AU2007362596B2 - Biodegradable fibers formed from a thermoplastic composition containing polylactic acid and a polyether copolymer - Google Patents

Abstract

A biodegradable fiber for use in forming a nonwoven web is provided. The fiber is formed from a thermoplastic composition comprising at least one polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the polyether copolymer contains from about 40 mol.% to about 95 mol.% of a repeating unit (A) having the following formula. wherein, x is an integer from 1 to 250, the polyether copolymer further containing from about 5 mol.% to about 60mol.% of a repeating unit (B) having the following formula. wherein, n is an integer from 3 to 20; and y is an integer from 1 to 150. Such polyether copolymers have been found to improve a variety of characteristics of the resulting thermoplastic composition, including its ability to be melt processed into fibers and webs, as well as its sensitivity to moisture.

Description

BIODEGRADABLE FIBERS FORMED FROM A THERMOPLASTIC COMPOSITION CONTAINING POLYLACTIC ACID AND A POLYETHER COPOLYMER 5 Background of the Invention Various attempts have been made to form nonwoven webs from biodegradable polymers. Although fibers prepared from biodegradable polymers are known, problems have been encountered with their use. For example, polylactic acid ("PLA") is one of the most common biodegradable and sustainable 10 (renewable) polymers used to form nonwoven webs. Unfortunately, PLA nonwoven webs generally possess a low bond flexibility and high roughness due to the high glass transition temperature and slow crystallization rate of polylactic acid. In turn, thermally bonded PLA nonwoven webs often exhibit low elongations that are not acceptable in certain applications, such as in an absorbent article. 15 Likewise, though polylactic acid may withstand high draw ratios, it requires high levels of draw energy to achieve the crystallization needed to overcome heat shrinkage. Other biodegradable polymers, such as polybutylene succinate (PBS), polybutylene adipate terephthalate (PBAT) and polycaprolactone (PCL), have a low glass transition temperature and softness characteristic similar to polyethylene. 20 However, these polymers typically possess a small bonding window, which leads to difficulty in forming a nonwoven web from such polymers at high speeds. As such, a need currently exists for fibers that are biodegradable and exhibits good mechanical properties. As used herein, except where the context requires otherwise the term 25 "comprise" and variations of the term, such as "comprising", "comprises" and "comprised", are not intended to exclude other additives, components, integers or steps. Reference to any prior art in the specification is not, and should not be taken as, an acknowledgment or any form of suggestion that this prior art forms 30 part of the common general knowledge in Australia or that this prior art could reasonably be expected to be ascertained, understood and regarded as relevant by a person skilled in the art. Summary of the Invention In accordance with one embodiment of the present invention, a 1 biodegradable fiber for use in forming a nonwoven web is disclosed. The fiber is formed from a thermoplastic composition comprising at least one polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the 5 polyether copolymer comprises from about 40 mol.% to about 95 mol.% of a repeating unit (A) having the following formula:

C

2

H

4 0 (A) wherein, 10 x is an integer from 1 to 250, the polyether copolymer further comprising from about 5 mol.% to about 60 mol.% of a repeating unit (B) having the following formula: CnH 2 nO (B) 15 wherein, n is an integer from 3 to 20; and y is an integer from 1 to 150. In accordance with another embodiment of the invention, there is provided a nonwoven web comprising biodegradable fibers, the fibers being formed from a 20 thermoplastic composition comprising at least one polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the polyether copolymer comprises from about 40 moI% to about 95 mol.% of a repeating unit (A) having the following formula:

C

2

H

4 0 25 (A) wherein, x is an integer from 1 to 250, the polyether copolymer further comprising from about 5 mol.% to about 60 2 mol.% of a repeating unit (B) having the following formula: CnH 2 nO (B) wherein, 5 n is an integer from 3 to 20; and y is an integer from 1 to 150. According to yet another embodiment of the invention, there is provided a method for forming a nonwoven web, the method comprising: melt extruding a thermoplastic composition that comprises at least one 10 polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the polyether copolymer comprises from about 40 mol.% to about 95 mol.% of a repeating unit (A) having the following formula:

C

2

H

4 0 15 (A) wherein, x is an integer from 1 to 250, the polyether copolymer further comprising from about 5 mol.% to about 60 mol.% of a repeating unit (B) having the following formula: CnH 2 n O 20 (B) wherein, n is an integer from 3 to 20; and y is an integer from 1 to 150; and 25 randomly depositing the extruded thermoplastic composition onto a surface to form a nonwoven web. Brief Description of the Drawings A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth more 2a particularly in the remainder of the specification, which makes reference to the appended figures in which: Fig. 1 is a schematic illustration of a process that may be used in one embodiment of the present invention to form a nonwoven web; and 5 Fig. 2 is a schematic illustration of a process that may be used in one embodiment of the present invention to form a coform web. Repeat use of references characters in the present specification and drawings is intended to represent same or analogous features or elements of the invention. 10 Detailed Description of Representative Embodiments Reference now will be made in detail to various embodiments of the invention, one or more examples of which are set forth below. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and 15 variations may be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment, may be used on another embodiment to yield a still further embodiment. Thus, it is intended that the present invention covers such 2b WO 2009/078849 PCT/US20071087339 modifications and variations as come within the scope of the appended claims and their equivalents. Definitions As used herein, the term "biodegradable" or "biodegradable polymer" 5 generally refers to a material that degrades from the action of naturally occurring microorganisms, such as bacteria, fungi, and algae; environmental heat; moisture; or other environmental factors. The biodegradability of a material may be determined using ASTM Test Method 5338.92. As used herein, the term "fibers" refer to elongated extrudates formed by 10 passing a polymer through a forming orifice such as a die. Unless noted otherwise, the term "fibers" includes discontinuous fibers having a definite length and substantially continuous filaments. Substantially filaments may, for instance, have a length much greater than their diameter, such as a length to diameter ratio ("aspect ratio") greater than about 15,000 to 1, and in some cases, greater than 15 about 50,000 to 1. As used herein, the term "monocomponent" refers to fibers formed from one polymer. Of course, this does not exclude fibers to which additives have been added for color, anti-static properties, lubrication, hydrophilicity, liquid repellency, etc. 20 As used herein, the term "multicomponent" refers to fibers formed from at least two polymers (e.g., bicomponent fibers) that are extruded from separate extruders. The polymers are arranged in substantially constantly positioned distinct zones across the cross-section of the fibers. The components may be arranged in any desired configuration, such as sheath-core, side-by-side, 25 segmented pie, island-in-the-sea, and so forth. Various methods for forming multicomponent fibers are described in U.S. Patent Nos. 4,789,592 to Taniguchi et al. and U.S. Patent No. 5,336,552 to Strack et al., 5,108,820 to Kaneko, et al., 4,795,668 to Kruege, et al., 5,382,400 to Pike, et al., 5,336,552 to Strack, et al., and 6,200,669 to Marmon, et al., which are incorporated herein in their entirety by 30 reference thereto for all purposes. Multicomponent fibers having various irregular shapes may also be formed, such as described in U.S. Patent Nos. 5,277,976 to HoqIe, et al., 5,162,074 to Hills, 5,466,410 to Hills, 5,069,970 to Larqman, et al., 3 WO 2009/078849 PCT/US20071087339 and 5,057,368 to Largman, et al., which are incorporated herein in their entirety by reference thereto for all purposes. As used herein, the term "multiconstituent" refers to fibers formed from at least two polymers (e.g., biconstituent fibers) that are extruded as a blend. The 5 polymers are not arranged in substantially constantly positioned distinct zones across the cross-section of the fibers. Various multiconstituent fibers are described in U.S. Patent No. 5,108,827 to Gessner, which is incorporated herein in its entirety by reference thereto for all purposes. As used herein, the term "nonwoven web" refers to a web having a structure 10 of individual fibers that are randomly interlaid, not in an identifiable manner as in a knitted fabric. Nonwoven webs include, for example, meltblown webs, spunbond webs, carded webs, wet-laid webs, airlaid webs, coform webs, hydraulically entangled webs, etc. The basis weight of the nonwoven web may generally vary, but is typically from about 5 grams per square meter ("gsm") to 200 gsm, in some 15 embodiments from about 10 gsm to about 150 gsm, and in some embodiments, from about 15 gsm to about 100 gsm. As used herein, the term "meltblown" web or layer generally refers to a nonwoven web that is formed by a process in which a molten thermoplastic material is extruded through a plurality of fine, usually circular, die capillaries as 20 molten fibers into converging high velocity gas (e.g., air) streams that attenuate the fibers of molten thermoplastic material to reduce their diameter, which may be to microfiber diameter. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a collecting surface to form a web of randomly dispersed meltblown fibers. Such a process is disclosed, for example, in 25 U.S. Patent Nos. 3,849,241 to Butin, et al.; 4,307,143 to Meitner, et al.; and 4,707,398 to Wisneski, et al., which are incorporated herein in their entirety by reference thereto for all purposes. Meltblown fibers may be substantially continuous or discontinuous, and are generally tacky when deposited onto a collecting surface. 30 As used herein, the term "spunbond" web or layer generally refers to a nonwoven web containing small diameter substantially continuous filaments. The filaments are formed by extruding a molten thermoplastic material from a plurality of fine, usually circular, capillaries of a spinnerette with the diameter of the 4 WO 2009/078849 PCT/US20071087339 extruded filaments then being rapidly reduced as by, for example, eductive drawing and/or other well-known spunbonding mechanisms. The production of spunbond webs is described and illustrated, for example, in U.S. Patent Nos. 4,340,563 to Appel, et al., 3,692,618 to Dorschner, et al., 3,802,817 to Matsuki, et 5 al., 3,338,992 to Kinney, 3,341,394 to Kinney, 3,502,763 to Hartman, 3,502,538 to Levy, 3,542,615 to Dobo, et al., and 5,382,400 to Pike, et al., which are incorporated herein in their entirety by reference thereto for all purposes. Spunbond filaments are generally not tacky when they are deposited onto a collecting surface. Spunbond filaments may sometimes have diameters less than 10 about 40 micrometers, and are often between about 5 to about 20 micrometers. Detailed Description Generally speaking, the present invention is directed to a biodegradable nonwoven web that is formed from a thermoplastic composition that contains polylactic acid and a polyether copolymer. The polyether copolymer has been 15 found to improve a variety of characteristics of the resulting thermoplastic composition, including its ability to be melt processed into fibers and webs, as well as its sensitivity to moisture. The relative amount of the polyether copolymer and polylactic acid in the thermoplastic composition is selectively controlled to achieve a desired balance between biodegradability and the mechanical properties of the 20 resulting fibers and webs. For example, polylactic acid typically constitutes from about 75 wt.% to about 99 wt.%, in some embodiments from about 80 wt.% to about 98 wt.%, and in some embodiments, from about 85 wt.% to about 95 wt.% of the thermoplastic composition. Likewise, the polyether copolymer may constitute from about 1 wt.% to about 25 wt.%, in some embodiments from about 2 wt.% to 25 about 20 wt.%, and in some embodiments, from about 5 wt.% to about 15 wt.% of the thermoplastic composition. Various embodiments of the present invention will now be described in more detail. I. Thermoplastic Composition 30 A. Polylactic Acid Polylactic acid may generally be derived from monomer units of any isomer of lactic acid, such as levorotory-lactic acid ("L-lactic acid"), dextrorotatory-lactic acid ("D-lactic acid"), meso-lactic acid, or mixtures thereof. Monomer units may 5 WO 2009/078849 PCT/US20071087339 also be formed from anhydrides of any isomer of lactic acid, including L-lactide, D lactide, meso-lactide, or mixtures thereof. Cyclic dimers of such lactic acids and/or lactides may also be employed. Any known polymerization method, such as polycondensation or ring-opening polymerization, may be used to polymerize lactic 5 acid. A small amount of a chain-extending agent (e.g., a diisocyanate compound, an epoxy compound or an acid anhydride) may also be employed. The polylactic acid may be a homopolymer or a copolymer, such as one that contains monomer units derived from L-lactic acid and monomer units derived from D-lactic acid. Although not required, the rate of content of one of the monomer unit derived from 10 L-lactic acid and the monomer unit derived from D-lactic acid is preferably about 85 mole% or more, in some embodiments about 90 mole% or more, and in some embodiments, about 95 mole% or more. Multiple polylactic acids, each having a different ratio between the monomer unit derived from L-lactic acid and the monomer unit derived from D-lactic acid, may be blended at an arbitrary 15 percentage. Of course, polylactic acid may also be blended with other types of polymers (e.g., polyolefins, polyesters, etc.) to provided a variety of different of benefits, such as processing, fiber formation, etc. In one particular embodiment, the polylactic acid has the following general structure:

