CA2204628A1 - Signage articles and methods of making same - Google Patents

Abstract

The present invention discloses signage articles having a layer of fused dry toner powder which is fused by employing a tacky pressure-sensitive adhesive and low compression. Suitable tacky pressure-sensitive adhesives include alkyl acrylate polymers or copolymers, alkyl vinyl ether polymers or copolymers, polyisobutylene, polybutadiene, and butadiene-styrene copolymers. Such signage articles further comprise a transparent cover layer disposed over the fused dry toner powder-bearing surface. Also disclosed are methods of forming signage articles, one method comprising the steps of applying dry toner powder to a first substrate surface, applying a composition including a tacky pressure-sensitive adhesive to a second substrate surface, and laminating the two substrates to admix the dry toner powder and the tacky pressure-sensitive adhesive. Either the first or second substrate may be the transparent cover layer of the resulting signage article.

Description

CA 02204628 1997-0~-06 W O96/14604 PCTrUS9S/14564 SIGNAGE ARTICLES AND METEODS OF MAKll~G SAME

Background of the Invention 1. Field of Invention This invention relates to signage articles. In particular, the invention relates to low temperature formation of indicia using dry toner powder.

2. RPI~lt~l Art Dry toner powder is known for printing on paper and other substrates, and compositions of dry toner powders are described in, for eY~mple~ U.S. Pat.
5,085,918. Typically, dry toner powders comprise a colorant and a binder, and optionally a charge carrier and flow control additive. The binder is a non-tacky solid at room temperature, but melts or softens sufficiently to enable permanent fusion of the composition and adherence to the substrate at temperatures ranging from about 120-240~C.
Various methods are known in the art for applying dry toner powder onto a substrate to form indicia. One method is to apply dry toner powder electrophotographically, wherein a charge carrier is added to the composition. In this method, a laser is used to alter the electrostatic charge on a portion of the surface of a rotating drum to form a latent image. Portions defined by the latent image accept dry toner powder from a reservoir. The rotating drum then transfers the dry toner powder in the desired image definition to a substrate cont~cting or nearly cont~cting the rotating drum. The laser can be controlled to form indicia that are generated in digital form by a computer, either directly by a computer operator, reproduced from data stored in digital form, or from an optically scanned and ~ligiti7ed image. Such electrophotographic im~ginp is commonly used in copy m~hines and laser printers.
After transferring dry toner powder from the rotating drum to a substrate, forming a desired image, the applied dry toner powder is fused to fix the image in place. The process of fusing involves converting the particles of dry toner powder in the transferred image to a continuous phase in which discrete particles are no longer present. Fusing aids in keeping toner within the int~n(led edges ofthe image and in forming an image of acceptable quality. Dry toner powder generally is fused or fixed ~ =
CA 02204628 1997-0~-06 W O 96/14604 PCTrUS95/14S64 on a substrate by heating the dry toner powder to a temperature in the range of about 200~ to about 220~C for applo~inlately 0.1 seconds, although temperatures approaching 220~C typically are required to obtain s~ti~f~ctory image quality~
For example, the '918 patent describes articles wherein the substrate onto which the dry toner powder is L-~llsrt;,-ed in the form of a desired image is - orenective signage, wherein the dry toner powder is fused to form the image through a high temperature process. Optionally, there is disclosed a clear polymeric film formed over the image bearing surface of the signage articles, e.g., by dip coating or l~" .;~ g, to provide a protective coating.
HP Laser Jet 4 and 3M Printers User's Manual (First Edition: October 1992) and HP Laser Jet IIP Printer User's Manual (First Edition: June 1989) indicate that substrates, as well as pigments and other components of which the substrate is comprised, must be able to tolerate fusing temperatures in excess of 200~C for at least 0.1 seconds without physical or chemical deterioration. Similarly, Siemens Nixdorf Electronic Printing Systems Manual (January 1992 Edition) states that pigments and substrates must be able to tolerate temperatures of at least 200~C at a pressure of 2.4 x 105 Pascals (Pa). Fusing at such te"")e~lures and pressures limits the composition of substrates to which dry toner powder can be applied since a substrate must tolerate the temperatures used for fusing without noticeable chemical or physical degradation.
In attempting to develop additional processes for fusing of dry toner to a substrate, high pressure, in the range of about 14 megaPascals (~a) to about 28 MPa (2000 to 4000 psi), has been used to achieve fusion at lower temperatures. Toward that end, an ideal dry toner fusion process would require no m~ ine warm-up time, a minimum power input and reduced fuser roll degradation. Unfortunately, the fusing pressures, such as those indicated above, required for adequate print quality cause considerable corl,pressive damage to the substrate. This type of damage results, for example, in the calendering of paper, and an uns~ti.cf~ctory glossy appearance.
Numerous attempts have been made to utilize a noncontact fusing technology where no surface touches the dry toner powder side of the paper until fusing is complete. For example, unfilsed dry toner powder may be exposed to solvent vapors which soften the binder in the dry toner powder and thus accomplish fusing, for example, asdisclosed inU.S. PatentNo. 2,684,301 (Mayo). U.S. PatentNo. 4,311,723 _ (Mugraner) also discloses a vapor fusing system that utilizes a trichlorotrifluoroethane and either acetone or methylene chloride in an azeotropic mixture.
Fusing dry toner powder at high temperatures or at high pressures also imposes the additional requirement of complex equipment that is capable of exerting uniform heat or pressure upon the substrate surface. On the other hand, fusing dry toner powder to a substrate by solvent vapors is limited to substrates that would not be damaged by the chemical action of the solvents, and nece~it~tes the additional processing step of passing the substrate through a chamber cot-f ~;"i--~ the solvent vapors. Furthermore, the use of solvent vapors is likely to have undesirable environmçnt~l consequences, and printing meçh~tlicm.c using such r.h~mic~lly based fi~sing processes may, in turn, be subject to significant regulation relating to release of the solvents into the atmosphere.
Thus, there exists a need to provide a low-temperature, low-pressure, solvent-free chemical fusion process that is relatively simple and economical to1 5 implement.

Summaly of the Invention In accordance with the present invention, signage articles and methods of making same are presented which overcome some of the limitations of previously known articles and methods. One aspect of the invention is a signage article comprising:
a) a first substrate having first and second major surfaces;
b) a fused dry toner powder (preferably in the form of a computer-generated image) adhered to the first major surface of the first substrate, the fused dry toner powder comprised of a colorant and a binder, the binder comprising a combination of first and second adhesives, the first adhesive being non-tacky at 25~C, the second adhesive being aggressively tacky at 25~C;
c) a second substrate adhered by an adhesive layer to the fused dry toner powder and first surface of the first substrate, the adhesive layer comprising a major portion of the second adhesive, at least one of the first or second substrates being transparent. As used herein "fused dry toner powder" comprises two binding adhesives, while "dry toner powder" only includes the non-tacky adhesive. As used herein "transparent" means transmitting at least 90% of incident light in the visible , _ electrom~netic spectrum (about 400-700 nanometers), as de~e~ ined using a standard spectrophotometer.
Alternatively, the fused dry toner powder may be adhered to the second substrate rather than to the first surface of the first substrate, or to both the first and S second substrates.
In more specific terms, the signage articles of the invention preferably comprise:
a) a liner;
b) a first adhesive layer having fir~st and second major surfaces, the first surface removably adhered to the liner;
c) a plastic film layer having first and second major surfaces, the plastic film layer coterminous with and the first adhesive layer, the first major surface of the plastic film layer adhered to the second major surface of the adhes*e layer;d) a retlor~nective layer having first and second surfaces, wherein the first surface of the rell o, ~nective layer is preferably defined by a plurality of concavities, a first portion of the concavities filled with and adhered to the second major surface of the plastic film layer, a second portion of the concavities not filled with or adhered to the second major surface of the plastic film layer, the second surface of the retroreflective layer being substantially smooth;
e) a plurality of areas of fused dry toner powder adhered to the second surface of the I ~ll ol enective layer, the fused dry toner powder comprised of a colorant and a binder, the binder comprised of first and second adhesives, the first adhesive being non-tacky at about 25~C, the second adhesive being transparent and aggressively tacky at 25~C; and f) an optional transparent protective layer adhered by a second adhesive layer to the fused dry toner powder and second surface of the .elloleflective layer, the second adhesive layer comprising a major portion of the second adhesive (this layer only required in outdoor signage articles).
Preferred inventive articles are those wherein the concavities of the ~t;llureflective layer are defined by cube-corner elements, for example, when the rellorenective layer comprises a l~min~te of polymethylmethacrylate (PMMA) sheeting and a polycarbonate layer, the PMMA sheeting forming the smooth surface, the CA 02204628 1997-0~-06 W O 96/14604 PCTnUS9~114564 _5 _ polycarbonate layer forming a plurality of geometric projections having at least two planar facets, and thus d~finin~ the plurality of concavities. Further, the first and second ~ adhesive layers are preferably the same and comprise a tacky copolymer of a major portion of isooctyl acrylate and a minor portion of acrylic acid, and the dry toner powder adhesive is a non-tacky acrylate. Plere"ed tacky copolymers are those which comprise about 95.5 weight percent of isooctyl acrylate and about 4.5 weight percent of acrylic acid. The transparent protective layer preferably comprises a copolymer of ethylene and acrylic acid or PMMA, polyurethane, and the like.
Another aspect of the invention are methods of making the signage articles of the invention. One inventive method, wherein the dry toner powder and the tacky adhesive are applied to the same layer, comprises the steps of:
(a) providing a first substrate having a first major surface;
(b) applying a dry toner powder composition to at least a portion of the first major surface of the first substrate, the dry toner powder compositioncomprising a colorant and a first adhesive which is non-tacky at about 25~C;
(c) applying over the dry toner powder composition and first major surface of the substrate a coatable composition comprising a second adhesive, the second adhesive being transparent and aggressively tacky state at about 25~C, thus forming a tacky adhesive layer;
d) applying a second substrate over the coatable composition, at least one of the first and second substrates being transparent, thus forming an intermediate article; and e) applying sufficient compression to the intermediate article to fuse the dry toner powder composition.
Preferably, the dry toner powder composition is applied in the form of indicia, such as alphanumeric symbols formed by a computer program, but this is not required. In fact, the dry toner powder composition may be applied to the entire surface of one of the substrates.
Alternatively, the dry toner powder composition may be applied to a protective layer, and the adhesive layer applied thereover, followed by application ofthe substrate. Another alternative is to first apply dry toner powder composition and then the coatable composition comprising the tacky adhesive to a protective layer, followed CA 02204628 1997-0~-06 W O96/14604 PCT~US9SI1456 by pressing the together the tacky adhesive-coated protective layer having dry toner powder therein with a substrate which previously had the same or dirrer~nl dry toner powder applied thereto.
Further aspects and advantages of the invention will become apparel,~
after reviewing the brief description of the drawing figures and description of p-ert;llt;d embodiments which follow.

