electrochemical device of the present invention will be explained.
The liquid electrolyte for electrochemical device of the present embodiment comprises an asymmetric type BF3 complex represented by the below-mentioned general formula (2) as a solvent:
[0048]
(Chemical Formula 6]
Q~_' General Formula(2) FB-_F
F
[0049]
(in the general formula (2), each of R3 and R4 is an alkyl group having 1 to 5 carbon atoms and is a different alkyl group).
According to the present embodiment, a liquid electrolyte for electrochemical device having a wide potential window can be obtained by using the asymmetric type BF3 complex as a solvent.
As an acidity of the BF3 part is very strong in the asymmetric type BF3 complex used in the present embodiment, an electron of a coordinating organic molecule (carbonate) is pulled to the ... ... _... _........ ..... ..._ ..... _ ......
BF3 part. Thus, an oxidation resistance of the organic molecule part in the complex improves and a liquid electrolyte having a wide potential window can be obtained.
[0050]
Moreover, as explained in the above-mentioned section of "A. Asymmetric Type BF3 Complex", the asymmetric type BF3 complex used in the present embodiment also has an asymmetric structure.
Thus, it is possible to lower a melting point and heat of fusion of the asymmetric type BF3 complex compare to those of similar symmetric type BF3 complex. Accordingly, for example, even if the asymmetric type BF3 complex is solid at room temperature, the complex can be made to liquid by adding a small amount of an organic solvent. Therefore, it has an advantage of providing a wide selection in the solvent composition.
[0051]
The liquid electrolyte for electrochemical device of the present embodiment comprises the above-mentioned asymmetric type BF3 complex represented by the general formula (2) as a solvent.
In the present embodiment, the asymmetric type BF3 complex is contained by, generally 10 % by weight or more to all of the solvent, preferably 20 % by weight or more, and more preferably 50 % by weight or more.
Hereinafter, the liquid electrolyte for electrochemical device of the present embodiment will be explained by each technical structure.
[0052) (1) Asymmetric Type BF3 Complex First, an asymmetric type BF3 complex used in the present embodiment will be explained. The asymmetric type BF3 complex used in the present embodiment is represented by the above-mentioned general formula (2) . As the asymmetric type BF3 complex used in the present embodiment has an asymmetric structure, it is very useful as a solvent for a liquid electrolyte for electrochemical device similarly to the case of the above-explained first embodiment. Therefore, it is possible in the present embodiment to provide the solvent for a liquid electrolyte for electrochemical device represented by the above-mentioned general formula (2).
[0053]
In the general formula (2), each of R3 and R4 is generally an alkyl group having 1 to 5 carbon atoms. The number of the carbon atoms is preferably within the range of 1 to 3, and more preferably within the range of 1 to 2. Each of R3 and R4 may be an alkyl group not branched or a branched alkyl group, but an alkyl group not branched is preferable. Further, R3 and R4 are different alkyl group. This is because, if they are the same alkyl group, the asymmetric type BF3 complex cannot have an asymmetric structure.
[0054]
In particular, in the present embodiment, the asymmetric type BF3 complex is preferably a complex represented by the below-mentioned structural formula (2a). This is because such asymmetric type BF3 complex is useful as a solvent for a liquid .............. ............ _.._..........
..........._..........._...........,_......_........... .
electrolyte for electrochemical device. In the present embodiment, the structural formula (2a) may sometimes be referred as "BF3-EMC complex".
[0055]
[Chemical Formula 7]
0 Y 0,,,,,-O
F---B-'`F
F
Structural Formula (2a) [0056]
A method of producing an asymmetric type BF3 complex of the present embodiment is not particularly limited. As an example, a method of aerate a BF3 gas to a raw material carbonate can be cited. The asymmetric type BF3 complex can be identified, for example, by a carbon-nuclear magnetic resonance method (13C-NMR
method) and a hydrogen-nuclear magnetic resonance method (1H-NMR
method).
[0057]
(2) Solvent for Liquid Electrolyte for Electrochemical Device In the present embodiment, an asymmetric type BF3 complex represented by the above-mentioned general formula (2) is used as a solvent. For example, when a melting point of the asymmetric type BF3 complex is sufficiently low, solvents used for the liquid electrolyte for electrochemical device may all be asymmetric type BF3 complexes. On the other hand, when a melting point of the asymmetric type BF3 complex is higher than room temperature, solvents other than the asymmetric type BF3 complex is generally used. As the asymmetric type BF3 complex used in the present embodiment has a low heat of fusion, it has an advantage of providing a wide selection in the solvent composition. The preferable solvent composition is the same those as explained above.