CH

3 O O -C-C 20 One specific example of a suitable polylactic acid polymer that may be used in the present invention is commercially available from Biomer, Inc. of Krailling, Germany) under the name BIOMER T M L9000. Other suitable polylactic acid polymers are commercially available from Natureworks LLC of Minnetonka, 25 Minnesota (NATUREWORKS@) or Mitsui Chemical (LACEA

TM

). Still other suitable polylactic acids may be described in U.S. Patent Nos. 4,797,468; 5,470,944; 5,770,682; 5,821,327; 5,880,254; and 6,326,458, which are incorporated herein in their entirety by reference thereto for all purposes. The polylactic acid typically has a melting point of from about 100 0 C to 30 about 240 0 C, in some embodiments from about 120"C to about 220'C, and in 6 WO 2009/078849 PCT/US20071087339 some embodiments, from about 140 0 C to about 2000C. Such polylactic acids are useful in that they biodegrade at a fast rate. The glass transition temperature ("Tg") of the polylactic acid may be relatively high, such as from about 20'C to about 80'C, in some embodiments from about 300C to about 700C, and in some 5 embodiments, from about 400C to about 650C. As discussed in more detail below, the melting temperature and glass transition temperature may all be determined using differential scanning calorimetry ("DSC") in accordance with ASTM D-3417. The polylactic acid typically has a number average molecular weight ("M,") ranging from about 40,000 to about 160,000 grams per mole, in some 10 embodiments from about 50,000 to about 140,000 grams per mole, and in some embodiments, from about 80,000 to about 120,000 grams per mole. Likewise, the polymer also typically has a weight average molecular weight ("Mw") ranging from about 80,000 to about 200,000 grams per mole, in some embodiments from about 100,000 to about 180,000 grams per mole, and in some embodiments, from about 15 110,000 to about 160,000 grams per mole. The ratio of the weight average molecular weight to the number average molecular weight ("Mw/M,"), i.e., the "polydispersity index", is also relatively low. For example, the polydispersity index typically ranges from about 1.0 to about 3.0, in some embodiments from about 1.1 to about 2.0, and in some embodiments, from about 1.2 to about 1.8. The weight 20 and number average molecular weights may be determined by methods known to those skilled in the art. The polylactic acid may also have an apparent viscosity of from about 50 to about 600 Pascal seconds (Pa-s), in some embodiments from about 100 to about 500 Pa-s, and in some embodiments, from about 200 to about 400 Pa-s, as 25 determined at a temperature of 1900C and a shear rate of 1000 sec 1 . The melt flow rate of the polylactic acid (on a dry basis) may also range from about 0.1 to about 40 grams per 10 minutes, in some embodiments from about 0.5 to about 20 grams per 10 minutes, and in some embodiments, from about 5 to about 15 grams per 10 minutes. The melt flow rate is the weight of a polymer (in grams) that may 30 be forced through an extrusion rheometer orifice (0.0825-inch diameter) when subjected to a load of 2160 grams in 10 minutes at a certain temperature (e.g., 1900C), measured in accordance with ASTM Test Method D1238-E. 7 WO 2009/078849 PCT/US20071087339 B. Polvether Copolymer The polyether copolymer employed in the thermoplastic composition contains a repeating unit (A) having the following formula:

C

2

H

4 0 5 (A) wherein, x is an integer from 1 to 250, in some embodiments from 2 to 200, and in some embodiments, from 4 to 150. The polyether copolymer also contains a repeating unit (B) having the following formula: 10 CnH2O (B) wherein, n is an integer from 3 to 20, in some embodiments from 3 to 10, and in some embodiments, from 3 to 5; and 15 y is an integer from 1 to 150, in some embodiments from 2 to 125, and in some embodiments, from 4 to 100. Specific examples of monomers for use in forming the repeating unit (B) may include, for instance, 1,2-propanediol ("propylene glycol"); 1,3-propanediol ("trimethylene glycol"); 1,4-butanediol ("tetramethylene glycol"); 2,3-butanediol ("dimethylene glycol"); 1,5-pentanediol; 20 1,6-hexanediol; 1,9-nonanediol; 2-methyl-1,3-propanediol; neopentyl glycol; 2 methyl-1,4-butanediol; 3-methyl-1,5-pentanediol; 3-oxa-1,5-pentanediol ("diethylene glycol"); spiro-glycols, such as 3,9-bis(1,1-dimethyl-2-hydroxyethyl) 2,4,8,10-tetraoxa-spiro [5,5] undecane and 3,9-diethanol-2,4,8,10-tetraoxa-spiro [5,5] undecane; and so forth. Among these polyols, propylene glycol, dimethylene 25 glycol, trimethylene glycol, and tetramethylene glycol are particularly suitable for use in the present invention. The present inventors have discovered that an appropriate balance between the content of the repeating units (A) and (B), as well as their respective molecular weights, may result in a copolymer having optimal properties for 30 facilitating the formation of nonwoven webs from polylactic acid. The repeating 8 WO 2009/078849 PCT/US20071087339 unit (A) of the polyether copolymer, for instance, helps reduce the glass transition temperature of the polylactic acid, thereby improving its ability to be processed into a web of sufficient strength and elongation properties. The repeating unit (A) is, however, generally semi-crystalline in nature and thus may gradually crystallize 5 during and after melt processing, which increases the brittleness of webs formed therefrom. Further, the repeating unit (A) is also relatively hydrophilic in nature and thus soluble in water, which may result in phase separation of the polymer when exposed to conditions of high humidity. The repeating unit (B) of the polyether copolymer of the present invention helps counteract the 10 crystallanity/moisture-sensitivity of the repeating unit (A). That is, the repeating unit (B) is generally amorphous and is unlikely to crystallize during melt processing. Owing to its longer carbon chain, the repeating unit (B) is also relatively insoluble in water and thus less sensitive to moisture. In this regard, the repeating unit (A) of the copolymer typically constitutes 15 from about 40 mol.% to about 95 mol.%, in some embodiments from about 50 mol.% to about 90 mol.%, and in some embodiments, from about 60 mol.% to about 85 mol.% of the polyether copolymer. Likewise, the repeating unit (B) typically constitutes from about 5 mol.% to about 60 mol.%, in some embodiments from about 10 mol.% to about 50 mol.%, and in some embodiments, from about 15 20 mol.% to about 40 mol.% of the polyether copolymer. The number average molecular weight of the repeating unit (A) may range from about 500 to about 10,000, in some embodiments from about 750 to about 8,000, and in some embodiments, from about 1,000 to about 5,000. The number average molecular weight of the repeating unit (B) may likewise range from about 100 to about 2,000, 25 in some embodiments from about 200 to about 1,500, and in some embodiments, from about 400 to about 1,000. The number average molecular weight of the entire copolymer may also range from about 600 to about 10,000, in some embodiments from about 1,000 to about 8,000, and in some embodiments, from about 1,250 to about 5,000. 30 Of course, it should be understood that other repeating units or constituents may also be present in the copolymer. For instance, the copolymer may contain another repeating unit (C) that is different than the repeating units (A) and/or (B), yet selected from one or more of the monomers references above. As an 9 WO 2009/078849 PCT/US20071087339 example, the repeating unit (A) may have the structure described above, the repeating unit (B) may be formed from 1,2-propanediol ("propylene glycol") and the repeating unit (C) may be formed from 1,4-butanediol ("tetramethylene glycol"). The polyether copolymer may possess any desired configuration, such as 5 block (diblock, triblock, tetrablock, etc.), random, alternating, graft, star, etc. The repeating units (A) and (B) of the polyether copolymer may likewise be distributed in any desired fashion throughout the polymer. In one embodiment, for example, the polyether copolymer has the following general structure: A C 2