Brief Description of the Drawings FIG. 1 is a cross section view (enlarged) of a portion of a first signage article embodiment according to the invention;
FIG. 2 is a sch~ tic diagram of a method of making the atticles of the invention making use of embossed substrates;
FIG. 3 is a schematic diagram of a method of making the articles of the invention using a smooth substrate where the image is printed onto the substrate;
FIG. 4 is a cross section view (enlarged) of another signage article embodiment of the invention;
FIG. S is a cross section view (enlarged) of a particularly plefel,ed signage article embodiment;
FIG. 6 is a diagram of the data flow within the preferred computer program of the present invention;
FIG. 7 is a process control flow chart for the p, ~rt;ll ed computer program of the present invention;
FIG. 8 is an illustration of the make character function of the program;
FIG. 9 is an illustration of the scan function of the program;
FIG. 10 is an illustration ofthe contrast function ofthe program;
FIG. 11 is an illustration of the make string function of the program;
FIG. 12 is an illustration of a portion of the scale function of the program;
FIG. 13 is an illustration of a second portion of the scale function of the program;
FIG. 14 is an illustration of the merge function of the program; and FIG. 15 is an illustration of the print function of the program.

_ ' CA 02204628 1997-0~-06 W O96/14604 PCTrUS95/14564 These figures are not to scale and are only illustrative of the invention.

D~s~ ,lion of Preferred Embodiments 1. Tacly ~r~j~ur~ Sensitive Adhesives The present invention is based on the discovery that dry toner powder, comprising a non-tacky adhesive, can be effectively fused at a te."pe,~t.lre ranging from about 20~C to about 125~C (more preferably at about 25~C) and ples~u,~ ranging from about 250 to about 1500 kiloPascals (kPa), preferably about 690 to about 1380 kPa (depending on the temperature and time at temperature and pressure), onto a substrate surface by use of an aggressively tacky pl es~l l e-sensitive adhesive (PSA).
As used herein the term "fused" means that when viewed under a microscope at 40X magnification, no dry toner powder particles are present in the image, and preferably no dry toner particles are seen at 70X magnification.
Tack refers to "the prope. Ly of a material which enables it to form a bond l 5 of measurable strength immediately on contact with another surface. " (American Society for Testing and Materials (ASTM) test no. D 1878-61 T, ASTM ~ull. No.
221,64 (1957)). A common tester used by ASTM is a Polyken probe tack tester, which, acco..ling to Handbook of Adhesives, 3rd Ed. p. 656 (l990), comprises a 5 millimeter diameter flat-ended rod (usually steel) connected to a load cell. The instrumentmechanically lifts the probe to make contact with the PSA, holds it there for a preset time of contact, variable in 10 steps from 0.1 to l O0 seconds, and then withdraws the probe at a controlled speed, which can be varied in steps from 0.02 to 2 cm/sec. The PSA, on some backing, is attached to the flat bottom of an inverted metal cup with a hole in the bottom through which the probe enters. Thus, the contact pressure can be varied using by using cups or annular weights of various masses. The most common test conditions reported are 100 g/cm contact pressure, l second contact time, and l cm/sec withdrawal speed (commonly denoted using the shorthand notation 100, 1, 1).
Experimental values of Polyken probe tack are expressed in terms of gram force, with all conditions specified. In the present invention, the phrases "tacky"
and "aggressively tacky" are used interchangeably and mean the PSA in question has a probe tack as measured in accordance with ASTM D1878-6lT of at least 500 g CA 02204628 1997-0~-06 W O96/14604 PCT~US95/1456 (100, 1, 1), preferably at least 1000 g, while the term "non-tacky" means having a tack of at most 400 g (100, 1, 1).
Tacky PSAs useful in the invention also may be characterized by having "180~ peel adhesion" ranging from about 170 to about 1000 gm/cm, more preferablyranging from about 390 to about 560 gm/cm, measured using a standard test procedure.
In this procedure, the force nec~Cc~ry to remove (i.e. peel) a PSA-coated substrate from a test substrate when the PSA-coated substrate is peeled from the test substrate is termed the "peel adhesion" value. A standard glass plate is cleaned using a solvent (such as one wash of diacetone alcohol followed by three washes of n-heptane). With very light tension, a sample having a PSA-baclr.ci7e coating is then applied along the center of the standard glass plate, PSA side down. The sample is then rolled once with a 2.04 Kg hand roller. The standard glass plate is then secured to a horizontal platen in a standard peel adhesion tester such as that known under the trade name "IMASS." One end of the sample is then ~ttaçhed to a hook which is a part of the peel adhesion tester. The l 5 sample is peeled from the standard glass plate at a 180~ angle (i.e., one end of the sample is pulled toward the other end) by moving the platen horizontally at a speed of 228.6 cm/min (90 in/min)~ and the force required recorded, in gm/cm of sample width, for various dwell times.
The shear strength is a measure of the cohesiveness or internal strength of an adhesive. It is based upon the amount of force required to pull an adhesive strip from a standard flat surface in a direction parallel to the surface to which it has been affixed with a definite pressure. It is measured in terms of time (in minllt~c) required to pull a standard area of adhesive coated sheet material from a stainless steel test panel under stress of a constant, standard load. The tests are conducted on adhesive coated strips applied to a stainless steel panel such that a 12.5 mm by 12.5 mm portion of each strip is in firm contact with the panel with one end portion of the tape being free. The panel with coated strip attached is held in a rack such that the pane! forms an angle of 178~ with the extended tape free end which is then tensioned by application of a force of one kilogram applied as a h~nging weight from the free end of the coated strip. The ~~
less than 180~ is used to negate any peel forces thus insuring more accurate detel .nil~ation of the holding power of the tape being tested. The time elapsed for each CA 02204628 1997-0~-06 W O 96/14604 PCT~US95/14564 _9_ tape example to separate from the test panel is recorded as the shear strength. Internal cohesive strength (shear strength) of usefi~l tacky PSAs can range from about 1 minute ~ to over 10,000 minllt~s The use of aggressively tacly PSAs for low-tel~p~lalllre~ low-pressure fusion of dry toner powder can provide process and product advantages normally only achieved with materials or processes that allow wetting out or solubilizing of the dry toner powder onto a substrate. For example, a PSA can effectively filse a dry toner powder at low temperatures, temperatures as low as room temperature (about 25~C).
One advantage of the methods of the present invention is that dry toner powder may conveniently be filsed on a wider variety of substrates than previously possible, particularly those substrates that do not tolerate high temperature filsing processes.
Such substrates include, for example, delicate composite materials, and re~-orenective sheeting materials.
A first embodiment 100 of an article prepared according to one method of the present invention is illustrated sch~m~tic~lly in cross section (enlarged) in FIG. 1.
Article 100 comprises a substrate 102, having a first surface 104 and a second surface 106. A transparent adhesive layer 110, comprising an aggressively tacky PSA, is substantially continuously bonded to first surface 104, interspersed by those portions that are adjacent to a fi~sed dry toner layer 108. Fused dry toner layer 108 is adhered directly to surface 104 in this embodiment and comprises fused dry toner powder that is at least partially solubilized or wetted by the aggressively tacky PSA in adhesive layer 110. Article 100 further comprises a protective layer 116 that is adhered to adhesive layer 110. In article 100 illustrated in FIG. 1, layer 116 is a transparent cover film.
Fused dry toner layer 108 preferably forms indicia that are visible to an observer through transparent cover film layer 116 and adhesive layer 110 against the background of substrate surface 104.
Usefill Tacky PSAs are typically and preferably aggressively and permanently tacky at room temperature, adhere to substrates without the need for more than hand pressure, and require no activation by water, solvent or heat.
Tacky PSAs useful in the present invention are selected from the group consisting of alkylacrylate polymers and copolymers; copolymers of alkylacrylates with acrylic acid; terpolymers of alkylacrylates, acrylic acid, and vinyl-lactates; alkyl vinyl CA 02204628 1997-0~-06 W O~6/14604 PCTrUS95/14564 ether polymers and copolymers; polyisoalkylenes; polyalkyldienes; alkyldiene-styrene copolymers; styrene-isoprene-styrene block copolymers; polydialkylsiloxanes;
polyalkylphenylsiloxanes; natural rubbers; synthetic rubbers; chlorinated rubbers; latex crepe; rosin; cumarone resins; alkyd polymers; and polyacrylate esters and mixtures thereo~ Examples include polyisobutylenes, polybutadienes, or but~ ne-styrene copolymers, and mixtures thereof (such polymers and copolymers p,erel~bly have no reactive moieties, i.e., are not oxidized in the presence of air); silicone-based compounds such as polydimethylsiloxane, and polymethylphenylsiloxane combined with other resins and/or oils.
Useful tacky PSAs also include tackified thermoplastic resins and tackified thermoplastic elastomers, ~I-erein the tackifier comprises one or morecompounds which increases the tack of the composition. An example of a tackifiedthermoplastic resin useful as an aggressively tacky PSA is the combination of a vinyl acetate/ethylene copolymer known under the trade de.ci~n~tion VYNATHENE EY 902-30 (available from Quantum Chemicals, Cinçinn~ti~ Ohio) with s~lbst~nti~lly equal portions of the tackifiers known under the trade designations PICCOTEX LC (a water-white thermoplastic resin produced by copolymerization of vinyltoluene and alpha-methylstyrene monomers having a ring and ball softening point of about 87-95~C, available from Hercules Incorporated, Wilmington, DE) and WINGTACK 10 (a liquid aliphatic C-5 petroleum hydrocarbon resin available from Goodyear Chemical) and an organic solvent such as toluene. An example of a tackified thermoplastic elastomer useful as an aggressively tacky PSA is the combination of the styrene-poly(ethylene-butylene)-styrene block copolymer known under the trade designation KRATON G1657(available from of Shell Chemicals) with one or more of the low molecular weighthydrocarbon resins known under the trade de~ign~tion REGALREZ (from Hercules) and an organic solvent such as toluene. Both of these formulations may be coated using a knife coater and air dried, or air dried followed by oven drying. Of course, the invention is not limited to use of these specific combinations of thermoplastic resins, thermoplastic elastomers, and tackifiers.
The presently plerelled PSAs, because oftheir extended shelflife and resi~t~nce to det~cl~ifying under atmospheric conditions, are acrylic-based copolymer adhesives as disclosed in U.S. Pat. No. Re 24,906. One example of such an acrylic-CA 02204628 l997-0~-06 W O 96/14604 PCTrUS95/14564 based copolymer is a 9~.5:4.5 (measured in parts by weight of each) isooctylacrylate/acrylic acid copolymer. Another 1~l e~ll ed adhesive is the copolymer of a 90:10 weight ratio cGl~lbindlion ofthese two monomers. Yet other p,~re"~d adhesives are terpolymers of ethyl acrylate, butyl acrylate, and acrylic acid; copolymers of isooctylacrylate and acrylamide; and terpolymers of isooctylacrylate, vinyl-acetate, and acrylic acid.
Tacly acrylic PSAs useful in the invention can be coated out of a coatable composition comprising an organic solvent, such as a heptane:isopropanol solvent mixture, and the solvent subsequently evaporated, leaving a pressure-sensitive adhesive coating. Layer 110 is preferably from about 0.038 c~ntimeters (cm) to about 0.11 cm (5 to 15 mils) thick when the substrate is a rellolenective sheetin~ material.