[0058]
As solvents other than the asymmetric type BF3 complex is the same to those explained in the above-mentioned section of "1. First Embodiment", explanation here is omitted. Further, the electrolyte, the application of the liquid electrolyte for electrochemical device, and other factors of the present embodiment are the same to those explained in the above-mentioned section of "1. First Embodiment", explanation here is omitted.
[00591 C. Lithium Secondary Battery Next, a lithium secondary battery of the present invention will be explained. The lithium secondary battery of the present invention comprises: a cathode layer containing a cathode active material, an anode layer containing an anode active material, a separator provided between the cathode layer and the anode layer, and a liquid electrolyte impregnated at least with the separator, characterized in that the liquid electrolyte is the liquid electrolyte for electrochemical device explained above.
[0060]
According to the present invention, a lithium secondary battery which can be used at a high voltage can be obtained by using a liquid electrolyte comprising the above-mentioned asymmetric type BF3 complex as a solvent.
[0061]
The lithium secondary battery of the present invention comprises at least a cathode layer, an anode layer, a separator, and a liquid electrolyte. As the liquid electrolyte is the same to that explained in the above-mentioned section of "B. Liquid Electrolyte for Electrochemical Device", explanation here is omitted.
[0062]
The cathode layer used in the present invention contains at least a cathode active material. As examples of the cathode active material, LiCoO2, LiMn2O4, LiNi02, LiNi0 8Coo.202, LiNi1/3Mn1/3Co1/302r LiNio.5Mno.502, LiNio.5Mni.504, LiCoPO4, LiMnPO4r LiFePO4 can be cited. Among them, LiCo02 is preferable. Further, the cathode active material generally contains a conductive material and a binder. As examples of the conductive material, carbon black and acetylene black can be cited. As examples of thebinder, fluorine--based resins such as polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), and ethylenetetrafluoroethylene (ETFE) can be cited. Further, the lithium secondary battery of the present invention generally comprises a cathode active material which corrects current of a cathode layer. As examples of a material for the cathode current collector, aluminum, stainless, nickel, iron, and titanium can be cited.
[0063]
The anode layer used in the present invention contains at least an anode active material. As examples of the anode active material, metal lithium, a lithium alloy, metal oxide, metal sulfide, metal nitride, and carbon material such as graphite can be cited. Among them, graphite is preferable. The anode layer may contain a conductive material and a binder as needed.
As for the conductive material and the binder, the same materials as the cathode layer can be used. Further, the lithium secondary battery of the present invention normally comprises an anode current collector which corrects currents of the anode layer.
As examples of a material for the anode current collector, copper, stainless, and nickel can be cited.
[0064]
As for the separator used in the present invention, the same materials as the separator substrates used in general lithium secondary batteries can be used, and thus, not particularly limited. For example, resins such as polyethylene (PE), polypropylene (PP), polyester, cellulose, and polyamide can be cited. Among them, polyethylene and polypropylene are preferable . Further, a shape of a battery case used in the present invention is not particularly limited as long as it can store the above-mentioned cathode layer, anode layer, and a separator.
As specific example, a cylindrical type, a square type, a coin type, and a laminate type can be cited.
[0065) EXAMPLES
[0066]
The present invention will be further specifically explained by way of examples.
[Example 1-1]
Prepared as a raw material ester was gamma -butyrolactone (GBL) and it was aerated with a BF3 gas in 0 C nitrogen atmosphere for 20 minutes or longer. A white liquid was obtained consequently. The obtained liquid was filtered and a solid was removed, and thereby, a white BF3-GBL complex was obtained.
Next, a melting point and a heat of fusion of the obtained BF3-GBL complex were measured. Measurement was conducted by sealing the BF3-GBL complex in a SUS closed container, using a differential scanning calorimeter (DSC), and setting the temperature rising conditions to 2 C/minute and the upper limit of the temperature to 180 C. As a result, as shown in FIG. 1, a melting point of the BF3-GBL complex was 70.23 C, and a heat of fusion thereof was 54.16 J/g.
[0067]
[Example 1-2]
A BF3-EP complex was obtained in the same manner as in Example 1-1 except that ethyl propionate (EP) was used as a raw material ester.
Next, a melting point and a heat of fusion of the obtained BF3-EP complex were measured in the same manner as in Example 1-1. As shown in FIG. 2, a melting point of the BF3-EP complex was 43.06 C, and a heat of fusion thereof was 76.30 J/g.