H

4 0 CnH 2 nO C 2

H

4 O B 10 wherein, x is an integer from 1 to 250, in some embodiments from 2 to 200, and in some embodiments, from 4 to 150; y is an integer from 1 to 150, in some embodiments from 2 to 125, and in some embodiments, from 4 to 100; 15 z is an integer from 0 to 200, in some embodiments from 2 to 125, and in some embodiments from 4 to 100; n is an integer from 3 to 20, in some embodiments from 3 to 10, and in some embodiments, from 3 to 6; A is hydrogen, an alkyl group, an acyl group, or an aryl group of 1 to 10 20 carbon atoms, and B is hydrogen, an alkyl group, an acyl group, or an aryl group of 1 to 10 carbon atoms. When "z" is greater than 0, for example, the copolymer has an "ABA" configuration and may include, for instance, polyoxyethylene / polyoxypropylene / polyoxyethylene copolymers (EO/PO/EO) such as described in 25 U.S. Patent Application Publication No. 2003/0204180 to Huang, et al., which is incorporated herein in its entirety by reference thereto for all purposes. Suitable EO/PO/EO polymers for use in the present invention are commercially available under the trade name PLURONIC@ (e.g., F-127 L-122, L-92, L-81, and L-61) from BASF Corporation, Mount Olive, New Jersey. 30 The polyether copolymer may be formed using any known polymerization technique as is known in the art. For example, the monomers may be 10 WO 2009/078849 PCT/US20071087339 simultaneously reacted to form the copolymer. Alternatively, monomers may be separately reacted to form prepolymers, which are then copolymerized with monomers and/or other prepolymers. A catalyst may optionally be employed to facilitate the copolymerization reaction. Suitable reaction catalysts may include, 5 for instance, tin catalysts, such as tin octylate, tin stearate, dibutyltin dioctoate, dibutyltin dioleylmaleate, dibutyltin dibutylmaleate, dibutyltin dilaurate, 1,1,3,3 tetrabutyl-1,3-dilauryloxycarbonyldistannoxane, dibutyltind acetate, dibutyltin diacetylacetonate, dibutyltin bis(o-phenylphenoxide), dibutyltin oxide, dibutyltin bis(triethoxysilicate), dibutyltin distearate, dibutyltin bis(isononyl-3 10 mercaptopropionate), dibutyltin bis(isooctyl thioglycolate), dioctyltin oxide, dioctyltin dilaurate, dioctyltin diacetate, and dioctyltin diversatate; and tertiary amine compounds and their analogues, such as triethylamine, triphenylamine, trimethylamine, N,N-dimethylaniline, and pyridine. Other suitable polymerization catalysts include titanium-based catalysts, such as tetraisopropyltitanate, 15 tetraisopropoxy titanium, dibutoxydiacetoacetoxy titanium, or tetrabutyltitanate. The amount of the catalyst added in the reaction is not particularly limited, but may range from about 0.0001 to about 3 parts by weight, based on 100 parts by weight of the copolymer. C. Nucleating Agents 20 A beneficial aspect of the present invention is that suitable thermal and mechanical properties of the thermoplastic composition may be provided without the need for conventional additives. Nevertheless, a nucleating agent may be employed if desired to improve processing and to facilitate crystallization during quenching. Suitable nucleating agents for use in the present invention may 25 include, for instance, inorganic acids, carbonates (e.g., calcium carbonate or magnesium carbonate), oxides (e.g., titanium oxide, silica, or alumina), nitrides (e.g., boron nitride), sulfates (e.g., barium sulfate), silicates (e.g., calcium silicate), stearates, benzoates, carbon black, graphite, and so forth. Still another suitable nucleating agent that may be employed is a "macrocyclic ester oligomer", which 30 generally refers to a molecule with one or more identifiable structural repeat units having an ester functionality and a cyclic molecule of 5 or more atoms, and in some cases, 8 or more atoms covalently connected to form a ring. The ester oligomer generally contains 2 or more identifiable ester functional repeat units of 11 WO 2009/078849 PCT/US20071087339 the same or different formula. The oligomer may include multiple molecules of different formulae having varying numbers of the same or different structural repeat units, and may be a co-ester oligomer or multi-ester oligomer ( i.e., an oligomer having two or more different structural repeat units having an ester 5 functionality within one cyclic molecule). Particularly suitable macrocyclic ester oligomers for use in the present invention are macrocyclic poly(alkylene dicarboxylate) oligomers having a structural repeat unit of the formula: wherein, 10 R' is an alkylene, cycloalkylene, or a mono- or polyoxyalkylene group, such as those containing a straight chain of about 2-8 atoms; and A is a divalent aromatic or alicyclic group. Specific examples of such ester oligomers may include macrocyclic poly(1,4-butylene terephthalate), macrocyclic poly(ethylene terephthalate), 15 macrocyclic poly(1,3-propylene terephthalate), macrocyclic poly(1,4-butylene isophthalate), macrocyclic poly(1,4-cyclohexylenedimethylene terephthalate), macrocyclic poly(1,2-ethylene 2,6-naphthalenedicarboxylate) oligomers, co-ester oligomers comprising two or more of the above monomer repeat units, and so forth. Macrocyclic ester oligomers may be prepared by known methods, such as 20 described in U.S. Patent Nos. 5,039,783; 5,231,161; 5,407,984; 5,527,976; 5,668,186; 6,420,048; 6,525,164; and 6,787,632. Alternatively, macrocyclic ester oligomers that may be used in the present invention are commercially available. One specific example of a suitable macrocyclic ester oligomer is macrocyclic poly(1,4-butylene terephthalate), which is commercially available from Cyclics 25 Corporation under the designation CBT@ 100. The amount of nucleating agents may be selectively controlled to achieve the desired properties for the fibers. For example, nucleating agents may be present in an amount of about 0.1 wt.% to about 25 wt.%, in some embodiments from about 0.2 wt.% to about 15 wt.%, in some embodiments from about 0.5 wt.% 30 to about 10 wt.%, and in some embodiments, from about 1 wt.% to about 5 wt.%, based on the dry weight of the thermoplastic composition. 12 WO 2009/078849 PCT/US20071087339 D. Other Components Other components may of course be utilized for a variety of different reasons. For instance, water may be employed in the present invention. Under appropriate conditions, water is also capable of hydrolytically degrading the 5 polylactic acid and/or polyether copolymer and thus reducing their molecular weight. The hydroxyl groups of water are believed to attack the ester linkages of the polylactic acid, for example, thereby causing chain scission or "depolymerization" of the polylactic acid molecule into one or more shorter ester chains. The shorter chains may include polylactic acids, as well as minor portions 10 of lactic acid monomers or oligomers, and combinations of any of the foregoing. The amount of water employed relative to the thermoplastic composition affects the extent to which the hydrolysis reaction is able to proceed. However, if the water content is too great, the natural saturation level of the polymer may be exceeded, which may adversely affect resin melt properties and the physical 15 properties of the resulting fibers. Thus, in most embodiments of the present invention, the water content is from about 0 to about 5000 parts per million ("ppm"), in some embodiments from about 20 to about 4000 ppm, and in some embodiments, from about 100 to about 3000, and in some embodiments, from about 1000 to about 2500 ppm, based on the dry weight of the starting polymers 20 used in the thermoplastic composition. The water content may be determined in a variety of ways as is known in the art, such as in accordance with ASTM D 7191 05, such as described in more detail below. The technique employed to achieve the desired water content is not critical to the present invention. In fact, any of a variety of well known techniques for 25 controlling water content may be employed, such as described in U.S. Patent Application Publication Nos. 2005/0004341 to Culbert, et al. and 2001/0003874 to Gillette, et al., which are incorporated herein in their entirety by reference thereto for all purposes. For example, the water content of the starting polymer may be controlled by selecting certain storage conditions, drying conditions, the conditions 30 of humidification, etc. In one embodiment, for example, the polylactic acid and/or polyether copolymer may be humidified to the desired water content by contacting pellets of the polymer(s) with an aqueous medium (e.g., liquid or gas) at a specific temperature and for a specific period of time. This enables a targeted water 13 WO 2009/078849 PCT/US20071087339 diffusion into the polymer structure (moistening). For example, the polymer may be stored in a package or vessel containing humidified air. Further, the extent of drying of the polymer during manufacture of the polymer may also be controlled so that the thermoplastic composition has the desired water content. In still other 5 embodiments, water may be added during melt processing as described herein. Thus, the term "water content" is meant to include the combination of any residual moisture (e.g., the amount of water present due to conditioning, drying, storage, etc.) and also any water specifically added during melt processing. Still other materials that may be used include, without limitation, wetting 10 agents, melt stabilizers, processing stabilizers, heat stabilizers, light stabilizers, antioxidants, pigments, surfactants, waxes, flow promoters, particulates, and other materials added to enhance processability. II. Melt Processing The melt processing of the thermoplastic composition and any optional 15 additional components may be performed using any of a variety of known techniques. In one embodiment, for example, the raw materials (e.g., polylactic acid, polyether copolymer, etc.) may be supplied separately or in combination. For instance, the raw materials may first be dry mixed together to form an essentially homogeneous dry mixture. The raw materials may likewise be supplied either 20 simultaneously or in sequence to a melt processing device that dispersively blends the materials. Batch and/or continuous melt processing techniques may be employed. For example, a mixer/kneader, Banbury mixer, Farrel continuous mixer, single-screw extruder, twin-screw extruder, roll mill, etc., may be utilized to blend and melt process the materials. One particularly suitable melt processing 25 device is a co-rotating, twin-screw extruder (e.g., ZSK-30 twin-screw extruder available from Werner & Pfleiderer Corporation of Ramsey, New Jersey). Such extruders may include feeding and venting ports and provide high intensity distributive and dispersive mixing. For example, the polylactic acid and polyether copolymer may be fed to the same or different feeding ports of the twin-screw 30 extruder and melt blended to form a substantially homogeneous melted mixture. If desired, water or other additives (e.g., organic chemicals) may be thereafter injected into the polymer melt and/or separately fed into the extruder at a different point along its length. Alternatively, one or more of the polymers may simply be 14 WO 2009/078849 PCT/US20071087339 supplied in a pre-humidified state. Regardless of the particular melt processing technique chosen, the raw materials may be blended under high shear/pressure and heat to ensure sufficient dispersion. For example, melt processing may occur at a temperature of from 5 about 500C to about 5000C, in some embodiments, from about 100 C to about 3500C, and in some embodiments, from about 1500C to about 3000C. Likewise, the apparent shear rate during melt processing may range from about 100 seconds- to about 10,000 seconds", in some embodiments from about 500 seconds- 1 to about 5000 seconds-, and in some embodiments, from about 800 10 seconds- to about 1200 seconds-. The apparent shear rate is equal to 4Q/IzR 3 , where Q is the volumetric flow rate ("m 3 /s") of the polymer melt and R is the radius ("m") of the capillary (e.g., extruder die) through which the melted polymer flows. Of course, other variables, such as the residence time