2. Dry Toner Powder When viewed under a microscope, for example, at 40X, preferably 70X
l 5 magnification, fused dry toner powder present in fused dry toner layer 108 (FIG. I ) appears continuously distributed within the boundaries of the layer, and few, if any, discrete particles of dry toner powder are visible. This is evidence that fused dry toner Iayer 108 is sufficiently fused by ingredients in the adhesive layer 110 so that the boundaries between discrete powder particles are reduced or çlimin~te~l; in such a condition the dry toner powder is considered to be fusibly admixed. However, it should be noted that microscopic e,~.,.;t~lion indicated that chemical fusion of dry toner powder present in fused dry toner layer 108 did not result in migration ofthe dry toner powder throughout the adhesive layer, i.e., there is no ~~nint~-n-led blurring of images forrned by dry toner layer 108.
The basic characteristics of dry toner powders are known and described in, for example, T. I. Martin, Tutorial: Dry Toner Fundamentals, Tm~ging Materials Seminar Series, Seventh Annual Toner & Developer Industry Conference (September 16-18, 1990). See also coassigned U.S. Pat. No. 5,085,918. Dry toner powders generally are non-toxic, have excellent flow characteristics, are stable during storage and have high transfer efficiency. Dry toner powder compositions include colorants and norrnally non-tacky binder adhesives which become tacky only at elevated te",pe,~t-lres (i.e. much above ambient). Other optional additives can be included in a dry toner CA 02204628 1997-0~-06 W O96/14604 -12- PCTrUS95/14564 powder to adjust properties of the toner, e.g., charge control agents, m~gnetic additives, bulk additives, surface additives and conductive additives.
The pl ere- I ed dry toner powder binding adhesives are characterized by relatively high transparency and clarity. Additionally, pre~el,ed binding adhesives have glass transition temperatures (Tg) from about - 15~C to about 150~C, preferably from about 35~C to about 110~C, and most preferably about 50~C. The most ~lerel,ed dry toner powder binding adhesives are chosen based upon their potential strong chemical interactions with the surface to be printed. Specifically envisioned as factors to be considered as providing the potential for strong chemical interactions are the likelihood of formation of bonds such as ionic or covalent bonds, dono!-acceptor bonds, as well as secondary bonds such as hydrogen bonds and van der Waals bonds between the dry toner powder binding adhesive and the surface to be printed. In ev~lu~ting the potential, the relevant bond energies may be obtained from textbooks such as Adhesion and Adhesives: Science and Technology by A.J. Kinloch; 1987, University Press Cambridge, Great Britain.
Additionally, the most pl eft;l . ed dry toner powder binding adhesives can be laminated, when incorporated in a dry toner powder, at temperatures of from about 20~C to about 12S~C, preferably at room temperature (about 25~C). For example, the well known REFLECTO-LITE brand ~ ~l~ orenective sheeting available from the Minnesota Mining and M~ f~ct1lring Company of St. Paul, Minnesota, has a polyvinyl butyral surface and therefore compatible binding agents, which cause dry toner powders to laminate at te-npe-al~lres from about 20~C to about 125~C, may be filsed during l~min~tion of an ethylene acrylic acid (EAA) copolymer protective film to the lel.u.enective sheeting. T ~min~ting temperatures refer to those measurable at the surface of l~min~tion rollers. Temperatures at surfaces being laminated may be lower than the l~min~ting temperatures mentioned here. Most p-e~..ed are binding adhesives which may be used at temperatures of about 25~C. Preferred dry toner powder binding adhesives are also resistant to ultraviolet (UV) light degradation and are adhesive to the surface upon which the toner is printed.
Dry toner binder adhesives must function dually in that they must allow the dry toner powder to flow easily as a powder, and must melt at temperatures within a CA 02204628 1997-0~-06 W O96/14604 PCTrUS95/14564 pc~L-lre ranging from about 20~C to about 125~C. They also are preferably cornpaLil)le with a wide variety of tacky PSAs. A large variety of compounds can serve as dry toner powder binding adhesives, inclu~in~, but not limited to, polymers in the general classes of polyesters, epoxies, polyalkylacrylates, polyalkylmeth~.rylates, polyureth~n~c cellulose esters, polycarbonates, polyolefins, polyvinyl acetals, fluorine-CO.~ g polymers, thermoplastic elastomers such as ionomers and ionomeric copolymers, copolymers of styrene with n-butylmeth~c.rylate, n-butylacrylate, orbutadiene, and copolyrners of ethylene or propylene and vinyl~cet~te, acrylic acid or methacrylic acid.
A suitable non-tacky dry toner powder binding adhesive may be an alkyl substituted acrylate or methacrylate polyrner, with alkyl groups having from 1 to 9 carbon atoms, or mixtures of such acrylates and especially a copolymer of methyl and butyl meth~crylates (such as for example, those known under the trade d~ei~n~tions ACRYLOID B-66 and ACRYLOID B-48 available from Rohm & Haas Co""la"y).
Other suitable non-tacky binding adhesives are polyvinyl acetals; for example, polyvinyl butyral (such as BUTVAR brand polyvinyl butyrals B-90 or I3-72 available from the Monsanto Chemical Company); polyolefins; polyesters (such as VITEL brand PE-200Dfrom the Goodyear Tire & Rubber Company or ARAKOTE 3000 brand carboxyl termin~ted polyester optionally in mixture with ARAL-DITE PT810 brand polyfunctional epoxy resin (triglycidyl isocyanurate) both available from the Ciba-Geigy Chemical Company; and vinyl resins (such as VINYLITE brand vinyl resin VAGH, a copolymer of vinyl chloride and vinyl acetate available from the Union Carbide Corporation).

3. Charge Carriers Suitable charge carriers may be positive or negative charge control agents designed for use as additives in dry toner powder formulations, depending on the type of printer used. Examples of positively charged control agents include copolymers of butyl and methyl methacrylate (such as TRIBLOX PC-100 brand acrylic polymer (available from E.I. DuPont de Nemours Company)). An example of a suitable negatively charged control agent is that known under the trade designation T-77, from Hodogaya Chemical Co. Ltd. Tokyo (JP), which is an azo-dye metal complex (black).