[0068]
[Example 1-3]
A BF3-MP complex was synthesized in the same manner as in Example 1-1 except that methyl propionate (MP) was used as a raw material ester. In the present example, the obtained liquid was filtered while it was cooled down after aerated with a BF3 gas, and a solid was removed. The obtained BF3-MP complex was liquid at room temperature.
[0069]
[Example 1-4]
A BF3-EMC complex was obtained in the same manner as in Example 1-1 except that ethyl methyl carbonate (EMC) was used as a raw material carbonate instead of raw material ester.
Next, a melting point and a heat of fusion of the obtained BF3-EMC complex were measured in the same manner as in Example 1-1. As shown in FIG. 3, a melting point of the BF3-EMC complex was 65.43 C, and a heat of fusion thereof was 63.98 J/g.
[0070]
[Comparative Example 1-1]
A BF3-DMC complex was obtained in the same manner as in Example 1-1 except that diethyl carbonate (DMC) was used as a symmetric type organic molecule.
Next, a melting point and a heat of fusion of the obtained BF3-DMC complex were measured in the same manner as in Example 1-1. A melting point of the BF3-DMC complex was 110.79 t, and a heat of fusion thereof was 125.5 J/g.
[0071]
[Comparative Example 1-2]
A BF3-DEC complex was obtained in the same manner as in Example 1-1 except that diethyl carbonate (DMC) was used as a symmetric type organic molecule.
Next, a melting point and a heat of fusion of the obtained BF3-DEC complex were measured in the same manner as in Example 1-1. A melting point of the BF3-DEC complex was 58.45 C, and a heat of fusion thereof was 156.4 J/g.
The above-mentioned results are shown in below Table 1.
[0072]
[Table 13 Melting Point Heat of Fusion Complex ( C) (J/g) Example 1-1 BF3-GBL 70.23 54.16 Example 1-2 BF3-EP 43.06 76.30 Room Example 1-3 BF3-MP Temperature or -Lower Example 1-4 BF3-EMC 65.43 63.98 Comparative BF3-DMC 110.79 125.5 Example 1-1 Comparative BF3-DEC 58.45 156.4 Example 1-2 [0073]
As apparent fromTable 1, all complexes obtained in examples showed low melting points and heat of fusion. In contrast, the symmetric type organic molecule of Comparative Example 1-1 showed high value in both of melting point and heat of fusion. Further, the symmetric type organic molecule of Comparative Example 1-2 showed low melting point, but also showed high heat of fusion, so that it was necessary to add a large amount of other organic solvent to obtain a liquid electrolyte in a liquid state at room temperature.
[0074]
[Example 2-1]
A BF3-GBL complex obtained in Example 1-1 and diethyl carbonate (DEC) was mixed so as the mol ratio thereof becomes $
1:1, and a homogenous mixed solvent was obtained. Subsequently, LiPF6was dissolved by 1M to the obtained mixed solvent and a liquid electrolyte for electrochemical device was obtained.
[0075]
[Comparative Example 2-1]
A liquid electrolyte for electrochemical device was obtained in the same manner as in Example 2-1 except that ethylene carbonate (EC) was used instead of a BF3-GBL complex.
[0076]
[Evaluation]
The oxidation potential of the respective liquid electrolyte for electrochemical device obtained in Example 2-1 and Comparative Example 2-1 were measured. Measurement was conducted by using a three electrode cell provided with glassy carbon for a working electrode, lithium metals for a counter electrode and a reference electrode, and under a linear sweep voltammetric technique. At the time of measuring, potential of the working electrode was swept from the immersed potential to the high potential side. The sweep speed was 5 mVsec-1.
The results (LSV curves) are shown in FIG. 4. As shown in FIG. 4, with the liquid electrolyte for electrochemical device of Comparative Example 2-1, elevation in current value were confirmed from the potential of about 6.5 VvsLi/Li+. When glassy carbon is used for a working electrode, no particularly active RedOx series is present in electrodes and a solution. Thus, the current confirmed here is thought to be caused by oxidative decomposition of the liquid electrolyte itself. In contrast, with the liquid electrolyte for electrochemical device of Comparative Example 2-1, no substantial current was flowing even at potentials higher than 6.5 VvsLi/Li+. Thus, the liquid electrolyte for electrochemical device of the present invention was found excellent in oxidation resistance.
[0077]
[Example 2-2]
A BF3-MP complex obtained in Example 1-3 and diethyl carbonate (DEC) was mixed so as the mol ratio thereof becomes 1:1, and a homogenous mixed solvent was obtained. Subsequently, LiPF6 was dissolved by 1M to the obtained mixed solvent and a liquid electrolyte for electrochemical device was obtained.