during melt processing, which is inversely proportional to throughput rate, may also be controlled to 15 achieve the desired degree of homogeneity. As a result of the modification by the polyether copolymer, the thermoplastic composition may have a relatively low glass transition temperature. More specifically, the thermoplastic composition may have a glass transition temperature that is at least about 50C, in some embodiments at least about 10 C, and in some 20 embodiments, at least about 150C less than the glass transition temperature of polylactic acid. For example, the thermoplastic composition may have a T. of less than about 60"C, in some embodiments from about -10 C to about 600C, in some embodiments from about 0 C to about 55'C, and in some embodiments, from about 10 C to about 550C. On the other hand, polylactic acid typically has a Tg of 25 about 600C. The melting point of the thermoplastic composition may also range from about 50CC to about 170 C, in some embodiments from about 100 C to about 1650C, and in some embodiments, from about 1200C to about 1600C. The melting point of polylactic acid, on the other hand, normally ranges from about 1600C to about 2200C. 30 The thermoplastic composition may also crystallize at a higher temperature and at a faster crystallization rate than polylactic acid alone, which may allow the thermoplastic composition to more readily processed. The crystallization 15 WO 2009/078849 PCT/US20071087339 temperature may, for instance, be increased so that the ratio of the thermoplastic composition crystallization temperature to the polylactic acid crystallization temperature is greater than 1, in some embodiments at about 1.2 or more, and in some embodiments, about 1.5 or more. For example, the crystallization 5 temperature of the thermoplastic composition may range from about 600C to about 1300C, in some embodiments from about 801C to about 1300C, and in some embodiments, from about 100 C to about 1200C. Likewise, the ratio of the crystallization rate during the first cooling cycle (expressed in terms of the latent heat of crystallization, AHC) of the thermoplastic composition to the crystallization 10 rate of the polylactic acid is greater than 1, in some embodiments about 2 or more, and in some embodiments, about 3 or more. For example, the thermoplastic composition may possess a latent heat of crystallization (AHe) during the first cooling cycle of about 10 J/g or more, in some embodiments about 20 J/g or more, and in some embodiments, about 30 J/g or more. The thermoplastic composition 15 may also have a latent heat of fusion (AHf) of about 15 Joules per gram ("J/g") or more, in some embodiments about 20 J/g or more, and in some embodiments about 30 J/g or more, and in some embodiments, about 40 J/g or more. Furthermore, the composition may also exhibit a width (AW1/2) at the half height of the crystallization peak of about 200C or less, in some embodiments about 10*C or 20 less, and in some embodiments, about 50C or less. The latent heat of fusion (AHf), latent heat of crystallization (AHc), crystallization temperature, and width at the half height of the crystallization peak may all be determined as is well known in the art using differential scanning calorimetry ("DSC") in accordance with ASTM D-3417. Due to the increase in the crystallization temperature, the temperature 25 window between the glass transition temperature and crystallization temperature is also increased, which provides for greater processing flexibility by increasing the residence time for the material to crystallize. For example, the temperature window between the crystallization temperature and glass transition temperature of the thermoplastic composition may be about 200C apart, in some embodiments 30 about 400C apart, and in some embodiments greater than about 600C apart. In addition to possessing a higher crystallization temperature and broader temperature window, the thermoplastic composition may also exhibit improved 16 WO 2009/078849 PCT/US20071087339 processability due to a lower apparent viscosity and higher melt flow rate than polylactic acid alone. Thus, when processed in equipment lower power settings can be utilized, such as using less torque to turn the screw of the extruder. The apparent viscosity may for instance, be reduced so that the ratio of polylactic acid 5 viscosity to the thermoplastic composition viscosity is at least about 1.1, in some embodiments at least about 2, and in some embodiments, from about 15 to about 100. Likewise, the melt flow rate may be increased so that the ratio of the thermoplastic composition melt flow rate to the starting polylactic acid melt flow rate (on a dry basis) is at least about 1.5, in some embodiments at least about 5, in 10 some embodiments at least about 10, and in some embodiments, from about 30 to about 100. In one particular embodiment, the thermoplastic composition may have a melt flow rate (dry basis) of from about 1 to about 500 grams per 10 minutes, in some embodiments from about 2 to about 200 grams per 10 minutes, and in some embodiments, from about 5 to about 160 grams per 10 minutes (determined at 15 1900C, 2.16 kg). Of course, the apparent viscosity, melt flow rate, etc. may vary depending on the intended application. Ill. Fiber Formation Fibers formed from the thermoplastic composition may generally have any desired configuration, including monocomponent, multicomponent (e.g., sheath 20 core configuration, side-by-side configuration, segmented pie configuration, island in-the-sea configuration, and so forth), and/or multiconstituent (e.g., polymer blend). In some embodiments, the fibers may contain one or more additional polymers as a component (e.g., bicomponent) or constituent (e.g., biconstituent) to further enhance strength and other mechanical properties. For instance, the 25 thermoplastic composition may form a sheath component of a sheath/core bicomponent fiber, while an additional polymer may form the core component, or vice versa. The additional polymer may be a thermoplastic polymer that is not generally considered biodegradable, such as polyolefins, e.g., polyethylene, polypropylene, polybutylene, and so forth; polytetrafluoroethylene; polyesters, e.g., 30 polyethylene terephthalate, and so forth; polyvinyl acetate; polyvinyl chloride acetate; polyvinyl butyral; acrylic resins, e.g., polyacrylate, polymethylacrylate, polymethylmethacrylate, and so forth; polyamides, e.g., nylon; polyvinyl chloride; polyvinylidene chloride; polystyrene; polyvinyl alcohol; and polyurethanes. More 17 WO 2009/078849 PCT/US20071087339 desirably, however, the additional polymer is biodegradable, such as aliphatic polyesters, such as polyesteramides, modified polyethylene terephthalate, polylactic acid (PLA) and its copolymers, terpolymers based on polylactic acid, polyglycolic acid, polyalkylene carbonates (such as polyethylene carbonate), 5 polyhydroxyalkanoates (PHA), polyhydroxybutyrates (PHB), polyhydroxyvalerates (PHV), polyhyd roxybutyrate-hyd roxyvalerate copolymers (PHBV), and polycaprolactone, and succinate-based aliphatic polymers (e.g., polybutylene succinate, polybutylene succinate adipate, and polyethylene succinate); aromatic polyesters; or other aliphatic-aromatic copolyesters. 10 Any of a variety of processes may be used to form fibers in accordance with the present invention. For example, the melt processed thermoplastic composition described above may be extruded through a spinneret, quenched, and drawn into the vertical passage of a fiber draw unit. The fibers may then be cut to form staple fibers having an average fiber length in the range of from about 3 to about 80 15 millimeters, in some embodiments from about 4 to about 65 millimeters, and in some embodiments, from about 5 to about 50 millimeters. The staple fibers may then be incorporated into a nonwoven web as is known in the art, such as bonded carded webs, through-air bonded webs, etc. The fibers may also be deposited onto a foraminous surface to form a 20 nonwoven web. Referring to Fig. 1, for example, one embodiment of a method for forming meltblown fibers is shown. Meltblown fibers form a structure having a small average pore size, which may be used to inhibit the passage of liquids and particles, while allowing gases (e.g., air and water vapor) to pass therethrough. To achieve the desired pore size, the meltblown fibers are typically "microfibers" in 25 that they have an average size of 10 micrometers or less, in some embodiments about 7 micrometers or less, and in some embodiments, about 5 micrometers or less. The ability to produce such fine fibers may be facilitated in the present invention through the use of a thermoplastic composition having the desirable combination of low apparent viscosity and high melt flow rate. 30 In Fig. 1, for instance, the raw materials (e.g., polylactic acid, macrocyclic ester oligomer, etc.) are fed into an extruder 12 from a hopper 10. The raw materials may be provided to the hopper 10 using any conventional technique and in any state. The extruder 12 is driven by a motor 11 and heated to a temperature 18 WO 2009/078849 PCT/US20071087339 sufficient to extrude the melted polymer. For example, the extruder 12 may employ one or multiple zones operating at a temperature of from about 50 0 C to about 5000C, in some embodiments, from about 10 C to about 4000C, and in some embodiments, from about 1500C to about 2500C. Typical shear rates range 5 from about 100 seconds-' to about 10,000 seconds-, in some embodiments from about 500 seconds' to about 5000 seconds-, and in some embodiments, from about 800 seconds- to about 1200 seconds-. If desired, the extruder may also possess one or more zones that remove excess moisture from the polymer, such as vacuum zones, etc. The extruder may also be vented to allow volatile gases to 10 escape. Once formed, the thermoplastic composition may be subsequently fed to another extruder in a fiber formation line (e.g., extruder 12 of a meltblown spinning line). Alternatively, the thermoplastic composition may be directly formed into a fiber through supply to a die 14, which may be heated by a heater 16. It should be 15 understood that other meltblown die tips may also be employed. As the polymer exits the die 14 at an orifice 19, high pressure fluid (e.g., heated air) supplied by conduits 13 attenuates and spreads the polymer stream into microfibers 18. Although not shown in Fig. 1, the die 14 may also be arranged adjacent to or near a chute through which other materials (e.g., cellulosic fibers, particles, etc.) 20 traverse to intermix with the extruded polymer and form a "coform" web. The microfibers 18 are randomly deposited onto a foraminous surface 20 (driven by rolls 21 and 23) with the aid of an optional suction box 15 to form a meltblown web 22. The distance between the die tip and the foraminous surface 20 is generally small to improve the uniformity of the fiber laydown. For example, 25 the distance may be from about 1 to about 35 centimeters, and in some embodiments, from about 2.5 to about 15 centimeters. In Fig. 1, the direction of the arrow 28 shows the direction in which the web is formed (i.e., "machine direction") and arrow 30 shows a direction perpendicular to the machine direction (i.e., "cross-machine direction"). Optionally, the meltblown web 22 may then be 30 compressed by rolls 24 and 26. The desired denier of the fibers may vary depending on the desired application. Typically, the fibers are formed to have a denier per filament (i.e., the unit of linear density equal to the mass in grams per 9000 meters of fiber) of less than about 6, in some embodiments less than about 19 WO 2009/078849 PCT/US20071087339 3, and in some embodiments, from about 0.5 to about 3. In addition, the fibers generally have an average diameter of from about 0.1 to about 20 micrometers, in some embodiments from about 0.5 to about 15 micrometers, and in some embodiments, from about 1 to about 10 micrometers. 