CA 02204628 1997-0~-06 W O96/14604 PCTrUS9S/14564 Another useful negatively charged carrier is COPY CHARGE NX VP 434 (quaternary ammonium salt) from Hoechst-Celanese which is colorless. Another useful colorless, negatively charged carrier is BONTRON E-82 (a metal complex of an alkyl derivative of salicylic acid) from Orient Chemical Co., Port Newark, N.J. Polyesters and vinyl resins may also be used as charge carriers. A l)l er~l, ed acrylic copolymer charge carrier has the following characteristics: molecular weight ranging from about 2000 to 5000; glass transition temperature (Tg) ranging from about 53~C to 59~C, onset at about 46~C, nitrogen content of about 1% as measured by NMR. Pl er~l I ed charge carriers are also relatively light tr~n~mi~sive or l-~nsya-~,.L materials, and are resistant to W light degradation. For a black dry toner powder, a ll ~ns,ual ell~ charge carrier is not essential.
For example, an azine dye (Nigrosine Solvent Black 7, CI#50415:1) available fromOrient Chemical Co., may be used as a charge carrier for such a toner. The most pler~lled charge carriers ate acrylic polymers (i.e. alkyl acrylates or alkyl methacrylates) having amine functionality (i.e. functional groups including amine nitrogen or quaternary l 5 ammonium nitrogen).
Suitable colorants may be pigments such as PIG M ENT RED ]79 or 224 available from the Harmon-Mobay Chemical Company; PIG~vlENT YELLOW 110 or PIGMENT VIOLET 37 available from the Ciba-Geigy Company; PIGMENT GREEN 7 or 36 available from the Sun Chemical Company; the colorant known under the trade designation PIGMENT BLUE 15;1 or BLUE 15;6 available from BASF; the colorant known under the trade designation REGAL 500R (carbon black) available from CabotCorporation; the colorant known under the trade designation HELIOGEN BLUE
K691 lD (available from BASF); and the colorant known under the trade designation PROJET 900MP (available from ICI Ltd.) (the latter sometimes used primarily for infrared absorption). Suitable colorants may also be dyes such as that known under the trade design~tion AMAPLAST YELLOW available form the Color-Chem International Corporation or LATYL BRILLIANT BLUE BGA available from the DuPont Company.
Generally, pigments or dyes should be resistant to environmçnt~l pollutant chemical degradation and UV light degradation. Preferably, pigments are dispersed in a dispersing resin, for example RED 229 dispersed in an acrylic resin known under the trade designation ACRYLOID B-66 in a 1:3 weight ratio. Such dispersion helps to CA 02204628 1997-0~-06 W O 96tl4604 PCTrUS95114564 the small pigment particle size that is desired for obtaining a light l image.
. The fused dry toner powder on l~L~orenective signs is prere.~bly light tr~ncmi~ive for all colors except black. That is, at least 10% of light entering the fused dry toner area passes through the filsed dry toner powder, except in the case of carbon black. In the case, however, of black images res-lltin~ from the use of carbon black, the fused dry toner powder is preferably opaque. That is, none of the light entering the black area passes through the fused dry toner powder.
Suitable dry toner powders may be prepared by colllbil~illg from about 64 percent to about 98 percent non-tacky binding adhesive, about 1 percent to about 20 percent charge carrier agent and about 1 percent by weight to about 16 percent colorant;
preferably cGlll~inillg from about 76 percent to about 92 percent non-tacky binding adhesive with about 2 percent to about 12 percent charge carrier agent and with about 6 percent to about 12 percent colorant; and most plerel~bly combining about 88 percent binding adhesive with about 4 percent charge carrier agent and about 8 percent colorant, all percent~çs in weight percent of the total weight of dry toner powder composition.

4. Applying Dry Toner Powder to Substrates The non-tacky binding adhesive, colorant, and optional charge carrier agent (required for electrophotographic printing) and other optional ingredients may be mechanically mixed (and the binding adhesive as well as the charge carrier melted) using a twin screw extruder such as a variable speed twin screw extruder, for example a Baker Perkins gear drive model having a Haake rheocord torque rheometer. Preferably, the twin screw extruder generates a te,-,l,c,~lure of apploxi",ately 150~C to app,o~i",at~ly 225~C during extrusion. The extruded product may be ha."me, l.. illed and then jet milled to generate a mixture having particle si~es ranging from about 5 to 100 micrometers, preferably from about 5 to 50 micro~neters and most preferably from about 5 to about 20 micrometers. A suitable jet mill is NPA Supersonic Jetmill model PJM IDS-2 available from the Nippon Pneumatic ~m~f~ctllring Company. The res--lting material 3 0 may be used in the toner hopper of a laser type printer.
Suitable surfaces to be printed may be made from materials in~ (ling polymers selected from the group consisting of polyalkylacrylates, .

CA 02204628 1997-0~-06 W O96/14604 PCTrUS9S/14564 polyalkylmeth~rylates, polyesters, vinyl polymers, polyureth~n~s, cellulose esters, fluoropolymers, polycarbonates, polyolefins, ionomeric copolymers and copolymers of ethylene or propylene with acrylic acid, methacrylic acid, or vinyl acetate. Suitable rt;;l~orenective sheeting substrates include those known under the trade design~tions SCOTCH-LITE brand HIGH INTENSITY, t;l, Ol enective sheeting and RE~LECTO-LITE brand retroreflective sheeting. The surface layers of such substrates may be made of polyalkylacrylates or polyalkylmethacrylates (especially polymethyl meth~crylate (PMMA)), polyesters, vinyl polymers and polyvinyl acetals such as, for example, polyvinyl butyrals. The SCOTCH-LITE brand and REFLECTO-LITE brand ,~L,o,enective sheetings are available from the Minnesota Mining and ~n~lf~ctllring Company, St. Paul, Minnesota ("3M").
Any one of a number of processes may be employed to apply dry toner powder to a substrate to produce articles of the invention, including electrophotographic printing, screen printing, spray printing, and the like.
One ~), erel, ed process is electrophotographic printing. A wide range of electrophotographic printers may be used to practice the present invention. One suitable printer is a 3M brand Multifunction Printer Model 1800 available from 3M. The Model 1800 printer was originally designed for automatic paper-feed, but may be operated on continuous webs with modifications which are within the skill of the art. The dry toner powders described herein are substituted for the toner usually used with the printer. The Model 1800 printer is a dual-mode printer. The printer is capable of printing from 35mm aperture cards or microfilm. The printer also accepts digital i,.fo"n~Lion from a host computer (such as a Sun Microsystems Computer) in the form of raster files.Another suitable printer is a 3M brand Model 679 LBQ LASER PRIN-TER available from 3M. Preferably, such a printer is used in conjunction with a 3M brand Model 1811 CONIROLLER, also available from 3M. Both of these printers are capable of 200 dots per inch (dpi)(i.e. 79 dots per cçntimçter or 3.95 line pairs per millimet~r) horizontal and vertical resolution and accept raster data files either from a raster-based host system (such as a Sun Microsystems Computer) or vector-based host system through a vector-to-raster converter.
Standard computer programs for defining an image to be printed, in the form of raster files, are well known. However, many of these programs tend to suffer W O 96/14604 -17- PCTrUS9S/14564 from a lack of speed in defining an image and/or tend to produce images with unacceptably "rough" edges when enlarged to sizes typically employed for an alpha numeric image on a license plate (i.e. about 6.0 cm in height). For example, ArtisanTM, a graphics printing program available from Media Logic, Inc. of Santa Monica, California S and SunDrawTM, a graphics plilllill~, program available from Sun Miclos~L~Ills, Inc. of Mountain View, California each provide one bit raster character files having only about 20% of the resolution of the program of this invention.
The pl~rel.ed computer program is capable of utili7ing the best resolution ofthe printer, that is 200 dots per inch (i.e. about 79 dots per centimet~r or 3.95 dots per millimetçr). The program also provides a number of "pro""ulil~g screens"
to a video monitor to enable an operator to compose and review an image for alphanumeric identification on a license plate or other substrate. The images are reviewed in reduced or downsized form to enable the image for an entire license plate or other substrate to be viewed on a video monitor.
The computer program of the present invention may be generally understood by reference to the overview of FIGS. 6 and 7. In the following description, two forms of raster files are mentioned: raw raster files and Sun raster files. By "raw raster files" is meant raster files having a specific identifying header for recognition and processing compatibility within the program of this invention. Those skilled in the art will recognize that many alternative identifying header types could be used to render raster file data structures internally consistent within a program.
FIG. 6 shows an overall data flow pattern associated with program. The data initially supplied to the computer ope~ ~ling the program may be provided either as an eye readable image, such as an image on paper which may be optically scanned and entered at the scanner interface or alternatively, the image may be prog,~ ,latically developed, such as the alpha numeric characters generated for license plates.
From the scanner interface, the scan filnction acts on the input image and converts it into an 8-bit Sun raster file which ncludes grey scale information. The contrast function converts the 8-bit raster file into a l-bit Sun raster file which is in black and white form.
The data for dçfining an image may also be provided by using the character function. Data generated by the character function is stored in a character _ CA 02204628 1997-0~-06 W O96/14604 PCT~US95/14564 library file. The m~k~string function is used to combine a plurality of files of individual characters from the character library, then act upon the combined data and converts it to a l-bit Sun raster file. Once an image is available as a 1-bit Sun raster file format, either the merge function and/or the scale function may be used to e-nh~nce or modify the final image. A l-bit Sun raster file may be converted by the print function into a l-bit raw raster file and then sent to the printer, via a Versatec printer interface, for conversion from raster from into a laser written latent image on a reusable drum surface. As explained earlier, portions of dry toner powder are accepted by the latent image portions of the reusable surface and subsequently L.~n~r~. ~ ed to the polymeric surface to be 1 0 printed.
In the data flow diagram of FIG. 6, the large outside circle represents all of the program or software of this invention within the computer. The four smaller circles repl esenls classes of files, such as 8-bit Sun raster files, compressed l-bit Sun raster files, l-bit Sun raster files (unco...~. essed) and l-bit raw raster files. Within the class of l-bit Sun raster files, several types may occur. For example, a l-bit Sun raster file might be a file resulting from a scanned image, a programmatically developed image, such as a single alpha numeric character, a file resulting from operation of the merge function on a pre-existing l-bit Sun raster file, or a file resulting from operation of the scale function on a pre-existing l-bit Sun raster file. Files may be reviewed through the printing process or by well known screen preview programs. The l-bit Sun raster files have a 36 byte header which inr~ic~te the data length of the file, the raster line length and the height, and the number of lines per image. A l-bit raw raster file by co---pa- ison, has to be predefined for the printer. The print function requires files with a header including the definition of the line width, typically pre-defined as 400 bytes per line.
As shown in FIG. 7, a process control flow chart shows the major logical flow of the program through all the furictions. Beginning with the scan function, an image file is converted from a grey scale to a l-bit Sun raster file using the contrast function. A user may review and confirm that an image file corresponds to the desired image. If not, the user may edit that image file or rescan the image. A user may repeat this sequence until the image is acceptable. An acceptable image is purely subjective to the user, however, for a typical license plate, an acceptable image will typically be recognized as large, solid printed alpha numeric regions on a unprinted background.