[0078]
[Comparative Example 2-21 A liquid electrolyte for electrochemical device was obtained in the same manner as Example 2-2 except that ethylene carbonate (EC) was used instead of a BF3-MP complex.
[0079]
[Evaluation]
The reduction potential of the respective liquid electrolyte for electrochemical device obtained in Example 2-2 and Comparative Example 2-2 were measured. Measurement was conducted by using a three electrode cell provided with glassy carbon for a working electrode, lithium metals for a counter electrode and a reference electrode, and under a linear sweep voltammetric technique. At the time of measuring, potential of the working electrode was swept from the immersed potential to the low potential side. The sweep speed was 5 mVsec-1.
The results (LSV curves) are shown in FIG. 5. As shown in FIG. 5, with the liquid electrolyte for electrochemical device of Comparative Example 2-2, reduction current were confirmed from the potential of about 0.5 VvsLi/Li+. This is thought to be caused by reductive degradation of the liquid electrolyte itself. In contrast, with the liquid electrolyte for electrochemical device of Comparative Example 2-2, no substantial current was flowing until 0.2 VvsLi/Li+. Thus, it was confirmed that the reduction-resistance of the liquid electrolyte was improved.
[0080]
[Example 2-3]
A BF3-EMC complex obtained in Example 1-4 and EMC was mixed so as the mol ratio thereof becomes 1: 1, and a homogenous mixed solvent was obtained. Subsequently, LiTFSI was dissolved by 1M
to the obtained mixed solvent and a liquid electrolyte for electrochemical device was obtained.
[0081]
[Comparative Example 2-3]
A liquid electrolyte for electrochemical device was obtained in the same manner as Example 2-3 except that only EMC
was used as a solvent.
[0082]
[Evaluation]
The oxidation potential of the respective liquid electrolyte for electrochemical device obtained in Example 2-3 and Comparative Example 2-3 were measured. Measurement was conducted by using a three electrode cell provided with glassy carbon for a working electrode, lithium metals for a counter electrode and a reference electrode, and under a linear sweep voltammetric technique. At the time of measuring, potential of the working electrode was swept from the immersed potential to the high potential side. The sweep speed was 5 mVsec-1.
The results (LSV curves) are shown in FIG. 6. As shown in FIG. 6, with the liquid electrolyte for electrochemical device of Comparative Example 2-3, elevation in current value were confirmed from the potential of about 5. 2 VvsLi /Li+. In contrast, with the liquid electrolyte for electrochemical device of Example 2-3, no substantial current was flowing until about 5.6 VvsLi/Li+.
Thus, the liquid electrolyte for electrochemical device of the present invention was found excellent in oxidation resistance.
Claims (5)
1. A liquid electrolyte for electrochemical device comprising an asymmetric type BF3 complex represented by the following general formula (1) as a solvent:
wherein each of R1 and R2 is an alkyl group having 1 to 6 carbon atoms and may be the same or different, and R1 and R2 may be branched or may form a ring.
wherein each of R1 and R2 is an alkyl group having 1 to 6 carbon atoms and may be the same or different, and R1 and R2 may be branched or may form a ring.
2. The liquid electrolyte for electrochemical device according to claim 1, characterized in that the asymmetric type BF3 complex is a kind of complex selected from the group consisting of the following structural formulae (1a), (1b) and (1c):
3. A liquid electrolyte for electrochemical device comprising the asymmetric type BF3 complex represented by the following general formula (2) as a solvent:
wherein each of R3 and R4 is an alkyl group having 1 to 5 carbon atoms and is a different alkyl group.
wherein each of R3 and R4 is an alkyl group having 1 to 5 carbon atoms and is a different alkyl group.
4. The liquid electrolyte for electrochemical device according to claim 3, characterized in that the asymmetric type BF3 complex is a complex represented by the following structural formula (2a):
5. A lithium secondary battery comprising:
a cathode layer containing a cathode active material, an anode layer containing an anode active material, a separator provided between the cathode layer and the anode layer, and a liquid electrolyte impregnated at least with the separator, characterized in that the liquid electrolyte is the liquid electrolyte for electrochemical device according to any one of claims 1 to 3.
a cathode layer containing a cathode active material, an anode layer containing an anode active material, a separator provided between the cathode layer and the anode layer, and a liquid electrolyte impregnated at least with the separator, characterized in that the liquid electrolyte is the liquid electrolyte for electrochemical device according to any one of claims 1 to 3.