5 Once formed, the nonwoven web may then be bonded using any conventional technique, such as with an adhesive or autogenously (e.g., fusion and/or self-adhesion of the fibers without an applied external adhesive). Autogenous bonding, for instance, may be achieved through contact of the fibers while they are semi-molten or tacky, or simply by blending a tackifying resin and/or 10 solvent with the polylactic acid(s) used to form the fibers. Suitable autogenous bonding techniques may include ultrasonic bonding, thermal bonding, through-air bonding, calendar bonding, and so forth. For example, the web may be further bonded or embossed with a pattern by a thermo-mechanical process in which the web is passed between a heated smooth anvil roll and a heated pattern roll. The 15 pattern roll may have any raised pattern which provides the desired web properties or appearance. Desirably, the pattern roll defines a raised pattern which defines a plurality of bond locations which define a bond area between about 2% and 30% of the total area of the roll. Exemplary bond patterns include, for instance, those described in U.S. Patent 3,855,046 to Hansen et al., U.S. Patent No. 5,620,779 to 20 Levy et al., U.S. Patent No. 5,962,112 to Haynes et al., U.S. Patent 6,093,665 to Sayovitz et al., as well as U.S. Design Patent Nos. 428,267 to Romano et al.; 390,708 to Brown; 418,305 to Zander, et al.; 384,508 to Zander, et al.; 384,819 to Zander, et al.; 358,035 to Zander, et al.; and 315,990 to Blenke, et al., all of which are incorporated herein in their entirety by reference thereto for all purposes. The 25 pressure between the rolls may be from about 5 to about 2000 pounds per lineal inch. The pressure between the rolls and the temperature of the rolls is balanced to obtain desired web properties or appearance while maintaining cloth like properties. As is well known to those skilled in the art, the temperature and pressure required may vary depending upon many factors including but not limited 30 to, pattern bond area, polymer properties, fiber properties and nonwoven properties. In addition to meltblown webs, a variety of other nonwoven webs may also be formed from the thermoplastic composition in accordance with the present 20 WO 2009/078849 PCT/US20071087339 invention, such as spunbond webs, bonded carded webs, wet-laid webs, airlaid webs, coform webs, hydraulically entangled webs, etc. For example, the polymer may be extruded through a spinnerette, quenched and drawn into substantially continuous filaments, and randomly deposited onto a forming surface. 5 Alternatively, the polymer may be formed into a carded web by placing bales of fibers formed from the thermoplastic composition into a picker that separates the fibers. Next, the fibers are sent through a combing or carding unit that further breaks apart and aligns the fibers in the machine direction so as to form a machine direction-oriented fibrous nonwoven web. Once formed, the nonwoven web is 10 typically stabilized by one or more known bonding techniques. If desired, the nonwoven web may also be a composite that contains a combination of the thermoplastic composition fibers and other types of fibers (e.g., staple fibers, filaments, etc). For example, additional synthetic fibers may be utilized, such as those formed from polyolefins, e.g., polyethylene, polypropylene, 15 polybutylene, and so forth; polytetrafluoroethylene; polyesters, e.g., polyethylene terephthalate and so forth; polyvinyl acetate; polyvinyl chloride acetate; polyvinyl butyral; acrylic resins, e.g., polyacrylate, polymethylacrylate, polymethylmethacrylate, and so forth; polyamides, e.g., nylon; polyvinyl chloride; polyvinylidene chloride; polystyrene; polyvinyl alcohol; polyurethanes; polylactic 20 acid; etc. If desired, biodegradable polymers, such as poly(glycolic acid) (PGA), poly(lactic acid) (PLA), poly(p-malic acid) (PMLA), poly(6-caprolactone) (PCL), poly(p-dioxanone) (PDS), poly(butylene succinate) (PBS), and poly(3 hydroxybutyrate) (PHB), may also be employed. Some examples of known synthetic fibers include sheath-core bicomponent fibers available from KoSa Inc. of 25 Charlotte, North Carolina under the designations T-255 and T-256, both of which use a polyolefin sheath, or T-254, which has a low melt co-polyester sheath. Still other known bicomponent fibers that may be used include those available from the Chisso Corporation of Moriyama, Japan or Fibervisions LLC of Wilmington, Delaware. Polylactic acid staple fibers may also be employed, such as those 30 commercially available from Far Eastern Textile, Ltd. of Taiwan. The composite may also contain pulp fibers, such as high-average fiber length pulp, low-average fiber length pulp, or mixtures thereof. One example of suitable high-average length fluff pulp fibers includes softwood kraft pulp fibers. 21 WO 2009/078849 PCT/US20071087339 Softwood kraft pulp fibers are derived from coniferous trees and include pulp fibers such as, but not limited to, northern, western, and southern softwood species, including redwood, red cedar, hemlock, Douglas fir, true firs, pine (e.g., southern pines), spruce (e.g., black spruce), bamboo, combinations thereof, and so forth. 5 Northern softwood kraft pulp fibers may be used in the present invention. An example of commercially available southern softwood kraft pulp fibers suitable for use in the present invention include those available from Weyerhaeuser Company with offices in Federal Way, Washington under the trade designation of "NF-405." Another suitable pulp for use in the present invention is a bleached, sulfate wood 10 pulp containing primarily softwood fibers that is available from Bowater Corp. with offices in Greenville, South Carolina under the trade name CoosAbsorb S pulp. Low-average length fibers may also be used in the present invention. An example of suitable low-average length pulp fibers is hardwood kraft pulp fibers. Hardwood kraft pulp fibers are derived from deciduous trees and include pulp fibers such as, 15 but not limited to, eucalyptus, maple, birch, aspen, etc. Eucalyptus kraft pulp fibers may be particularly desired to increase softness, enhance brightness, increase opacity, and change the pore structure of the sheet to increase its wicking ability. Bamboo fibers may also be employed. Nonwoven composites may be formed using a variety of known techniques. 20 For example, the nonwoven composite may be a "coform material" that contains a mixture or stabilized matrix of the thermoplastic composition fibers and an absorbent material. As an example, coform materials may be made by a process in which at least one meltblown die head is arranged near a chute through which the absorbent materials are added to the web while it is forming. Such absorbent 25 materials may include, but are not limited to, pulp fibers, superabsorbent particles, inorganic and/or organic absorbent materials, treated polymeric staple fibers, and so forth. The relative percentages of the absorbent material may vary over a wide range depending on the desired characteristics of the nonwoven composite. For example, the nonwoven composite may contain from about 1 wt.% to about 60 30 wt.%, in some embodiments from 5 wt.% to about 50 wt.%, and in some embodiments, from about 10 wt.% to about 40 wt.% thermoplastic composition fibers. The nonwoven composite may likewise contain from about 40 wt.% to about 99 wt.%, in some embodiments from 50 wt.% to about 95 wt.%, and in some 22 WO 2009/078849 PCT/US20071087339 embodiments, from about 60 wt.% to about 90 wt.% absorbent material. Some examples of such coform materials are disclosed in U.S. Patent Nos. 4,100,324 to Anderson, et al.; 5,284,703 to Everhart, et al.; and 5,350,624 to Georqer, et al., which are incorporated herein in their entirety by reference thereto for all purposes. 5 Referring to Fig. 2, for example, one embodiment of an apparatus for forming a nonwoven coform composite structure is generally represented by reference numeral 110. -Initially, the raw materials (e.g., polylactic acid, etc.) are supplied to a hopper 112 of an extruder 114, and then extruded toward two meltblowing dies 116 and 118 corresponding to a stream of gas 126 and 128, 10 respectively, which are aligned to converge at an impingement zone 130. One or more types of a secondary material 132 (fibers and/or particulates) are also supplied by a nozzle 144 and added to the two streams 126 and 128 at the impingement zone 130 to produce a graduated distribution of the material within the combined streams 126 and 128. The secondary material may be supplied 15 using any known technique in the art, such as with a picker roll arrangement (not shown) or a particulate injection system (not shown). The secondary stream 132 merges with the two streams 126 and 128 to form a composite stream 156. An endless belt 158 driven by rollers 160 receives the stream 156 and form a composite structure 154. If desired, vacuum boxes (not shown) may be employed 20 to assist in retention of the matrix on the surface of the belt 158. Nonwoven laminates may also be formed in the present invention in which one or more layers are formed from the thermoplastic composition. For example, the nonwoven web of one layer may be a meltblown or coform web that contains the thermoplastic composition, while the nonwoven web of another layer contains 25 thermoplastic composition, other biodegradable polymer(s), and/or any other polymer (e.g., polyolefins). In one embodiment, the nonwoven laminate contains a meltblown layer positioned between two spunbond layers to form a spunbond / meltblown / spunbond ("SMS") laminate. If desired, the meltblown layer may be formed from the thermoplastic composition. The spunbond layer may be formed 30 from the thermoplastic composition, other biodegradable polymer(s), and/or any other polymer (e.g., polyolefins). Various techniques for forming SMS laminates are described in U.S. Patent Nos. 4,041,203 to Brock et al.; 5,213,881 to Timmons, et al.; 5,464,688 to Timmons, et al.; 4,374,888 to Bornslaeger; 23 WO 2009/078849 PCT/US20071087339 5,169,706 to Collier, et al.; and 4,766,029 to Brock et al., as well as U.S. Patent Application Publication No. 2004/0002273 to Fitting, et al., all of which are incorporated herein in their entirety by reference thereto for all purposes. Of course, the nonwoven laminate may have other configuration and possess any 5 desired number of meltblown and spunbond layers, such as spunbond / meltblown / meltblown / spunbond laminates ("SMMS"), spunbond / meltblown laminates ("SM"), etc. Although the basis weight of the nonwoven laminate may be tailored to the desired application, it generally ranges from about 10 to about 300 grams per square meter ("gsm"), in some embodiments from about 25 to about 200 gsm, 10 and in some embodiments, from about 40 to about 150 gsm. If desired, the nonwoven web or laminate may be applied with various treatments to impart desirable characteristics. For example, the web may be treated with liquid-repellency additives, antistatic agents, surfactants, colorants, antifogging agents, fluorochemical blood or alcohol repellents, lubricants, and/or 15 antimicrobial agents. In addition, the web may be subjected to an electret treatment that imparts an electrostatic charge to improve filtration efficiency. The charge may include layers of positive or negative charges trapped at or near the surface of the polymer, or charge clouds stored in the bulk of the polymer. The charge may also include polarization charges that are frozen in alignment of the 20 dipoles of the molecules. Techniques for subjecting a fabric to an electret treatment are well known by those skilled in the art. Examples of such techniques include, but are not limited to, thermal, liquid-contact, electron beam and corona discharge techniques. In one particular embodiment, the electret treatment is a corona discharge technique, which involves subjecting the laminate to a pair of 25 electrical fields that have opposite polarities. Other methods for forming an electret material are described in U.S. Patent Nos. 4,215,682 to Kubik, et al.; 4,375,718 to Wadsworth; 4,592,815 to Nakao; 4,874,659 to Ando; 5,401,446 to Tsai, et al.; 5,883,026 to Reader, et al.; 5,908,598 to Rousseau, et al.; 6,365,088 to Knight, et al., which are incorporated herein in their entirety by reference thereto 30 for