CA 02204628 1997-0~-06 Wo 96/14604 PCT/US9~/14564 Further, the edges of the alpha numeric image will be well define~l smooth lines or curves. Once an acceptable image file is present, the user proceeds to the next decision box.
Alternatively, a user may pro~ ic~lly generate character files using the make character function. A collection of character files is stored in cGr"~"t;ssed form in a library. A di~, ell~ Iibrary may be formed for each complete set of images. From the co...~"essed character files in a library, the makestring function combines a particular selected set of files to form a string of characters. For example, if a desired image string were "ABC"; the m~kestring function would first obtain the file for "A", second, the filnction would obtain the file for "B", third, the function would obtain the file for "C";
fourth, the function would append the files together, and fifth, the function would store the appended file as a l-bit Sun raster file.
Next, a user may check the image for acceptable size. If unacceptable, the user can use the scale function to increase the size or decrease the size of that image.
For example, if an image corresponding to the Statute of Liberty had been scanned in, the image size might be acceptable in shape but unacceptably small, for example only half the desired size. The user could double the image size using the scaling function.
Once the scaling function is used, a new 1-bit Sun raster file is formed.
The next step is to consider a character string and another image using the merge function. For example, the Statue of Liberty file might be combined with a character string file for a vehicle identification number, the two initial files and the final file being l-bit Sun raster files. Additional files may be subsequently added one at a time or three or four images can be combined in one operation.
Once a desired combined image file is formed, the file may be printed.
Any 1-bit Sun raster file may be accepted by the print function and sent to a Versatec printer interface. Those skilled in the art will recognize that raw raster files could alternatively be sent to other types of printer interfaces having the capability of accepting raw raster data and driving raster printers. The print function may also take a number of print files and sequentially send them to the printer.
A more detailed description ofthe particular functions ofthe plerelled program, with reference to FIGS. 8 through 15, follows.

CA 02204628 1997-0~-06 W O96114604 PCTrUS9S/1~561 As shown in the flow chart of FIG. 8, the make character function of the program allows a user to pro~ ;c~11y prepare files for specific images. For example, in the case of vehicle identific~tion numbers for license plates, a user may wish to prepare a set of alpha numeric characters.
A graphical user interface is displayed upon the computer screen to assist and prompt the user for this and other functions. The user first selects or accepts an appl op. iate character size input. The make character function of the program accepts the character size input and next allows prog,i."""il-g of a group of standard raster lines that are repeated as portions of characters within a set of characters. The make character function also de.sign~tes a "liberty" or directory for storage of the character files being prepared. Next, the program proceeds to prompt for the next character to be pl epa~ ed.
For a set of alpha numeric characters, the process is repeated 36 times, once for each numeral and letter. For each character, each raster line must be checked. The next line count allows the progressive advancing to the next raster line of the character file. For example, a 3 inch (7.6 cm) high character file at a resolution of 200 dots per inch, has about 600 raster lines, corresponding to about 600 horizontal lines.
If a particular raster line corresponds to a portion of the character that may be present in a repetitive or standard format, then that standard forrnat is used. For example, a letter "I" has two cross or horizontal bars connected by an upright or vertical bar. In the region of the upright bar, each raster line includes a portion or line segment of the upright bar. Thus, each raster line going through the upright bar uses the standard pregenerated raster line segm~ont to reduce the prog,;.,..l-.;n effort required for the character file "I". Similarly, standard raster line segments may be prepared for the two cross bars. Next, the user decides whether any more raster lines are needed to prepare the file. For example, if line number 300 has been written and the same line will be repeated until line 600, we go get the next line An alternative logic route is followed when a standard line is not appropriate. For example, in the case of the curves in the letter "C": The program calculates where the printed portion would appear for each raster line, depending upon the size of the characters to be printed.
Typically, character files are not long, although the more complex alpha numeric characters i.e. "S", "2" and "5" tend to be relatively large.

CA 02204628 1997-0~-06 W O96/14604 PCTrUS95/14564 One of the final operations of the make character function is to colllpress the file. Col,,yl ~s~ion of files serves to reduce the total amount of data in the file and - more efficiently uses memory as well as speeding data retrieval in later functions.
The logic of the scan function is shown in FIG. 9. Again the scan S function causes the display of a user interface screen to prompt and assist the user. The scan function first accepts a set a scanner parameters regarding the size of the image.
The scan function verifies that the selected parameters are such that the scanner can supply the number of lines corresponding to the lines specified by the parameters.
Parameters exceeding the accepted boundaries are rejected and the user prompted to supply a,. plop,i~le parameters. Next, a communication line to the scanner is opened and an output file opened to accept the data. For example, a Howtec scanner is capable of the following resolution possibilities: 75 dots per inch, 100 dots per inch, 150 dots per inch, 200 dots per inch and 300 dots per inch.
The scanner then provides information on a line by line basis corresponding to the eye readable image being scanned. The information, on a line by line basis is written to the output file. The resl-lting scan data is in 8-bit format, in order to include grey scale information for each pixel or dot. If an image was scanned at a resolution of 300 dots per inch in 10 inches, that would entail 3,000 lines and 3,000 repetitions of the logic loop. Finally, the scanner device and the output file would be closed.
As shown in FIG. 10, the contrast function is used to convert the grey scale 8-bit image information from the scanner to a black and white (print/no print) system more suitable for a reflective sing. A user interface screen from the contrast function yl OlllytS for a file name. If the file exists, the program retrieves it and proceeds.
The function first assists the user in selecting the best contrast point, i.e., a particular number between 0 and 25~ which serves as the best a,bil~,y division between grey~ scale values which will be considered black and grey scale values which will be considered white. Generally, the best contrast point is found from the distribution curve of frequency of occurrences plotted against grey scale value. On such a distribution curve, the best contrast point is a minimllm (preferably the deepest ~--;.. ;.,.~.-) located between a pair of maximums (as opposed to a minimllm at one end of the gray scale.) CA 02204628 1997-0~-06 W O96/14604 -22- PCTrUS9S114564 After selecting the best contrast point, the file is converted by ~,h~nging the data from an 8-bit file header to 1-bit file header. Effectively, the conversion divides the total file length by 8 and ch~n~es the grey scale tones to black or white. Each raster line is read until we find the end of file. If 600 raster lines are used, the process is repeated 600 times. Within the data, each byte r~:pl ~o~e.~ g grey scale information greater than the contrast point is set to 0. Bytes less than the contrast point are set to 1.
(Note that the l-bit raster format has 0 equal to white and an 8-bit raster format has 0 equal to black.) Once the end of each raster line is reached, the next raster line is started until all the data has been processed, then the file is closed.
As shown in FIG. 1 1, the makesL~ g function initially prol"pts and accepts user input consisting of a string of characters and a character type, corresponding to a predefined library. For example, for a 7 digit license plate for the U.S. displaying six characters and one blank, the ple~,.ed characters are about 3 inches high by about 1.25 inches wide (i.e., 7.6 cm X 3.2 cm).
l 5 The file for each selected character is retrieved and uncompressed to provide a l-bit raster format. The parameters of the output file are computed next. This entails adding the widths of all the character files together and then combining the width times the height of the character. For example, for a license plate having six letters each of image size 3 inches (7.6 cm) high by 1.25 inches (3.2 cm) wide the file must accommodate about 900,000 dots (i.e., 1.25 inches/letter X 6 letters X 200 dots per inch) X (3 inches/letter X 200 lines/inch). The files are combined by first reading a line from each file. Each of these lines should be the same number of lines down from the top of the image. The lines are next appended to form a single line. The process eventually results in a set of 600 output lines. The output lines are then written to an output file.
Finally, the output file is compressed and sent to the library.
As shown in FIGS. 12 and 13, the scale function is best explained as a two part function. In the first part, shown in FIG. 12, the vertical dimension of the image is expanded or contracted by adding or subtracting raster lines. In the second part, the horizontal dimension of the image is expanded or contracted by adding or subtracting data from each raster line.
As shown in FIG. 12, a user first instructs or inputs the file name and scale value. The scale value may be any value from 0 to 2.0 in increments of one-tenths.