all purposes. Ill. Articles The nonwoven web may be used in a wide variety of applications. For example, the web may be incorporated into a "medical product", such as gowns, 24 WO 2009/078849 PCT/US20071087339 surgical drapes, facemasks, head coverings, surgical caps, shoe coverings, sterilization wraps, warming blankets, heating pads, and so forth. Of course, the nonwoven web may also be used in various other articles. For example, the nonwoven web may be incorporated into an "absorbent article" that is capable of 5 absorbing water or other fluids. Examples of some absorbent articles include, but are not limited to, personal care absorbent articles, such as diapers, training pants, absorbent underpants, incontinence articles, feminine hygiene products (e.g., sanitary napkins), swim wear, baby wipes, mitt wipe, and so forth; medical absorbent articles, such as garments, fenestration materials, underpads, bedpads, 10 bandages, absorbent drapes, and medical wipes; food service wipers; clothing articles; pouches, and so forth. Materials and processes suitable for forming such articles are well known to those skilled in the art. Absorbent articles, for instance, typically include a substantially liquid-impermeable layer (e.g., outer cover), a liquid-permeable layer (e.g., bodyside liner, surge layer, etc.), and an absorbent 15 core. In one embodiment, for example, a nonwoven web formed according to the present invention may be used to form an outer cover of an absorbent article. If desired, the nonwoven web may be laminated to a liquid-impermeable film that is either vapor-permeable or vapor-impermeable. The present invention may be better understood with reference to the 20 following examples. Test Methods Water Content: Water content was determined using an Arizona Instruments Computrac Vapor Pro moisture analyzer (Model No. 3100) in substantial accordance with 25 ASTM D 7191-05, which is incorporated herein in its entirety by reference thereto for all purposes. The test temperature (§ X2.1.2) was 1300C, the sample size (§ X2.1.1) was 2 to 4 grams, and the vial purge time (§ X2.1.4) was 30 seconds. Further, the ending criteria (§ X2.1.3) was defined as a "prediction" mode, which means that the test is ended when the built-in programmed criteria (which 30 mathematically calculates the end point moisture content) is satisfied. Melt Flow Rate: The melt flow rate ("MFR") is the weight of a polymer (in grams) forced through an extrusion rheometer orifice (0.0825-inch diameter) when subjected to a 25 WO 2009/078849 PCT/US20071087339 load of 2160 grams in 10 minutes, typically at 1900C or 2300C. Unless otherwise indicated, the melt flow rate was measured in accordance with ASTM Test Method D1238-E. The melt flow rate may be measured before or after drying. Polymers measured after drying (dry basis) generally have a water content of less than 500 5 parts per million. Thermal Properties: The melting temperature, glass transition temperature and degree of crystallinity of a material was determined by differential scanning calorimetry (DSC). The differential scanning calorimeter was a DSC Q100 Differential 10 Scanning Calorimeter, which was outfitted with a liquid nitrogen cooling accessory and with a UNIVERSAL ANALYSIS 2000 (version 4.6.6) analysis software program, both of which are available from T.A. Instruments Inc. of New Castle, Delaware. To avoid directly handling the samples, tweezers or other tools were used. The samples were placed into an aluminum pan and weighed to an 15 accuracy of 0.01 milligram on an analytical balance. A lid was crimped over the material sample onto the pan. Typically, the resin pellets were placed directly in the weighing pan, and the fibers were cut to accommodate placement on the weighing pan and covering by the lid. The differential scanning calorimeter was calibrated using an indium metal 20 standard and a baseline correction was performed, as described in the operating manual for the differential scanning calorimeter. A material sample was placed into the test chamber of the differential scanning calorimeter for testing, and an empty pan is used as a reference. All testing was run with a 55-cubic centimeter per minute nitrogen (industrial grade) purge on the test chamber. For resin pellet 25 samples, the heating and cooling program was a 2-cycle test that began with an equilibration of the chamber to -25 0 C, followed by a first heating period at a heating rate of 10 C per minute to a temperature of 2000C, followed by equilibration of the sample at 2000C for 3 minutes, followed by a first cooling period at a cooling rate of 10 0 C per minute to a temperature of -250C, followed by 30 equilibration of the sample at -250C for 3 minutes, and then a second heating period at a heating rate of 10 C per minute to a temperature of 2000C. For fiber samples, the heating and cooling program was a 1-cycle test that began with an 26 WO 2009/078849 PCT/US20071087339 equilibration of the chamber to -25'C, followed by a heating period at a heating rate of 10 C per minute to a temperature of 2001C, followed by equilibration of the sample at 2000C for 3 minutes, and then a cooling period at a cooling rate of 10 C per minute to a temperature of -25'C. All testing was run with a 55-cubic 5 centimeter per minute nitrogen (industrial grade) purge on the test chamber. The results were then evaluated using the UNIVERSAL ANALYSIS 2000 analysis software program, which identified and quantified the glass transition temperature (Tg) of inflection, the endothermic and exothermic peaks, and the areas under the peaks on the DSC plots. The glass transition temperature was 10 identified as the region on the plot-line where a distinct change in slope occurred, and the melting temperature was determined using an automatic inflection calculation. The areas under the peaks on the DSC plots were determined in terms of joules per gram of sample (J/g). For example, the heat of fusion of a resin or fiber sample was determined by integrating the area of the endothermic 15 peak. The area values were determined by converting the areas under the DSC plots (e.g. the area of the endotherm) into the units of joules per gram (J/g) using computer software. The exothermic heat of crystallization (AHe) was determined during the first cooling cycle. In certain cases, the exothermic heat of crystallization was also determined during the first heating cycle (AHc 1 ) and the 20 second cycle (AHc 2 ). If desired, the % crystallinity may also be calculated as follows: % crystallinity = 100 * (A - B)/C wherein, A is the sum of endothermic peak areas during the heating cycle (J/g); 25 B is the sum of exothermic peak areas during the heating cycle (J/g); and C is the heat of fusion for the selected polymer where such polymer has 100% crystallinity (J/g). For polylactic acid, C is 93.7 J/g (Cooper-White, J. J., and Mackay, M. E., Journal of Polymer Science, Polymer Physics Edition, p.1806, Vol. 37, (1999)). The areas under any exothermic peaks encountered in the DSC scan 30 due to insufficient crystallinity may also be subtracted from the area under the endothermic peak to appropriately represent the degree of crystallinity. 27 WO 2009/078849 PCT/US20071087339 Tensile Properties: The strip tensile strength values were determined in substantial accordance with ASTM Standard D-5034. Specifically, a nonwoven web sample was cut or otherwise provided with size dimensions that measured 25.4 millimeters (width) x 5 152.4 millimeters (length). A constant-rate-of-extension type of tensile tester was employed. The tensile testing system was a Sintech Tensile Tester, which is available from Sintech Corp. of Cary, North Carolina. The tensile tester was equipped with TESTWORKS 4.08B software from MTS Corporation to support the testing. An appropriate load cell was selected so that the tested value fell within 10 the range of 10-90% of the full scale load. The sample was held between grips having a front and back face measuring 25.4 millimeters x 76 millimeters. The grip faces were rubberized, and the longer dimension of the grip was perpendicular to the direction of pull. The grip pressure was pneumatically maintained at a pressure of 40 pounds per square inch. The tensile test was run at a 300 15 millimeter per minute rate with a gauge length of 10.16 centimeters and a break sensitivity of 40%. Three samples were tested by applying the test load along the machine direction ("MD") and three samples were tested by applying the test load along the cross direction ("CD"). In addition to tensile strength ("peak load"), peak elongation 20 (i.e., % strain at peak load), and "energy to peak" were measured. EXAMPLE 1 Polylactic acid resins were initially obtained from Natureworks as PLA 6200D or 6250D. PEG 3350 and 8000 were purchased from Dow. PPG P-4000 was purchase from BASF. PEG-PPG-PEG block copolymers and PEG-ran-PPG 25 copolymer, were purchased from Aldrich. Their composition and Molecular weights were listed in Table 1. Table 1 Polyethylene glycol (PEG), Polypropylene glycol (PPG), and their copolymers Plasticizers Mn Weight % of Ethylene Oxide PEG-3350 3350 100 PEG-8000 8000 100 PPG P-4000 4000 0 PEG-ran-PPG 2500 2500 75 PEG-PPG-PEG 2800 2800 10 PEG-PPG-PEG 4400 4400 30 PEG-PPG-PEG 1900 1900 50 PEG-PPG-PEG 8400 8400 80 28 WO 2009/078849 PCT/US20071087339 A co-rotating, twin-screw extruder was employed (ZSK-30, diameter) that was manufactured by Werner and Pfleiderer Corporation of Ramsey, New Jersey. The screw length was 1328 millimeters. The extruder had 14 barrels, numbered consecutively 1-14 from the feed hopper to the die. The first barrel (#1) received 5 the PLA resin and solid plasticizer via a volumetric feeder at a total throughput of 15-25 pounds per hour. Liquid plasticizer was added into the fifth barrel (#5) at a final ratio of 10-15% by weight via a pressurized injector connected with an Eldex pump. The screw speed was from 150 to 500 revolutions per minute ("rpm"). The die used to extrude the resin had 3 die openings (6 millimeters in diameter) that 10 were separated by 4 millimeters. Upon formation, the extruded resin was cooled on a fan-cooled conveyor belt and formed into pellets by a Conair pelletizer. Reactive extrusion parameters were monitored during the reactive extrusion process. The conditions are shown below in Table 2. Table 2 15 Lone Lone Throughput Speed Zone Zone 3 4 Zone Zone Zone Tmelt Torque Samples PLA Plasticizers (Ib/h) (rpm) 1 ("C) 2 ("C) ("C) ("C) 5 ("C) 6 ("C) 7 ("C) ("C) Pmelt (%) No 1 6200D n/a 25 250 160 210 225 230 230 200 170 188 170 75 No2 6200D 10% PEG-3350 20 250 80 180 225 230 230 200 160 176 135 68 No3 6200D 17% PEG-8000 25 450 100 235 240 240 235 190 125 140 65 50 No4 6200D 11% PPG P-4000 23 250 160 210 225 230 230 200 160 180 95 48 No 5 6200D 11% PEG-ran-PPG 2500 20 400 170 230 235 240 230 200 160 170 130 53 No6 6200D 11% PEG-PPG-PEG 2800 25 250 160 210 225 230 230 200 160 180 110 56 No7 6200D 11% PEG-PPG-PEG 4400 25 250 160 210 225 230 230 200 160 180 110 56 No8 6200D 10% PEG-PPG-PEG 1900 25 400 170 230 235 240 235 200 170 181 125 53 No 9 6200D 10% PEG-PPG-PEG 8400 20 400 170 230 235 240 235 200 160 170 115 43 As indicated, the torque and die pressure of extruder were reduced with various amount of different plasticizers. The melt flow index of the sample was 20 determined by the method of ASTM D1239, with a Tinius Olsen Extrusion Plastometer at 1900C and 2.16 kg. The results are set forth below in Table 3. Table 3 MFI for PLA with PEG, PPG or PEG/PPG copolymers blends Samples No 1 No2 No3 No4 No 5 No 6 No7 No 8 No 9 MFI at 190 0 C and 2.16Kg 27 65 80 112 60 90 140 60 100 From the melt flow analysis, it was determined that the viscosity of PLA 25 could be significantly reduced by these copolymers. Compared with PLA modified 29 WO 2009/078849 PCT/US20071087339 with PEG-ran-PPG with a MFI of 60 (Sample 5), PLA modified with PEG-PPG PEG block copolymers had a higher MFI of about 100. The compounded PLA and plasticizer resins were also subjected to DSC analysis. 5 Table 4 Thermo properties of PLA blends with plasticizers by DSC 2nd Heat 1st Cool Tg AHc Samples ('C) Tm ('C) AHc (J/g) AHf (J/g) (J/g) Tc AW 1

/

2 1 60.1 166.8 24.2 28 N/A N/A N/A 2 - 164.6 3 35.2 14.3 85.1 18 3 - 164.5 N/A 28.9 14.2 85.8 13.7 4 59.1 166.3 21.8 28.5 N/A N/A N/A 5 40 164.4 N/A 32.5 20.4 89.3 11.3 6 54.4 164.7 15.6 28.1 1.8 86.7 14.4 7 57.1 165 18.3 29.6 0.5 86.6 12.1 8 41.2 164.2 7.85 33.8 6.5 82.1 19.8 9 38.7 164.5 6.5 34.7 8 84.3 20.5 Thermograms of the above blends showed that high MW PPG alone had little effects on Tg reduction (Sample 4). The effects of the PEG-PPG-PEG block copolymer on Tg reduction increased with the increasing PEG/PPG ratio in block 10 copolymers (Sample 6-9). Surprisingly 10% PEG-ran-PPG addition significantly reduced PLA glass transition temperature from 600C to about 400C (Sample 5). In addition, the latent heat of crystallization of PLA modified PEG-ran-PPG was 20 J/g compared with no crystallization peaks observed from PLA (Sample 1) or PLA modified with PPG (Sample 4). The heat of crystallization was increased in PLA 15 modified with PEG-PPG-PEG block copolymers (Sample 6-9) having increasing PEG/PPG ratios. EXAMPLE 2 20 pounds of a modified PLA (Sample 1-9) were used to form a meltblown web. Meltblown spinning was conducted with a pilot line that included a Killion 20 extruder (Verona, New York), a 10-feet hose from Dekoron/Unitherm (Riviera Beach, Florida), and a 14-inch meltblown die with an 11.5-inch spray and an orifice size of 0.0145 inch. The modified resin was fed via gravity into the extruder and then transferred into the hose connected with the meltblown die. Table 5 shows the process conditions used during spinning. Meltblown Sample Nos. 10-18 were 25 made from PLA blends (Sample 1-9), respectively. 30 WO 2009/078849 PCT/US20071087339 Table 5 MB spinning of PLA modified with PEG, PPG, and their copolymers Forming Extruder profile Height Primary Air Samples Resins Zone ternp from 1-4 (F) Speed (rpm) Pressure (Psi) Hose (F) Die (F) (Inches) Ternp (F) Press (Psi) No 10 No 1 280 375 380 375 25 250 350 370 7 430 55 No 11 No 2 280 375 380 375 25 90 350 370 7 430 55 No 12 No 3 280 375 380 375 25 83 350 370 7 420 55 No 13 No 4 280 375 380 375 25 75 350 370 7 430 55 No 14 No 5 280 375 380 375 25 93 350 370 6 430 55 No 15 No 6 280 375 380 375 25 85 350 370 6 480 55 No 16 No 7 280 375 380 375 25 63 350 370 7 430 55 No 17 No B 280 375 380 375 25 105 350 370 6.25 430 55 No 18 No 9 280 375 380 375 25 80 350 370 6.25 430 55 The tensile properties of melt blown samples No 10-18 were also tested. 5 The results are shown below in Table 6. Table 6 Tensile properties of Melt blown webs from modified PLA resins with polyether copolymers Samples Base weight (g) Peak Load (gf) Strain at Peak (%) % Strain at Break Energy to Break (in*lbf) MD 23 N/A N/A N/A N/A No 10 CD 23 N/A N/A N/A N/A MD 23 834 ± 27 18 ± 32 78.9 ± 13.3 No 11 CD 23 510 ± 21 110 ± 4.5 118 ± 7 MD 23.8 809 ± 64 4.4 0.24 51 ± 14.5 3.3 ± 1.2 No 12 CD 25.8 418 ± 12 5.2 0.4 67 9.3 2.25 ± 0.36 MD 23 235 ± 28 3.8 t 0.45 3.9 ± 0.5 No 13 CD 23 87±4.6 41 10 55 ± 10.5 MD 21.2 1027 79 179 ± 25 187 ± 29 13.8 ± 2.4 No 14 CD 22.7 608 ± 11 192 ± 8 196 ± 10 8.1 0.45 MD 23.2 679 ± 76 3.9 ± 0.1 51.7 ± 16 2.7 ± 0.9 No 15 CD 25.3 314 ± 15 58.3± 16 68.1 ± 16 1.8± 0.5 MD 23 310 39 4.5 0.4 7.6 ± 3.4 No 16 CD 23 79 ± 4.3 5.33 3.6 18 ± 4.5 MD 21.7 804 ± 30 4.1 ± 0.13 61.4 17 3.95i 1.21 No 17 CD 23.8 417 ± 17 110 13 122 18 4.0 0.73 MD 22.2 805 ± 48 4.3 0.3 61.2 21.7 3.8 1.4 No 18 CD 22.2 429 ± 13 92 10 104 10 3.7 0.42 As indicated, the meltblown web made from PLA alone gave loose fine fibers without strength in either the MD or CD direction (web sample 10). 10 Meltblown webs made from PLA modified with PPG gave weak strength in both MD and CD (web sample 13). Meltblown webs made from PLA modified with PEG-PPG-PEG with a low PEG/PPG ratio also gave a relatively weak strength, but the strength increased significantly from PLA modified with PEG-PPG-PEG block copolymers with increasing PEG/PPG ratios (e.g., web sample 18 versus 15 web samples 15 and 16). Meltblown webs made from PLA modified with PEG-ran PPG were very strong in both the MD and CD. The energy to break was also much higher than those from PLA alone or PLA modified with PPG (e.g., web sample 14 versus web sample 10 and 13). 31 WO 2009/078849 PCT/US20071087339 EXAMPLE 3 Meltblown web samples obtained from Example 2 were used for accelerated or stressed aging study. The webs were placed in an aging chamber with a temperature of 550C and without humidity control for one week, or with a 5 temperature of 40'C and 75% relative humidity condition for I month. The tensile properties of aged meltblown webs were analyzed as described above. The results are shown below in Table 7. Table 7 Tensile properties of aged meltblown webs from modified PLA resins with polyether copolymers Samples Peak Load (gf) Strain at Peak (%) % Strain at Break MD 809 * 64 4.4 0.24 51 14.5 No 12 CD 418± 12 5.2 0.4 67 9.3 1 week aged MD 778± 59 11.4 ±3.8 14.4± 3.5 No 12 CD 496 ± 22 23.8 5.6 25.5 ± 5.8 1 Month MD 770 105 3.6 ± 0.6 4.2 ± 1.2 aged No 12 CD 433 34 3.5 ± 0.6 3.6 ± 0.7 MD 1027 79 179 25 187 ±29 No14 CD 608 11 192 8 196± 10 1 week aged MD 1133 110 46.3 6.4 50 ± 6 No 14 CD 754 21 79 ±6.1 82± 5.9 MD 805 48 4.3 ± 0.3 61.2 ±21.7 No18 CD 429 13 92 ±10 104 ±10 1 Month MD 670 77 12.5 ± 0.13 17 ± 2 aged No 18 CD 572 31 4± 0.4 11 ±2.5 10 It was observed that the tensile strength of the 1-week aged Sample 14, which was modified with PEG-ran-PPG copolymer, had a much higher strain at break than those of the 1-week aged Sample 12, which was modified with PEG 8000. Similarly, the tensile strength of the 1 -month aged Sample 18, which was modified with PEG-PPG-PEG 8400 copolymer, had a much higher strain at break 15 than those of the 1-month aged Sample 12, which was modified with PEG-8000. While the invention has been described in detail with respect to the specific embodiments thereof, it will be appreciated that those skilled in the art, upon attaining an understanding of the foregoing, may readily conceive of alterations to, variations of, and equivalents to these embodiments. Accordingly, the scope of 20 the present invention should be assessed as that of the appended claims and any equivalents thereto. 32