- - - = = ~ =
CA 02204628 1997-0~-06 W O96/14604 PCTrUS95114564 The scale value of 2.0 means that the image will be dou~led on in both width and height and therefore the res llting image will be four times the area of the initial image.
Conversely if a scale factor of 0.5 is chosen the resultin~ image will be half as high and half as wide and the area will be one-quarter of the original. For clarity of explanation, the process will be e~rpl~ined for a scale factor of 2.0 (i.e., a doubling of image height and width.) Next, the initial file is read entirely into the buffèr. The initial file is treated as a two dimensional array of lines and height. The al,go,i~hl-, begins by finding the line segm~nte for the first line. This first line is temporarily named "y" or "previous line". The next line found and temporarily named "x" or '.'current line". The two lines are evaluated in order to calculate a line which will be inserted between the previous and current lines and thereby begin to double the image height. Be~inning points of line segm~nt~, (i.e., portions which will be printed) are averaged to determine a be~inning line segm~n~ point for the new line. Similarly, ending points are averaged to determine l 5 an cnding point for the new line segm~nt For example, if a beginning point of line y is at raster No. 232, and the beginning point of line x is at raster No. 234, then the line segment in the new line begins at raster dot 233. If the end point of line y is at 555 and the end point of line x is at 575, then the new line segment end point is a 565. Next, the points between the beginning and the end of the new line segmçnt are filled with "ones", such that those points will be printed as a black line egmçnt For some lines there may be multiple line segments, however all of the line segments in lines x and y that match or are partially overlapping are treated in the above manner.
The result is a newly calculated line inserted between the line y, which is on the top, and line x, on the bottom, and an image having increased height. To continue, a newer line must be calculated for insertion between the current line and the next succes.~ive line of the original image. For scale factors between 1.0 and 2.0, proportionately fewer insertions of newly calculated lines are made. For scale factors less than 1.0, a proportionate number of lines are deleted and no new lines need be calculated.
In the second part ofthe scale function, as shown in FIG. 13, the length of the line se~.. ,e~-l s to print will be increased or decreased. Each pixel or dot is treated as a member of a vertical column. Vertical columns are calculated and inserted to CA 02204628 1997-0~-06 W O96/14604 PCTrUS9~/14564 expand the image or alternatively deleted to reduce the image based upon the scale factors used in the first part of the scale function.
The completed image file resulting from the scale function is in l-bit Sun raster format and is written to a new file. The new l-bit Sun raster file can be merged, scaled or printed.
As shown in FIG. 14, the merge function allows a user to combine a plurality of image files into a single file. The user begins by identifying the files desired to be merged together and entering the file names. Next, the function computes the dimensions for the file which will be output based upon the dimensional parameters.of the files to be merged. If an unprinted border is desired, the border values are added to the file dimellsions and top border lines written to the new file. Next, the function determines whether there are more lines to combine. Subsequently, a raster line of each file is combined into a single new raster line and written to the new file. Finally, a bottom border may be added.
The print function as shown in FIG. 15, begins by accepting the file names of the files to be printed. If the file does not exist, the user is notified and requested to enter another file name. This function is designed to sequentially print multiple files and produce pl~ml)ts for additional files. When all the files to be printed have been identified, the function proceeds to open an input file and to open a print file, specifically, a l-bit raw raster file. (A l-bit raw raster file is shown in the data flow diagram of FIG. 6 as a circle.) Next, an input line from the input file is read. The input line is padded or truncated, if necessary, to assure that the line will contain exactly 400 bytes of information. Next, the input file and output l-bit raw raster file are closed.
Tmmedi~tely following that, the 1-bit raw raster print file is reopened as an input file and the printer device (a Versatec printer interface) is opened as output. A block of data is read from the input file. The block may be of any size, however, it is pre~" ed that the entire file is used as a single unit. Once the data has been read into the buffer, the data is written to the printer. At the end of the file, an end of file co,.".,and is sent to the printer device and the next file to print is found.
Computer programs useful in the present invention preferably include a number of program steps which, in combination, perform the major functions of the program. Specifically, the programs preferably include a function for making a character CA 02204628 1997-0~-06 W O 96114604 PCTrUS95/14564 which may be used as an image or a portion of an image; a fimction for sc~nnin~ in eye readable images; a fimction for adjusting contrast from grey scale to black and white; a ~ function for adjusting scale or size of the image definition; a fimction for assembling the individual characters in a string; a function for merging an image definition with a second preferably repetitive image; and a function for sending the image definition to a printer.
If a charge control agent is include~, it is recognized that colorants and adhesive binders can also affect the charging properties of the res-llting dry toner powder. See, for example, H.T. Macholdt and A. Sieber, "Triboelectric Charging Properties of Organic Color Pigment~," J. Imaging Technology 14:89-93 (1988).
The aggressively tacky PSA in adhesive layer 110 is selected as appl upl iate for the particular application, that is, depending upon the substrate, dry toner powder and protective layer composition, and use environment of the article.
Based upon the teaching.c contained herein, one of skill in the app-upliate chemical arts would be able to select the proper tacky PSA composition for a desired application to obtain approp, iate image quality, within the constraints of cost efficiency. For example, the tacky PSA in adhesive layer 110 is preferably compatible with the non-tacky binder adhesive of the dry toner powder so that their combination does not produce "haziness"
upon fusing. An acrylic-based tacky PSA is typically and preferably used in conjunction with a non-tacky acrylic dry toner powder binder adhesive, and this coml)indLionpreferably l~min~ted to an acrylic top-layer 104 of substrate 102. The charge control agent (if any) would preferably be a functionalized acrylic, and so on.
In embodiment 100 illustrated in FIG. 1, cover film 116 is intçntled as a permanent component of article 100, for example, as a protective covering for a license plate co---,~)-ising a ~eL-u~nective substrate. In this and similar embodiments, cover film 116 will preferably be weatherable, resistant to oils and grease, exhaust fumes, and transparent. Suitable materials for a transparent, weatherable cover film include copolymers of ethylene and acrylic acid, polymethylmethacrylate and other acrylate-based polymers and copolymers. Illustrative examples of suitable cover films aredisclosed in U.S. Patent No. 4,664,966 (Bailey et al.), U.S. Patent No. 4,767,659 (Bailey et al.), and 5,085,918, all incorporated herein by reference. Cover film 116 may be bonded to the rçm~inder of signage article 100 by the inherent adhesive properties of ~ . .

CA 02204628 1997-0~-06 W O96tl4604 PCTrUS95/14564 the tacky PSA in adhesive layer 110. Alternatively, bonding may be provided or enhanced by physical techniques such as corona tre~tmP-nt or by an optional primer or tie layer (not shown) interposed between cover film 116 and adhesive layer 110.
In other embo-iim~nts, protective material 116iS not ~ ar~ . For example, when material 116iS intended to serve as a temporary protective sheeting, e.g.
a removable protective liner of about 0.0013 cm to about 0.0076 cm thickness may be used. In such embo~liment~, protective material 116 is designed to provide temporary protection a~er m~nuf~ctllre and during shipping and storage. For such use, material 116 generally is made with score marks to allow material 116 to be easily peeled from article 100. A removable liner is useful when, for example, adhesive layer 110 of article lOO.is to be applied to a Llansl)aren~ object (such as a vehicle window) and dry toner powder layer 108 is to be viewed through the object. When applied to a tl~ns~aleobject, substrate 102 effectively serves as a protective material.
One advantageous feature of the present invention is that substrate 102 may be selected from a wide variety of materials, which include, but are not limited to, metal, wood, fibrous sheeting such as paper and cardboard, polymeric sheetin~
~ el- ol enective sheeting and combinations of these materials. In many previously known applications, selection of such substrates would prove impractical due to the effects of thermal and/or pressure treatment experienced during the fusing process. In certain prerel.c:d embodiments ofthe present invention, substrate 102 comprises retrolenective elements in a polymeric sheeting, such as an encapsulated-lens .shPeting (see, for example, U.S. Patents 3,190,178; 4,025,159; 4,896,943; 5,064,272; and 5,066,098), enclosed-lens sheeting (see, for example, U.S. Patent 2,407,680) or r~ r~nective-cube corner elements (see, for example, U.S. Patents 3,684,348; 4,801,193; 4,895,428; and 4,938,563), the disclosures of which are incorporated herein by reference.
Fused dry toner layer 108 adheres to at least a portion of surface 104 of substrate 102 in the embodiment 100 of FIG. 1. Fused dry toner layer 108 preferably forms indicia such as alphanumeric characters, bar codes, graphics, logos or desi~ns Such articles may or may not be combined with additional components to create signage articles for i.~o.lna~ional and/or decorative purposes. Although fused dry toner layer 108 generally is discontinuous over the surface of the substrate, in some embodiments a CA 02204628 1997-0~-06 W 096/14604 -27- PCTrUS95/14564 continuous layer may be desired. For example, a street name sign may have a continuous colored background layer.
~ If substrate 102 is a rell~r~nective sheetin~ a signage article may be used for traffic control materials, l eL- ul enective and non-, t;ll Ol ~;nective vehicle markings, rel,orenective garments, indoor/outdoor labeling products, frangible security stickers, product ~lthPntic~tion materials, inventory labeling and control products, identification systems, or license plates. Alternatively, if substrate 102is a fibrous sheeting, a signage article may be used for shipping and storage containers, store display packages, doc~lm~ntc and the like.
A plel~"ed inventive method for producing a signage article ofthis invention comprises the steps of applying dry toner powder composition to at least a portion of a first substrate surface, followed by l~min~ting a transparent plote~ e sheeting to the image precursor bearing surface. The protective sheeting comprises an inner tacky PSA adhesive layer and an outer cover film, and l~min~tion results when the l 5 tacky PSA adhesive layer contacts (with light pressure) the dry toner powder and fuses the dry toner powder. In an alternate second inventive method, the surfaces to which the dry toner powder and the tacky PSA adhesive layer are applied are reversed, i.e., dry toner powder is applied to a cover layer, and the dry toner powder-bearing cover layer is laminated to a substrate having a tacky PSA adhesive layer on its surface.
An embodiment of a method for producing a signage article according to the present invention is illustrated in FIG. 2. In method 200, substrate 202 is provided with raised portions 204 embossed into substrate 202. A station 206 applies dry toner powder obtained from a reservoir (not shown) to raised portions 204. Station 206comprises a rotating drum 208 carrying a layer 210 of dry toner powder. Rotating drum 208, which may be, for example, a hard rubber roller, contacts or nearly contacts raised portions 204 of substrate 202. The contact or near contact between the rotating drum 208 and raised portion 204 aliows transfer of at least a portion of dry toner powder layer 210 onto raised portion 204 to form an image layer 212, without ~ -srt:"h~g dry toner powder onto non-raised portions 214 of substrate 202. Optionally, L,~n~rel of dry toner powder may be f~cilit~ted by warming substrate 202 with a heat element 216 to a temperature above room t~ll,pe-~L-~re, but be!ow a temperature which would have a W O 96/1460~ PCTrUS9~/14564 degradative effect on the substrate or co",ponent of the substrate. Such te"")e,~ re would typically be less than about 125~C.
Next, a l,~nspa,e,ll cover film 21~ is provided from roll 220. Tacky adhesive precursor 222 comprising a tacky PSA and a volatile organic solvent is applied from a reservoir 224 to cover film 218 to form L,~,1s~alel,L prote~ e sheeting 226.
Solvent is evaporated, and a contro.l roller 228 guides protective sheeting 226 into close p,o~i",iLy to the image-bearing substrate 202 at a nip 230 that is forrned by rollers 232 and 234. Sufficient pressure is applied at nip 230 to l~min~te protective ~heeting 226, tacky adhesive side down, to substrate 202, yielding signage article 236 having fused dry toner powder thereon. Sufficient pressure for l~r.. in~ g substrate 202 and protective sheeting 226 will vary, depending upon the substrate, PSA and cover film materials used. For a substrate comprising r~L~ ol-enective sheeting having a vinyl protective layer and using a tacky acrylic PSA, the pressure at nip 230 typically ranges from about 690 kPa (100 psi) to about 1,380 kPa (200 psi) when the temperature is about 25~C, and the l 5 speed through the nip is about I to 100 meters/min, with low speeds being generally used with low nip pressure, and high speeds generally used with high nip pressure.
T.~min~tion of.sheeting 226 to substrate 202 also may be carried out by stamping or other similar processes. Alternatively, protective sheeting 226 can be supplied with a removable protective liner disposed on the tacky PSA adhesive layer side. The liner is peeled away from the tacky adhesive layer side before sheeting 226 is brought into pro~ill,;Ly with image-bearing substrate 202 at nip 230.
Substrate 202 may be provided as a continuous web or as discrete sheets.
If provided as a continuous web, the web can be cut to the approp,iate size after application of the protective covering film to yield finished articles. If the substrate is provided in discrete sheets, the cover film can similarly be provided and l~min~ted to the substrate as discrete sheets.
If desired, substrate 202 may optionally be treated after applying dry toner powder but before application of tacky adhesive in order to ~iiminich the physical shifting of the dry toner powder and to m~int~in the desired edge definition in image layer 212. Such treatment may be, for example, passage through a nip or past a heating element 217, illustrated in Figure 2, to a temperature less than about 150~C, or using CA 02204628 1997-0~-06 W O96/14604 PCTrUS95114564 static charge to hold the dry toner powder in place until application of the tacky PSA
coated pl ote~ e covering.
~ An alternative embodiment of a method for producing an article is shown in FIG. 3, in which the substrate is not embossed. Method 300 comprises the step of S applying dry toner powder to the surface of substrate 302, using station 304. Station 304 is co-,lp, ised of laser im~Ein~ device 310 and rotating drum 306 having a reusable surface 308 that is initially electrostatically charged. The electrostatic charge on surface 308 is altered by laser im~ging device 310 to form a latent image on surface 308, which then accepts dry toner powder from reservoir 312 to form a layer of dry toner powder 314 on at least a portion of surface 308 arranged in a pattern corresponding to the image defined by laser im~in~ device 310.
Dry toner powder layer 314 carried upon surface 308 is brought into contact or near contact with substrate 302 and transferred to the surface thereofto produce a dry toner powder-bearing substrate 317. The transferred dry toner powder preferably forms an image layer 316 on the surface of substrate 302. Reusable surface 308 is subsequently used in ~,~nsre-ling new images to other portions of substrate 302 or to new substrates.
Next, cover film 320 is provided from a roll 322. A tacky adhesive precursor layer 324 comprising a tacky PSA and solvent carrier is applied from areservoir 326 to cover film 320 to form t~ns~,are~,~ protective sheeting 32~, the solvent being evaporated. A control roller 330 guides sheeting 328 into close pro~;",;Ly to dry toner powder-bearing substrate 317 at a nip 332 that is formed by two rollers 334 and 336. Nip 332 applies sufficient pressure to attach cover film 320 to substrate 302 and fuse the dry toner powder. When the substrate is a I t;ll u, ~nective sheeting having a vinyl protective layer and the dry toner powder binding adhesive is acrylic, as well as the tacky PSA, the pressure between rollers preferably ranges from about 100 to about 200 KPa at 25~C at a web speed of about 1-100 meters/min, as previously mentioned. As in method 200, cover sheet material can be provided with the tacky adhesive layer already applied and protected by a removable protective liner. The substrate and the cover film can be supplied as continuous webs or as discrete sheets.
A sch- m~tic cross section view (enlarged) of a second embodiment of a signage article is illustrated in FIG. 4. Signage article 400 co"""ises substrate 102, CA 02204628 1997-0~-06 W O 96/14604 pcTrus95ll4s64 adhered by a tacky adhesive layer 408 CO~ .;S;ilg a tacky PSA to a ll~.lsyare-.~ cover film 420, with a fused dry toner powder layer 414. Tacky adhesive layer 408 is ~tt~rhed to substrate surface 104, and is s~lbsl;~ ;Ally continuously bonded to surface 418 of transparent cover film 420, except for those portions that are a(lj~cent to layer 414.
Fused dry toner powder layer 414 is at least partially solubilized or wetted by PSA in tacky adhesive layer 408. Layer 414 comprises fused dry toner powder that has been applied to surface 418 of film 420 and is fusibly admixed with the PSA in adhesive layer 408 within the boundaries defined by the application of the dry toner powder. Infinished form, fused dry toner powder layer 414 preferably co...l,.;ses indicia which is visible to an observer through ~-anspare.. ~ cover film 420.
A method for producing signage article 400 of FIG. 4 is illustrated sçh~m~tic~lly in FIG. 3 except that dry toner powder is applied by a . ~,taLing drum mech~nicm to a ~nsl,alenl cover film rather than the substrate, and a tacky adhesive layer is applied to a substrate rather than the t.anspa,en~ cover film.
In the methods illustrated in FIGs. 2 and 3, optional processing steps may include adhesion promoting steps such as chemical and/or mech~nic~l tre~tm~nt ofsurfaces to increase adhesion, such as mechanical roughing, corona trç~tment and or chemical priming. Corona tre~tment of films is a well-known technique, and is described generally in Cramm, R.H., and Bibee, D.V., The Theory and Practice of Corona Treatment for Improving Adhesion~ TAPPI, Vol. 65, No. 8, pp 75-78 (August 1982).Examples of chemical primers for vinyl and polyethylene terephth~l~te films include crosslinked acrylic ester/acrylic acid copolymers disclosed in U.S. Pat. No. 3,578,622.
An advantage of the present invention is an increase in the types of substrates to which dry toner powder may be applied, in particular, substrates such as reL,orenective sheeting.c that cannot withct~nd fusing of dry toner powder a~ high temperatures. Another advantage relates to the equipment used to produce articles of the invention. Costly and complicated equipment is no longer needed to fuse dry toner powder by heat. With less heating required, fewer and less costly safety devices are needed. T ~ AI;I~ equipment used to apply an adhesive layer in the present invention, such as rollers, stampers and the like, generally is less expensive and less prone to breakdown than equipment used to heat-fuse dry toner powder. Further, operating costs are reduced when practicing methods of the invention, since the ~iiminiched heating CA 02204628 l997-0~-06 W O 96/14604 PCTrUS95/14564 requirements for fusing dry toner powder also reduces energy e~rçn~itllres. Because of lower inv~ costs, the articles and methods of the invention are suited for small, as well as large, production runs.
A further advantage relates to costs of stopping production of signage S articles during a m~n-lf~ct--ring cycle. Known methods of applying and fusing dry toner powder to a substrate may result in damage to the res~lltinp. signage articles when production must be stopped prior to completion of a m~nllf~ctllring cycle. Such damage often results from the high ten")e,~lures typically used in fusing dry toner powder to a substrate. In contrast, articles produced according to methods of the invention do not have such telllpel alure-related damage if production is stopped within a cycle, thus redllcing waste.
The products resulting from the present invention are dçsi~ned to be viewed by an observer. The ultim~te uc~fi-lne~ ofthe invention will be at least partially determined by the quality of the image produced. The image quality of articles produced according to the present invention is as good or better than the image quality produced by conventional fusing techniques utili7ing high tem~e,~ res and/or pressures. Articles made according to this invention have sharp edge definition, more image density, and less light scattering than similar articles having images fused by known fusing methods.
Another advantage relates to color development in articles of the invention. Such articles have better color development in that not only do such articles reflect more light, but colors appear more vivid and more intense than articles made by known fusing techniques. Articles according to the invention typically are ~,~rt;llt;d over articles produced by known methods because of the improved color development.
Therefore, the invention is not only important for enlarging the range of substrates that are suitable for printing and fusing dry toner powder thereupon, but it is ~ also useful as an inexpensive and convenient procedure for producing very high quality images on many different substrates when a protective cover layer is desired.

EXAMPLES
Features and advantages of this invention are further illustrated in the following Examples. It is to be expressly understood, however, that while the Examples CA 02204628 l997-0~-06 W O96/1460~ PCTrUS95/1456 serve this purpose, the particular ingredients and amounts used as well as otherconditions and details are not to be construed in a manner that would unduly limit the scope of this invention. All parts and pelce~ es are by weight unless otherwise specified.
Example 1 This example dPmon~trates a method of making a particularly p,~;;rel,ed signage article of the invention, as illustrated in cross-section in FIG. 5.
Dry toner powder was plc;pa~ed from a mixture co",~ h~g: 79 parts acrylic binder resin known under the trade desi~n~tion ACRYLOID B-48 (Rohm &
Haas Company); 8 parts of charge carrier known under the trade designation TRIBLOX
PC-100 (DuPont Co~ )arly);13 parts of colorant known under the trade de~ign~tionHELIOGEN BLUE K691 lD (BASF Corporation); 0.2 part of colorant known under the trade dç~ign~tion PROJET 900 MP (ICI Ltd.); and 0.1 part of a flow additive known under the trade designation CAB-O-SIL TS530 (Cabot Corporation). The components were mixed in a Baker Perkins gear drive variable speed twin screw extruder with a Haake record torque, l,eol"eter and extruded as a mixture at a temperature range between 150~C to 225~C. The extruded mixture was hammermilled,and subsequently jet milled in a NPK supersonic jetmill known under the trade designation PJM TDS-2 from Nippon Pnel~m~tic Manufacturing Company. The jet milled sample was then classified to collect material having a particle size ranging from 5 to 20 micrometers.
The dry toner powder was placed in the toner hopper of a Siemens Brand MODEL 2900 printer. The MODEL 2900 printer was originally designed for paper, but may be operated on continuous film-based webs with modifications that are within the skill of the art. The printer is capable of printing 240 dots per inch (94.5 dots per centimeter) ho,i~onlal and vertical resolution. The dry toner powder was applied by the printer to form the word SAMPLE. Each letter was about 7.3 centimeters in height and about 3 centimet~rs in width. The substrate for printing was a transparent cover film of ethylene acrylic acid (EAA) copolymer about 0.0061 cm thick, disposed on a removable polyethylene terephth~l~te (PET) carrier about 0.0025 cm thick.