Claims (20)

1. A biodegradable fiber for use in forming a nonwoven web, the fiber being formed from a thermoplastic composition comprising at least one polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the polyether copolymer comprises from about 40 mol.% to about 95 mol.% of a repeating unit (A) having the following formula: C 2 H 4 0 (A) wherein, x is an integer from 1 to 250, the polyether copolymer further comprising from about 5 mol.% to about 60 mol.% of a repeating unit (B) having the following formula: CnH 2 nO (B) wherein, n is an integer from 3 to 20; and y is an integer from 1 to 150.

2. The biodegradable fiber of claim 1, wherein the polylactic acid comprises monomer units derived from L-lactic acid, D-lactic acid, meso-lactic acid, or mixtures thereof; wherein the polylactic acid is a copolymer that comprises monomer units derived from L-lactic acid and monomer units derived from D-lactic acid; or wherein the polylactic acid has a glass transition temperature from about 200C to about 800C.

3. The biodegradable fiber of claim 1 or claim 2, wherein the polylactic acid constitutes from about 80 wt.% to about 98 wt.% of the thermoplastic composition.

4. The biodegradable fiber of any one of the preceding claims, wherein n is an integer from 3 to 5; or 33 wherein the repeating unit (B) is derived from a monomer selected from the group consisting of 1,2-propanediol; 1,3-propanediol; 1,4-butanediol; 2,3 butanediol; 1,5-pentanediol; 1,6-hexanediol; 1,9-nonanediol; 2-methyl-1,3 propanediol; neopentyl glycol; 2-methyl-1,4-butanediol; 3-methyl-1,5-pentanediol; 3-oxa-1,5-pentanediol; or a combination thereof.

5. The biodegradable fiber of any one of the preceding claims, wherein the repeating unit (B) is derived from 1,2-propanediol.

6. The biodegradable fiber of any one of the preceding claims, wherein the polyether copolymer has the following general structure: A C 2 H 4 0 CnH2n C 2 H 4 0 B wherein, x is an integer from 1 to 250; y is an integer from 1 to 150; z is an integer from 0 to 200; n is an integer from 3 to 20; A is hydrogen, an alkyl group, an acyl group, or an aryl group of 1 to 10 carbon atoms, and B is hydrogen, an alkyl group, an acyl group, or an aryl group of 1 to 10 carbon atoms.

7. The biodegradable fiber of claim 6, wherein A is hydrogen, B is hydrogen, and z is an integer from 2 to 125.

8. The biodegradable fiber of any one of the preceding claims, wherein the repeating unit (A) constitutes from about 50 mol.% to about 90 mol.% of the copolymer and the repeating unit (B) constitutes from about 10 mol.% to about 50 mol.% of the copolymer; or wherein the repeating unit (A) has a number average molecular weight of 500 to about 10,000 and the repeating unit (B) has a number average molecular weight of from about 100 to about 2,000, the number average molecular weight of the polyether copolymer further ranging from about 600 to about 10,000.

9. The biodegradable fiber of any one of the preceding claims, wherein the thermoplastic composition has a glass transition temperature of about 600C or less; or 34 wherein the thermoplastic composition has a glass transition temperature of from about 10 C to about 550C.

10. A nonwoven web comprising biodegradable fibers, the fibers being formed from a thermoplastic composition comprising at least one polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the polyether copolymer comprises from about 40 mol.% to about 95 mol.% of a repeating unit (A) having the following formula: C 2 H 4 0 (A) wherein, x is an integer from 1 to 250, the polyether copolymer further comprising from about 5 mol.% to about 60 mol.% of a repeating unit (B) having the following formula: (B) wherein, n is an integer from 3 to 20; and y is an integer from 1 to 150.

11. The nonwoven web of claim 10, wherein the web is a meltblown web, spunbond web, or a combination thereof; or wherein the web is a carded web.

12. An absorbent article comprising the nonwoven web of claim 10 or claim 11.

13. A method for forming a nonwoven web, the method comprising: melt extruding a thermoplastic composition that comprises at least one polylactic acid in an amount from about 75 wt.% to about 99 wt.% and at least one polyether copolymer in an amount from about 1 wt.% to about 25 wt.%, wherein the polyether copolymer comprises from about 40 mol.% to about 95 mol.% of a 35 repeating unit (A) having the following formula: C 2 H 4 0 (A) wherein, x is an integer from 1 to 250, the polyether copolymer further comprising from about 5 mol.% to about 60 mol.% of a repeating unit (B) having the following formula: CnH2nOy (B) wherein, n is an integer from 3 to 20; and y is an integer from 1 to 150; and randomly depositing the extruded thermoplastic composition onto a surface to form a nonwoven web.

14. The method of claim 13, wherein the polylactic acid constitutes from about 80 wt.% to about 98 wt.% of the thermoplastic composition.

15. The method of claim 13 or claim 14, wherein the repeating unit (B) is derived from a monomer selected from the group consisting of 1,2-propanediol; 1,3-propanediol; 1,4-butanediol; 2,3-butanediol; 1,5-pentanediol; 1,6-hexanediol; 1,9-nonanediol; 2-methyl-1,3-propanediol; neopentyl glycol; 2-methyl-1,4 butanediol; 3-methyl-1,5-pentanediol; 3-oxa-1,5-pentanediol; or a combination thereof.

16. The method of any one of claims 13-15, wherein the repeating unit (A) constitutes from about 50 mol.% to about 90 mol.% of the copolymer and the repeating unit (B) constitutes from about 10 mol.% to about 50 mol.% of the copolymer.

17. The method of any one of claims 13-16, wherein the thermoplastic composition has a glass transition temperature of about 600C or less; or 36 wherein the thermoplastic composition has a glass transition temperature of from about 10 C to about 55*C.

18. The method of any one of claims 13-17, wherein melt extruding occurs at a temperature of from about 100 C to about 500 0 C and an apparent shear rate of from about 100 seconds- to about 10,000 seconds-.

19. The method of any one of claims 13-18, wherein the thermoplastic composition is melt extruded through a meltblowing die.

20. The biodegradable fiber of any one of claims 1-9, the nonwoven web of claim 10 or claim 11, the absorbent article of claim 12 or the method of any one of claims 13-19 substantially as herein described and/or illustrated with reference to any one of the embodiments. 37