CA 02204628 1997-0~-06 W O96/14604 PCTrUS9S/14~64 A~er printing, the film was sent through a nip at 100~C, just sufflcient to hold the dry toner powder in place. 3M Co. REFLECTO-LITE Brand reLlu~enective - ~hf~etin~ was coated on top of the reflective surface with a PSA p~ u~ :~or composition colllyli~ing a 95.5/4.5 weight ratio isooctyl acrylate/acrylic acid copolymer and a S heptane.isop,upanol solvent to a dried thirl~ness of about 0.1 cm. The printed surface of the EAA film was brought in contact with the adhesive-coated ~ ~ nective sheeting and the two materials were l~min~ted with a squeeze roll applicator at ambient temperature (about 25~C). The pressure between squeeze roll application rolls was about 40 PSIG (276 KPa), and the speed ofthe web through the nip was 1.2 meters/min. The carrier web was removed from the EAA film a~cer l~.. ;.. ~;on, resulting in a finichPd signage article 500 as illustrated in enlarged cross section in FIG. 5. Article 500 consists of a plastic liner 502; a tacly PSA layer 504 comprising a 95.5/4.5 weight ratio isooctyl acrylate/acrylic acid copolyrner; another plastic film layer 506, known under the trade desi~n~tion SCOTCHPACK, available from 3M Co. (a blend of polyethylene and polyethylene terephth~l~te) which is heat sealed at areas 508 to a portion of the concavities of a leLIolenective sheeting 510 known under the trade de~i~n~tion DIAMOND GRADE, from 3M Co.; fused dry toner powder layer 512;
tacky PSA layer 514 comprising the same tacky PSA as layer 504; and a Ll ~nspal enl EAA copolymer cover film 516. The same article was subsequently put in the nip rollers and held at 25~C for 15 mimltç~ 1 hour, and 15 hours at different letters ofthe word SAMPLE to determine the effect of longer COIlll)I ession times on image clarity. The image was more fully fused with increased time of compression, producing a deeper blue color.
It should be noted that the substrate R in FIG. 5 could also comprise any number of substrates, such as enclosed-lens r~L,o, ~nective sheetings as disclosed in U.S.
Pat. Nos. 5,085,918 and 4,664,966, incorporated by reference herein for their te~çlling of such l e~l orenective sheetings.

COMPARATIVE EXAMPLE
A top film of EAA copolymer was printed with dry toner powder as described in Example 1. The EAA film was l~min~te-l7 image-bearing side down, to a lellolenective sheeting similar to Example 1, but without a tacky PSA layer on the CA 02204628 1997-0~-06 W 096/14604 PCT~US95/14564 surface. The dry toner powder was fi~sed by using a conventional heat/pressure fusing techni1ue using a fusing temperature of 1 50~C and nip roll pressure of about 1 megaPascal.

E~cample 2 A variety of samples of signage articles were pl~l)alt;d according to the method of Examples 1 and the Co-,-pa-aLi~re Example method at various te---pe-~ res.
The resulting articles were evaluated accol dh~g to a number of criteria: overall appea,~l~ce, visual color, uniro----ily, edge definition, and image shal~,ness, among others. The relative rankings for the evaluated samples, along with their compositions and fusion lle~l~..e~ are reported in Table 1. In each case the speed ofthe web through the nip rollers was 2 meter/min.
In Table 1, the following design~tions are used:

"Acrylic CC" = cube-corner rt:~oreflective sheeting having acrylic cube-corners.
"Alkyl-enclosed bead" = enclosed bead l~llolenective sheeting having an alkyd binder.

"Acrylic-encapsulated bead" = encapsulated bead retroreflective ~heeting having an acrylic binder.

"A" = a 95.5/4.5 weight ratio copolymer of isooctyl acrylate/acrylic acid.

"B" = a 90/10 weight ratio copolymer of isooctyl acrylate/acrylic acid.

"C" = made by mixing 50 parts VYNATHENE 902 (Quantum Chemicals); 24.8 parts PICCOTEX LC (Hercules); 25.2 parts WINGTACK 10 (Goodyear); and 100 parts toluene for two hours, coated using a knife coater and dried (air dry for 20 min., oven dried for 10 min at 70~C).
"D" = made by mixing 44 parts KRATON G1657 (Shell Chemicals); 44.4 parts REGALREZ 1085 and 14.6 parts REGALREZ 1018 (both from Hercules Company); and 100 parts toluene for two hours, coated using a knife coater and dried (air dried for 20 rnin., oven dried for 10 min. at 70~C).

Color Density = ranking based on a scale of 1 to 10, a relative co,l,~;son of samples within the same set (a set insl~ldes the same printed substrate). Attributes considered were overall appe~nce, visual color, unirolll~lly, edge definition, image sh~l,ness, and the like, as judged by an observer skilled in the art.

CA 02204628 l997-05-06 W O96/14604 PCTrUS95/14564 c ~9 ~ ~ ~ ~ _ L. ~
~ ~u~ ~o o X o ~ t~
o _ ~ . C'i C~

C ~
-o ~_ ~
o ~ ~Ll ~ ~Ll ~ L~

~ O o O O ~ C .~

-o ~ ~
V ~ ~ ~ O o C ~ C c~ C ~ C
3 ~ D .~ D

U~ oo O~

W O 96/14604 _ 37 _ PCTrUS95/14564 .~3 ~ -- 'D ~ I _ o .
_ _ _ _ C C~ V
E~ o o o ~ o ~ ~D ~ ~ ~ ~_ r ¢ ~, ¢ ~ o ~o ~ D ~ D Y D ~ D ~ ~ D ~ ~ D

C~ O ~ C'l ~ d If~
ca W O96/14604 PCTrUS95/14564 The density and the overall print quality of the images produced in acco..lal~ce with the invention were subst~nti~lly better than the co--.pa,~Li~re examples where no tacky PSA was used to fuse the dry toner powder.
hou~h the present invention has been described with reference to the p,~r~ d embo~ , workers skilled in the art will recognize that challges may be made in form and detail without departing from the scope of the appended claims

Claims (11)

CLAIMS:

1. A signage article comprising:
a) a first substrate e having first and second major surfaces;
b) a fused dry toner powder adhered to the first surface of the first substrate, the fused dry toner powder comprised of a colorant and a binder, the binder comprising a combination of first and second adhesives, the first adhesive beingnon-tacky at about 25°C, the second adhesive being transparent and aggressively tacky at 25°C; and c) a second substrate adhered by an adhesive layer to the fused dry toner powder and first surface of the first substrate, the adhesive layer comprising a major portion of the second adhesive, either the first or second substrate beingtransparent.

2. Article in accordance with claim 1 wherein the fused dry toner powder is in the form of alphanumeric symbols.

3. Article in accordance with claim 1 wherein the first substrate is selected from the group consisting of encapsulated-lens retroreflective sheeting and enclosed-lens retroreflective sheeting.

4. A signage article comprising:
a) a liner;
b) a first adhesive layer having first and second major surfaces, the first surface removably adhered to the liner;
c) a plastic film layer having first and second major surfaces, the plastic film layer coterminous with the first adhesive layer, the first major surface of the plastic film layer adhered to the second major surface of the adhesive layer;
d) a retroreflective layer having first and second surfaces;
e) a plurality of areas of fused dry toner powder adhered to the second surface of the retroreflective layer, the fused dry toner powder comprised of a colorant and a binder, the binder comprised of first and second adhesives, the first adhesive being non-tacky at about 25°C, the second adhesive being transparent and aggressively tacky at 25°C; and f) an optional transparent protective layer adhered by a second adhesive layer to the fused dry toner powder and second surface of the retroreflective layer, the second adhesive layer comprising a major portion of the second adhesive.

5. Article in accordance with claim 4 wherein the first surface of the retroreflective layer is defined by a plurality of concavities, a first portion of the concavities filled with and adhered to the second major surface of the plastic film layer, a second portion of the concavities not filled with or adhered to the second major surface of the plastic film layer, the second surface of the retroreflective layer being substantially smooth.

6. Article in accordance with claim 5 wherein the concavities of the retroreflective layer are defined by cube-corner elements.

7. Article in accordance with claim 4 wherein the retroreflective layer comprises a laminate of polymethylmethacrylate sheeting and polycarbonate layer, the polymethylmethacrylate sheeting forming the smooth surface, the polycarbonate layer forming the plurality of concavities.

8. Article in accordance with claim 4 wherein said retroreflective layer is selected from the group consisting of enclosed-lens retroreflective sheeting and encapsulated-lens retroreflective sheeting.

9. Article in accordance with claim 4 wherein the first adhesive layer is comprised of the second adhesive.

10. Article in accordance with claim 9 wherein the first and second adhesive layers comprise a tacky copolymer of a major portion of isooctyl acrylate and a minor portion of acrylic acid, and wherein the first adhesive is a non-tacky acrylate.

11. A method of making a signage article comprising the steps of:
a) providing a first substrate having a first major surface;
b) applying a dry toner powder composition to at least a portion of the first major surface of the first substrate, the dry toner powder composition comprising a colorant and a first adhesive which is non-tacky at about 25°C;
c) applying over the dry toner powder composition and the first surface of the first substrate a coatable composition comprising a second adhesive, the second adhesive being transparent and aggressively tacky at about 25°C, thus forming a tacky adhesive layer;
d) applying a second substrate over the coatable composition, at least one of the first and second substrates being transparent, thus forming an intermediate article; and e) applying sufficient compression to the intermediate article to fuse the dry toner powder composition.